ACCUPLUS MAKE

TH-270A

Features:
Compact plastic case，suitable for use under poor working conditions. Test at any angle, even
upside down.
Wide measuring range. It can measure the hardness of all metallic materials. Direct display of
hardness scales HRB, HRC, HV, HB, HS, HL
Large screen (segment LCD), showing all functions and parameters. With EL background light.
Large capacity memory could store 100 groups information.
Datapro Software to connect with PC via RS232 port. Micro printer support
Software calibration function.

Technical Specifications:
Measuring Range：
(170-960)HLD,(17-68.5)HRC,(19-651)HB,(80-976)HV,(30-100)HS,(59-
85)HRA,(13-100)HRB
Measuring direction：360°（↓↖↗↘↙→←↑）
Hardness Scale：HL、HB、HRB、HRC、HRA、HV、HS
Display：segment LCD
Data memory：max. 100 groups（relative to impact times 32～1）
Working voltage：3V（2 AA size alkaline battery）
Continuous working period：about 100 hours（With backlight off）
Communication interface：RS232

Main Application :

Die cavity of moulds

Bearings and other parts
Failure analysis of pressure vessel, steam generator and other equipment
Heavy work piece
The installed machinery and permanently assembled parts.
Testing surface of a small hollow space
 Material identification in the warehouse of metallic materials
Rapid testing in large range and multi-measuring areas for large-scale work piece

Configuration:

No. Item Quantity Remarks

Standard 1 Main unit 1
Configuration 2 D type impact device 1 With cable
3 Standard test block 1
4 Cleaning brush (I) 1
5 Small support ring 1
6 Alkaline battery 2 AA size
7 Manual 1
8 Instrument package 1
case
Optional 9 Cleaning brush (II) 1 For use with G
Configuration type impact
device
10 Other type of impact Refer to Table 3
devices and support and Table 4 in
rings the appendix.
11 DataPro software 1
12 Communication cable 1
13 Micro Printer 1
14 Print cable 1

Testing Range:

Other type of impact devices

 Impact device
Material Method
D/DC D+15 C G E DL
HRC 20～68.5 19.3～67.9 20.0～69.5 22.4～70.7 20.6～68.2
HRB 38.4～99.6 47.7～99.9 37.0～99.9
Steel and cast HRA 59.1～85.8 61.7～88.0
steel HB 127～651 80～638 80～683 90～646 83～663 81～646
HV 83～976 80～937 80～996 84～1042 80～950
35.8～102.
HS 32.2～99.5 33.3～99.3 31.8～102.1 30.6～96.8
6
Cold work HRC 20.4～67.1 19.8～68.2 20.7～68.2 22.6～70.2
tool steel HV 80～898 80～935 100～941 82～1009
HRB 46.5～101.7
Stainless steel
HB 85～655
HV 85～802
HRC
Grey cast iron
HB 93～334 92～326
HV
HRC
Nodular cast iron HB 131～387 127～364
HV
Cast aluminium HB 19～164 23～210 32～168
alloys HRB 23.8～84.6 22.7～85.0 23.8～85.5
BRASS(copper- HB 40～173
zinc alloys)
HRB 13.5～95.3
BRONZE(copper-
aluminium/tin HB 60～290
alloys)
Wrought copper
HB 45～315
alloys
 Testing Conditions:

Type of impact DC(D)/DL D+15 C G E

device
Impacting energy 11mJ 11mJ 2.7mJ 90mJ 11mJ
Mass of impact body 5.5g/7.2g 7.8g 3.0g 20.0g 5.5g
Test tip hardness: 1600HV 1600HV 1600HV 1600HV 5000HV
Dia. Test tip: 3mm 3mm 3mm 5mm 3mm
Material of test tip: Tungsten carbide Tungsten Tungsten Tungsten synthetic
carbide carbide carbide diamond
Impact device 20mm 20mm 20mm 30mm 20mm
diameter: 86(147)/ 75mm50g 162mm 141mm 254mm 155mm
Impact device 80g 75g 250g 80g
length:
Impact device
weight:
Max. hardness of 940HV 940HV 1000HV 650HB 1200HV
sample
Mean roughness 1.6μm 1.6μm 0.4μm 6.3μm 1.6μm
value of sample
surface Ra:

DC: D+15: C: G: E: DL:

Test hole or Test groove Test large,
hollow or reentrant Test small, Test super Test slender
Available type cylindrical surface light, thin thick, heavy high narrow
of impact parts and and rough hardness groove or
device surface of surface steel material hole
hardened
layer
Min. weight of
sample:
Measure directly >5kg >5kg >1.5kg >15kg >5kg
Need support firmly 2～5kg 2～5kg 0.5～1.5kg 5～15kg 2～5kg
Need coupling 0.05～2kg 0.05～2kg 0.02～0.5kg 0.5～5kg 0.05～2kg
tightly
Min. thickness of
sample Coupling 5mm 5mm 1mm 10mm 5mm
tightly
Min. layer thickness ≥0.8mm ≥0.8mm ≥0.2mm ≥1.2mm ≥0.8mm
for surface
hardening

Size of tip indentation

Hardness Indentation 0.54mm 0.54mm 0.38mm 1.03mm 0.54mm
300HV diameter
Depth of 24μm 24μm 12μm 53μm 24μm
indentation
Hardness Indentation 0.54mm 0.54mm 0.32mm 0.90mm 0.54mm
600HV diameter
Depth of 17μm 17μm 8μm 41μm 17μm
indentation
Hardness Indentation 0.35mm 0.35mm 0.35mm -- 0.35mm
800HV diameter
Depth of 10μm 10μm 7μm -- 10μm
indentation

Support rings for Shaped Materials:

Other type of support rings

 Sketch of non-conventional
No. Type Remarks
Supporting ring
1 Z10-15 For testing cylindrical outside surface
R10～R15

2 Z14.5-30 For testing cylindrical outside surface

R14.5～R30

3 Z25-50 For testing cylindrical outside surface

R25～R50

4 HZ11-13 For testing cylindrical inside surface

R11～R13

5 HZ12.5-17 For testing cylindrical inside surface

R12.5～R17

6 HZ16.5-30 For testing cylindrical inside surface

R16.5～R30

7 K10-15 For testing spherical outside surface

SR10～SR15

For testing spherical outside surface

8 K14.5-30
SR14.5～SR30

9 HK11-13 For testing spherical inside surface

SR11～SR13

10 HK12.5-17 For testing spherical inside surface

SR12.5～SR17

11 HK16.5-30 For testing spherical inside surface

SR16.5～SR30
 For testing cylindrical outside surface,
12 UN
radius adjustable R10～∞