    1) Dichtol WFT Standard #1532 can be applied by dipping, brushing, injecting, or spraying at a surface temperature of up to 40°C. 2) Curing time varies from 4 to 30 minutes depending on wall thickness, with lighter loads possible after 6 to 24 hours and full loads after 24 to 48 hours. 3) It provides pore sizes of 0.1mm or less and can withstand continuous temperatures between -40°C and +300°C, or short term temperatures up to +450°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Dichtol WFT Standard 1532 en 1

    Uploaded by

    unknown unexplained
    212 views2 pages
    1) Dichtol WFT Standard #1532 can be applied by dipping, brushing, injecting, or spraying at a surface temperature of up to 40°C. 2) Curing time varies from 4 to 30 minutes depending on wall thickness, with lighter loads possible after 6 to 24 hours and full loads after 24 to 48 hours. 3) It provides pore sizes of 0.1mm or less and can withstand continuous temperatures between -40°C and +300°C, or short term temperatures up to +450°C.

    Original Description:

    Sealer

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    1) Dichtol WFT Standard #1532 can be applied by dipping, brushing, injecting, or spraying at a surface temperature of up to 40°C. 2) Curing time varies from 4 to 30 minutes depending on wall thickness, with lighter loads possible after 6 to 24 hours and full loads after 24 to 48 hours. 3) It provides pore sizes of 0.1mm or less and can withstand continuous temperatures between -40°C and +300°C, or short term temperatures up to +450°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    212 views2 pages

    Dichtol WFT Standard 1532 en 1

    Uploaded by

    unknown unexplained
    1) Dichtol WFT Standard #1532 can be applied by dipping, brushing, injecting, or spraying at a surface temperature of up to 40°C. 2) Curing time varies from 4 to 30 minutes depending on wall thickness, with lighter loads possible after 6 to 24 hours and full loads after 24 to 48 hours. 3) It provides pore sizes of 0.1mm or less and can withstand continuous temperatures between -40°C and +300°C, or short term temperatures up to +450°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    Technical data dichtol WFT Standard #1532

    Application
    dip x
    brush x
    inject x
    spray x
    Surface temperature for application
    40°C
    [max.]
    Exposure time [min.]
    up to 5 mm wall thickness 4
    5 - 10 mm wall thickness 8
    10 - 15 mm wall thickness 13
    > 15 mm wall thickness 30
    Curing at + 20°C [hours]
    light (full)
    load-bearing capacity
    Surface drying [min.] 6
    up to 5 mm wall thickness 6 (24)
    5 - 10 mm wall thickness 10 (24)
    10 - 15 mm wall thickness 17 (48)
    > 15 mm wall thickness 24 (48)
    Technical data
    Pore size [mm] 0 - 0.1
    Continuous temperature resistance
    -40 / +300
    [°C]
    Short-term. Temperature resistance
    -40 / +450
    [°C]
    Viscosity DIN4 cup, + 23°C
    13
    ISO 2431 (4 mm nozzle) [sec.]
    Remaining
    3
    Surface layer thickness [μm]

    All material values ​​are average values ​​and vary due to the mixing ratio, the amount
    of material and the environmental conditions. The values ​​stated are based on testing
    under normal conditions (STP) + 20°C and 1013 mbar.
    Resistance list
    Chemicals Conc. in % WFT Standard
    acetate ─
    acetylene x
    alkanes x
    alcohols x
    animal based oils x
    brake oil x
    citric acid ○
    crude oil x
    cutting oil x
    diesel fuels x
    diethyl ether ─
    engine oil x
    glycol x
    hydraulic fluid x
    hydrocarbons x
    aromatics x
    hydrochloric acid < 20 ─
    hydrochloric acid > 20 ○
    keton ─
    kerosene x
    lubricating oil x
    machine oil x
    machinefat x
    natural gas x
    nitric acid ○
    petrol x
    phthalates ○
    plantbase oils x
    potassium chloride, hs x
    potassium hydroxide x
    potassium phosphate x
    salicylic acid ○
    sulphuric acid < 20 ─
    sulphuric acid > 20 ○
    Nomenclature: hs = aqueous solution / conc. = Concentration
    Symbols: x = stable / ○ = conditionally stable / ─ = unstable
    The measurements were carried out at a temperature of 20°C.
    Individual examinations can be carried out after consultation.