Product Texts: P:Partial Break

HOSTAFORM C 9021 | POM | Ticona - 2008-06-03
Request for Information | Disclaimer
Product Texts
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 03-002
POM copolymer
Standard-Injection molding type with high rigidity, hardness and

toughness; good chemical resistance to solvents, fuel and strong
alkalis as well as good hydrolysis resistance; high resistance to
thermal and oxidative degradation.
Fulfils EG-directive 2002/72/EU as well as the recommendation

XXXIII for consumer goods of the BgVV,
FDA compliant according to 21 CFR 177.2470
UL-registration for all colours and a thickness more than 1.5 mm as

UL 94 HB, temperature index UL 746 B electrical 110 °C, mechanical
90 °C.
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more
than 1 mm.
Ranges of applications: automotive engineering, precision

engineering, electric and electronical industry, domestic
appliances.
FDA = Food and Drug Administration (USA)

BgVV = Bundesinstitut fr gesundheitlichen Verbraucherschutz und
Veterin rmedizin
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)
Rheological properties Value Unit Test Standard

Melt volume-flow rate 8 cm³/10min ISO 1133
Temperature 190 °C ISO 1133
Load 2.16 kg ISO 1133
Molding shrinkage (parallel) 2.0 % ISO 294-4, 2577
Molding shrinkage (normal) 1.8 % ISO 294-4, 2577
Mechanical properties Value Unit Test Standard

Tensile Modulus 2850 MPa ISO 527-1/-2
Yield stress 64 MPa ISO 527-1/-2
Yield strain 9 % ISO 527-1/-2
Nominal strain at break 30 % ISO 527-1/-2
Tensile creep modulus (1h) 2500 MPa ISO 899-1
Tensile creep modulus (1000h) 1300 MPa ISO 899-1
Charpy impact strength (+23°C) 180[P] kJ/m² ISO 179/1eU
Charpy impact strength (-30°C) 160 kJ/m² ISO 179/1eU
Charpy notched impact strength (+23°C) 6.5 kJ/m² ISO 179/1eA
Charpy notched impact strength (-30°C) 6 kJ/m² ISO 179/1eA
P:Partial Break
Thermal properties Value Unit Test Standard

Melting temperature (10°C/min) 166 °C ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa) 104 °C ISO 75-1/-2
Vicat softening temperature (50°C/h 50N) 150 °C ISO 306
Coeff. of linear therm. expansion (parallel) 1.1 E-4/°C ISO 11359-1/-2
Coeff. of linear therm. expansion (normal) 1.1 E-4/°C ISO 11359-1/-2
Burning Behav. at 1.5 mm nom. thickn. HB class IEC 60695-11-10
Thickness tested 1.5 mm IEC 60695-11-10
UL recognition UL - -
Burning Behav. at thickness h HB class IEC 60695-11-10
Thickness tested 3.0 mm IEC 60695-11-10
UL recognition UL - -
Electrical properties Value Unit Test Standard

Relative permittivity (100Hz) 4 - IEC 60250
Relative permittivity (1 MHz) 4 - IEC 60250
Dissipation factor (100 Hz) 20 E-4 IEC 60250
Dissipation factor (1 MHz) 50 E-4 IEC 60250
Volume resistivity 1E12 Ohm*m IEC 60093
Surface resistivity 1E14 Ohm IEC 60093
Electric strength 35 kV/mm IEC 60243-1
Comparative tracking index 600 - IEC 60112
Other properties Value Unit Test Standard

Water absorption 0.65 % Sim. to ISO 62
Humidity absorption 0.2 % Sim. to ISO 62
Density 1410 kg/m³ ISO 1183
Rheological calculation properties Value Unit Test Standard

Density of melt 1200 kg/m³ -
Thermal conductivity of melt 0.155 W/(m K) -
Spec. heat capacity melt 2210 J/(kg K) -
Eff. thermal diffusivity 4.85E-8 m²/s -
Ejection temperature 165 °C -
Test specimen production Value Unit Test Standard

Processing conditions acc. ISO 9988 - ISO ....-2
Injection Molding, melt temperature 195 °C ISO 294
mold temperature 85 °C ISO 10724
injection velocity 200 mm/s ISO 294
pressure at hold 90 MPa ISO 294

Multi-point data
Characteristic
Regional Availability
North America, Europe, Asia Pacific, South and Central America, Near East/Africa, India

Processing
Injection Molding, Film Extrusion, Profile Extrusion, Sheet Extrusion, Other Extrusion, Blow Molding

Delivery form
Pellets

Additives
Release agent

Other text information
Injection molding
PREPROCESSING
General drying is not necessary due to low moisture absorption of

the resin.
In case of bad storage conditions (water contact or condensed water)

the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
PROCESSING
Standard injection moulding machines with three phase (15 to 25 D)

plasticating screws will fit.
Melt temperature 190-230 °C

Mould temperature 60-120 °C
POSTPROCESSING
Conditioning e.g. moisturizing is not necessary.
Film extrusion
PREPROCESSING

the resin.

PROCESSING
Standard extruders with grooved feed zone and short compression

screws (minimum 25 D) will fit.

POSTPROCESSING
In case of very thick wall thickness profiles after-annealing it is

recommended to reduce internal stress.
Annealing temperature 130-140 °C

Annealing time 10 min/mm thickness
Other extrusion
PREPROCESSING

the resin.

PROCESSING

POSTPROCESSING


Profile extrusion
PREPROCESSING

the resin.


PROCESSING

POSTPROCESSING


Sheet extrusion
PREPROCESSING

the resin.

PROCESSING

POSTPROCESSING



Product Texts: P:Partial Break

Uploaded by

Copyright:

Available Formats

Product Texts: P:Partial Break

Uploaded by

Document Information

Original Description:

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Product Texts: P:Partial Break

Uploaded by

Copyright:

Available Formats

HOSTAFORM C 9021 | POM | Ticona - 2008-06-03

Request for Information | Disclaimer

Standard-Injection molding type with high rigidity, hardness and

Fulfils EG-directive 2002/72/EU as well as the recommendation

UL-registration for all colours and a thickness more than 1.5 mm as

Ranges of applications: automotive engineering, precision

FDA = Food and Drug Administration (USA)

Rheological properties Value Unit Test Standard

Mechanical properties Value Unit Test Standard

Thermal properties Value Unit Test Standard

Electrical properties Value Unit Test Standard

Other properties Value Unit Test Standard

Rheological calculation properties Value Unit Test Standard

Test specimen production Value Unit Test Standard

General drying is not necessary due to low moisture absorption of

In case of bad storage conditions (water contact or condensed water)

Max. Water content 0,2 %

Standard injection moulding machines with three phase (15 to 25 D)

Melt temperature 190-230 °C

Conditioning e.g. moisturizing is not necessary.

General drying is not necessary due to low moisture absorption of

In case of bad storage conditions (water contact or condensed water)

Max. Water content 0,2 %

Standard extruders with grooved feed zone and short compression

Melt temperature 180-190 °C

Conditioning e.g. moisturizing is not necessary.

In case of very thick wall thickness profiles after-annealing it is

Annealing temperature 130-140 °C

General drying is not necessary due to low moisture absorption of

In case of bad storage conditions (water contact or condensed water)

Max. Water content 0,2 %

Standard extruders with grooved feed zone and short compression

Melt temperature 180-190 °C

Conditioning e.g. moisturizing is not necessary.

In case of very thick wall thickness profiles after-annealing it is

Annealing temperature 130-140 °C

General drying is not necessary due to low moisture absorption of

In case of bad storage conditions (water contact or condensed water)

Max. Water content 0,2 %

Standard extruders with grooved feed zone and short compression

Melt temperature 180-190 °C

Conditioning e.g. moisturizing is not necessary.

In case of very thick wall thickness profiles after-annealing it is

Annealing temperature 130-140 °C

General drying is not necessary due to low moisture absorption of

In case of bad storage conditions (water contact or condensed water)

Max. Water content 0,2 %

Standard extruders with grooved feed zone and short compression

Melt temperature 180-190 °C

Conditioning e.g. moisturizing is not necessary.

In case of very thick wall thickness profiles after-annealing it is

Annealing temperature 130-140 °C