Unbrako US Product Guide PDF
Unbrako US Product Guide PDF
Unbrako US Product Guide PDF
PRODUCT
GUIDE
INDUSTRIAL FASTENERS
Socket Screws 13
Pins 79
Wrenches and Tools 89
®
Durlok 97
Technical Section 105
www.unbrakousa.com
Manufacturing Unit
Warehouse
UNBRAKO AUSTRALIA
Deepak Fasteners Australia Ltd., 67-69 Licola
Crescent Dandenong South Victoria 3175, Australia
Tel: +61-3-98940026, Fax: +61-3-98940038
UNBRAKO EUROPE
Note: The proper tightening of threaded fasteners
Deepak Fasteners Shannon Ltd., Bays 25-30
can have a significant effect on their performance.
Shannon Industrial Estate, County Clare, Ireland
Many application problems such as self-loosening
Tel: +353-61-716-500, Fax: +353-61-716-584
& fatigue can be minimized by adequate tightening.
The recommended seating torques listed in the
UNBRAKO INDIA catalog tables serve as guidelines only. Even when
Deepak Fasteners India Ltd., 4th Floor, First Mall, using the recommended seating toques, the induced
The Mall Ludhiana - 141001 (Pb.) India loads obtained may vary as much as ±25% depending
Tel: +91-161-3911111, 7131111, Fax: +91-161-2774400 upon the uncontrolled variables such as mating
material, lubrication, surface finish, hardness, bolt/joint
UNBRAKO UK compliance, etc. Performance data listed is for
Deepak Fasteners UK Ltd., 12-14 Tower Street, standard production items only. It is suggested that
New Town Birmingham - B19 3RR, U.K. the user verify performance for critical applications.
Tel: +44-121-333-4610, Fax: +44-121-333-4525
Pins
Dowel Pins 82 84
Pull-Out Dowel Pins – 87
Tools
Hexagon Wrenches 92 94
and Keys
International Certifications
Our production facilities are ISO 9001, ISO/TS 16949,
ISO 14001 and BS OHSAS 18001 Certified. Our
fasteners meet or exceed International Standards like
DIN, ISO, ASTM, IS, BS etc. We have expertise not only
ISO 9001:2008 AD 2000 ISO/TS 16949:2009 CE Certification
14399 & 15048 in standard products, but also in made-to-order
customized products.
Specialized Coatings
We excel in a variety of coatings, which are done in-house.
These are designed to provide required protection in
different environments, e.g. Hot Dip Galvanizing,
Mechanical Galvanizing, Electroplating (Zinc & Copper
Cadmium), PTFE Coating, Zinc-Al Flake Coating
(Geomet, Delta Protekt) and Unbrako Wiscoat Coating.
Unbrako excels in a variety of coatings done in-house, designed specifically to provide the required protection in
such harsh environment. Technical information of a few of these coatings is set out below:
ELECTROLYTIC
HOT-DIP METALLIC COATING
MAIN COATINGS COATINGS PTFE
GALVANISATION ZINC FLAKE
ZINC CADMIUM
Descaling with
Descaling with
Hydrogen inhibitor
inhibitor No risk process No risk process
embrittlement imperative baking
No risk process
for 100 Mpa steels
Thread Terminology
BEARING Pitch
FILLET SURFACE
BODY Crest
Major
Angle Diameter
nk
Pitch
Fla
Diameter
Minor
SHANK
Diameter
Root
Pitch/2
CREST
NOMINAL
The outermost tip of a male thread as seen in a thread
SIZE
profile.
BODY FLANK
The unthreaded portion of the shank of a threaded The thread surface connecting the crest with the root.
fastener.
BEARING SURFACE
FILLET The supporting or locating surface of a fastener with
Concave junction between the head and shank. respect to the part it fastens or mates.
SHANK ROOT
The portion of a headed fastener which lies between the The bottom area between the
head and the extreme end of the fastener. sides of two adjacent threads.
Yield
an
deformationoccurring.
FATIGUE LIFE
is the number of cycles of
fluctuating stress and strain
of a specified nature that a fastener will sustain before
failure occurs.
IMPACT TEST
A test to determine the energy absorbed in fracturing a
test bar at high velocity.
Carbon (C)
Although this is not considered to be an alloying element,
it is the most important component in steel. It improves
tensile strength, hardness and abrasion resistance. It
reduces ductility, rigidity and machining.
Manganese (Mn)
This is an oxidiser and degasifier and reacts with sulphur
to improve forgeability. It increases tensile strength,
hardness and durability.
Phosphorus (P)
This increases tensile strength and hardness and improves
machinability. It causes fragility in steel.
Sulphur (S)
Improves machining qualities in the presence of
manganese. It reduces weldability, impact, roughness,
and ductility.
Silicon (Si)
This is a deoxidiser and degasifier. It increases tensile
strength, elasticity, hardness and forgeability.
Chromium (Cr)
Increase breaking strength, hardness, durability,
roughness, and resistance to high temperatures.
Nickel (Ni)
This raises strength and hardness, while maintaining
ductility and rigidity. It increases resistance to cracking
and high temperatures.
Molybdenum (Mo)
This increases strength, hardness, durability, and rigidity,
together with resistance to creaking & to high temperatures.
Titanium (Ti)
This is used as a stabilising element in stainless steels.
It has a great affinity for carbon.
14
Head with increased bearing area
for greater load carrying capability.
Precision forged for symmetrical grain Total Traceability: Patented E-CODETM
flow, maximum strength. head marking system allows tracing of
test records to specific production batches
Specially designed
Elliptical fillet doubles fatigue life at
critical head-shank juncture.
Socket Set Screws Fasten collars, sheaves, gears, knobs on shafts. Locate machine
(Grub Screws) parts. Self-locking knurled cup point is standard. Special Points
Alloy / Stainless like Flat, Dog, Cone & Plain Cup are also available.
Flat Head Countersunk Controlled angle under the head ensures maximum flushness
Socket Screws and side wall contact. Non-slip Hex socket prevents marring of
Alloy / Stainless material.
15
Socket Head Cap Screws Metric
Micro Series - M1.4 to M2.6
A
H L
HIGH-GRADE ALLOY STEEL
130° da
min
16
Socket Head Cap Screws Metric
M3 to M48
A H L
W F
17
Socket Head Cap Screws - Metric
• LG is the maximum grip length and is the distance from the bearing surface to the first complete thread.
• LB is the minimum body length and is the length of the unthreaded cylindrical portion of the shank.
• Dimensions for LB and LG are calculated from the following formula:
LG
T Ref = (2x Nominal Dia) plus 12mm.
LB
LG max = Nominal length “L” minus “T”
LB min = Nominal length “L” minus (T + 5 pitches)
L LB LG LB LG LB LG LB LG LB LG LB LG LB LG LB LG LB LG
Nom. (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.)
25 4.5 7
30 9.5 12 6.5 10 4 8
35 11.5 15 9 13 6 11
40 16.5 20 14 18 11 16 5.75 12
45 19 23 16 21 10.75 17 5.5 13
50 24 28 21 26 15.75 22 10.5 18
55 26 31 20.75 27 15.5 23 10.25 19
60 31 36 25.75 32 20.5 28 15.25 24 10 20
65 30.75 37 25.5 33 20.25 29 15 25 11 21
70 35.75 42 30.5 38 25.25 34 20 30 16 26
80 45.75 52 40.5 48 35.25 44 30 40 26 36
90 50.5 58 45.25 54 40 50 36 46
100 Length ‘L’ Tolerance (mm) 60.5 68 55.25 64 50 60 46 56
110 Screws Up to and 65.25 74 60 70 56 66
Over including Tolerance
120 75.25 84 70 80 66 76
- 50 ±0.25
130 80 90 76 86
50 80 ±0.50
140 90 100 86 96
80 120 ±0.71
150 96 106
120 250 ±0.79
160 106 116
250 - ±1.02
180
Length M18 M20 M22 M24 M27 M30 M33 M36 M42
LB LG LB LG LB LG LB LG LB LG LB LG LB LG LB LG LB LG
Nom. (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.) (Min.) (Max.)
70 9.5 22
80 19.5 32 15.5 28 11.5 24
90 29.5 42 25.5 38 21.5 34 15 30
100 39.5 52 35.5 48 31.5 44 25 40 19 34
110 49.5 62 45.5 58 41.5 54 35 50 29 44 20.5 38 14.5 32
120 59.5 72 55.5 68 51.5 64 45 60 39 54 30.5 48 24.5 42 16 36
130 69.5 82 65.5 78 61.5 74 55 70 49 64 40.5 58 34.5 52 26 46
140 79.5 92 75.5 88 71.5 84 65 80 59 74 50.5 68 44.5 62 36 56 21.5 44
150 89.5 102 85.5 98 81.5 94 75 90 69 84 60.5 78 54.5 72 46 66 31.5 54
160 99.5 112 95.5 108 91.5 104 85 100 79 94 70.5 88 64.5 82 56 76 41.5 64
180 119.5 132 115.5 128 111.5 124 105 120 99 114 90.5 108 84.5 102 76 96 61.5 84
200 135.5 148 131.5 144 125 140 119 134 110.5 128 104.5 122 96 116 81.5 104
220 151.5 164 145 160 139 154 130.5 148 124.5 142 116 136 101.5 124
240 165 180 159 174 150.5 168 144.5 162 136 156 121.5 144
260 179 194 170.5 188 164.5 182 156 176 141.5 164
280 190.5 208 184.5 202 176 196 161.5 184
18
Socket Head Cap Screws - Metric
M2 (0.4) - Key Size 1.5mm M5 (0.8) - Key Size 4mm M8 (1.25) - Key Size 6mm
M2 x 3 104151 200 30.44 0.44 M5 x 10 122243 200 17.94 6.69 M8 x 10 103056 200 23.69 22.31
4 104152 200 46.95 0.48 12 121094 200 16.94 7.22 12 114972 200 24.03 23.61
5 104154 200 48.73 0.53 14 400513 200 17.94 7.74 14 400524 200 24.36 24.99
6 104155 200 58.33 0.57 15 400510 200 17.94 8.03 15 400514 200 24.36 25.74
8 104157 200 61.12 0.64 16 103024 200 17.94 8.29 16 103058 200 24.36 26.42
10 104159 200 63.39 0.73 18 400522 200 20.30 8.82 18 400569 200 26.43 27.81
12 106216 200 65.92 0.81 20 113970 200 19.35 9.35 20 122086 200 26.43 29.19
22 400523 200 23.10 9.88 22 120642 200 29.12 30.49
M2.5 (0.45) - Key Size 2mm 25 121096 200 22.03 10.67 25 119351 200 29.12 32.63
M2.5 x 5 104161 200 51.34 0.77 30 103029 200 24.54 12.32 30 119383 200 31.20 36.08
6 104162 200 52.60 0.95 35 115292 200 28.53 13.95 35 122113 200 33.69 39.51
8 104163 200 53.36 1.08 40 103030 200 29.12 15.58 40 113143 200 35.07 43.65
10 104164 200 55.30 1.21 45 103031 200 32.78 17.20 45 121076 200 37.63 48.55
12 104166 200 56.49 1.32 50 103035 200 35.62 18.83 50 121068 100 41.46 52.07
55 103038 200 41.88 20.48 55 103063 100 51.60 56.30
M3 (0.5) - Key Size 2.5mm 60 103040 200 45.38 22.11 60 121070 100 54.81 60.50
M3 x 5 106218 200 27.45 1.50 65 106225 200 46.46 23.74 65 103064 100 66.23 65.45
6 103002 200 27.45 1.58 70 106228 200 48.89 25.37 70 103066 100 75.65 69.67
10 113583 200 19.10 1.96 75 103069 100 87.69 73.90
12 120870 200 19.77 2.13 80 103070 100 99.69 78.12
14 400509 200 20.05 2.33 90 103073 100 109.13 86.55
15 400506 200 20.05 2.42 M6 (1) - Key Size 5mm 100 103075 100 128.55 94.60
16 103003 200 20.18 2.51 M6 x 8 103042 200 23.53 9.57 110 103076 100 140.57 103.44
20 113623 200 21.11 2.88 10 122111 200 18.81 10.32 120 103077 100 187.04 111.89
25 103010 200 25.28 3.34 12 120872 200 19.67 11.07 130 106230 100 206.22 120.34
30 103013 200 30.28 3.94 14 400567 200 20.53 11.84 140 106231 100 230.41 127.95
35 106219 200 34.78 4.51 15 400512 200 20.53 11.84 150 106232 100 348.05 143.00
16 103044 200 20.53 12.21 160 106233 50 540.32 144.83
18 103045 200 22.08 13.35 180 106234 50 594.10 162.56
M4 (0.7) - Key Size 3mm 20 119790 200 21.44 14.15 200 106235 50 786.92 179.43
M4 x 5 106220 200 19.94 3.06 22 103046 200 24.36 14.85
6 106223 200 19.94 3.21 25 119937 200 24.36 16.04 M10 (1.5) - Key Size 8mm
8 113810 200 16.94 3.54 30 122121 200 27.19 17.93 M10 x 10 106236 200 86.88 39.34
10 113839 200 16.94 3.87 35 121090 200 31.04 20.61 12 106237 200 84.90 41.65
12 121077 200 17.94 4.22 40 121075 200 32.46 22.99 15 400525 200 48.10 44.75
14 400568 200 18.27 4.53 45 122087 200 33.21 25.37 16 103080 200 36.42 45.83
15 400511 200 18.27 4.58 50 112624 200 36.28 27.74 18 400526 200 36.67 48.00
16 103014 200 18.27 4.86 55 113128 200 47.64 30.10 20 113163 200 36.67 50.16
18 103015 200 19.51 5.21 60 122088 200 51.05 32.47 25 115060 200 38.86 55.57
20 125753 200 19.51 5.54 65 103047 200 55.72 34.85 30 122114 200 42.32 61.23
22 400521 200 24.95 5.87 70 103048 200 61.15 37.20 35 113257 200 44.93 86.37
25 125381 200 24.95 6.36 75 103049 200 68.24 39.58 40 100845 100 47.04 72.09
30 103018 200 24.95 7.39 80 103051 200 72.17 41.95 45 121088 100 52.44 78.45
35 103019 200 25.10 8.43 90 103052 200 80.01 46.68 50 125660 100 54.20 85.07
40 103021 200 29.36 9.46 100 103053 200 97.36 51.41
Pieces per Box Sizes above the bold line are threaded to head.
Property Class: 12.9 19
Socket Head Cap Screws - Metric
M10 (1.5) - Key Size 8mm M14 (2) - Key Size 12mm M18 (2.5) - Key Size 14mm
M10 x 55 103087 100 66.01 93.02 M14 x 35 400530 50 283.65 140.36 M18 x 90 400550 25 772.47 486.6
60 122217 100 71.06 98.32 40 400531 50 309.29 151.14 100 400551 25 1283.24 532.2
65 103088 100 83.37 104.94 45 400532 50 338.50 161.90 120 400552 25 2558.57 618.6
70 125786 100 90.96 112.90 50 120863 50 350.52 172.68
75 103090 100 102.76 119.55 55 400533 50 395.20 183.46 M20 (2.5) - Key Size 17mm
80 103091 100 119.79 126.17 60 112000 50 410.68 196.48 M20 x 30 107465 25 326.63 329.4
90 103094 50 137.07 126.48 65 400534 50 451.05 209.48 35 107466 25 332.58 352.1
100 103095 50 163.38 137.35 70 400535 50 478.98 227.46 40 103130 25 337.44 374.7
110 103096 50 174.58 164.56 75 400536 50 562.74 235.53 45 103131 25 350.79 397.3
120 103097 50 198.35 179.26 80 400537 50 579.92 248.56 50 103132 25 363.80 420.0
130 106240 50 219.82 192.52 90 400538 50 591.08 274.58 55 103136 25 381.74 442.7
140 106241 50 246.63 212.08 100 400539 50 629.32 300.63 60 103137 25 401.47 465.3
150 106242 50 288.98 225.94 110 400540 50 781.81 326.66 65 103138 25 423.43 487.9
160 106243 50 402.60 239.80 120 400508 50 841.95 352.10 70 103141 25 438.88 510.6
180 106244 50 602.02 258.85 75 103142 25 452.14 537.3
200 106245 50 829.66 285.38 M16 (2) - Key Size 14mm 80 103143 25 470.01 563.9
220 400517 25 1251.16 311.92 M16 x 25 106248 25 159.75 169.7 90 103144 25 501.22 617.2
30 103112 25 159.75 184.1 100 103145 25 832.63 670.5
M12 (1.75) - Key Size 10mm 35 103113 25 168.22 199.1 110 103146 25 862.23 723.8
M12 x 12 106246 100 157.52 60.24 40 125751 25 177.11 213.6 120 103148 25 1650.70 777.1
16 106247 100 144.90 66.53 45 103115 25 185.25 228.1 130 103150 10 1684.14 826.8
20 112607 100 76.24 72.82 50 112474 25 194.99 242.0 140 103151 10 1724.18 880.0
25 122250 100 79.74 80.67 55 103117 25 208.32 256.5 150 103152 10 1791.08 934.3
30 122251 100 88.77 88.55 60 112594 25 226.02 271.0 160 107462 10 1817.78 990.2
35 125530 100 97.68 96.40 65 103118 25 242.30 288.0 180 107463 10 1884.60 1096.8
40 114996 50 99.02 104.28 70 103119 25 249.35 305.0 200 107464 5 2085.23 1203.3
45 115075 50 108.70 112.13 75 103120 25 262.78 322.1 220 400553 5 3451.80 1321.5
50 112360 50 114.88 119.90 80 125658 25 276.37 339.2 240 400554 5 3745.40 1428.2
55 122255 50 127.38 129.58 90 103122 25 310.77 371.8 260 400555 5 4049.10 1534.9
60 122260 50 130.47 139.48 100 103123 25 332.25 407.3 280 400556 5 4302.17 1641.9
65 122261 50 147.74 152.13 110 103124 25 366.14 441.4 300 400557 5 4554.76 1748.4
70 103098 50 153.08 158.14 120 103126 25 417.83 475.5 340 796973 5 5167.80 1960.30
75 103099 50 165.01 171.23 130 103127 25 470.51 509.6 M22 (2.5) - Key Size 17mm
80 103100 50 177.02 180.77 140 103128 25 496.10 541.2 M22 x 80 180186 10 1770.90 739.2
90 103103 50 191.04 196.26 150 103129 25 521.94 577.8 90 180187 10 1888.41 805.2
100 122142 50 218.15 218.97 160 103364 25 1444.67 609.4 100 180188 10 3137.14 871.2
110 125791 50 259.61 238.06 180 107460 25 1452.47 679.1 110 180189 10 3248.71 937.2
120 103104 50 273.55 253.48 200 107448 25 1640.78 748.2 140 180192 10 6533.47 1135.2
130 103107 50 291.56 272.54 300 400578 5 3024.16 1096.5
140 103108 50 314.33 291.61 M24 (3) - Key Size 19mm
150 103110 50 337.19 310.68 M18 (2.5) - Key Size 14mm M24 x 40 106249 10 1691.09 594.0
160 107456 50 354.05 334.40 M18 x 35 400541 25 512.55 272.8 45 103153 10 1565.62 627.0
180 107458 50 427.79 367.88 40 400542 25 520.06 290.8 50 103155 10 1458.69 672.7
200 107459 50 590.17 406.01 45 400606 25 540.62 308.8 55 103157 10 1714.78 705.7
260 400572 25 1470.46 524.48 50 100844 25 560.67 326.0 60 103158 10 1483.67 738.1
60 400544 25 619.01 362.9 65 103159 10 1503.70 770.7
M14 (2) - Key Size 12mm 65 400545 25 652.60 380.9 70 103160 10 1523.80 801.8
M14 x 25 400528 50 283.65 118.82 70 400546 25 676.40 402.6 75 103161 10 1585.25 836.0
30 400529 50 283.65 129.60 80 400549 25 724.37 445.7 80 103162 10 1563.85 868.7
Pieces per Box Sizes above the bold line are threaded to head.
20 Property Class: 12.9
Socket Head Cap Screws - Metric
$Price lbs.
Size Part No.
/100 /1000
Threaded to Head
H
F G
T
HIGH-GRADE ALLOY STEEL
A da B
U 190
‘X’ represents Lot
X X
Traceability E-CODE
22
Socket Head Cap Screws - 1960 series Inch
5/8 to 3 - UNRC/UNRF
H
F G
T
23
Socket Head Cap Screws - 1960 series
Body and Grip Lengths
LG
LB
HIGH-GRADE ALLOY STEEL
24
Socket Head Cap Screws - 1960 series
Body and Grip Lengths
LG
LB
25
Socket Head Cap Screws - 1960 Series
#0-80 UNF - Key Size 0.05” #6-32 UNC - Key Size 7/64” #10-24 UNC - Key Size 5/32”
#0 x 3/16 117137 100 43.13 0.17 #6 x 3/8 113440 100 17.44 2.42 #10 x 1 3/4 103248 100 27.82 14.96
1/4 117153 100 43.38 0.18 1/2 118792 100 17.79 2.86 2 103264 100 30.09 16.94
3/8 121059 100 43.54 0.22 5/8 118808 100 18.20 3.30 2 1/4 108823 100 39.46 19.12
3/4 118824 100 18.87 3.61 2 1/2 106226 100 41.72 20.83
#1-72 UNF - Key Size 1/16” 7/8 118840 100 20.97 4.00 2 3/4 103477 100 136.99 23.01
#1 x 1/4 117202 100 40.38 0.36 1 118856 100 22.58 4.38 3 106355 100 140.76 24.46
3/8 102704 100 40.38 0.45 1 1/4 112179 100 31.06 5.68 3 1/2 116278 100 159.93 28.38
1 1/2 114328 100 34.12 6.45 4 116279 100 181.76 32.34
#2-56 UNC - Key Size 5/64”
#2 x 3/16 105493 100 30.28 0.47 #6-40 UNF - Key Size 7/64” #10-32 UNF - Key Size 5/32”
1/4 105509 100 31.71 0.58 #6 x 1/4 102720 100 19.07 2.09 #10 x 1/4 111756 100 25.54 4.80
3/8 113307 100 31.78 0.75 3/8 111564 100 18.27 2.53 5/16 116280 100 25.54 5.30
1/2 113323 100 32.87 0.93 1/2 111581 100 18.86 2.79 3/8 117733 100 16.10 5.50
5/8 700572 100 41.00 1.05 5/8 111597 100 19.19 3.19 1/2 117749 100 16.45 6.25
3/4 700573 100 49.30 1.18 3/4 114012 100 21.36 3.56 5/8 117765 100 17.68 7.00
1 700574 100 65.74 1.44 1 700842 100 37.72 4.22 3/4 117781 100 18.63 7.70
7/8 117798 100 19.87 8.45
#8-32 UNC - Key Size 9/64” 1 117814 100 21.78 9.20
#3-48 UNC - Key Size 5/64” #8 x 1/4 118872 100 14.70 3.08 1 1/4 117830 100 23.63 11.79
#3 x 1/4 113374 100 16.91 0.80 5/16 117320 100 39.87 3.63 1 1/2 117847 100 26.07 13.07
3/8 107750 100 17.14 0.98 3/8 118888 100 14.27 3.96 1 3/4 117863 100 29.04 14.96
1/2 107766 100 17.50 1.22 1/2 118904 100 15.01 4.53 2 117879 100 32.02 16.94
5/8 700581 100 17.89 1.47 5/8 118920 100 15.51 4.84 2 1/4 107085 100 44.00 19.54
3/4 700582 100 21.38 1.71 3/4 118936 100 16.51 5.50 2 1/2 107150 100 47.94 21.12
7/8 103140 100 17.77 6.20 3 107182 100 57.92 25.01
1 103156 100 19.44 6.69
#4-40 UNC - Key Size 3/32” 1 1/4 103174 100 22.68 8.12 1/4-20 UNC - Key Size 3/16”
#4 x 1/4 107783 100 16.60 1.21 1 1/2 103190 100 24.20 9.66 1/4 x 1/4 120048 100 19.07 9.00
3/8 107799 100 16.77 1.50 1 3/4 117451 100 37.77 11.18 3/8 105232 100 15.18 10.30
1/2 107816 100 17.35 1.72 2 117516 100 31.78 12.39 1/2 105248 100 16.60 11.59
5/8 107832 100 17.60 1.96 2 1/4 120791 100 115.71 15.29 5/8 108937 100 17.69 12.89
3/4 107849 100 18.44 2.27 3/4 108954 100 18.01 14.19
1 109394 100 25.10 2.88 #8-36 UNF - Key Size 9/64” 7/8 108969 100 19.10 15.49
1 1/4 120922 100 59.88 3.43 #8 x 3/8 700845 100 21.58 3.51 1 105256 100 21.44 16.72
1 1/2 109070 100 59.88 4.20 1/2 117699 100 24.70 4.40 1 1/4 105272 100 23.12 19.36
5/8 700847 100 30.00 4.78 1 3/8 117409 100 111.46 20.72
3/4 117715 100 36.00 5.54 1 1/2 105288 100 25.53 22.77
#5-40 UNC - Key Size 3/32” 1 700849 100 48.00 6.16 1 3/4 105304 100 27.62 26.16
#5 x 1/4 107865 100 16.51 1.61 2 105320 100 30.03 29.48
5/16 112658 100 17.18 1.76 #10-24 UNC - Key Size 5/32” 2 1/4 105336 100 37.63 32.91
3/8 107881 100 17.18 1.94 #10 x 1/4 109734 100 25.54 4.80 2 1/2 118338 100 41.80 36.30
1/2 107897 100 17.18 2.27 3/8 103206 100 15.74 5.50 2 3/4 118355 100 50.31 39.67
5/8 113390 100 17.35 2.60 1/2 112492 100 15.74 6.25 3 118371 100 55.40 43.05
3/4 113407 100 18.68 2.97 5/8 112508 100 16.36 7.00 3 1/4 117539 100 62.41 46.46
1 112049 100 28.56 3.83 3/4 112524 100 17.68 7.70 3 1/2 117573 100 70.83 49.81
7/8 112540 100 18.72 8.45 3 3/4 117605 100 84.27 53.20
#6-32 UNC - Key Size 7/64” 1 112557 100 20.56 9.20 4 109434 100 92.94 57.35
#6 x 1/4 113423 100 17.18 1.98 1 1/4 103215 100 23.54 11.13 4 1/2 109499 100 140.57 64.11
5/16 109328 100 17.44 2.29 1 1/2 103232 100 24.93 13.07 5 114978 100 220.94 70.86
Pieces per Box Sizes above the bold line are threaded to head.
26
Socket Head Cap Screws - 1960 Series
Pieces per Box Sizes above the bold line are threaded to head.
27
Socket Head Cap Screws - 1960 Series
1/2-13 UNC - Key Size 3/8” 5/8-11 UNC - Key Size 1/2” 3/4-10 UNC - Key Size 5/8”
1/2 x 2 3/4 110903 25 129.47 182.16 5/8 x 1 3/4 116335 25 167.61 225.39 3/4 x 3 1/2 111689 25 447.69 550.00
3 120761 25 137.65 195.91 2 111036 25 170.51 241.30 3 3/4 111246 25 455.00 577.30
3 1/4 111303 25 148.24 212.08 2 1/4 111069 25 179.11 255.82 4 111722 25 475.54 623.02
3 1/2 111575 25 158.92 223.23 2 1/2 111101 25 188.79 287.76 4 1/2 104539 25 521.69 674.78
3 3/4 103111 25 175.36 241.87 2 3/4 116639 25 213.39 305.49 5 110759 25 568.42 746.46
4 111608 25 192.46 257.51 3 116673 25 222.24 323.09 5 1/2 110793 10 614.15 798.16
4 1/4 107772 25 314.68 264.18 3 1/4 116705 25 231.42 351.74 6 121562 10 660.29 869.66
4 1/2 111641 25 223.00 287.98 3 1/2 116737 25 243.18 369.69 6 1/2 110858 10 859.97 921.58
4 3/4 119162 25 492.02 293.99 4 102196 25 268.46 408.58 7 110891 10 969.88 993.08
5 111673 25 246.27 305.76 4 1/2 102047 25 345.37 451.64 8 110924 10 1212.94 1116.28
5 1/4 107805 25 518.14 316.29 5 120714 25 373.65 498.10 8 1/2 103863 10 2602.08 1168.20
5 1/2 115511 25 269.54 340.78 5 ½ 120746 10 393.43 544.50 9 107374 10 2613.90 1239.92
5 3/4 107839 25 603.90 346.08 6 120778 10 430.17 580.14 9 1/2 107438 10 2637.15 1291.62
6 115544 25 307.13 371.36 6 ½ 111320 10 615.70 626.56 10 118545 10 2780.79 1363.12
6 1/4 105005 10 935.23 375.98 7 111354 10 763.23 672.98 11 121572 10 2887.93 1486.54
6 1/2 115576 10 460.13 393.73 7 1/2 122898 10 2209.44 708.47 12 118610 10 2965.95 1609.96
7 109736 10 524.35 416.83 8 104175 10 906.80 755.04 13 108283 10 4093.48 1733.38
7 1/2 107937 10 1001.63 446.62 8 1/2 109197 10 2219.99 801.46
8 109768 10 1193.54 468.95 9 118276 5 2278.90 836.88 3/4-16 UNF - Key Size 5/8”
8 1/2 108003 10 1700.41 501.16 10 106599 5 2441.08 922.46 3/4 x1 1/4 700952 25 361.00 298.54
9 102417 10 1737.53 523.60 11 107003 5 2850.44 1015.52 1 1/2 120615 25 378.55 324.50
10 102451 10 1861.49 578.16 12 115134 5 3051.99 1110.12 2 120376 25 411.55 376.29
11 108275 10 2428.52 637.78 2 1/2 138871 25 449.33 428.12
12 105569 10 2802.38 692.34 5/8-18 UNF - Key Size 1/2” 3 102344 25 471.84 499.64
5/8 x 1 117868 25 161.14 170.32 3 1/2 117976 25 528.90 551.41
1/2-20 UNF - Key Size 3/8” 1 1/4 117884 25 200.60 188.10 4 118041 25 561.78 623.04
1/2 x 3/4 116247 50 127.29 88.11 1 1/2 117901 25 200.60 205.81 4 1/2 114043 25 664.22 674.78
1 104609 50 84.99 100.12 1 3/4 117918 25 230.64 223.52 5 116293 25 913.98 746.46
1 1/4 104625 50 93.34 107.80 2 117935 25 287.92 241.34 6 700962 10 1096.77 869.66
1 1/2 109763 50 102.59 118.80 2 1/4 105032 25 287.92 258.94
1 3/4 109780 50 109.75 130.17 2 1/2 117951 25 287.92 287.76 7/8-9 UNC - Key Size 3/4”
2 109796 50 120.99 141.24 3 105894 25 352.71 323.18 7/8 x 2 110957 10 508.26 559.37
2 1/4 122870 25 130.81 154.88 3 1/2 121385 25 417.50 369.60 2 1/4 116447 10 528.81 594.88
2 1/2 107220 25 140.36 168.63 4 117038 25 447.50 416.24 2 1/2 116479 10 566.51 630.52
2 3/4 111047 25 180.63 182.16 4 1/2 700946 25 457.56 462.00 2 3/4 116511 10 639.12 665.94
3 107237 25 174.96 195.91 5 119030 25 467.51 498.08 3 104568 10 678.22 701.36
3 1/2 116617 25 227.65 223.21 5 1/2 700948 10 535.00 544.50 3 1/4 104600 10 706.74 765.16
4 119272 25 242.35 257.51 6 107467 25 602.93 580.14 3 1/2 104632 10 761.42 800.58
4 1/2 700928 25 269.00 287.98 4 104665 10 854.23 899.80
5 116285 25 296.24 317.31 3/4-10 UNC - Key Size 5/8” 4 1/2 104697 10 941.97 968.00
5 1/2 700930 25 323.68 346.92 3/4 x 1 1/4 104210 25 242.63 298.54 5 104729 10 1030.41 1041.79
6 116286 25 351.11 364.76 1 1/2 104244 25 259.58 324.96 5 1/2 104761 10 1118.84 1140.92
7 700932 25 600.21 430.28 1 3/4 113859 25 276.45 350.46 6 104793 10 1206.59 1210.00
8 700933 25 814.00 484.00 2 113892 25 292.31 376.64 6 1/2 110251 10 1451.10 1311.20
2 1/4 113924 25 306.33 402.16 7 115937 10 1696.21 1382.26
5/8-11 UNC - Key Size 1/2” 2 1/2 113957 25 319.24 428.34 8 115970 10 1974.58 1552.32
5/8 x 1 109802 25 134.28 170.32 2 3/4 113990 25 374.45 453.93
1 1/4 109593 25 145.75 188.08 3 111623 25 399.37 499.64
1 1/2 109626 25 157.20 205.81 3 1/4 111656 25 423.35 525.54
Pieces per Box Sizes above the bold line are threaded to head.
28
Socket Head Cap Screws - 1960 Series
H -P E R F O RMANCE
1-8 UNC - Key Size 3/4” 1 1/4-12 UNF - Key Size 7/8” HIG S TEEL
A I N L E S S
1 X 1 1/2 102584 10 1534.20 698.72 1 1/4X 3 1/2 106603 1 5506.11 1912.90
ST RS
2 1/4
2 116002
116035
10
10
595.39
637.02
809.29
836.00
4 116291
4 1/2 108258
1 6065.74 2086.48
1 6571.00 2260.06
FASTENE
2 1/2 115091 10 676.91 887.04 5 109017 1 7075.63 2433.86
2 3/4 115123 10 716.80 932.80 5 1/2 116292 1 7580.25 2607.44
3 104702 10 751.88 887.13 6 107644 1 8085.51 2781.24
3 1/4 115189 10 786.17 1026.34 Unbrako Stainless Steel
3 1/2 114821 10 831.74 1113.66 1 1/2-6 UNC - Key Size 1” 304/316
4 114853 10 994.47 1160.52 1 1/2 X 3 110217 1 3506.35 2772.66
4 1/2 114888 10 1162.84 1301.39 3 1/2 110234 1 3767.29 2984.30 Range in
5 114920 10 1250.77 1424.08 4 110250 1 4003.88 3195.94
A2-70, A2-80, A4-70
5 1/2 103572 10 1370.80 1520.82 4 1/2 115919 1 4129.51 3407.58
6 103589 10 1491.07 1646.35 5 115936 1 4393.38 3715.36 A4-80, A4-90 & A4-100
6 1/2 103606 10 1868.37 1775.18 5 1/2 115953 1 4469.38 3965.39
7 103623 10 2106.21 1868.68 6 115969 1 4757.61 4215.42
7 1/2 100398 10 3022.73 1997.27 6 1/2 115985 1 4884.16 4465.34
nly
8 122961 10 2587.27 2090.88 7 116001 1 5185.06 4323.00
l Orders O
8 1/2 105063 10 3133.93 2219.58 8 116017 1 5662.17 4816.02 Specia
9 116867 10 3334.08 2313.08 9 116033 1 6646.47 5715.60
9 1/2 121557 10 3346.23 2441.78 10 116050 1 7228.23 6215.88
10 116899 10 3362.78 2535.50 12 116068 1 8390.97 7215.78
11 102035 5 4476.29 2757.70
12 104168 5 4559.30 2979.90 1 1/2-12 UNF Key Size 1”
14 121558 5 5325.79 3424.52 1 1/2 X 3 103034 1 8060.57 2772.66
3 1/2 116143 1 8675.85 2984.30
1-12 UNF Key Size 3/4” 4 110258 1 9291.11 3195.94
1 X 2 3/4 117604 10 1706.19 964.06 4 1/2 110290 1 9906.38 3407.58
3 1/2 109908 10 2027.03 1108.21 5 110697 1 10801.14 3715.36
5 1/2 105362 10 2840.95 1520.20 5 1/2 109136 1 11527.41 3965.28
6 116289 10 3011.18 1646.26 6 106106 1 12254.90 4215.42
8 105350 10 3824.44 2090.88 8 100447 1 14000.94 4816.02
10 114786 1 18070.57 6215.88
1 1/4-7 UNC - Key Size 7/8”
Note:
1 1/4 X 2 1/2 115451 1 2437.41 1596.98
• Sizes above the bold line are threaded to head.
3 115468 1 2587.20 1745.57 • The following diameters are fully interchangeable • Socket Head Cap Screws
3 1/2 121587 1 2597.88 1893.98 between 1936 and 1960 series:- • Socket Countersunk Head Screws
4 104842 1 2672.86 2086.48 No 10, 1/4", 3/8", 1/2" both UNC and UNF • Socket Button Head Screws
4 1/2 104857 1 3000.06 2136.29 • Hex Head Screws
5 112918 1 3014.65 2433.86 • Hex Nuts
5 1/2 104887 1 3232.72 2596.00 • Plain Washer
6 110103 1 3477.15 2781.13 • Spring Washer
6 1/2 110118 1 3552.16 2954.82 • Socket Set Screws
7 110136 1 3828.62 3124.00 • Threaded Rod
8 110152 1 4142.20 3475.78 • Specials
9 110168 1 5248.29 3822.94
www.unbrakousa.com
Pieces per Box
29
SOCKET THE WORLD LEADER
LOW HEAD
HIGH-GRADE ALLOY STEEL
CAP SCREWS
Low Head Socket Cap Screws Low Head Socket Head Cap Low Head Socket Head Cap
are High Strength, precision Screws cannot be pre-loaded as Screws are manufactured from
fasteners designed for high as a standard socket head High Strength Alloy Steel and
applications where head height cap screw because of their have a Black Oxide finish.
clearance is a problem. reduced head height and smaller
socket size.
Hardness : 40 - 43 HRC
33 - 39 HRC
W H
APPROX 45°
da THREAD
A
SIZE
1. Body and Grip Lengths are same as metric Recommended Seating Torque
Thread
Socket Head Cap Screws. (see page no.16) Unplated Plated Induced Load
size
2. Thread Class: 6g nom. N-m lbf.ln. N-m lbf.ln. kN Ibf.
3. Working Temperature: -50°C to +300°C M4 3.8 33.6 2.9 25.7 5.65 1,270
M5 8.0 70.8 6.0 53.1 9.20 2,068
4. Sizes M5 and larger are stamped U 10.9. M6 13.0 115.0 9.8 86.7 13.00 2,920
Torques calculated in accordance with M8 32.0 283.0 24.0 212.0 23.90 5,370
VDI 2230 “Systematic calculation of high M10 64.0 566.0 48.0 425.0 38.00 8,540
duty bolted joints” with σ 0.2 = 900 N/mm2 M12 110.0 974.0 83.0 735.0 55.50 12,470
and μ = 0.125 for plain finish and M16 275.0 2,434.0 206.0 1,820.0 105.00 23,600
μ = 0.094 for plated. M20 550.0 4,870.0 405.0 3,585.0 164.00 36,800
as per Unbrako standard
Screws Up to and
Over including Tolerance
- 50 ±0.25
50 80 ±0.50
80 120 ±0.70
120 250 ±0.80
250 - ±1.00
BRA K O
UN Head markings may vary slightly
depending on manufacturing practice.
UNBRAKO and UNB are recognized
identifications for M5 diameter & larger.
31
Socket Low Head Cap Screws Inch
See Note 1
W L
H
APPROX 45°
HIGH-GRADE ALLOY STEEL
F LG
LB
R THREAD
A B SIZE
ASME B18.3
Body Head Hex Head Fillet
Thread Thread Diameter Diameter Socket Size Height Extension
size per Inch B A W H R
nom. UNRC UNRF max max min nom. max min max min
Hardness RC 38-43
#8 32 36 0.1640 .270 .265 .0781 .085 .079 .012 .007
Tensile Stress 170,000 psi min.
#10 24 32 0.1900 .312 .307 .0938 .098 .092 .014 .009
Yield Strength 150,000 psi min.
1/4 20 28 0.2500 .375 .369 .1250 .127 .121 .014 .009
5/16 18 24 0.3125 .437 .431 .1562 .158 .152 .017 .012
3/8 16 24 0.3750 .562 .556 .1875 .192 .182 .020 .015
Screw Over upto & incl Tolerance 1/2 13 20 0.5000 .750 .743 .2500 .254 .244 .026 .020
- 1 -.030
1 2 1/2 -.040 Socket Thread
2 1/2 - -.060 Thread Depth Length Recommended
size F T seating torque
nom. min. ref. in-lbs.
Tensile Shear strength #8 .060 .875 25
Thread Strength in threads #10 .072 .875 35
size – lbs. min. (calculated lbs.) 1/4 .094 1.000 80
nom. UNRC UNRF UNRC UNRF 5/16 .110 1.125 157
#8 2,380 2,500 1,450 1,570 3/8 .115 1.250 278
#10 2,980 3,400 1,700 2,140 1/2 .151 1.500 667
1/4 5,410 6,180 3,090 3,900
5/16 8,910 9,870 4,930 6,210
3/8 13,200 14,900 7,450 9,400
1/2 24,100 27,200 13,600 17,100
B RAKO
UN Head markings may vary slightly
depending on manufacturing practice.
UNBRAKO and UNB are recognized
identifications for 1/4” diameter & larger.
32
Low Head Cap Screws
SCREWS
Unbrako shoulder screws are hardened shafts with a knurled head and threaded portion.
The shoulder formed where the threads meet the larger diameter body acts as a stop
when the screw is threaded into a tapped hole, permitting the screw to be used as a pivot,
shaft, or stationary guide.
Unbrako shoulder screws are used to operate stripper plates and in pressure pads a wide
variety of tool and die work. They are also used as shafts or pivots, holding pulleys, gears,
cams and cam followers, ratchets and circular form tools. Stationary guide applications
including locating pins in fixtures, latch stops, alignment of stationary members, linkage
blocks, and stock guides in dies. Unbrako shoulder screws are especially advantageous in
applications where the fastened part must be removed frequently. For instance, when the
shoulder screw is used as a shaft for circular form tools, the screw can be removed to
permit sharpening of the tool in a matter of seconds. Assembly is equally as fast.
Unbrako shoulder screws are made of high grade alloy steel the precision tolerance on
the shoulder provides close and accurate mating with the fastened components. Unbrako
manufactures to a tolerance position closer than that required by international standards.
Applications
FEATURES
Precision hex socket for maximum wrenching
strength permits full tightening without Controlled root radius doubles
cracking or reaming socket, yet provides fatigue life of threads by reducing stress Stationary Guide
ample metal in the crucial fillet area for concentrations and avoiding sharp corners
maximum head strength. where failures may start. Contour following
flow lines of rolled threads provide extra
strength, prevent stripping.
34
Socket Head Shoulder Screws Metric
T E
M
0.8 N
H 45°
LENGTH
+.25 APPROX.
W -0.00
Note
Because of their configuration, these Thread Recommended
Body Length seating torque
screws cannot be tensile tested.
size da N G M E
nom. max max max max max N-m in-lbs.
6 6.80 2.00 5.62 1.85 9.75 7 60
8 9.20 2.50 7.62 1.85 11.25 12 105
10 11.20 3.00 9.62 1.85 13.25 29 255
12 14.20 3.50 11.62 1.85 16.40 57 500
16 18.20 4.00 15.62 1.85 18.40 100 885
20 22.40 4.50 19.62 2.50 22.40 240 2,125
24 26.40 5.60 23.62 2.65 27.40 470 4,160
B RAKO
UN Head markings may vary slightly
depending on manufacturing practice.
UNBRAKO and UNB are recognized
identifications for M6 diameter & larger.
35
Socket Head Shoulder Screws - Metric
6mm (M5-0.8) - Key Size 3mm 16mm (M12-1.75) - Key Size 8mm
6 x 10 105364 50 251.69 12.43 16 x 80 105440 25 997.89 381.39
12 105365 50 234.50 13.49 90 106343 25 1073.65 417.08
16 105366 50 237.50 15.58 100 106344 25 1271.69 452.76
20 105368 50 244.43 17.93 120 106346 25 2057.77 524.11
25 105370 50 280.10 20.28
30 105372 50 316.25 22.90 20mm (M16-2) - Key Size 10mm
40 105373 50 376.49 28.14 20 x 40 105441 10 1555.52 423.61
50 105442 10 1642.96 479.14
8mm (M6-1) - Key Size 4mm 60 105444 10 1727.65 534.64
8 x 12 105375 50 282.38 26.00 70 105448 10 1812.21 590.17
16 105377 50 285.39 29.63 80 105449 10 1896.77 645.68
20 105379 50 291.39 33.29 90 105450 10 2098.76 701.21
25 105380 50 296.32 37.84 100 106347 10 2000.67 756.71
30 105381 50 302.32 42.39 120 106348 10 2294.22 867.75
40 105383 50 308.33 51.50
50 105386 50 369.89 60.59 24mm (M20-2.5) - Key Size 12mm
24 x 50 401488 5 4450.16 828.50
10mm (M8-1.25) - Key Size 5mm 60 401489 5 4869.08 906.49
10 x 16 105388 50 339.28 51.04 70 401490 5 5287.97 984.48
20 105390 50 345.20 56.72 80 401491 5 5707.02 1062.49
25 105392 50 353.21 63.82 90 401492 5 6125.91 1140.48
30 105393 50 362.23 70.91 100 401493 5 6544.82 1218.47
40 105394 50 370.23 85.07 120 401494 5 9291.94 1372.80
50 105395 50 379.16 99.26
60 105396 50 387.16 113.30
Note:
70 105402 50 396.17 127.60
• Precision ground to h8 Tolerance on the shoulder.
80 106422 50 410.11 141.79 • The Nominal Diameter of a shoulder screw is the
diameter of the shoulder and not the thread diameter,
12mm (M10-1.5) - Key Size 6mm but it is recommended that both are quoted when
12 x 15 401485 25 384.16 78.56 ordering Eg. 16mm x M12 x 70
70
80
105417
105420
25
25
554.76 190.15
611.76 210.43 INVALUABLE
90 105427 25 670.79 230.74 RESOURCE
100 105433 25 729.76 251.02 at Your Fingertips
16mm (M12-1.75) - Key Size 8mm
16 x 30 105434 25 689.49 203.02
40 105435 25 728.64 238.70
50 105436 25 802.28 274.38 FASTENER SELECTOR
60 105437 25 856.28 310.05
70 105438 25 920.99 345.73
T E
F
32
A K D G Thread
Size
H 45°
LENGTH
+.25 APPROX.
W -0.00
NOTES
Concentricity: Head to body – within .005 T.I.R. when checked in “V” block equal to or longer than body
length. Pitch diameter to body – within .004 T.I.R. when held in threaded bushing and checked at a
distance of 3/16” from shoulder at threaded end.
Shoulder must rest against face of shoulder of standard “GO” ring gage.
Bearing surface of head – perpendicular to axis of body within 2° maximum deviation.
B RAKO Tensile strength based on minimum neck area “G.” Shear strength based on shoulder diameter “D.”
UN Head markings may vary slightly
depending on manufacturing practice.
UNBRAKO and UNB are recognized Screw point chamfer: The point shall be flat or slightly concave, and chamfered. The plane of the point
identifications for 1/4” diameter & larger. shall be approximately normal to the axis of the screw. The chamfer shall extend slightly below the root
of the thread, and the edge between flat and chamfer may be slightly rounded. The included angle of the
point should be approximately 90°.
37
Socket Head Shoulder Screws - Inch
1/4” (#10-24) UNC - Key Size 1/8” 1/2” (3/8-16) UNC - Key Size 1/4” 3/4” (5/8-11) UNC - Key Size 3/8”
1/4” x 3/8 103614 25 124.38 11.84 1/2”x 2 3/4 113509 25 393.59 198.37 3/4”x 3 3/4 107525 10 1260.18 614.26
1/2 115475 25 126.23 13.55 3 102884 25 405.44 212.17 4 107557 10 1300.64 645.37
5/8 115729 25 128.40 15.82 3 1/4 111946 25 435.71 225.94 4 1/4 107590 10 1333.26 676.46
3/4 115859 25 130.97 16.96 3 ½ 111978 25 479.02 239.71 4 1/2 107622 10 1449.56 707.54
1 102352 25 138.90 21.34 3 3/4 112011 25 496.62 253.51 4 3/4 113276 10 1523.47 738.63
1 1/4 111469 25 148.74 23.80 4 108444 25 518.30 267.28 5 113308 10 1598.30 769.71
1 1/2 117980 25 154.59 27.21 4 1/4 108477 25 602.65 281.07 5 1/2 106420 10 2166.74 831.91
4 1/2 108510 10 630.02 294.84 6 106452 10 2440.04 894.08
5/16” (1/4-20) UNC - Key Size 5/32” 4 3/4 108544 10 700.75 308.62 6 1/2 117921 10 2779.99 956.25
5/16” x 3/8 118045 25 149.49 19.51 5 102921 10 718.11 322.41 7 117938 10 2960.72 1018.45
1/2 114047 25 145.65 22.20 5 1/2 116309 10 788.52 349.98
5/8 117628 25 148.74 24.88 6 116311 10 850.57 377.52 Note:
The nominal diameter of a shoulder screw is the
3/4 106137 25 151.17 27.54
diameter of the shoulder, and not the thread
1 106201 25 162.76 32.91 5/8” (1/2-13) UNC - Key Size 5/16” diameter, but it is recommended that both are
1 1/4 106266 25 170.60 38.26 5/8” x 1 115741 25 381.80 169.47 quoted when ordering. Eg 1/2 x 5/8 UNC x 1
1 1/2 106331 25 176.52 43.63 1 1/4 102954 25 447.15 191.03
1 3/4 106395 25 194.38 48.97 1 1/2 107083 25 486.35 212.61
2 106459 25 194.70 54.34 1 3/4 107114 25 499.96 234.17
2 107147 25 517.73 255.73
3/8” (5/16-18) UNC - Key Size 3/16” 2 1/4 104292 25 553.67 277.31
3/8” x 3/8 106524 25 171.69 33.77 2 1/2 104359 25 611.58 298.87
1/2 111791 25 172.02 37.64 2 3/4 110484 25 640.03 320.43
5/8 116768 25 172.60 41.49 3 109843 25 702.41 342.01
3/4 116800 25 175.69 45.36 3 1/4 103662 25 791.60 363.57
1 110993 25 176.78 53.09 3 1/2 103728 25 915.90 385.13
1 1/4 111025 25 188.37 60.83 3 3/4 117089 10 1010.92 406.71
1 1/2 118465 25 194.38 68.55 4 119174 10 1042.54 428.27
1 3/4 114133 25 227.70 76.30 4 1/4 114672 10 1316.83 449.83
2 114166 25 240.96 84.02 4 1/2 114737 10 1448.39 471.39
2 1/4 114200 25 258.14 91.74 4 3/4 119201 10 1570.27 492.98
2 1/2 114233 25 249.19 99.48 5 106617 10 1593.63 514.54
2 3/4 119970 25 267.26 107.21 5 1/2 119573 10 1982.79 557.68
3 120003 25 281.60 114.95 6 119605 10 2240.33 600.80
3 1/4 120036 25 358.56 122.67 6 1/2 116312 10 2453.81 643.94
3 1/2 120069 25 347.64 130.39 7 116313 10 2618.22 687.08
3 3/4 120101 25 379.01 138.14
4 118103 25 400.65 145.86 3/4” (5/8-11) UNC - Key Size 3/8”
3/4” x 3/4 102298 25 701.16 241.18
1/2” (3/8-16) UNC - Key Size 1/4” 1 102365 25 791.53 272.27
1/2” x 1/2 119560 25 273.30 74.36 1 1/4 102397 25 881.98 303.38
5/8 107602 25 277.14 81.25 1 1/2 108998 10 843.14 334.47
3/4 107634 25 277.29 88.13 1 3/4 125809 10 844.49 365.55
1 113288 25 279.38 101.90 2 113145 10 851.33 396.00
1 1/4 106400 25 293.32 115.70 2 1/4 107658 10 880.53 427.72
1 1/2 106432 25 301.16 129.47 2 1/2 107690 10 909.22 458.83
1 3/4 106465 25 320.09 143.26 2 3/4 107722 10 944.01 489.92
2 106497 25 342.91 157.04 3 113244 10 998.24 521.00
2 1/4 113444 25 346.46 170.81 3 1/4 107461 10 1085.49 552.09
2 1/2 113476 25 378.77 184.60 3 1/2 107493 10 1171.42 583.18
COUNTERSUNK
FEATURES
Uniform under-head angle gives
Precision forged head for continuous grain maximum contact with side walls.
flow and maximum strength
Radiused-root runout increases
Fully formed radiused threads rolled to fatigue life.
maintain continuous grain flow for greater
tensile and fatigue strength.
Deep, accurate socket for uniform
wrenching power and high
Heat treatment in a controlled
maximum torques.
atmosphere for maximum uniform
strength and surface integrity without
brittleness or decarburisation.
39
Countersunk Socket Head Screws Metric
W
APPROX
45°
HIGH-GRADE ALLOY STEEL
B THREAD
A A1
SIZE
T
H
Head Angle
See Note 3
General Note: Flat, countersunk head cap screws and button head cap screws are designed and
B RAKO
UN Head markings may vary slightly recommended for moderate fastening applications: machine guards, hinges, covers, etc. They
depending on manufacturing practice.
are not suggested for use in critical high load strength applications where socket head cap screws
UNBRAKO and UNB are recognized
identifications for M5 diameter & larger. should be used. Also due to their head configuration they may not meet the minimum ultimate
tensile requirements for property class 12.9 as specified in EN ISO 898-1. They are nevertheless
required to meet the other material and property requirements for property class 12.9.
40
Countersunk Socket Head Screws - Metric
L
LB
LG
L LB LG LB LG LB LG LB LG LB LG LB LG LB LG
Nom. (min) (max) (min) (max) (min) (max) (min) (max) (min) (max) (min) (max) (min) (max)
30
35 14.5 17.0 11.5 15.0
40 19.5 22.0 16.5 20.0 14.0 18.0
45 24.5 27.0 21.5 25.0 19.0 23.0 16.0 21.0
50 29.5 32.0 26.5 30.0 24.0 28.0 21.0 26.0 15.75 22.0
55 34.5 37.0 31.5 35.0 29.0 33.0 26.0 31.0 20.75 27.0
60 36.5 40.0 34.0 38.0 31.0 36.0 25.75 32.0 20.5 28.0
65 41.5 45.0 39.0 43.0 36.0 41.0 30.75 37.0 25.5 33.0 20.2 29.0
70 46.5 50.0 44.0 48.0 41.0 46.0 35.75 42.0 30.5 38.0 25.2 34.0
80 56.5 60.0 54.0 58.0 51.0 56.0 45.75 52.0 40.5 48.0 35.2 44.0
90 64.0 68.0 61.0 66.0 55.70 62.0 50.5 58.0 45.2 54.0
100 74.0 78.0 71.0 76.0 65.70 72.0 60.5 68.0 55.2 64.0
110 81.0 86.0 75.70 82.0 70.5 78.0 65.2 74.0
120 91.0 96.0 85.70 92.0 80.5 88.0 75.2 84.0
130 95.70 102.0 90.5 98.0 85.2 94.0
140 105.70 112.0 100.5 108.0 95.2 104.0
150 115.70 122.0 110.5 118.0 105.2 114.0
L LB LG LB LG LB LG LB LG LB LG LB LG
Nom. (Max.) (Max.) (Max.) (Max.) (Max.) (Max.) (Max.) (Max.) (Max.) (Max.) (Max.) (Max.)
70 20.0 30.0
80 30.0 40.0 26.0 36.0
90 40.0 50.0 36.0 46.0 29.5 42.0
100 50.0 60.0 46.0 56.0 39.5 52.0
110 60.0 70.0 56.0 66.0 49.5 62.0 45.5 58.0
120 70.0 80.0 66.0 76.0 59.5 72.0 55.5 68.0 51.5 64.0
130 80.0 90.0 76.0 86.0 69.5 82.0 65.5 78.0 61.5 74.0 55.0 70.0
140 90.0 100.0 86.0 96.0 79.5 92.0 75.5 88.0 71.5 84.0 65.0 80.0
150 100.0 110.0 96.0 106.0 89.5 102.0 85.5 98.0 81.5 94.0 75.0 90.0
160 106.0 116.0 99.5 112.0 95.5 108.0 91.5 104.0 85.0 100.0
180 126.0 136.0 119.5 132.0 115.5 128.0 111.5 124.0 105.0 120.0
200 139.5 156.0 135.5 148.0 131.5 144.0 125.0 140.0
220 151.5 164.0 145.0 160.0
240 165.0 180.0
41
Countersunk Socket Head Screws- Metric
M3 (0.5) - Key Size 2mm M6 (1) - Key Size 4mm M12 (1.75) - Key Size 8mm
M3 x 6 106283 200 22.53 0.84 M6 x 30 103333 200 44.96 14.08 M12 x 60 106313 50 174.55 115.50
8 103303 200 22.77 1.06 35 103334 200 48.38 16.13 70 106314 50 217.66 143.99
10 103304 200 22.94 1.25 40 103335 200 49.81 18.17 80 106315 50 248.33 163.68
12 103305 200 23.45 1.45 45 106295 200 72.82 20.04 90 106316 50 318.88 184.56
15 401672 200 26.70 1.76 50 106296 200 79.50 24.53 100 106330 50 353.88 204.82
16 103306 200 26.70 1.87
20 103308 200 29.04 2.27 M8 (1.25) - Key Size 5mm M16 (2) - Key Size 10mm
25 106284 200 33.79 2.79 M8 x 10 103336 200 38.33 11.70 M16 x 30 103359 50 206.47 118.60
30 106285 200 34.06 3.30 12 103337 200 38.31 13.18 35 103360 50 210.23 134.05
15 401680 200 37.46 15.40 40 103361 50 214.32 149.47
M4 (0.7) - Key Size 2.5mm 16 103338 200 37.46 16.15 45 106318 50 252.78 164.91
M4 x 8 103309 200 26.04 1.96 18 401681 200 37.95 17.62 50 103362 50 257.11 180.36
10 103311 200 26.19 2.33 20 103340 200 37.95 19.10 55 106320 25 275.81 195.78
12 103312 200 26.45 2.68 25 103341 200 39.13 22.77 60 103363 25 298.14 211.22
15 401674 200 26.04 3.23 30 103342 200 42.21 26.47 70 106321 25 341.85 242.09
16 103313 200 28.61 3.41 35 103343 200 45.14 30.16 80 106322 25 412.11 291.87
18 401675 200 30.37 3.76 40 103344 200 45.04 33.86
20 103315 200 30.37 4.11 45 106297 200 76.59 37.53 M20 (2.5) - Key Size 12mm
25 103316 200 34.20 5.02 50 106298 200 83.42 44.62 M20 x 35 106328 25 336.00 211.97
30 103317 200 39.04 5.92 55 106299 100 89.23 49.66 40 106332 25 374.23 236.10
35 106287 200 47.22 7.44 60 106300 100 94.86 53.53 45 106334 25 412.24 260.22
40 106288 200 49.05 8.56 70 106301 100 106.09 62.44 50 106335 25 450.68 284.35
60 106337 25 527.10 332.60
M5 (0.8) - Key Size 3mm M10 (1.5) - Key Size 6mm 70 106338 25 603.66 380.82
M5 x 8 103318 200 26.70 3.30 M10 x 12 103345 200 47.73 23.41 80 106339 25 680.11 429.07
10 103319 200 27.62 3.87 16 103347 200 43.88 28.05 100 106342 25 833.06 525.56
12 103320 200 27.69 4.44 20 103348 200 45.79 32.71 120 401685 10 1319.55 676.37
14 401676 200 28.61 5.04 25 103349 200 47.22 38.52 140 401686 10 1538.96 788.83
15 401660 200 28.61 5.32 30 103350 200 51.56 44.35 160 401687 10 1965.90 901.30
16 103321 200 28.61 5.61 35 103351 200 56.97 50.16
18 401677 200 29.95 6.18 40 103352 100 63.74 55.99 M24 (3) - Key Size 14mm
20 103322 200 29.95 6.75 45 106302 100 74.24 61.80 M24 x 50 220032 10 666.00 407.00
25 103323 200 35.21 8.18 50 106303 100 79.34 67.63 100 401693 10 1180.80 721.60
30 103324 200 42.87 9.61 55 106304 100 100.49 73.44 120 183179 10 1636.74 857.34
35 106289 200 51.22 11.04 60 106305 100 118.29 85.93
Sizes above the bold line are threaded to head.
40 106290 200 56.47 13.51 70 106306 50 132.81 99.57
45 106293 200 57.54 15.22 80 106308 50 149.13 113.98
50 106294 200 62.32 17.16 90 106309 50 193.86 128.00
100 106310 50 215.19 142.03
M6 (1) - Key Size 4mm
M6 x 8 103325 200 29.55 5.08 M12 (1.75) - Key Size 8mm
10 103328 200 31.78 5.90 M12 x 20 103353 100 87.35 48.07
12 103329 200 32.12 6.71 25 103354 100 97.11 56.50
14 401678 200 29.95 7.55 30 103355 100 106.78 64.92
15 401661 200 29.95 7.94 35 103356 100 106.78 73.37
16 103330 200 29.95 8.36 40 103357 100 117.29 81.80
18 401679 200 31.28 9.17 45 106311 100 127.55 90.22
20 103331 200 31.28 9.99 50 103358 50 138.56 98.65
25 103332 200 34.95 12.03 55 106312 50 161.88 107.07
LENGTH
W
APPROX
B G THREAD
A
SIZE
H
Controlled angle under the head
ensures maximum flushness and
side wall contact. Non-slip Hex
Head Hex Head Socket
socket prevents marring of material. Thread
Thread Diameter Socket Size Height Depth
size per Inch A W H T
nom. UNC UNF max* min** nom. max ref. min.
BS 2470, ANSI B18.3 #0 – 80 .138 .117 .035 .044 .025
#1 64 72 .168 .143 .050 .054 .031
#2 56 64 .197 .168 .050 .064 .038
Material: ASTM F835 #3 48 56 .226 .193 .0625 .073 .044
Hardness: Rc 39–43 #4 40 48 .255 .218 .0625 .083 .055
2
Tensile Strength: 96,000 lbf/in min. #5 40 44 .281 .240 .0781 .090 .061
#6 32 40 .307 .263 .0781 .097 .066
#8 32 36 .359 .311 .0937 .112 .076
over 1” over 2 1/2” #10 24 32 .411 .359 .1250 .127 .087
Diameter to 1” to 2 1/2” to 6” 1/4 20 28 .531 .480 .1562 .161 .111
#0 to 3/8” incl. –.03 –.04 –.06 5/16 18 24 .656 .600 .1875 .198 .135
7/16 to 3/4” incl. –.03 –.06 –.08 3/8 16 24 .781 .720 .2187 .234 .159
7/8 to 1” incl. –.05 –.10 –.14 7/16 14 20 .844 .781 .2500 .234 .159
1/2 13 20 .938 .872 .3125 .251 .172
5/8 11 18 1.188 1.112 .3750 .324 .220
3/4 10 16 1.438 1.355 .5000 .396 .220
Thread Maximum Tightening Torques
7/8 9 14 1.688 1.604 .5625 .468 .248
size Unplated Plated 1 8 12 1.938 1.841 .6250 .540 .297
nom. UNC UNF UNC UNF
#0 - 1.6 - 1.2 * maximum – to theoretical sharp corners
**minimum – absolute with A flat
#1 2.6 2.9 1.9 2.1
#2 4.4 4.8 3.3 3.6 Body Protrusion
#3 6.7 8.5 5.0 6.3 Thread thd-to-hd Diameter gage diameter Tensile
#4 8.9 10.0 6.6 7.5 size max B G Load lbf
#5 13.0 14.0 9.0 10.0 nom. ref max min max min UNC UNF
#0 .500 .060 .0568 .078 .077 - 265
#6 16.0 19.0 12.0 14.0
#1 .750 .073 .0695 .101 .100 390 390
#8 30.0 32.0 22.0 24.0
#2 .750 .086 .0822 .124 .123 555 555
#10 44.0 51.0 33.0 38.0
#3 .750 .099 .0949 .148 .147 725 725
1/4 100.0 120.0 75.0 90.0
#4 .875 .112 .1075 .172 .171 960 1,040
5/16 210.0 240.0 157.0 180.0
#5 .875 .125 .1202 .196 .195 1,260 1,310
3/8 380.0 430.0 285.0 322.0
#6 .875 .138 .1329 .220 .219 1,440 1,620
7/16 600.0 680.0 450.0 510.0
#8 1.000 .164 .1585 .267 .266 2,220 2,240
1/2 930.0 1,050.0 697.0 787.0
#10 1.250 .190 .1840 .313 .312 2,780 3,180
5/8 1,800.0 2,000.0 1,350.0 1,500.0
1/4 1.250 .250 .2435 .424 .423 5,070 5,790
3/4 3,200.0 3,560.0 2,400.0 2,670.0
5/16 1.500 .3125 .3053 .539 .538 8,350 9,250
7/8 5,400.0 6,000.0 4,050.0 4,500.0
3/8 1.750 .375 .3678 .653 .652 12,400 14,000
1 8,200.0 8,900.0 6,150.0 6,675.0
7/16 2.000 .4375 .4294 .690 .689 16,900 18,900
1/2 2.250 .500 .4919 .739 .738 22,800 25,600
5/8 2.500 .625 .6163 .962 .961 36,000 40,800
3/4 3.000 .750 .7406 1.186 1.185 53,200 59,300
B RAKO
UN Head markings may vary slightly 7/8 3.250 .875 .8647 1.411 1.410 73,500 81,000
depending on manufacturing practice.
UNBRAKO, and UNB are recognized 1 3.750 1.000 .9886 1.635 1.634 96,300 106,000
identifications for #10 diameter & larger.
GENERAL NOTE: Flat, countersunk head cap screws and button head cap screws are designed
and recommended for moderate fastening applications: machine guards, hinges, covers, etc.
They are not suggested for use in critical high load strength applications where socket head cap
screws should be used.
43
Countersunk Socket Head Screws - Inch
Maximum Lengths
• LG is the maximum grip length and is the distance from the bearing surface to the first complete thread.
HIGH-GRADE ALLOY STEEL
LG
Length ‘L’
Thread
Size 3/4 7/8 1 11/4 11/2 13/4 2 21/4 21/2 23/4 3 31/4 31/2 33/4 4 41/4 41/2 43/4 5
44
42
Countersunk Socket Head Screws
UNC/UNF
Pieces per Box Sizes above the bold line are threaded to head. 45
WHAT YOU BUILD
IS ONLY AS GOOD AS
WHAT HOLDS
IT TOGETHER
High Strength Structural Bolts
Tension Control Structural Bolts
A325 / A490
BS EN 14399, 15048
Arc Welding Studs
Rebar Couplers
nly
l Orders O
Specia
HEAD CAP
Unbrako button head screws are made from high grade alloy steel and every manufacturing operation is
closely controlled. Heads are forged for greater strength and full formed radius-root rolled threads assure
close tolerances, maximum strength and superior fatigue resistance. Deep
accurate sockets allow full tightening, and customized heat treatment of
each heat of steel ensures maximum strength and hardness without
brittleness.
GENERAL NOTE
Flat, countersunk head cap screws and button head cap screws are designed and recommended for
moderate fastening applications: machine guards, hinges, covers, etc. These are not suggested for use in
critical high strength applications where socket head cap screws should be used.
47
Button Head Socket Screws Metric
W H
HIGH-GRADE ALLOY STEEL
A D THREAD
SIZE
R da
General Note: Flat, countersunk head cap screws and button head cap screws are designed and
recommended for moderate fastening applications: machine guards, hinges, covers, etc. They
are not suggested for use in critical high strength applications where socket head cap screws
should be used. Also due to their head configuration they may not meet the minimum ultimate
tensile requirements for property class 12.9 as specified in EN ISO 898-1. They are nevertheless
required to meet the other material and property requirements for property class 12.9.
B RAKO
UN Head markings may vary slightly
depending on manufacturing practice.
UNBRAKO, and UNB are recognized
identifications for M5 diameter & larger.
48
Button Head Socket Screws - Metric
Black / Plain
W H
T
HIGH-GRADE ALLOY STEEL
THREAD
A B SIZE
R da
50
Button Head Socket Screws - Inch
BUTTON HEAD
HIGH-GRADE ALLOY STEEL
CAP SCREWS
Unbrako flange button head screws allow the covering of large diameter holes in sheet metal. As the large
under head surface pressure by area is low, this fastener can also be used with softer materials without
harm or damage. Flange button heads are ideal to fix strips, cover plates and sheet metal housings.
The radius on the button head presents a streamlined profile, virtually eliminating the sharp edges which
could occur with a bolt and washer assembly.
Unbrako flange button head screws are available with metric threads and are made from high grade alloy
steel.
52
Flange Button Head Socket Screws Metric
W H Length
T ± 0.25
R da
Material: Unbrako High Grade Alloy Steel Thread Head Hex Head Socket Transition
Heat Treatment: Rc 39-44 Size Pitch Diameter Socket Size Height Depth Dia
A W H T da Q R
nom. max. nom max. min max max ref
M3 0.50 7.12 2.0 1.65 1.05 3.60 0.70 3.00
1. Thread Class: 4g 6g M4 0.70 9.29 2.5 2.20 1.35 4.70 0.80 4.20
2. Full thread length to within 2½ pitches M5 0.80 11.40 3.0 2.75 1.92 5.70 0.90 5.20
of head.
M6 1.00 13.59 4.0 3.30 2.08 6.80 1.20 5.60
3. Working Temperature: -50°C +300°C
M8 1.25 17.00 5.0 4.40 2.75 9.20 1.30 7.50
4. Length tolerance = ±0.25mm.
M10 1.50 20.80 6.0 5.50 3.35 11.20 1.75 10.00
M12 1.75 24.69 8.0 6.60 4.16 13.70 2.40 11.00
5. Torques calculated in accordance with
VDI 2230 "Systematic calculation of high
duty bolted joints with σ 0.2 = 720 N/mm2 Recommended
and μ = 0.125 for plain finish. Thread Tightening Torques Tensile
Size Unplated Loads
nom. N-m lbf.in kN
M3 1.96 18 5.23
M4 4.52 40 9.13
M5 9.08 80 14.77
Up to and
Screws Over including Tolerance M6 15.40 138 20.90
- 1" ± 0.16" M8 36.80 330 38.06
1" 2" + 0.031" - 0.016" M10 72.30 650 60.32
2" 6" ± 0.031" M12 126.00 1134 87.67
6" - ± 0.062"
B RAKO
UN Head markings may vary slightly
depending on manufacturing practice.
UNBRAKO and UNB are recognized
identifications for M5 diameter & larger.
53
Flange Button Head Socket Screws Inch
W H L
T
HIGH-GRADE ALLOY STEEL
A D
B RAKO
UN Head markings may vary slightly
depending on manufacturing practice.
UNBRAKO and UNB are recognized
identifications for 1/4” diameter & larger.
54
Flange Button Head Socket Screws - Metric
Pieces per Box All flange button head socket screws are supplied with full thread
55
NABL ISO/IEC 17025:2005
CERTIFIED LAB
PRECISION
in Every Fastener
Unbrako Lab is equipped state-of-the-art equipment for testing of both physical
and metallurgical aspects of fasteners for the most demanding industries:
SET SCREWS
concentrations and can cause can cause cracking, even However, there is one cup point that can give you both
at lower tightening torques. By eliminating the corners, a maximum holding power and of resistance to
the radii distribute tightening stresses to reduce the vibration. It is the exclusive UNBRAKO knurled cup point,
chance of splitting to a minimum. whose locking knurls bite into the shaft and resist the
tendency of the screw to back out of the tapped hole.
Controlled Manufacturing – The fully-formed threads The chart on this page shows clearly how much better
of UNBRAKO set screws are rolled under extreme the UNBRAKO set screws resist vibration in comparison
pressure to minimize stripping and handle the higher with plain cup point set screws. UNBRAKO knurled cup
tightening torques. Also, with rolled threads, tolerances point self-locking set screws give you excellent per-
can be more closely maintained. Unbrako set screws formance under conditions of extreme vibration.
57
SOCKET THE WORLD LEADER
SET SCREWS
HIGH-GRADE ALLOY STEEL
In contrast to other types of fasteners, set screws are they are stronger than other set screws. The superior
primarily used in compression. They must hold fast strength and dimensional uniformity of Unbrako set
against three types of forces, torsional (rotational), screws permit use of consistently higher seating
axial (lateral movement) and vibrational. To be torques than with other set screws. Consequently you
effective, socket set screws should produce a strong can often save money because you can reduce the
clamping action which resists the relative motion size or the number of set screws you require in your
between the assembled parts, because of the assembly.
compression developed by tightening the set screw.
Since holding power is proportional to seating torque, Here are some of the reasons why Unbrako
the tighter you can seat the screw, the higher the set screws are so strong and stay tight. Unbrako set
compression force will be. screws are made of high grade alloy steel and
heat treated to a minimum hardness of Rc 45.
But there is a limit to how much you can tighten the Deep accurate sockets give more key engagement for
average set screw. If you’re not careful, you’ll ream or extra wrenching areas. Radiused socket corners
crack the socket, or strip the threads. So you’re never minimize points of weakness where cracks may start.
sure if the screw is tight enough, and whether it will Distribute stresses. Fully formed rolled threads
stay tight. provide greater strength and resistance to stripping.
Controlled heat treatment assures uniform hardness
But you can be sure that Unbrako set screws will without brittleness.
‘stay put’ because you can tighten them until the key
twists off, with no damage to the screws. Unbrako Unbrako socket set screws are available in knurled
recommend tightening torques as much as 40% cup, cone, half dog, flat and plain cup point styles in
higher than other set screws, giving you extra holding plain or plated finishes. Stainless steel set screws are
power and additional safety and reliability. available in plain cup points only.
Unbrako socket set screws hold tighter because
58
SOCKET THE WORLD LEADER
SET SCREWS
APPROX. APPROX.
See Note 1 A 45° 45°
L L
W J J
Thread
size Nm lbf.in.
M3 0.87 7.7
APPROX.
M4 2.20 19.5 A 45°
See Note 1 L
L
M5 4.60 41.0
M6 7.80 69.0
M8 18.00 160.0 W J J
M10 36.00 320.0 Y
FLAT CONE
M12 62.00 550.0
(M14) 62.00 550.0
M16 150.00 1330.0 Thread Hex Cone Point
(M18) 290.00 2570.0 size Pitch Socket Size Flat Point y° ± 2°
M20 290.00 2570.0 A W J L - min J L - min 90° for these Lengths
(M22) 475.00 4200.0 nom. nom. max. Preferred max. Preferred & Over; and 120° Under
M24 475.00 4200.0 M3 0.50 1.5 2.0 3.0 Sharp 4.0 4.0
M4 0.70 2.0 2.5 3.0 Sharp 4.0 5.0
M5 0.80 2.5 3.5 4.0 Sharp 5.0 6.0
M6 1.00 3.0 4.0 4.0 1.5 6.0 8.0
Up to and M8 1.25 4.0 5.5 5.0 2.0 6.0 10.0
Screws Over including Tolerance M10 1.50 5.0 7.0 6.0 2.5 8.0 12.0
- Screw Dia +0.25 - 0.00 M12 1.75 6.0 8.5 8.0 3.0 10.0 14.0
Screw Dia 50 ±0.25 (M14) 2.00 6.0 10.0 10.0 4.0 12.0 14.0
50 80 ±0.50 M16 2.00 8.0 12.0 12.0 4.0 14.0 18.0
80 120 ±0.70 (M18) 2.50 10.0 13.0 12.0 5.0 16.0 20.0
120 250 ±0.80 M20 2.50 10.0 15.0 14.0 5.0 18.0 22.0
(M22) 2.50 12.0 17.0 16.0 6.0 20.0 28.0
M24 3.00 12.0 18.0 20.0 6.0 20.0 28.0
All Dimensions In Millimetres.
Sizes In Brackets Are Non-preferred Standards.
60
Socket Set Screws Metric
Full and Half Dog Point
H HL
V V
W
FULL DOG HALF DOG
61
Socket Set Screws - Metric
specific safety factors appropriate to the given application and load conditions.
Thread Seating Axial Shaft diameter (shaft hardness Rc 15 to Rc 35) Torsional holding power Nm
Size Torque Holding 1.4 1.6 1.8 2.0 3.0 4.0 5.0 6.0 8.0 10 12 14
Nm Power (kN)
M1.4 .10 .19 .13 .15 .17 .19 .29 .38 .48
M1.6 .10 .22 .15 .18 .20 .22 .33 .44 .55 .66
M1.8 .10 .25 .18 .20 .23 .25 .38 .50 .63 .75 1.0
M2.0 .21 .29 .20 .23 .26 .29 .44 .58 .73 .87 1.2 1.5
M2.5 .60 .53 .42 .48 .53 .80 1.10 1.30 1.60 2.1 2.7 3.2
M2.6 .60 .56 .50 .56 .84 1.10 1.40 1.70 2.2 2.8 3.4 3.9
M3 .87 .71 .71 1.07 1.40 1.80 2.10 2.8 3.6 4.3 5.0
M4 2.20 1.70 1.70 2.60 3.40 4.30 5.10 6.8 8.5 10.0 12.0
M5 4.60 2.50 3.80 5.00 6.30 7.50 10.0 13.0 15.0 18.0
M6 7.80 4.20 11.00 13.00 17.0 21.0 25.0 29.0
M8 18.00 6.70 20.00 27.0 34.0 40.0 47.0
M10 36.00 9.30 37.0 47.0 56.0 65.0
M12 62.00 12.00 60.0 72.0 84.0
M14 62.00 15.00 90.0 105.0
M16 150.00 18.00 126.0
Thread Seating Axial Shaft diameter (shaft hardness Rc 15 to Rc 35) Torsional holding power Nm
Size Torque Holding 16 18 20 25 30 40 50 60 70 80 90 100
Nm Power (kN)
M2.6 .60 .56 4.5
M3 .87 .71 5.7 6.4 7.1
M4 2.20 1.70 14.0 15.0 17.0 21
M5 4.60 2.50 20.0 23.0 25.0 31 38
M6 7.80 4.20 34.0 38.0 42.0 53 63 84
M8 18.00 6.70 54.0 60.0 67.0 84 101 134 168 201
M10 36.00 9.30 74.0 84.0 93.0 116 140 186 233 279
M12 62.00 12.00 96.0 108.0 120.0 150 180 240 300 360 420
M14 62.00 15.00 120.0 135.0 150.0 188 225 300 375 450 525 600
M16 150.00 18.00 144.0 162.0 180.0 225 270 360 450 540 630 720 810
M18 290.00 21.00 168.0 189.0 210.0 263 315 420 525 630 735 840 945 1050
M20 290.00 23.00 207.0 230.0 288 345 460 575 690 805 920 1040 1150
M22 475.00 26.00 260.0 325 390 520 650 780 910 1040 1170 1300
M24 475.00 29.00 363 435 580 725 870 1020 1160 1310 1450
62
Socket Set Screws - Metric
63
Socket Set Screws - Metric
$ Price lbs
Size Part No.
Flat Point Dog Point /100 /1000
HIGH-GRADE ALLOY STEEL
Pieces per Box Property Class: 45H * Half dog point as standard
64
Socket Set Screws - Metric
$ Price lbs
Size Part No.
Cone Point Plain Point /100 /1000
65
Socket Set Screws Inch
#0 to #10
HIGH-GRADE ALLOY STEEL
T T T T
L
L
C C C J
P
118° 118° 118° Y
SEE NOTE 1 PLAIN CUP FLAT SEE NOTE 2 HALF DOG
Fasten collars, sheaves, gears, knobs on KNURLED CUP CONE
Recommended ** screw
1. Knurled Cup Point: When length equals nom. Q T* P seating torque length
nominal dia or less, included angle is 130°. size max min min max min In-lbs nom.
2. Cone Cup Point: When length equals #0 .017 .013 .035 .040 .037 1.0 3/32
nominal diameter or less, included angle #1 .021 .017 .035 .049 .045 1.8 1/8
is 118°. (#4 x 1/8 and #8 x 3/16 also have #2 .024 .020 .035 .057 .053 1.8 1/8
118° angle) #3 .027 .023 .060 .066 .062 5 5/32
#4 .030 .026 .075 .075 .070 5 5/32
#5 .033 .027 .075 .083 .078 10 5/32
#6 .038 .032 .075 .092 .087 10 3/16
#8 .043 .037 .075 .109 .103 20 3/16
#10 .049 .041 .105 .127 .120 36 3/16
*CAUTION: Values shown in column T are for minimum stock length cup point screws.
Screws shorter than nominal minimum length shown do not have sockets deep enough
to utilize full key capability which can result in failure of socket, key or mating threads.
L
L
C C C J
P
118° 118° 118° Y
PLAIN CUP FLAT HALF DOG
Fasten collars, sheaves, gears, knobs on
shafts. Locate machine parts. Self-locking
knurled cup point is standard. Special
Points like Flat, Dog, Cone & Plain Cup
A
are also available.
*CAUTION: Values shown in column T are for minimum stock length cup point screws.
Screws shorter than nominal minimum length shown do not have sockets deep enough
to utilize full key capability which can result in failure of socket, key or mating threads.
Tabulated axial and torsional holding powers are typical strengths and should be used accordingly, with
specific safety factors appropriate to the given application and load conditions.
Seating Axial Shaft diameter (shaft hardness Rc 15 to Rc 35) Torsional Holding Power lbf.in.
Thread Holding
Torque 1/16 3/32 1/8 5/32 3/16 7/32 1/4 5/16 3/8 7/16 1/2 9/16
Size Power (lbf.)
lbf.in.
#0 1.0 50 1.5 2.3 3.1 3.9 4.7 5.4 6.2
#1 1.8 65 2.0 3.0 4.0 5.0 6.1 7.1 8.1 10.0
#2 1.8 85 2.6 4.0 5.3 6.6 8.0 9.3 10.6 13.2 16.0
#3 5.0 120 3.2 5.6 7.5 9.3 11.3 13.0 15.0 18.7 22.5 26.3
#4 5.0 160 7.5 10.0 12.5 15.0 17.5 20.0 25.0 30.0 35.0 40.0
#5 10.0 200 12.5 15.6 18.7 21.8 25.0 31.2 37.5 43.7 50.0 56.2
#6 10.0 250 19.0 23.0 27.0 31.0 39.0 47.0 55.0 62.0 70.0
#8 20.0 385 30.0 36.0 42.0 48.0 60.0 72.0 84.0 96.0 108.0
#10 36.0 540 51.0 59.0 68.0 84.0 101.0 118.0 135.0 152.0
1/4 87.0 1,000 125.0 156.0 187.0 218.0 250.0 281.0
5/16 165.0 1,500 234.0 280.0 327.0 375.0 421.0
3/8 290.0 2,000 375.0 437.0 500.0 562.0
7/16 430.0 2,500 545.0 625.0 702.0
1/2 620.0 3,000 750.0 843.0
9/16 620.0 3,500 985.0
Seating Axial Shaft diameter (shaft hardness Rc 15 to Rc 35) Torsional Holding Power lbf.in.
Thread
Torque Holding 5/8 3/4 7/8 1 1 1/4 1 1/2 1 3/4 2 2 1/2 3 3 1/2 4
Size
lbf.in. Power (lbf )
#5 10.0 200 62
#6 10.0 250 78 94 109
#8 20.0 385 120 144 168 192
#10 36.0 540 169 202 236 270 338
1/4 87.0 1,000 312 375 437 500 625 750
5/16 165.0 1,500 468 562 656 750 937 1125 1310 1500
3/8 290.0 2,000 625 750 875 1000 1250 1500 1750 2000
7/16 430.0 2,500 780 937 1095 1250 1560 1875 2210 2500 3125
1/2 620.0 3,000 937 1125 1310 1500 1875 2250 2620 3000 3750 4500
9/16 620.0 3,500 1090 1310 1530 1750 2190 2620 3030 3500 4370 5250 6120
5/8 1,325.0 4,000 1250 1500 1750 2000 2500 3000 3750 4000 5000 6000 7000 8000
3/4 2,400.0 5,000 1875 2190 2500 3125 3750 4500 5000 6250 7500 8750 10000
7/8 5,200.0 6,000 2620 3000 3750 4500 5250 6000 7500 9000 10500 12000
1 7,200.0 7,000 3500 4375 5250 6120 7000 8750 10500 12250 14000
68
Socket Set Screws - Inch
69
Socket Set Screws - Inch
$ Price lbs
Size Part No.
Knurled Point Plain Point /100 /1000
HIGH-GRADE ALLOY STEEL
70
Socket Set Screws - Inch
Plain Point
#3/8-16 UNC - Key Size 3/16” 1/2-20 UNF - Key Size 1/4”
3/8” x 1/4 114999 100 22.31 4.38 1/2” x 1/2 103619 100 59.27 17.36
5/16 108247 100 18.63 4.99 5/8 103635 100 70.78 22.73
3/8 118815 100 19.34 6.40 3/4 115447 100 69.95 28.07
1/2 118879 100 20.56 9.13 1 115463 100 87.61 38.81
5/8 118911 100 22.27 11.86
71
TAPER
PRESSURE PLUGS
BRASS, ALLOY & STAINLESS STEEL
®
LEVL SEAL TYPE Dryseal Thread
Form with 7/8-inch per foot
Precision hex socket with maximum depth for
Dryseal Type With 3/4-inch Taper per Foot positive wrenching at higher seating torques
- Dryseal-thread form achieves a seal Heat treated alloy steel for strength Rounded
without need for compound closely controlled for better sealing
- Heat treated alloy steel for strength
- Roundness-closely controlled for better sealing High pressure is developed through a deliberate
- Uniform taper of 3/4 inch per foot difference of taper between the plug and the
tapped hole having standard 3/4” taper
Pressure plugs are not pipe plugs. torque. Galling and seizure are TYPES OF PRESSURE
Pipe plugs (plumber’s fittings) are caused by metal pickup on the PLUG THREADS
limited to pressures of 600 psi, are mating surfaces and are directly Three thread forms are commonly
sealed with a compound, and are related to force on the surface, used for pipe plugs and pressure
made of cast iron with cut threads material hardness, lubrication used, plugs:
and protruding square drive. and thread finish.
NPT: National Pipe thread, Tapered.
Pressure plugs are made to closer How Pressure Plugs Seal This is the thread form commonly
tolerances, are generally of higher Sealing is achieved by crushing the used for commercial pipe and fittings
quality, and almost all have taper crest of one thread against the root for low pressure applications. A lubri-
threads. Properly made and used, of the mating thread. If too much of cant and sealer are generally used.
they will seal at pressures to 5000 compressive force is required to
psi and without a sealing com- torque the plug, it will tend to gall ANPT: Aeronautical National Pipe
pound (pressure tests are usually at in the hole. Too little force will not thread, Tapered. Covered by MIL-S-
20,000 psi.) they are often used in deform the crest of threads enough 7105, this thread form was developed
hydraulic and pneumatic designs. to produce a seal. Increasing the for aircraft use. It is basically the same
hardness of the material will reduce as the NPT thread except that tole-
Performance Requirements galling but will also increase the rances have been reduced about 50
Pressure plugs used in industrial required sealing force. Generally a percent. Plugs made with this thread
applications should: hardness range of Rc 30 to 40 will should be used with lubricants and
- not leak at pressures to 5000 psi meet most requirements. The sealers. They are not to be used for
- need no sealing compounds tightening force must be low hydraulic applications.
- be reusable without seizure enough to cause no galling in this
- give a good seal when reused range. NPTF: National Pipe thread, Tapered,
- seal low viscosity fluids Fuel. This is the standard thread for
- require minimum seating torque Cost Considerations pressure plugs. They make pressure-
- require minimum re-tooling or Dryseal plugs are more frequently tight joints without a sealant. Tole-
special tools. used, especially where reuse is rances are about 1/4 those for NPT
frequent. Reason: more threads are threads. The standard which applies
For a satisfactory seal, the threads engaged and they therefore resist is ANSI B1.20.3. Applicable for fluid
of the plug and those in the mating leakage better. They are also power applications.
hole must not gall or seize up to preferred in soft metals to reduce
maximum possible tightening of over-torquing.
72
TAPER
PRESSURE PLUGS
High pressure seal— Achieved Flush seating—Design of LEVL-SEAL PTF fully formed Dryseal threads
through metal-to-metal contact at plug permits seating within half a designed to achieve seal in tapped
the large end of the plug. High load pitch in a normally tapped hole. holes without need for sealing
placed on the few mating threads Conventional plugs have the greater compounds.
near the top of the hole. tolerance of a full pitch and usually
protrude above the surface.
73
Taper Pressure Plugs Metric
DIN 906
min
W 2mm
F
ALLOY STEEL
A 3°42’
3°26’
74
BSPT Threads
Taper Pressure Plugs - Inch
3/4 Taper
W
F E
Plug Socket
Size E Drill
min Size
1/8 0.076 0.1923
1/4 0.107 0.2564
3/8 0.139 0.3205
1/2 0.170 0.3847
5/8 0.170 0.5129
3/4 0.232 0.5770
7/8 0.232 0.5770
1 0.232 0.6400
1 1/4 0.300 0.7680
1 1/2 0.300 0.7680
75
Taper Pressure Plugs - Inch NPTF Threads
Dry Seal (3/4 Taper)
W
F E
BRASS, ALLOY & STAINLESS STEEL
A 3°42’
3°26’
76
Taper Pressure Plugs - Inch PTF Threads
LEVL SEAL (7/8 Taper)
L
W
A 4°19’ 10”
4°1’ 18”
Head Marking
77
Taper Pressure Plugs - Metric
$ Price lbs
Size Part No.
/100 /1000
ALLOY STEEL
Page
82 Dowel Pins
Installation Warning –
Do not strike. Use safety shield or glasses
when pressing chamfered end in first.
APPLICATIONS
Widely used as plug gages in various
production operations, and as guide pins,
stops, wrist pins, hinges and shafts. Also Continuous grain flow resists
used as position locators on indexing chipping of ends. Precision heat
machines, for aligning parts, as feeler treated for greater strength and
gages in assembly work, as valves and surface hardness.
valve plungers on hydraulic equipment, Chamfered end provides easier
as fasteners for laminated sections and insertion in hole. Surface finish to
machine parts, and as roller bearings in 8 microinch maximum.
casters and truck wheels.
81
Dowel Pins Metric
-0.5
Length
C
HIGH-GRADE ALLOY STEEL
R
16°
10° 0.2
A B
82
Dowel Pins - Metric
Length
HIGH-GRADE ALLOY STEEL
Q R
10°
5° 16
A B
84
Dowel Pins - Inch
5/16” 5/8”
5/16” x 1/2 120557 40 31.74 12.65 5/8” x 1 107650 10 245.20 86.83
5/8 120621 40 34.29 14.85 1 1/4 107682 10 277.15 110.00
3/4 117265 40 38.66 16.28 11/2 107714 10 310.56 173.65
7/8 117298 40 47.94 18.99 1 3/4 121862 10 348.29 160.70
1 117331 40 46.47 21.71 2 107453 10 380.97 189.20
1 1/4 117363 40 54.28 29.70 2 1/4 107485 10 445.76 209.00
1 1/2 117397 40 62.53 35.20 2 1/2 107517 10 437.58 217.06
1 3/4 117429 40 72.81 42.35 3 107549 10 564.16 268.40
2 117462 40 83.24 43.41 3 1/2 107582 10 640.99 310.20
2 1/4 117494 40 98.13 48.84 4 107614 10 702.85 358.60
2 1/2 117527 40 101.92 59.95 4 1/2 113268 10 866.85 409.20
3 117561 40 123.95 69.85 5 113300 10 1005.31 440.00
FEATURES
Formed ends resist chipping Surface hardness-Rockwell C60 minimum
Surface finish-8 micro inch maximum
Core hardness-Rockwell C 50–58
Exclusive spiral grooves afford uniform
relief for insertion and removal, Shear strength: 150,000 psi (calculated
reduce chances of hole-scoring based on conversion from hardness)
Heat treated alloy steel for strength
and toughness
Tapped hole for easy
Held to precise tolerance
pull-out (ANSI B1.1)
86
Pull-Out Dowel Pins Inch
T
D
THREADS PER ANSI B1.1
P
LENGTH
±.010
87
Pull-Out Dowel Pins - Inch
Its about
Safety
& Reliability...
Using unbrako tools says a lot:
You’re proud,
You’re professional,
You don’t cut corners.
88
HEXAGON
WRENCHES
A 5/64” UNBRAKO key will twist up Twisted to about 270°, the key shears The socket hasn’t been reamed or
to 180° without weakening. off clean. Note the extension bar damaged. Broken section can be
illustrated for test purposes only. lifted out with a magnet.
91
Hexagon Wrenches Metric
HIGH-GRADE ALLOY STEEL
A
B
Size Socket Head Low Head Flat Head Button Head Socket Set
nom. Cap screws Cap Screws Socket screws screws screws
0.71 - - - - M1.6
0.89 - - - - M2
1.27 - - - - M2.5
1.50 M1.6/M2 - - - M3
2.00 M2.5 - M3 - M4
2.50 M3 - M4 - M5
3.00 M4 M4 M5 M6 M6
4.00 M5 M5 M6 M8 M8
5.00 M6 M6 M8 M10 M10
6.00 M8 M8 M10 M12 M12
8.00 M10 M10 M12 M16 M16
10.00 M12 M12 M16 M20 M20
12.00 M14 M16 - M24 M24
14.00 M16 M20 - - -
17.00 M20 M24 - - -
19.00 M24 - - - -
22.00 M30 - - - -
27.00 M36 - - - -
32.00 M42 - - - -
36.00 M48 - - - -
B
C
94
Hexagon Wrenches - Inch
HIGH-PERFORMANCE
STAINLESS STEEL FASTENERS
Unbrako fasteners are now available in all grades of
Stainless Steel A2-70, A2-80, A4-70, A4-80, A4-90 and A4-100.
• Socket Head Cap Screws
• Socket Countersunk Head Screws
• Socket Button Head Screws
• Hex Head Screws
• Hex Nuts
• Plain Washer Only
l Orders
• Spring Washer Specia
• Socket Set Screws
• Threaded Rod
• Specials
Unbrako Stainless Steel Not attracted by a magnet. Retention of a high percentage Useful in cryogenic application
Fasteners - available in SS304 Maximum permeability is 1.2. of tensile strength and good (like Liquid Nitrogen Gas(LNG)
& SS316 - offer excellent High valuable characteristic creep resistance up to 800°F Processing), especially SS304,
corrosion resistance in a wide in electrical applications. (without scaling or oxidation). because it dose not become
variety of environments. brittle as it is chilled.
96
www.unbrakousa.com
THE WORLD LEADER
H D
D2
Durlok
Page Contents
101 Durlok® Screws
®
102 Durlok Nuts
Why do fasteners rotate loose under How does DURLOK® work? Advantages of DURLOK®
vibration? Durlok® Free Spinning Self-locking Durlok® Bolts & Nuts are suitable for
The basic design & function of a fasteners come with all the benefits multiple re-use because the serrations
threaded fastener is to join multi- of serrated fasteners but with none do not groove the clamped material
-component assemblies so that the of the disadvantages. Unlike serrated and maintain locking ability. .
whole assembly performs as a single fasteners, with the unique Durlok® tooth
component. . formation, the locking is caused by the The Durlok® fastener system is effective
elastic spring back of the material at on a wide variety of engineering
In most cases, even in preloaded joints, clamping load. A little wall of material materials including steel both heat-
the external forces create minimal builds up behind each tooth thereby -treated and non heat-treated, cast
relative displacements between the blocking the bolt from turning. . irons including nodular types, non-
clamped parts, resulting in small sliding -ferrous metals and sheet materials. .
movements both in threads and under Durlok® is designed with long, ramp
the head. Thus, the fastener becomes shaped, radial teeth blended evenly The presence of oil or other lubricants,
free of friction in a circumferential into a smooth slightly conical outer organic or inorganic coatings will not
direction and the internal loosening bearing surface. It is this plain outer adversely affect the locking ability.
or “off-torque” created by the preload bearing ring that prevents excessive In addition, the corrosion resistance of
on the threads will rotate the fastener penetration into the bearing material, protected surfaces will generally be
loose. . together with the long radial teeth maintained because the smooth
which embed with only moderate annular ring of Durlok® fastener
In addition to self-loosening, fatigue edge pressure just sufficient to shields the bearing area against liquid
failures can occur because the fastener guarantee self-locking. . penetration. .
will lose preload as soon as partial
loosening takes place. Durlok® Bolts of strength grade 12.9 Durlok® Fasteners can be used at
are manufactured from alloy steel and elevated temperatures up to 300°C.
are through hardened to give the same
hardness from the tooth surface to the
core. These are typically heavy duty
bolts and can be used for all joints
subjected to high loads.
AD 2000 15048 ISO ISO/TS ISO OHSAS
14399 9001 16949 14001 18001
98
THE WORLD LEADER
1
Preload Fv
Table 3
These results clearly show that spring washers
do not possess any genuine self-locking ability. DURLOK bolts, however do not rotate loose when
1. Hex Head Bolt M 10x30 DIN 933-8.8 unlocked. tested in the same way, even under the heaviest
2. Hex Head Bolt M 10x30 DIN 933-8.8 locked with amplitudes. Even when only half of the recommended
spring washer according to DIN128B. preload was used. Durlok bolts still did not loosen.
3. Hex Head Bolt M 10x30 DIN 933-8.8 locked This is illustrated by the figure:2, which is an original
with spring washer according to DIN 127A. recording of a vibration test on M 10 DURLOK bolts.
This shows that there is a mineral loss of preload even
when the fastener is re-used.
[N]
30 000 [N]
50 000
Fv=Fv 12.9
40 000
20 000
34 000
Preload Fv
Fv=Fv 10.8
30 000
Preload Fv
10 000 20 000
17 000 Fv=1/2 Fv 10.8
1 3 10 000
2
0 100 200 300 400 0
0 200 400 600 800 1000
Number of Cycles Number of Cycles
figure:2
99
THE WORLD LEADER
® Bolt
lok
r
Du
Durlok®
Effectiveness at elevated Nu Embedding is no greater
t
temperatures upto 300° C than with standard
is ensured. types of fasteners.
Closely controlled
Reusability is guaranteed with manufacturing for
locking ability maintained. The DURLOK Advantage extra safety and reliability.
Durlok® anti-vibration nuts & bolts. The Durlok 12.9 nuts & bolts are Percentage of preload Remaining
M8 Bolt - Half Load
Frequency : 12.5 Hz
Clamp Length: 30.00mm
2 Pairs of Durlok Washers
2 Pairs of Competitor Washer
Tighten at B
designed for high-performance critical applications and do not require 100%
No Washer
product in washer form for applications where it was deemed desirable 80%
to use a washer in the joint design. Thus we began researching and 70%
50%
20%
It is an anti-vibration solution that not only prevents 10%
bolted joint failure, but also enables the bolted joint 0%
250 500 750 1000 1250 1500 1750 2000
to retain its pre-load, thus reducing maintenance No. of Cycles
requirements. The test regime highlighted this
feature (fig 1).
K
D Length D1
H
D2
45°
TEETH
D D1 D2 K K1 H S P Length
Property Class: 12.9 Size max min nom min min max max ref
Material: Alloy Steel ISO 898-1 M5 12 11.0 5.5 4.5 1.0 2.09 8 3.65 50.0
Hardness: 40 - 43HRc M6 14 11.8 6.6 5.2 1.1 2.69 10 4.35 50.0
Tensile Strength: 1220N/mm² min M8 18 15.2 9.0 7.2 1.3 4.21 13 5.90 60.0
Thread class: 6g M10 21 17.2 11.0 9.0 1.6 5.47 15 7.50 60.0
Threads: ANSI B1.13M, ISO 261, M12 25 20.6 14.0 11.0 1.9 6.71 17 9.10 80.0
ISO 262 (coarse series only) M14 28 22.8 16.0 12.5 2.2 7.65 19 10.65 80.0
M16 32 25.5 18.0 16.0 3.8 9.27 22 12.55 100.0
M20 39 31.2 22.0 18.0 3.1 11.86 27 15.70 100.0
Tightening Torque
Stress Proof Load at load at Induced Tmax (Nm) for μ head
Area Load yield min UTS preload of
Size mm2 (N) (N) (N) (N) 0.125 0.16 0.2
M5 14.2 13,750 15,600 17,300 11,300 10.8 12.4 14.2
M6 20.1 19,500 22,100 24,500 15,950 18.2 21.0 24.0
M8 36.6 35,500 40,300 44,600 29,300 44.0 50.0 58.0
M10 58.0 56,300 63,800 70,800 46,600 84.0 96.0 109.0
M12 84.3 81,800 92,700 102,800 68,000 148.0 169.0 194.0
M14 115.0 111,500 126,500 140,000 93,000 233.0 266.0 304.0
M16 157.0 152,000 172,500 191,500 129,000 362.0 413.0 472.0
M20 245.0 238,000 270,000 299,000 201,000 695.0 797.0 913.0
Note
*Fmax for μ thread =0.125
101
Durlok® Nuts - Metric
D1
K D2
D K1
HIGH-GRADE ALLOY STEEL
TEETH
Radii as
S 20° Forged
D D1 D2 S H K K1
Size max min max max min nom min
Material: Alloy Steel ISO 898-1
M5 12 10.0 6.2 8 2.46 4.5 1.0
Hardness: 28-36HRc
Thread class: 6H M6 14 11.8 7.4 10 3.06 5.2 1.1
Head marking: U 12 M8 18 15.2 9.5 13 4.60 7.2 1.3
Threads: ANSI B1.13M, ISO 261, M10 21 17.2 12.5 15 5.90 9.0 1.6
ISO 262 (coarse series only) M12 25 20.6 15.0 19 7.45 11.0 1.9
Property Class: 12 M14 28 23.4 17.0 22 8.55 12.5 2.2
M16 32 26.4 19.0 24 10.25 16.0 2.3
M20 39 32.4 23.0 30 13.05 18.0 2.9
The Durlok fastener system is effective on a wide variety of a joint stiffness which occurs under snug conditions with a
engineering materials including steel - both heat treated and clamping length of 2.5 - 4d. In addition , the values are based
non-heat treated, cast irons including nodular types, non on an average friction co-efficent for the threads of μ = 0.125.
ferrous metals and sheet materials.
The value of the friction coefficient in the bearing area μh, has
The Presence of oil or other lubricants, organic or inorganic a different value to that of the friction coefficient in the threads
coatings should not adversely affect the locking ability. Durlok μt, due to the serrations. As for all bolts the friction coefficient
Fasteners can be used at elevated temperatures up to 300ºC. under the head is a function of the material, surface finish and
lubrication condition of the contacting materials. To account for
The Induced assembly pre-load Fmax and the corresponding this the tightening torques are listed for various values of μh.
tightening torques, T max are based on a 90% utilisation of the
minimum yield strength by combined tension and torsional For guidance the following chart is designed to indicate the
stresses. For cases where the yield strength must never be appropriate value of friction coefficient to be applied for various
exceeded during tightening, the tightening torque must be engineering materials and finishes. The value of μh are based
reduced by a value equivalent to the scatter. Comprehensive on the results of comprehensive tests:
investigation has shown that the scatter, due to variations
in friction coefficient and torque scatter when tightening Coated Surface Fine Turning Turning, Boring, Rough Turning
with torque wrench, must be accounted for by using a Bare Bolt Surface Grinding Milling Rough Milling
reduced torque T which is 90% of the tabulated value Steel Hardness
0.125 0.16 0.125 0.160 0.125 0.125
T max, T = 0.9 x Tmax Accordingly the induced pre-load 250-350 HV
Steel Hardness
Fmax will be reduced to the new pre-load F, Ff = 0.9 x Fmax 0.160 0.20 0.160 0.160 0.160 0.160
150-250HV
Grey cast Iron
It should be noted that pre-load and tightening torque are a 0.20 0.160 0.125
Nodular Cast Iron
function of the joint stiffness. The tabulated values are valid for
102
Self-locking Anti-vibration Fasteners
Metric
® $ Price lbs
Durlok Bolts Size Part No.
/100 /1000
M14 (2)
M14 x 25 190730 25 262.61 131.32
30 190370 25 273.97 142.12
35 190740 25 277.04 152.92
40 190380 25 294.01 163.72
103
Durlok® Washers - Metric
H D
D2
HIGH-GRADE ALLOY STEEL
$ Price lbs
Size Part No.
/100 /1000
Zinc Flake Coated
M6 183794 200 57.70 0.91
M8 183795 200 61.40 1.80
M10 183796 200 69.90 2.73
M12 183797 200 114.30 3.58
M14 183798 100 140.30 5.88
M16 183799 100 166.30 8.45
M20 183801 100 249.40 11.50
When the screw or the nut is tightened the radial teeth of Durlok Thread
Angle
washer locks itself onto the surface, allowing movement only across Wedge Angle > Thread Angle
the wedge faces. During vibration, even a smallest turn of the screw
causes an increase in pre-load force due to the wedge effect and the Wedge
Angle
screw locks itself. Thread
Angle
Thus the screw will not loosen or unscrew, even under severe jarring &
vibration. Durlok washers are re-usable with locking ability maintained.
Note: the washers are always used in pairs. For through holes two pairs of Durlok washers should be used. For studbolt Durlok washers lock the nut.
Durlok washers must not be used with other flat washers.
104
L
A H
Engineering Guide
Technical Section
150° da
MIN
106 Screw Fastener Theory and Application
110 Joint Diagrams
116 The Torque-Tension Relationship
118 Stripping Strength of Tapped Holes
W High-Temperature Joints
122
125 Corrosion In Threaded Fasteners
129 Impact Performance
133 Product Engineering Bulletin
134 Metric Threads
135 Through-Hole Preparation
136 Drill and Counterbore Sizes
137 Hardness-Tensile Conversion Chart
138 Thread Stress Area
139 Thread Size Comparison NOTE:
The technical discussions represent typical
140 Comparison of Different Strength Grades applications only. The use of the information
is at the sole discretion of the reader. Because
applications vary enormously, UNBRAKO does
not warrant the scenarios described are
appropriate for any specific application. The
reader must consider all variables prior to using
this information.
Screw Fastener Theory & Applications
Joint Material
If the joint material is relatively stiff compared to the bolt
material, it will compress less and therefore provide a less
sensitive joint, less sensitive to loss of preload as a result
of brinelling, relaxation and even loosening. OTHER DESIGN CONSIDERATIONS
Application Temperature
Thread Stripping Strength For elevated temperature, standard alloy steels are useful
Considering the material in which the threads will be to about 550°F–600°F. However, if plating is used, the
tapped or the nut used, there must be sufficient maximum temperature may be less (eg. cadmium should
engagement length to carry the load. Ideally, the length of not be used over 450°F.
thread engagement should be sufficient to break the
fastener in tension. When a nut is used, the wall thickness Austenitic stainless steels (300 Series) may be useful to
of the nut as well as its length must be considered. 800°F. They can maintain strength above 800°F but will
begin to oxidize on the surface.
An estimate, a calculation or joint evaluation will be
required to determine the tension loads to which the bolt Corrosion Environment
and joint will be exposed. The size bolt and the number A plating may be selected for mild atmospheres or salts.
necessary to carry the load expected, along with the If plating is unsatisfactory, a corrosion resistant fastener
safety factor, must also be selected. may be specified. The proper selection will be based
upon the severity of the corrosive environment.
The safety factor selected will have to take into
consideration the consequence of failure as well as the FATIGUE STRENGTH
additional holes and fasteners. Safety factors, therefore, S/N Curve
have to be determined by the designer. Most comparative fatigue testing and specification fatigue
test requirements are plotted on an S/N curve. In this
SHEAR APPLICATIONS curve, the test stress is shown on the ordinate (y-axis)
Shear Strength of Material and the number of cycles is shown on the abscissa
Not all applications apply a tensile load to the fastener. In (x-axis) in a logarithmic scale. On this type curve, the high
many cases, the load is perpendicular to the fastener in load to low load ratio must be shown. This is usually
shear. Shear loading may be single, double or multiple R =.1, which means the low load in all tests will be 10% of
loading. the high load.
80,000
tensile/shear relationship and it is usually 50-55%
70,000
60,000
Single/Double Shear 50,000
0
104 105 106 107
Cycles to Failure
Effect of Preload
Increasing the R to .2, .3 or higher will change the curve
shape. At some point in this curve, the number of cycles
will reach 10 million cycles. This is considered the
106
Screw Fastener Theory & Applications
160
VARIABLES IN TORQUE
Coefficient of Friction
140
Since the torque applied to a fastener must overcome all
friction before any loading takes place, the amount of
120
friction present is important.
20
If these interfaces are lubricated (cadmium plate,
molybdenum disulfide, anti-seize compounds, etc.), the
0
friction is reduced and thus greater preload is produced
0 20 40 60 80 100 120 140 160 180 with the same torque.
Mean Stress (ksi)
Their disadvantages are... large quantities of bolts, hot forging is more expensive
• lower tensile strength. then cold forging.
• reduced vibrational resistance.
• coarse adjustment. Some materials, such as stainless steel, are warm forged
at temperatures up to 1000°F. The heating results in two
Fine Threads provide... benefits, lower forging pressures due to lower yield
• higher tensile strength. strength and reduced work hardening rates.
• greater vibrational resistance.
• finer adjustment. Machining is the oldest method and is used for very large
diameters or small production runs.
Their disadvantages are…
• easier cross threaded. The disadvantage is that machining cuts the metal grain
• threads damaged more easily by handling. flow, thus creating planes of weakness at the critical head-
• tap drill size slightly more critical. to-shank fillet area. This can reduce tension fatigue
• slightly lower thread stripping strength. performance by providing fracture planes.
108
Screw Fastener Theory & Applications
This is the accepted practice for high fatigue performance Fatigue tests on threaded fasteners are usually alternating
bolts such as those used in aircraft and space applications. tension-tension loading. Most testing is done at more
severe strain than its designed service load but usually
below the material yield strength.
FASTENER POINT END
Shear testing, as previously mentioned, consists of
loading a fastener perpendicular to its axis. All shear
testing should be accomplished on the un-threaded
portion of the fastener.
When a fastener tensile test is plotted, a load/ elongation In summary, in order to prevent service failures,
curve can be obtained. From this curve, a yield determi- many things must be considered:
nation known as Johnson‘s 2/3 approximate method for
determination of yield strength is used to establish The Application Requirements
fastener yield, which will be acceptable for design Strength Needed – Safety Factors
purposes. It is not recommended for quality control or • Tension/Shear/Fatigue
specification requirements. • Temperature
• Corrosion
Torque-tension testing is conducted to correlate the • Proper Preload
required torque necessary to induce a given load in a
mechanically fastened joint. It can be performed by hand The Fastener Requirements
or machine. The load may be measured by a tensile • Material
machine, a load cell, a hydraulic tensile indicator or by a • Fabrication Controls
strain gage. • Performance Evaluations
109
Joint Diagrams
AN EXPLANATION OF JOINT DIAGRAMS must then be applied to the bolt. If the external load
When bolted joints are subjected to external tensile loads, is alternating, the increased stress levels on the bolt
what forces and elastic deformation really exist? The producea greatly shortened fatigue life.
majority of engineers in both the fastener manufacturing
and user industries still are uncertain. Several papers, When seating requires a certain minimum force or
articles, and books, reflecting various stages of research when transverse loads are to be transformed by friction,
into the problem have been published and the volume of the minimum clamping load FJ min is important.
this material is one reason for confusion. The purpose of
this article is to clarify the various explanations that have FJ min = FB max – Fe
been offered and to state the fundamental concepts which
apply to forces and elastic deformations in concentrically
loaded joints. The article concludes with general design
formulae that take into account variations in tightening,
preload loss during service, and the relation between
preloads, external loads and bolt loads.
110
Joint Diagrams
Spring Constants When the outside diameter of the joint is smaller than
To construct a joint diagram, it is necessary to determine or equal to the bolt head diameter, i.e.,as in a thin
the spring rates of both bolt and joint. In general, spring bushing, the normal cross sectioned area is computed:
rate is defined as: A s = π (Dc2 — Dh2)
4
K= F
∆l where
From Hook’s law: Dc = OD of cylinder or bushing and
Dh = hole diameter
∆ l = lF
EA When the outside diameter of the joint is larger than
Therefore: head or washer diameter DH , the stress distribution
is in the shape of a barrel, Fig 5. A series of
K = EA investigations proved that the areas of the following
l substitute cylinders are close approximations for
To calculate the spring rate of bolts with different cross calculating the spring contents of concentrically
sections, the reciprocal spring rates, or compliances, loaded joints.
of each section are added:
When the joint diameter DJ is greater than DH but
1 = 1 + 1 + .... + 1 less than 3DH;
KB K1 K2 Kn
Thus, for the bolt shown in Fig. 4:
1 =
KB
1
E ( 0.4d + l 1 + l 2 + l 3 + 0.4d
A1 A1 A2 Am Am ) 20
0
-20
where -40
40
d = the minor thread diameter and -60
-30
0.4d
I1
-35
-40
Fig. 4 Analysis
of bolt lengths
I2 d Ij contributing to
the bolt spring
rate.
I3
Fig. 5 Lines of equal axial stresses in a bolted joint
0.4d
obtained by the axisymmetric finite element method
are shown for a 9/16—18 bolt preloaded to 100 KSI.
Positive numbers are tensile stresses in KSI;
negative numbers are compressive stresses in KSI.
111
Joint Diagrams
Fe Fe
σB
Fe Fe
2 2 2 2
σB B σB
A σB
Fe
Fe
Fe Fe Fe Fe
2 2 2 2
Fi Fi
Fig. 6 Joint diagram of a springy bolt in a stiff joint (A), is compared to a diagram of a stiff bolt in a springy joint (B).
Preload Fi and external load Fe are the same but diagrams show that alternating bolt stresses are significantly lower with
a spring bolt in a stiff joint.
112
Joint Diagrams
Fe Fe
FeB 2 2
λ 1
ß
2
Fe
FeJ
nl j Ij
3
λ
4
Fe Fe
2 2
α ß
∆lB ∆lJ
Fe
Fe
113
Joint Diagrams
Fe
Fe
Fe
Fe
Fe
Fe
FeB =0
FeB
FeB
Fe
Fe
Fe
Fi Fi
Fi
FeB = ΦFe
Fe
FeJ = (1-Φ) Fe
FB max
Fi
FJ min
114
Joint Diagrams
SYMBOLS
115
The Torque-Tension Relationship
TIGHTENING TORQUES AND THE fastener underhead, full friction reduction will not be
TORQUE-TENSION RELATIONSHIP achieved. Similarly, if the material against which the
fastener is bearing, e.g. aluminum, is different than the
All of the analysis and design work done in advance will internal thread material, e.g. cast iron, the effective friction
have little meaning if the proper preload is not achieved. may be difficult to predict, These examples illustrate the
Several discussions in this technical section stress the importance and the value of identifying the torque-tension
importance of preload to maintaining joint integrity. There relationship. It is a recommend practice too contact the
are many methods for measuring preload (see Table 12). lubricant manufacturer for K-value information if a
However, one of the least expensive techniques that lubricant will be used.
provides a reasonable level of accuracy versus cost is by
measuring torque. The fundamental characteristic The recommended seating torques for Unbrako headed
required is to know the relationship between torque and socket screws are based on inducing preloads
tension for any particular bolted joint. Once the desired reasonably expected in practice for each type. The values
design preload must be identified and specified first, then for Unbrako metric fasteners are calculated using
the torque required to induce that preload is determined. VDI2230, a complex method utilized extensively in
Europe. All values assume use in the received condition in
Within the elastic range, before permanent stretch is steel holes. It is understandable the designer may need
induced, the relationship between torque and tension is preloads higher than those listed. The following
essentially linear (see figure 13). Some studies have found discussion is presented for those cases.
up to 75 variables have an effect on this relationship:
materials, temperature, rate of installation, thread
helix angle, coefficients of friction, etc. One way that has TORSION-TENSION YIELD AND TENSION
been developed to reduce the complexity is to depend CAPABILITY AFTER TORQUING
on empirical test results. That is, to perform experiments Once a headed fastener has been seated against a
under the application conditions by measuring the induced bearing surface, the inducement of torque will be translated
torque and recording the resulting tension. This can be into both torsion and tension stresses. These stresses
done with relatively simple, calibrated hydraulic pressure combine to induce twist. If torque continues to be induced,
sensors, electric strain gages, or piezoelectric load cells. the stress along the angle of twist will be the largest
Once the data is gathered and plotted on a chart, the stress while the bolt is being torqued. Consequently, the
slope of the curve can be used to calculate a correlation stress along the bolt axis (axial tension) will be something
factor. This technique has created an accepted formula less. This is why a bolt can fail at a lower tensile stress
for relating torque to tension. during installation than when it is pulled in straight tension
T=KXDXP alone, eg . a tensile test. Research has indicated the axial
tension can range from 135,000 to 145,000 PSI for industry
T = torque, lbf.-in. socket head cap screws at torsion-tension yield, depending
D = fastener nominal diameter, inches on diameter. Including the preload variation that can
P = preload, lbf. occur with various installation techniques, eg. up to 25%,
K = “nut factor,” “tightening factor,” or “k-value” it can be understood why some recommended torques
If the preload and fastener diameter are selected in the induce preload reasonably lower than the yield point.
design process, and the K-value for the application
conditions is known, then the necessary torque can be Figure 13 also illustrates the effect of straight tension
calculated. It is noted that even with a specified torque, applied after installation has stopped. Immediately after
actual conditions at the time of installation can result in stopping the installation procedure there will be some
variations in the actual preload achieved (see Table 12). relaxation, and the torsion component will drop toward
zero. This leaves only the axial tension, which keeps
One of the most critical criteria is the selection of the
the joint clamped together. Once the torsion is relieved,
K-value. Accepted nominal values for many industrial
the axial tension yield value and ultimate value for the
applications are:
fastener will be appropriate.
K = 0.20 for as-received steel bolts into steel holes
K = 0.15 steel bolts with cadmium plating, which acts like
a lubricant, Table 12
Industrial Fasteners Institute’s
K = 0.28 steel bolts with zinc plating. Torque-Measuring Method
The K-value is not the coefficient of the friction (µ); it is
an empirically derived correlation factor. Preload Measuring Accuracy Relative
Method Percent Cost
It is readily apparent that if the torque intended for a Feel (operator’s judgement) ±35 1
zinc plated fastener is used for cadmium plated fastener, Torque wrench ±25 1.5
the preload will be almost two times that intended; it Turn of the nut ±15 3
may actually cause the bolt to break. Load-indicating washers ±10 7
Fastener elongation ±3 to 5 15
Another influence is where friction occurs. For steel Strain gages ±1 20
bolts holes, approximately 50% of the installation torque
is consumed by friction under the head, 35% by thread
friction, and only the remaining 15% inducing preload
tension. Therefore, if lubricant is applied just on the
116
The Torque-Tension Relationship
Elongation (in.)
117
Stripping Strength of Tapped Holes
STRIPPING STRENGTH OF TAPPED HOLES • Stripping strength values vary with diameter of screw.
For a given load and material, larger diameter bolts
Charts and sample problems for obtaining minimum
required greater engagement.
thread engagement based on applied load, material,
type of thread and bolt diameter.
• Minimum length of engagement (as a percent of screw
Knowledge of the thread stripping strength of tapped diameter) is a straight line function of load. This permits
holes is necessary to develop full tensile strength of the easy interpolation of test data for any intermediate load
bolt or, for that matter, the minimum engagement needed condition.
for any lesser load.
• When engagement is plotted as a percentage of bolt
Conversely, if only limited length of engagement is diameter, it is apparent that stripping strengths for a wide
available, the data help determine the maximum load that range of screw sizes are close enough to be grouped in
can be safely applied without stripping the threads of a single curve. Thus , in the accompanying charts, data
the tapped hole. for sizes #0 through #12 have been represented by a
single set of curves.
Attempts to compute lengths of engagement and related
factors by formula have not been entirely satisfactory- With these curves, it becomes a simple matter to
mainly because of subtle differences between various determine stripping strengths and lengths of engagement
materials. Therefore, strength data has been empirically for any condition of application. A few examples are given
developed from a series of tensile tests of tapped below:
specimens for seven commonly used metals including
steel, aluminum, brass and cast iron. Example 1. Calculate length of thread engagement
necessary to develop the minimum ultimate tensile
The design data is summarized in the six accompanying strength (190,000 psi) of a 1/2–13 (National Coarse)
charts, (Charts E504-E509), and covers a range of screw Unbrako cap screw in cast iron having an ultimate shear
thread sizes from #0 to one inch in diameter for both strength of 30,000 psi. E505 is for screw sizes from #0
coarse and fine threads. Though developed from tests of through #10; E506 and E507 for sizes from 1/4 in. through
Unbrako socket head cap screws having minimum 5/8 in.; E508 and E509 for sizes from 3/4 in. through 1 in.
ultimate tensile strengths (depending on the diameter) Using E506 a value 1.40D is obtained. Multiplying nominal
from 190,000 to 180,000 psi , these stripping strength bolt diameter (0.500 in.) by 1.40 gives a minimum
values are valid for all other screws or bolts of equal or length of engagement of 0.700 in.
lower strength having a standard thread form. Data are
based on static loading only. Example 2. Calculate the length of engagement for the
above conditions if only 140,000 psi is to be applied. (This
In the test program, bolts threaded into tapped specimens is the same as using a bolt with a maximum tensile
of the metal under study were stressed in tension until the strength of 140,000psi.) From E506 obtain value of 1.06D
threads stripped. Load at which stripping occurred and the Minimum length of engagement = (0.500) (1.06) = 0.530.
length of engagement of the specimen were noted.
Conditions of the tests, all of which are met in a majority Example 3. Suppose in Example 1 that minimum length
of industrial bolt applications, were: of engagement to develop full tensile strength was not
available because the thickness of metal allowed a tapped
• Tapped holes had a basic thread depth within the range hole of only 0.600 in. Hole depth in terms of bolt
of 65 to 80 per cent. Threads of tapped holes were dia. = 0.600/0.500 = 1.20D. By working backwards in
Class 2B fit or better. Fig. 2, maximum load that can be carried is approximately
159,000 psi.
• Minimum amount of metal surrounding the tapped
hole was 2 1/2 times the major diameter. Example 4. Suppose that the hole in Example 1 is to be
tapped in steel having an ultimate shear strength 65,000
• Test loads were applied slowly in tension to screws psi. There is no curve for this steel in E506 but a design
having standard Class 3A threads. (Data, though, will value can be obtained by taking a point midway between
be equally applicable to Class 2A external threads as curves for the 80,000 psi and 50,000 psi steels that are
well.) listed. Under the conditions of the example, a length of
engagement of 0.825D or 0.413 in. will be obtained.
• Study of the test results revealed certain factors that
greatly simplified the compilation of thread stripping
strength data:
118
Stripping Strength of Tapped Holes
119
Stripping Strength of Tapped Holes
120
Stripping Strength of Tapped Holes
121
High-Temperature Joints
122
High-Temperature Joints
Fw Fc Fc Fw 200
123
High-Temperature Joints
the clamping stress at assembly conditions, the apply preload (the most common and simplest method
elongation should be multiplied by the modulus of available), a plus or minus 25 per cent variation in
elasticity at room temperature. induced load can result. Therefore, the maximum load
which could be expected in this case would be 1.5 times
.0033 X 30.6 X 106 = 101,145 psi the minimum, or:
The assembly conditions will be affected by the difference (1.5)(102,635) = 153,950 psi
between th ideal and actual coefficients of expansion of
the joint. The ideal coeffienct for the fastener material was This value does not exceed the room-temperature yield
calculated to be 7.05 but the closest material — H-11 — strength for H-11 given in Table 19.
has a coefficient of 7.1. Since this material has a greater
expansion than calculated, there will be a reduction in Since there is a decrease in the clamping force with an
clamping force resulting from the increase in temperature. increase in temperature and since the stress at operating
This amount equals the difference between the ideal and temperature can be higher than originally calculated
the actual coefficients multiplied by the change in because of variations in induced load, it is necessary to
temperature, the length of the fastener, and the modulus ascertain if yield strength at 800°F will be exceeded
of elasticity at 70°F.
(max stress at 70°F + change in stress) X E at 800°F
[(7.1 — 7.05) X 10-6] [ 800 - 70] [1.333] X E at 70°F
[30.6 X 106] = 1,490 psi [153,950 + (-1490)] X 24.6 X 106 = 122,565
The result must be added to the initial calculated stresses 30.6 X 106
to establish the minimum required clamping stress needed This value is less than the yield strength for H-11 at 800°F,
for assembling the joint at room temperature. Table 19. Therefore, a 1/4-28 H-11 bolt stressed between
102,635 psi and 153,950 psi at room temperature will
101,145 + 1,490 = 102,635 psi maintain a clamping load 1500 lb at 800°F after 1000 hr of
operation. A cyclic loading of 100 lb, which results in a bolt
Finally, the method of determining the clamping force or loading between 1500 and 1600 lb will not cause fatigue
preload will affect the final stress in the joint at operating failure at the operating conditions.
conditions. For example, if a torque wrench is used to
Table 16
PHYSICAL PROPERTIES OF MATERIALS USED TO MANUFACTURE ALLOY STEEL SHCS’S
Coefficient of Thermal Expansion, µm/m/°K1 Table 19 - Yield Strength at Various Temperatures
20°C to 100 200 300 400 500 600 –––––– Temperature (F) ––––––
68°F to 212 392 572 752 932 1112 Alloy
70 800 1000 1200
Material
Stainless Steels
5137M, Type 302 35,000 35,000 34,000 30,000
2
51B37M – 12.6 13.4 13.9 14.3 14.6 Type 403 145,000 110,000 95,000 38,000
PH 15-7 Mo 220,000 149,000 101,000 –
41373 11.2 11.8 12.4 13.0 13.6 –
High Strength Iron-Base Stainless Alloys
41403 12.3 12.7 – 13.7 – 14.5 A 286 95,000 95,000 90,000 85,000
43403 – 12.4 – 13.6 – 14.5 AMS 5616 113,000 80,000 60,000 40,000
Unitemp 212 150,000 140,000 135,000 130,000
87353 11.7 12.2 12.8 13.5 – 14.1 High Strength Iron-Base Alloys
87403 11.6 12.2 12.8 13.5 – 14.1 AISI 4340 200,000 130,000 75,000 –
H-11 (AMS 6485) 215,000 175,000 155,000 –
AMS 6340 160,000 100,000 75,000 –
Nickel-Base Alloys
Modulus of Elongation (Young’s Modulus) Iconel X – - 98,000
115,000
E = 30,000,000 PSI/in/in Waspaloy 115,000 – 106,000 100,000
NOTES:
1. Developed from ASM, Metals HDBK, 9th Edition, Vol. 1 (°C = °K for values listed)
2. ASME SA574
3. AISI
4. Multiply values in table by .556 for µin/in/°F.
124
Corrosion in Threaded Fasteners
All fastened joints are, to some extent, subjected to tions.For example, stainless steel and aluminum resist
corrosion of some form during normal service life. Design corrosion only so long as their protective oxide film
of a joint to prevent premature failure due to corrosion remains unbroken. Alloy steel is almost never used, even
must include considerations of the environment, under mildly corrosive conditions, without some sort of
conditions of loading , and the various methods of protective coating. Of course, the presence of a specific
protecting the fastener and joint from corrosion. corrosive medium requires a specific corrosion-resistant
fastener material, provided that design factors such as
Three ways to protect against corrosion are: tensile and fatigue strength can be satisfied.
1. Select corrosion-resistant material for the fastener.
2. Specify protective coatings for fastener, joint interfaces, Protective Coating
or both. A number of factors influence the choice of a corrosion-
3. Design the joint to minimize corrosion. resistant coating for a threaded fastener. Frequently, the
corrosion resistance of the coating is not a principal
The solution to a specific corrosion problem may require consideration. At times it is a case of economics. Often,
using one or all of these methods. Economics often less-costly fastener material will perform satisfactorily in
necessitate a compromise solution. a corrosive environment if given the proper protective
coating.
Fastener Material
The use of a suitably corrosion-resistant material is often Factors which affect coating choice are:
the first line of defense against corrosion. In fastener
design, however, material choice may be only one of
• Corrosion resistance
several important considerations. For example, the most
corrosion-resistant material for a particular environment • Temperature limitations
may just not make a suitable fastener. • Embrittlement of base metal
• Effect on fatigue life
Basic factors affecting the choice of corrosion resistant • Effect on locking torque
threaded fasteners are:
• Compatibility with adjacent material
• Tensile and fatigue strength. • Dimensional changes
• Position on the galvanic series scale of the fastener and • Thickness and distribution
materials to be joined. • Adhesion characteristics
• Special design considerations: Need for minimum
weight or the tendency for some materials to gall. Conversion Coatings: Where cost is a factor and
• Susceptibility of the fastener material to other types corrosion is not severe, certain conversion-type coatings
of less obvious corrosion. For example, a selected are effective. These include a black-oxide finish for alloy-
steel screws and various phosphate base coatings for
material may minimize direct attack of a corrosive
carbon and alloy-steel fasteners. Frequently, a rust-
environment only to be vulnerable to fretting or stress preventing oil is applied over a conversion coating.
corrosion.
Some of the more widely used corrosion-resistant Paint: Because of its thickness, paint is normally not
materials, along with approximate fastener tensile considered for protective coatings for mating threaded
strength ratings at room temperature and other pertinent fasteners. However, it is sometimes applied as a supple-
properties, are listed in Table 1. Sometimes the nature of mental treatment at installation. In special cases, a
corrosion properties provided by these fastener materials fastener may be painted and installed wet, or the entire
is subject to change with application and other condi- joint may be sealed with a coat of paint after installation.
125
Corrosion in Threaded Fasteners
Electroplating: Two broad classes of protective For Direct Attack: Choose the right corrosion resistant
electroplating are: 1. The barrier type-such as chrome material. Usually a material can be found that will provide
plating-which sets up an impervious layer or film that is the needed corrosion resistance without sacrifice of other
more noble and therefore more corrosion resistant than important design requirements. Be sure that the fastener
the base metal. 2. The sacrificial type, zinc for example, material is compatible with the materials being joined.
where the metal of the coating is less noble than the
base metal of the fastener. This kind of plating corrodes Corrosion resistance can be increased by using a
sacrificially and protects the fastener. conversion coating such as black oxide or a phosphate-
base treatment. Alternatively, a sacrificial coating such as
Noble-metal coatings are generally not suitable for zinc plating is effective
threaded fasteners-especially where a close-tolerance fit
is involved. To be effective, a noble-metal coating must be For an inexpensive protective coating, lacquer or paint
at least 0.001 in. thick. Because of screw-thread geometry, can be used where conditions permit.
however, such plating thickness will usually exceed the
tolerance allowances on many classes of fit for screws. For Galvanic Corrosion: If the condition is severe,
electrically insulate the bolt and joint from each other..
Because of dimensional necessity, threaded fastener
coatings, since they operate on a different principle, are The fastener may be painted with zinc chromate primer
effective in layers as thin as 0.0001 to 0.0002 in. prior to installation, or the entire joint can be coated with
lacquer or paint.
The most widely used sacrificial platings for threaded
fasteners are cadmium, zinc, and tin. Frequently, the Another protective measure is to use a bolt that is
cadmium and zinc are rendered even more corrosion cathodic to the joint material and close to it in the galvanic
resistant by a posting-plating chromate-type conversion series. When the joint material is anodic, corrosion will
treatment. Cadmium plating can be used at temperatures spread over the greater area of the fastened materials.
to 450°F. Above this limit, a nickel cadmium or nickel-zinc Conversely, if the bolt is anodic, galvanic action is most
alloy plating is recommended. This consists of alternate severe.
deposits of the two metals which are heat-diffused into a Steel
uniform alloy coating that can be used for applications to
900°F. The alloy may also be deposited directly from the Insulation
plating bath. Copper washer
Insulation
Fastener materials for use in the 900 to 1200°F range gasket
(stainless steel, A-286), and in the 1200° to 1800°F range
(high-nickel-base super alloys) are highly corrosion resis-
tant and normally do not require protective coatings,
except under special environment conditions.
Steel
Silver plating is frequently used in the higher temperature
ranges for lubrication to prevent galling and seizing,
particularly on stainless steel. This plating can cause a
galvanic corrosion problem, however, because of the high
nobility of the silver. FIG. 1.1— A method of electrically insulating a bolted
joint to prevent galvanic corrosion.
Hydrogen Embrittlement: A serious problem, known as
hydrogen embrittlement, can develop in plated alloy steel
fasteners. Hydrogen generated during plating can diffuse For Concentration-Cell Corrosion: Keep surfaces
into the steel and embrittle the bolt. The result is often a smooth and minimize or eliminate lap joints, crevices,
delayed and total mechanical failure, at tensile levels far and seams. Surfaces should be clean and free of organic
below the theoretical strength, high-hardness structural material and dirt. Air trapped under a speck of dirt on the
parts are particularly susceptible to this condition. The surface of the metal may form an oxygen concentration
problem can be controlled by careful selection of plating cell and start pitting.
formulation, proper plating procedure, and sufficient
baking to drive off any residual hydrogen. For maximum protection, bolts and nuts should have
smooth surfaces, especially in the seating areas. Flush-
Another form of hydrogen embrittlement, which is more head bolts should be used where possible. Further,
difficult to control, may occur after installation. Since joints can be sealed with paint or other sealant material.
electrolytic cell action liberates hydrogen at the cathode,
it is possible for either galvanic or concentration-cell For Fretting Corrosion: Apply a lubricant (usually oil)
corrosion to lead to embrittling of the bolt to mating surfaces. Where fretting corrosion is likely to
material. occur: 1. Specify materials of maximum practicable hard-
ness. 2. Use fasteners that have residual compressive
Joint Design stresses on the surfaces that may be under attack. 3.
Certain precautions and design procedures can be Specify maximum preload in the joint. A higher clamping
followed to prevent, or at least minimize, each of the force results in a more rigid joint with less relative
various types of corrosion likely to attack a threaded joint. movement possible between mating services.
The most important of these are:
126
Corrosion in Threaded Fasteners
For Stress Corrosion: Choose a fastener material that If the solution consists of salts of the metal itself, a metal-
resists stress corrosion in the service environment. ion cell is formed, and corrosion takes place on the
Reduce fastener hardness (if reduced strength can be surfaces in close contact. The corrosive solution between
tolerated), since this seems to be a factor in stress the two surfaces is relatively more stagnant (and thus
corrosion. has a higher concentration of metal ions in solution) than
the corrosive solution immediately outside the crevice.
Minimize crevices and stress risers in the bolted joint and
compensate for thermal stresses. Residual stresses A variation of the concentration cell is the oxygen cell in
resulting from sudden changes in temperature accelerate which a corrosive medium, such as moist air, contains
stress corrosion. different amounts of dissolved oxygen at different points.
Accelerated corrosion takes place between hidden
If possible, induce residual compressive stresses into the surfaces (either under the bolt head or nut, or between
surface of the fastener by shot-peening or pressure rolling. bolted materials) and is likely to advance without
detection.
For Corrosion Fatigue: In general, design the joint for high
fatigue life, since the principal effect of this form of Fretting…corrosive attack or deterioration occurring
corrosion is reduced fatigue performance. Factors between containing, highly-loaded metal surfaces
extending fatigue performance are: 1. Application and subjected to very slight (vibratory) motion. Although the
maintenance of a high preload. 2. Proper alignment to mechanism is not completely understood, it is probably
avoid bending stresses. a highly accelerated form of oxidation under heat and
stress. In threaded joints, fretting can occur between
If the environment is severe, periodic inspection is mating threads, at the bearing surfaces under the head
recommended so that partial failures may be detected of the screw, or under the nut. It is most likely to occur in
before the structure is endangered. high tensile, high-frequency, dynamic-load applications.
There need be no special environment to induce this
As with stress and fretting corrosion, compressive form of corrosion...merely the presence of air plus
stresses induced on the fastener surfaces by thread vibratory rubbing. It can even occur when only one of the
rolling, fillet rolling, or shot peening will reduce corrosion materials in contact is metal.
fatigue. Further protection is provided by surface coating.
Stress Corrosion Cracking…occurs over a period of
TYPES OF CORROSION time in high-stressed, high-strength joints. Although not
Direct Attack…most common form of corrosion affecting fully understood, stress corrosion cracking is believed to
all metals and structural forms. It is a direct and general be caused by the combined and mutually accelerating
chemical reaction of the metal with a corrosive medium- effects of static tensile stress and corrosive environment.
liquid, gas, or even a solid. Initial pitting somehow tales place which, in turn, further
increases stress build-up. The effect is cumulative and,
Galvanic Corrosion…occurs with dissimilar metals in a highly stressed joint, can result in sudden failure.
contact. Presence of an electrolyte, which may be nothing
more than an individual atmosphere, causes corrosive Corrosion Fatigue…accelerated fatigue failure occurring
action in the galvanic couple. The anodic, or less noble in the presence of a corrosive medium. It differs from
material, is the sacrificial element. Hence, in a joint of stress corrosion cracking in that dynamic alternating
stainless steel and titanium, the stainless steel corrodes. stress, rather than static tensile stress, is the contributing
One of the worst galvanic joints would consist of agent.
magnesium and titanium in contact.
Corrosion fatigue affects the normal endurance limit of
Concentration Cell Corrosion…takes place with metals the bolt. The conventional fatigue curve of a normal bolt
in close proximity and, unlike galvanic corrosion, does not joint levels off at its endurance limit, or maximum dynamic
require dissimilar metals. When two or more areas on the load that can be sustained indefinitely without fatigue
surface of a metal are exposed to different concentrations failure. Under conditions of corrosion fatigue, however,
of the same solution, a difference in electrical potential the curve does not level off but continues downward to a
results, and corrosion takes place. point of failure at a finite number of stress cycles.
127
Corrosion in Threaded Fasteners
GALVANIC CORROSION
Magnesium †
M M M M M M M M M M M M M M M M M M M
Cadmium and Zinc Plate, Galvanized Steel,
Beryllium, Clad Aluminum B M M B T N T N N N N T N N B N N N
Aluminum, 1100, 3003, 5052, 6063,
6061, 356 M M B B N B T N N N T N T B N N N
128
Impact Performance
129
Impact Performance
TABLE 20
LOW-TEMPERATURE IMPACT PROPERTIES OF SELECTED ALLOY STEELS
Heat Temperature* Transition
Composition, % Impact Energy,
Temp.
Ft.-lb
Quenching Tempering (50%
Temp. Temp. Hardness Brittle)
AISI no. C Mn Ni Cr Mo F+ F Rc –300°F –200°F –100°F O°F 100°F °f
130
Impact Performance
180
TENSION IMPACT
FASTENER
160
TENSION IMPACT LBF.-FT.
140
120
100
80
60
40
CHARPY V NOTCH
SPECIMEN
20
FIG. 21
131
Impact Performance
ROOM TEMPERATURE
180
160
TENSION IMPACT LBF.-FT.
140
3/8
120
100
80
5/16
60
40
20
1/4
FIG. 22
132
Product Engineering Bulletin
There is a common, yet reasonable, misconception be met to be called “Grade 8”. Three of the most
that standard, inch, alloy steel socket head cap important characteristics are not consistent with
screws are “Grade 8”. This is not true. The requirements for industry standard SHCSs: tensile
misconception is reasonable because “Grade 8” is strength, hardness, and head marking. Some basic
a term generally associated with “high strength” differences between several fastener classifications
fasteners. A person desiring a “high strength” SHCS are listed below. The list is not comprehensive but
may request a “Grade 8 SHCS”. This is technically intended to provide a general understanding.
incorrect for standard SHCSs. The term Grade 8 SHCSs can be manufactured to meet Grade 8
defines specific fastener characteristics which must requirements on a special order basis.
Typical Bolts Screws Bolts Screws Bolts Screws Socket Head Socket Head
Fasteners Studs Hex Heads Studs Hex Heads Studs Hex Heads Cap Screw Cap Screw
133
Metric Threads
Nominal Size
Pitch
M5 X 0.8 – 4g6g
Tolerance Position )
(Allowance) ) Crest Diameter Tolerance Symbol
Tolerance Grade )
Tolerance Position )
(Allowance) ) Pitch Diameter Tolerance Symbol
Tolerance Grade )
DEVIATIONS +100
2B 6H
external internal basic clearance +50
h H none
g G small 0
e large Allowance Allowance = 0
–50
2A 6g 6h
–100
NOTES: –160 After
5/16 UNC plating
Lower case letters = external threads Plain
Capital letters = internal threads –200
µm BOLT THREAD
134
Through-Hole Preparation
Close Fit: Normally limited to holes for those lengths of Chamfering: It is considered good practice to chamfer or
screws threaded to the head in assemblies in which: (1) break the edges of holes that are smaller than “F”
only one screw is used; or (2) two or more screws are maximum in parts in which hardness approaches, equals
used and the mating holes are produced at assembly or or exceeds the screw hardness. If holes are not
by matched and coordinated tooling. chamfered, the heads may not seat properly or the sharp
edges may deform the fillets on the screws, making them
Normal Fit: Intended for: (1) screws of relatively long susceptible to fatigue in applications that involve dynamic
length; or (2) assemblies that involve two or more screws loading. The chamfers, however, should not be larger than
and where the mating holes are produced by conven- needed to ensure that the heads seat properly or that the
tional tolerancing methods. It provides for the maximum fillet on the screw is not deformed. Normally, the chamfers
allowable eccentricity of the longest standard screws and do not need to exceed “F” maximum. Chamfers exceeding
for certain deviations in the parts being fastened, such as these values reduce the effective bearing area and
deviations in hole straightness; angularity between the introduce the possibility of indentation when the parts
axis of the tapped hole and that of the hole for the shank; fastened are softer than screws, or the possibility of
differences in center distances of the mating holes and brinnelling of the heads of the screws when the parts are
other deviations. harder than the screws.
A X C hole dimensions
drill size for hole A
basic counter- countersink tap drill size **body counter-
nominal screw close fit normal fit bore diameter D drill bore
size diameter nom. dec. nom. dec. diameter Max.+2F(Max.) UNRC UNRF size size
0 0.0600 51* 0.0670 49* 0.0730 1/8 0.074 – 3/64 #51 1/8
1 0.0730 46* 0.0810 43* 0.0890 5/32 0.087 1.5mm #53 #46 5/32
2 0.0860 3/32 0.0937 36* 0.1065 3/16 0.102 #50 #50 3/32 3/16
3 0.0990 36* 0.1065 31* 0.1200 7/32 0.115 #47 #45 #36 7/32
4 0.1120 1/8 0.1250 29* 0.1360 7/32 0.130 #43 #42 1/8 7/32
5 0.1250 9/64 0.1406 23* 0.1540 1/4 0.145 #38 #38 9/64 1/4
6 0.1380 23* 0.1540 18* 0.1695 9/32 0.158 #36 #33 #23 9/32
8 0.1640 15* 0.1800 10 0.1935 5/16 0.188 #29 #29 #15 5/16
10 0.1900 5* 0.2055 2* 0.2210 3/8 0.218 #25 #21 #5 3/8
1/4 0.2500 17/64 0.2656 9/32 0.2812 7/16 0.278 #7 #3 17/64 7/16
5/16 0.3125 21/64 0.3281 11/32 0.3437 17/32 0.346 F I 21/64 17/32
3/8 0.0375 25/64 0.3906 13/32 0.4062 5/8 0.415 5/16 Q 25/64 5/8
7/16 0.4375 29/64 0.4531 15/32 0.4687 23/32 0.483 U 25/64 29/64 23/32
1/2 0.5000 33/64 0.5156 17/32 0.5312 13/16 0.552 27/64 29/64 33/64 13/16
5/8 0.6250 41/64 0.6406 21/32 0.6562 1 0.689 35/64 14.5mm 41/64 1
3/4 0.7500 49/64 0.7656 25/32 0.7812 1-3/16 0.828 21/32 11/16 49/64 1-3/16
7/8 0.8750 57/64 0.8906 29/32 0.9062 1-3/8 0.963 49/64 20.5mm 57/64 1-3/8
1 1.0000 1-1/64 1.0156 1-1/32 1.0312 1-5/8 1.100 7/8 59/64 1-1/64 1-5/8
1-1/4 1.2500 1-9/32 1.2812 1-5/32 1.3125 2 1.370 1-7/64 1-11/64 1-9/32 2
1-1/2 1.5000 1-17/32 1.5312 1-9/16 1.5625 2-3/8 1.640 34mm 36mm 1-17/32 2-3/8
135
Drill and Counterbore Sizes
DRILL AND COUNTERBORE SIZES FOR METRIC SOCKET HEAD CAP SCREWS
A X Y
136
Hardness Conversion Table
Superficial Rockwell
Superficial Rockwell
Superficial Rockwell
Superficial Rockwell
Superficial Rockwell
3000 KG 10mm Ball
Knoop Hardness
15 Kg N Diamond
30 Kg N Diamond
45 Kg N Diamond
Tensile Strength
100 Kg 1/16" Ball
60 Kg 1/16" Ball
150 Kg Diamond
60 Kg Diamond
60 Kg Diamond
DPH Vickers
Rockwell C
Rockwell D
Rockwell B
Rockwell A
Rockwell A
Rockwell F
15 Kg Ball
30 Kg Ball
45 Kg Ball
500g
500g
500g
KSI
KSI
C A D 15N 30N 45N HB HV KSI B A F 15T 30T 45T HB HV HK KSI
68 85.6 76.9 93.2 84.4 75.4 940 100 61.5 93.1 83.1 72.9 240 240 251 116
67 85 76.1 92.9 83.6 74.2 900 99 60.9 92.8 82.5 71.9 234 234 246 114
66 84.5 75.4 92.5 82.8 73.3 865 98 60.2 92.5 81.8 70.9 228 228 241 109
65 83.9 74.5 92.2 81.9 72 739 832 97 59.5 92.1 81.1 69.9 222 222 236 104
64 83.4 73.8 91.8 81.1 71 722 800 96 58.9 91.8 80.4 68.9 216 216 231 102
63 82.8 73 91.4 80.1 69.9 705 772 95 58.3 91.5 79.8 67.9 210 210 226 100
62 82.3 72.2 91.1 79.3 68.8 688 746 94 57.6 91.2 79.1 66.9 205 205 221 98
61 81.8 71.5 90.7 78.4 67.7 670 720 93 57 90.8 78.4 65.9 200 200 216 94
60 81.2 70.7 90.2 77.5 66.6 654 697 92 56.4 90.5 77.8 64.8 195 195 211 92
59 80.7 69.9 89.8 76.6 65.5 634 674 91 55.8 90.2 77.1 63.8 190 190 206 90
58 80.1 69.2 89.3 75.7 64.3 615 653 90 55.2 89.9 76.4 62.8 185 185 201 89
57 79.6 68.5 88.9 74.8 63.2 595 633 89 54.6 89.5 75.8 61.8 180 180 196 88
56 79 67.7 88.3 73.9 62 577 613 88 54 89.2 75.1 60.8 176 176 192 86
55 78.5 66.9 87.9 73 60.9 560 595 301 87 53.4 88.9 74.4 59.8 172 172 188 84
54 78 66.1 87.4 72 59.8 543 577 291 86 52.8 88.6 73.8 58.8 169 169 184 83
53 77.4 65.4 86.9 71.2 58.6 525 560 283 85 52.3 88.2 73.1 57.8 165 165 180 82
52 76.8 64.6 86.4 70.2 57.4 512 544 273 84 51.7 87.9 72.4 56.8 162 162 176 81
51 76.3 63.8 85.9 69.4 56.1 496 528 264 83 51.1 87.6 71.8 55.8 159 159 173 80
50 75.9 63.1 85.5 68.5 55 481 513 256 82 50.6 87.3 71.1 54.8 156 156 170 77
49 75.2 62.1 85 67.6 53.8 469 498 246 81 50 86.9 70.4 53.8 153 153 167 73
48 74.7 61.4 84.5 66.7 52.5 455 484 237 80 49.5 86.6 69.7 52.8 150 150 164 72
47 74.1 60.8 83.9 65.8 51.4 443 471 231 79 48.9 86.3 69.1 51.8 147 147 161 70
46 73.6 60 83.5 64.8 50.3 432 458 221 78 48.4 86 68.4 50.8 144 144 158 69
45 73.1 59.2 83 64 49 421 446 215 77 47.9 85.6 67.7 49.8 141 141 155 68
44 72.5 68.5 82.5 63.1 47.8 409 434 208 76 47.3 85.3 67.1 48.8 139 139 152 67
43 72 57.7 82 62.2 46.7 400 423 201 75 46.8 99.6 85 66.4 47.8 137 137 150 66
42 71.5 56.9 81.5 61.3 45.5 390 412 194 74 46.3 99.1 84.7 65.7 46.8 135 135 147 65
41 70.9 56.2 80.9 60.4 44.3 381 402 188 73 45.8 98.5 84.3 65.1 45.8 132 132 145 65
40 70.4 55.4 80.4 59.5 43.1 371 392 181 72 45.3 98 84 64.4 44.8 130 130 143 65
39 69.9 54.6 79.9 58.6 41.9 362 382 176 71 44.8 97.4 83.7 63.7 43.8 127 127 141 65
38 69.4 53.8 79.4 57.7 40.8 353 372 170 70 44.3 96.8 83.4 63.1 42.8 125 125 139 65
37 68.9 53.1 78.8 56.8 39.6 344 363 165 69 43.8 96.2 83 62.4 41.8 123 123 137 65
36 68.4 52.3 78.3 55.9 38.4 336 354 160 68 43.3 95.6 82.7 61.7 40.8 121 121 135 65
35 67.9 51.5 77.7 55 37.2 327 345 155 67 42.8 95.1 82.4 61 39.8 119 119 13 3 65
34 67.4 50.8 77.2 54.2 36.1 319 336 150 66 42.3 94.5 82.1 60.4 38.7 117 117 131 65
33 66.8 50 76.6 53.3 34.9 311 327 147 65 41.8 93.9 81.8 59.7 37.7 11 6 116 129 65
32 66.3 49.2 76.1 52.1 33.7 301 318 142 64 41.4 93.4 81.4 59 36.7 114 114 127
31 65.8 48.4 75.6 51.3 32.5 294 310 139 63 40.9 92.8 81.1 58.4 35.7 112 112 12 5
30 65.3 47.7 75 50.4 31.3 286 302 136 62 40.4 92.2 80.8 57.7 34.7 110 110 12 4
29 64.6 47 74.5 49.5 30.1 279 294 132 61 40 91.7 80.5 57 33.7 108 108 122
28 64.3 46.1 73.9 48.6 28.9 271 286 129 60 39.5 91.1 80.1 56.4 32.7 107 107 120
27 63.8 45.2 73.3 47.7 27.8 264 279 126 59 39 90.5 79.8 55.7 31.7 106 106 118
26 63.3 44.6 72.8 46.8 26.7 258 272 123 58 38.6 90 79.5 55 30.7 104 104 117
25 62.8 43.8 72.2 45.9 25.5 253 266 120 57 38.1 89.4 79.2 54.4 29.7 103 103 115
24 62.4 43.1 71.6 45 24.3 247 260 118 56 37.7 88.8 78.8 53.7 28.7 101 101 11 4
23 62 42.1 71 44 23.1 243 254 115 55 37.2 88.2 78.5 53 27.7 100 100 112
22 61.5 41.6 70.5 43.2 22 237 248 112 54 36.8 87.7 78.2 52.4 26.7 111
21 61 40.9 69.9 42.3 20.7 231 243 110 53 36.3 87.1 77.9 51.7 25.7 110
20 60.5 40.1 69.4 41.5 19.6 226 238 104 52 35.9 86.5 77.5 51 24.7 109
51 35.5 86 77.2 50.3 23.7 108
* Numbers above BHN 615 are outside recommended 50 35 85.4 76.9 49.7 22.7 107
range for Brinell testing ASTM method F10 49 34.6 84.8 76.6 49 21.7 10 6
** Tensile Strength in relation to hardness is inexact 48 34.1 84.3 76.2 48.3 20.7 105
unless determined for specific material 47 33.7 83.7 75.9 47.7 19.7 104
46 33.3 83.1 75.6 47 18.7 103
45 32.9 82.6 75.3 46.3 17.7 102
44 32.4 82 74.9 45.7 16.7 101
43 32 81.4 74.6 45 15.7 100
42 31.6 80.8 74.3 44.3 14.7 99
41 31.2 80.3 74 43.7 13.6 98
40 30.7 79.7 73.6 43 12.6 97
39 30.3 79.1 73.3 42.3 11.6 96
38 29.9 78.6 73 41.6 10.6 95
37 29.5 78 72.7 41 9.6 94
36 29.1 77.4 72.3 40.3 8.6 93
35 28.7 76.9 72 39.6 7.6 92
34 28.2 76.3 71.7 39 6.6 91
33 27.8 75.7 71.4 38.3 5.6 90
32 27.4 75.2 71 37.6 4.6 89
31 27 74.6 70.7 37 3.6 88
30 26.6 74 70.4 36.3 2.6 87
137
Thread Stress Area
Square Inches
Threads Per in.
Tensile Stress Area Per H-28
Diameter (in.) Diameter (mm) UNRC UNRF UNRC UNRF Nominal Shank
#0 0.06 1.52 – 80 – 0.00180 0.002827
#1 0.07 1.85 64 72 0.00263 0.00278 0.004185
#2 0.09 2.18 56 64 0.00370 0.00394 0.005809
#3 0.10 2.51 48 56 0.00487 0.00523 0.007698
#4 0.11 2.84 40 48 0.00604 0.00661 0.009852
#5 0.13 3.18 40 44 0.00796 0.00830 0.012272
#6 0.14 3.51 32 40 0.00909 0.01015 0.014957
#8 0.16 4.17 32 36 0.0140 0.01474 0.021124
#10 0.19 4.83 24 32 0.0175 0.0200 0.028353
1/4 0.25 6.35 20 28 0.0318 0.0364 0.049087
5/16 0.31 7.94 18 24 0.0524 0.0580 0.076699
3/8 0.38 9.53 16 24 0.0775 0.0878 0.11045
7/16 0.44 11.11 14 20 0.1063 0.1187 0.15033
1/2 0.50 12.70 13 20 0.1419 0.1599 0.19635
9/16 0.56 14.29 12 18 0.182 0.203 0.25
5/8 0.63 15.88 11 18 0.226 0.256 0.31
3/4 0.75 19.05 10 16 0.334 0.373 0.44179
7/8 0.88 22.23 9 14 0.462 0.509 0.60132
1 1.00 25.40 8 12 0.606 0.663 0.79
1-1/8 1.13 28.58 7 12 0.763 0.856 0.99402
1-1/4 1.25 31.75 7 12 0.969 1.073 1.2272
1-3/8 1.38 34.93 6 12 1.155 1.315 1.4849
1-1/2 1.50 38.10 6 12 1.405 1.581 1.7671
1-3/4 1.75 44.45 5 12 1.90 2.19 2.4053
2 2.00 50.80 4-1/2 12 2.50 2.89 3.1416
2-1/4 2.25 57.15 4-1/2 12 3.25 3.69 3.9761
2-1/2 2.50 63.50 4 12 4.00 4.60 4.9088
2-3/4 2.75 69.85 4 12 4.93 5.59 5.9396
3 3.00 76.20 4 12 5.97 6.69 7.0686
138
Thread Size Comparison
(M14) 2.00 12.50 1.50 17 14.00 0.551 1/2 13 20 0.500 1/2 12 16 0.500
M16 2.00 12.50 1.50 17 16.00 0.630 5/8 11 18 0.625 5/8 11 14 0.625
M24 3.00 8.50 2.00 12.50 24.00 0.945 1 1/8 7 12 1.125 1 1/8 7 9 1.125
(M27) 3.00 8.50 2.00 12.50 27.00 1.063 1 1/4 7 12 1.250 1 1/4 7 9 1.250
M30 3.50 7.25 2.00 12.50 30.00 1.181 1 1/2 6 12 1.500 1 1/2 6 8 1.500
139
Comparison of Different Strength Grades
140
NOTES
High Tensile
Alloy & Stainless
Steel Fasteners
NOTES
High Tensile
Alloy & Stainless
Steel Fasteners
We are always looking
for new partners.
UNBRAKO EUROPE
Deepak Fasteners Shannon Ltd.
Bays 25-30 Shannon Industrial
Estate, County Clare, Ireland
Tel: +353-61-716-500,
Fax: +353-61-716-584
UNBRAKO UK
Deepak Fasteners UK Ltd.
12-14 Tower Street, New Town
Birmingham - B19 3RR, U.K.
Tel: +44-121-333-4610,
Fax: +44-121-333-4525
UNBRAKO AUSTRALIA
Deepak Fasteners Australia Ltd.
67-69 Licola Crescent Dandenong
South Victoria 3175, Australia
Tel: +61-3-98940026,
Fax: +61-3-98940038
UNBRAKO INDIA
Deepak Fasteners India Ltd.
4th Floor, First Mall, Mall Road
Ludhiana- 141001 (Pb.) India
Tel: +91-161-3911111, 7131111
UNB-PUSDD-24072017
Fax: +91-161-2774400
Authorized Distributor:
www.unbrakousa.com
sales@unbrakousa.com