TECHNICAL DESCRIPTION
CONTENTS
1. SPECIFICATIONS ........................................................................................................................ 3
1.1 Function principle .......................................................................................................................... 3
1.2 ARL 3460 Optical Emission Spectrometer..................................................................................... 4
1.3 Stability which gives confidence to user ........................................................................................ 4
1.4 Accessories and options................................................................................................................ 4
1.5 Spectrometer computer system ..................................................................................................... 5
1.6 OXSAS Analytical Software ........................................................................................................... 5
1.7 Technical Description .................................................................................................................... 6
1.8 Storage ......................................................................................................................................... 9
1.9 Laboratory requirements ............................................................................................................... 9
1.10 Electrical requirements................................................................................................................ 10
1.11 Argon requirements..................................................................................................................... 11
3. SAMPLE PREPARATION........................................................................................................... 13
3.1 Sample Taking – Moulds............................................................................................................. 13
3.2 Surface Preparation - Sample Preparation Machines .................................................................. 15
1. SPECIFICATIONS
1.1 Function principle
The ARL 3460 Metals Analyzer is a simultaneous Quantometer. This means the instrument
measures the intensity of several spectral lines simultaneously in the light emitted by the sample,
when the atoms that compose it are exited by an external energy source. The analysed light is
located approximately into the 150nm to 800nm wavelength range. The whole measuring system
is therefore based on the physical phenomenon that is summarised as follows:
When certain energy is applied to an atom, some of its electrons change their orbit. When these
electrons return to their initial orbit, a precise energy is restored in the form of a light at a
determined wavelength. This is an atomic phenomenon, and consequently it is practically
unaffected by the chemical or crystalline form of the atom. This means the instrument can
determine, for example the quantity of silicon in steel; but will not give information about the form
under this silicon is to be found. The following figure gives a rough representation of this
excitation.
+4 +4 +4
A sample containing several different elements will therefore produce light composed of
wavelength specific to each of the elements. By separating these wavelengths by a dispersion
system, the spectrometer can determine which elements are present, the intensity of each of these
wavelengths being a function of the concentration of the considered element. By measuring this
luminous intensity (with a photomultiplier) and by processing this information with a computer, the
instrument can thus determine the concentration of the considered element.
An instrument that allows such analysis is therefore composed of the four following parts:
1) A source of excitation that supplies energy to the samples.
2) A dispersion device that discriminates the different wavelengths.
3) Electronics that measure the luminous intensity of each of the wavelengths.
4) A computer that processes the measurements and controls the instrument.
2
Spectrometer
3 4
1
Computer
Excitation Electronics
For over 60 years the metals industry has looked for one company to set the standard for
instrumental analysis of metals.
The ARL Model ARL 3460 is the latest instrument that brings the cost effective quality control. It
will meet the highest expectations, but at a price that is considerably below what users would
expect to pay.
The ARL 3460 is designed to excel as a mono-base or multi-base instrument and for high
throughput sample analysis
Business depends on consistently producing high quality metals or metal products, and user needs
an analysis system that will not let him down. The model ARL 3460 will go on working 24 hours per
day, 7 days per week to keep production facility on track.
Absolute accuracy of any analysis depends totally upon the calibration of the instrument. The
model ARL 3460 is factory calibrated using CARL. This sophisticated multi-variable regression tool
corrects for matrix effects as well as spectral interferences. The model ARL 3460 is ready to
deliver accurate analyses from the first day of its installation.
User needs to be sure that he will get the same accurate results tomorrow, next week, next year.
The model ARL 3460 inherits the sort of short and long term stability that have long been ARL
standards.
Includes factory installation and configuration of operating system and instrument software.
OXSAS is the most powerful software available for optical emission spectrometer, offering both
flexibility and comprehensive capabilities in “one state of art” package.
®
32 bits software that runs on Windows XP Professional and includes the following main features:
· Element display with possibilities to show units and grade limits. Precision: dynamic
(proportional to the concentration range), fixed number of decimals or fixed number of
significant digits. ASTM rounding is supported;
· Result validation and edition, with history;
· Grade check (target and alternative), grade search and sort;
· ‘Key to Metals for OXSAS’: a multilingual steel and nonferrous metals database. Unlimited
access to more than 3,400,000 records for chemical composition, properties and
specifications for metals. Easy direct export of grade concentration data to OXSAS grade
limits. Search and cross reference tools;
· Automatic method choice based on element(s) concentration(s) or sample identification
· Results recalculation (unknown samples, calibration samples, Setting-Up, Control and Type
Standards samples). With possibility to recalculate multiple samples in one operation;
· Result storage and post-treatment with powerful database query filters. Statistics. Export to
files in Excel or CSV formats. Tracing of result modification with integrated display of
modification history;
· Instrument check with on-line integrated SPC-Basic. On-line evaluation by SPC of control
samples with immediate feed-back. Automatic detection of out-of-control and other abnormal
states (bias, trends, etc.) according to numerous normalization rules. Control samples
analysis scheduling;
· Instrument standardization, with history;
· Type standardization, with history;
· Management of SCT samples: supervision of the status and maintenance of Setting-Up,
Control and Type Standards samples. One click creation of a batch with all samples
requiring analysis;
· Monitoring: instrument alarm monitoring, system event logging, peripheral device
monitoring, up to 10 configurable sample measurement run counters for helping defining
maintenance schedule;
· Integrated instrument profile tool allowing overlaid graphical view of selected channels
intensities;
· Integrated contextual help;
· Accounts with password protection with definable access and operational rights, database
maintenance tools;
· Text customization and translation into any language that have a character set supported by
the Windows operating system. Standard language delivery: English.
Spectrometer has the ability to measure up to 60 spectral lines simultaneously. It is used for
quantitative determination of elements by photo-electric measurement of characteristic
wavelengths. Consisting of:
Simultaneous spectrometer
With concave grating “Paschen-Runge” mounting, cast construction and 1m forcal length.
The spectrometer is shock mounted, insulated and temperature controlled to ±0.1°C at 38°C
to minimize profiling and standardisation frequency and maximise sample throughput.
Spectrometer
Photomultiplier tubes
housing
Excitation
Ar flushed stand
entrance spark source
optics
Grating Primary
Primary slit: 20 µm
Photomultiplier tubes: 28 mm, 10-stage side window tubes, fused quartz or glass envelope.
The phototubes are mounted outside the vacuum chamber in order to
avoid corona-discharge and for a better serviceability in case of line
addition.
-3
Max. degree of vacuum : 1 x 10 mm Hg
Spark stand: Argon flushed. Stand with built in ignitor for improved trace analysis.
Included closed water cooled system.
The safety circuit protects the operator and the instrument. It is not
possible to perform an analysis when the stand door is open. This
circuit conforms with the international norm CEI 1010-1.
Fatigue lamps: With built-in intensity level selectable by software. The fatigue
improves the stability of the photomultipliers as well as their life time.
Spectrometer control: ARL MMB 88 microprocessor utilising CMOS technology with status
measuring card A/D converters and attenuators included for each
channel. Up to 60 analytical channels
Dust protection: Built-in dust protection with high capacity cooling fans
119
67
1.8 Storage
If laboratory is not ready when the instrument arrives, the instrument must be stored in an
adequate room. Recommendations are as follows:
The storage room must be closed, dry and must have at least a cemented floor.
The instrument must stay on its transportation pallet. This makes subsequent moves easier and
limits any vibrations.
It is very important to have good air circulation around the instrument during storage. Dust can be
cleaned, but humidity is harmful.
400 cm min.
3
2 1 Quantometer ARL 3460
2 Table (for computer and peripherals)
3 Office desk
350 cm min.
4 4 Chair
5 Cupboard (for samples, material, docu-
mentation)
6 Washbasin
min. 80 1
6
5
Standard Network
Most of the European networks provide with mains within the requirements given at the beginning
of this chapter. In such case the connection diagram becomes:
Stabiliser
V 230 V ± x% V 230 V +10%/-15%
P ³ 5 kVA Instrument
Neutral blue Line N
Input
Filter
V 0V
Earth yellow/green E
V 0V
Earth
Note *: Stabiliser without link or connection between Input 2 and Output 2. Depending on the
design, such a stabiliser may be used as an insulation transformer too!
Argon pipes must be copper, and must have been cleaned before they are used (no oil nor
grease).
The required inlet pressure is about 2 bars (2 x 105 Pa). A two-stage pressure regulator (with
manual pressure adjustment from 0 to 3 bars of the second stage) must be installed.
The argon must have a minimum purity of 99.996% and conform to the following specifications:
· < 5 ppm O2
· < 20 ppm N2
· < 5 ppm H 2O
· < 5 ppm CO2 + CH4
For analysing cast iron with Si > 1%, for aluminium and magnesium alloy, the highest impurity
contents for oxygen and water vapours are:
· < 2 ppm O2
· < 3 ppm H 2O
For the analysis of nitrogen and oxygen the required quality is:
Argon quality Purity N2 O2
Argon 57 99.9997% < 0.6 ppm < 0.3 ppm
As far as the supplied Sircal purifier is connected and operational, it is possible to use a lower
argon quality, that is:
Argon quality Purity N2 O2
Argon 48 99.998% < 10 ppm < 2 ppm
The actual installation is carried out by the factory service engineer or by local ARL
representative's engineer. The service engineer will perform the following tasks:
· Check that the delivery conforms to the contract and the delivery packing slip.
· Unload the instrument from its transport pallet.
· Open the instrument before power up, so as to determine if the transport has caused any
internal damage that is not visible from outside.
· Check that the laboratory and the connections provided for the instrument that customer has
prepared meet the requirements (in chapters 2 to 5 in the pre-installation manual).
· Install and connect the peripherals (computer, printer, etc.) to the instrument.
· Start up the instrument.
· Carry out some typical operations that prove that the instrument is operating correctly.
· Check out (if applicable) the factory calibrated programs with certified standards samples (to be
provided by the end use) and instruct the customer how to use those programs.
· Give the customer a basic training on start up and routine maintenance of the instrument
(checks, precautions, changing Consumables). The customer will also be given an introduction
to the normal use of the software. This basic teaching should not exceed one day.
End of installation
At the end of the installation, the service engineer will write an end of installation protocol, as well
as a technical report on the installation.
The guarantee covers the instrument according to the terms of the contract.
Please, do not hesitate to call the ARL representative if you require any assistance. The
instrument has a model code (name of the instrument), as well as a serial number. These
indications are on a label behind the instrument. They are also written at the end of the installation
protocol. Kindly quote these as well as your company's name in all correspondence. This will help
us to give you an efficient service.
3. SAMPLE PREPARATION
For sample taking and surface preparation, several kinds of moulds and preparation machines are
readily available for purchase.
If required, your local ARL representative will advise you regarding which type and model best
suites your application. Following are some general examples of the various sample mould types
with associated sample preparation machines and their main applications.
Sample taking for spectrometer analysis is a fundamental technique. Several spectroscopy books
explain the procedure and advise which moulds should be used for a given application. DIN and
ASTM standards also provide specifications and information about this subject.
Generally:
· The sample cooling must be rapid to produce a fine grain metallic structure.
· The mould is normally made of copper and kept very clean.
· Any mould not in use must be turned upside down (or covered) to avoid dirt or any other
material ingress.
Here are some examples of moulds that are suitable for casting good quality samples and adapted
for optical emission spectroscopy analysis. A probe for direct sample taking is also shown.
Non-Ferrous Metals
The mushroom form sample taking mould is the most widely used for non-ferrous metals. There
are however segregation risks, and the mould diameter must be adapted accordingly.
cut
here
useful surface
for analysis
useful surface
for analysis
Cast Irons
The mould shown bellow is suitable for the following metals:
Pig Iron and mixer metal, cast iron, malleable iron and nodular cast iron.
The cooling speed is very high to suppress precipitates.
cut
here
useful surface
for analysis
Traces
The ring mould type shown bellow is suitable for the following metals:
Pure metals (for trace analysis), or metals that will have low tendency to segregation. The ring is
of stainless steel or ceramic, so that the sample will be mostly cooled by the bottom copper plate.
The sample is homogeneous on this surface, but for only a few millimetres in depth!
useful surface
for analysis
SPEMIS Probe
For steels, the sample taking can be greatly simplified with a SPEMIS probe that can take liquid
metal directly from the casting. The sample obtained has the following form:
cut
here
useful surface
for analysis
It is essential to use an appropriate machine in order to obtain a clean flat reproducible surface.
We recommend the use of the following sample preparation machine types:
Disk Sander
This is a sander with a rotary abrasive disk.
Some machines have two disks; which is convenient where a coarse grain disk is used for
preliminary surface preparation (roughing), and a fine grain for final sample surface preparation.
abrasive
disk
This surface preparation method is the quickest way to prepare iron, nickel and cobalt samples
(as well as a few coppers). The sample must be thick enough to allow the operator to hold without
the risk of injury to his fingers.
The abrasive paper disk, based with aluminium and silicon oxide mixed with resin (Al/Si = 1:47) is
usually suitable. A fine grain disk of "60" or "80" is recommended for the final finish and a coarse
grain disk of “40” for initial rough grinding.
For the analysis of soluble-insoluble aluminium, abrasive disks based with zirconium must be used
to avoid cross contamination.
Note: Copper, aluminium, lead, zinc, magnesium, pure or even very low alloyed, and
generally all soft materials, cannot be properly prepared using abrasive paper disks.
Surface Grinder
Rotating surface grinders with multiple grindstones fixed on a rotating arm are highly
recommended:
magnetic grindstone
table
This grinding method is suitable for all steels and cast irons, as well as for nickel and cobalt
alloys. Points to note:
- Cooling liquids must not be used.
- The magnetic samples will be kept in place by a magnetic table. The non-magnetic samples are
held in a vice that is then secured by the magnetic table.
- The grindstones must be regularly sharpened, otherwise the risk of surface overheat and
deterioration of the sample is high, causing bad sparking spots.
Note: If your preparation machine is ever used for other applications that required the use of oil,
water, or any other coolants, then the head, the milling machine table, the milling cutter and
the vice for holding the sample, must all be thoroughly cleaned before using again for
normal spectrometer sample surface preparation.
Example
Some steel springs can be analysed if prepared as shown in the following picture (flat surface
preparation by milling or polishing):
useful flat
surface for analysis
Press Machine
For soft wire samples, one can flatten them with a press using a pressure of between 20 to 40 tons
If the useful surface area to be analysed is smaller than the 15 mm standard hole of the standard
analysis table, one should use another smaller hole table or a special small sample adapter to
accommodate it’s size.
Inductive Furnace
Metallic chips can be re-melted in a furnace. This furnace provides solid samples that can be used
for spectroscopy analysis.