Abstract
Colloidal quantum dots are sub-10 nm semiconductors treated with liquid processes, rendering them attractive candidates for single-electron transistors operating at high temperatures. However, there have been few reports on single-electron transistors using colloidal quantum dots due to the difficulty in fabrication. In this work, we fabricated single-electron transistors using single oleic acid-capped PbS quantum dot coupled to nanogap metal electrodes and measured single-electron tunneling. We observed dot size-dependent carrier transport, orbital-dependent electron charging energy and conductance, electric field modulation of the electron confinement potential, and the Kondo effect, which provide nanoscopic insights into carrier transport through single colloidal quantum dots. Moreover, the large charging energy in small quantum dots enables single-electron transistor operation even at room temperature. These findings, as well as the commercial availability and high stability, make PbS quantum dots promising for the development of quantum information and optoelectronic devices, particularly room-temperature single-electron transistors with excellent optical properties.
Similar content being viewed by others
Introduction
Colloidal quantum dots (CQDs) are small semiconductor crystals with a diameter of several nanometers1. CQDs exhibit excellent light emission/absorption characteristics, and their optical bandgaps are widely tunable by adjusting their size. CQDs can be treated by liquid processes, and their functionality can be controlled by selecting suitable ligands. These properties make CQDs attractive candidates for use as transport channels in single-electron transistors (SETs) operating at high temperatures. However, there have been only a few evaluations of carrier transport through single CQDs in transistor geometries, which are limited to CdSe2, PbS3, HgSe4, and CdSe core-shell CQD systems5 measured only at cryogenic temperatures because of the technical difficulties in electrically accessing single CQDs prepared by bottom-up methods. To date, SETs using semiconductor quantum dots have mainly been fabricated in GaAs6,7,8,9, InAs10,11,12,13, and Si-based quantum dots14,15,16,17,18. These quantum dots are typically ~50â100ânm in size, leading to a small Coulomb charging energy of <~10âmeV. Therefore, most SETs operate only at cryogenic temperatures, which limits their practical applications. Through the utilization of the small size of CQDs, high-temperature SET operation is expected in single CQD transistors, which may serve as a basis for many single-electron devices19.
Moreover, improved electrical manipulation and read out of quantum states in single CQDs allow for the characterization of various CQD systems and further for their application to quantum information devices20,21. To date, the methodologies for the manipulation and read out of quantum states in single quantum dots have been limited to either optical methods or electrical methods; electrostatically defined quantum dots are primarily electrically controlled6,7,8, whereas bottom-up quantum dots are mainly optically controlled22,23. Exploring the transport properties for optically active single CQDs provides compatibility of optical and electrical manipulation of quantum states, which increases the functionality and flexibility of single-CQD devices and is expected to bring about innovation in quantum information technology.
Furthermore, CQDs form a thin film and can transport carriers when cross-linked. These properties make CQD systems excellent candidates for next-generation optoelectronic devices such as solar cells24,25, photodetectors26,27,28,29, and light-emitting devices30,31. Many studies on the transport properties of CQD ensembles have been reported thus far32,33,34,35,36,37,38,39,40,41 and have shown that ligand bridging and the morphology of the CQD array strongly influence carrier transport through CQD assembly. Characterization of the carrier transport at the single CQD level provides complementary information to that of CQD assemblies as performed by scanning tunneling microscopy/spectroscopy (STM/STS)42,43. It also helps in understanding the details of the carrier transport mechanism through CQDs and the role of ligands.
Among the various CQDs, lead sulfide (PbS) is one of the most attractive materials because of its broad emission/absorption spectral tunability range in the infrared regime. To date, PbS CQDs have been one of the standard materials commercially available. Additionally, they can be treated as a model material for investigation of the charge carrier transport properties in CQD assemblies, and any knowledge gained from such investigations can be translated to other CQDs of different compounds44. While detailed studies on PbS CQD assemblies have reported energy shell-dependent electrical conductivity properties39,41,45,46 and ligand bridging-dependent electron and hole mobilities44,45,46,47,48, the transport properties for single PbS CQDs have not yet been fully elucidated. Characterization of a single quantum dot can exclude the influence of size fluctuations and enables clear observation of intrinsic phenomena such as discrete energy levels and the energy shell-dependent conductivity in CQDs. For this purpose, the narrow bandgap of PbS CQDs is advantageous for the detection of a current through CQDs by nanogap metal electrodes.
In this article, we report the demonstration of single-CQD transistors based on commercially available high-quality PbS CQDs with oleic acid as a ligand. We demonstrate quantum dot size-dependent carrier transport, orbital-dependent electron charging energy and conductance, electric field modulation of the confinement potential of electrons, and spin-correlated coherent carrier transport called the Kondo effect in a PbS CQD system despite the rather long oleic acid capping. Furthermore, we find that single small-sized CQD transistors operate as SETs even at room temperature.
Results
Single-PbS-CQD transistors
Transport measurements were performed on single PbS CQDs in contact with nanogap source-drain electrodes, as shown in Fig. 1a, b. A back-gate electrode was used to tune the electronic state of the PbS CQDs. Figure 1c shows the source-drain current, ISD, as a function of the source-drain voltage, VSD, of sample A with CQD diameter dâ~â3.6ânm, measured for different back-gate voltages, VG. The sample exhibits a strongly suppressed current near VSDâ=â0âV, followed by a step-like current increase at high |VSD|. The voltage width of the suppressed conductance is modulated by changing VG. The suppressed current at VSDâ~â0âV is a manifestation of the strong Coulomb interaction in this system and is called the Coulomb blockade effect. A current step occurs at a large |VSD| at which an extra electron is energetically allowed to enter the CQD. The observed ISDâVSD characteristics clearly indicate that this sample operates as an SET. Coulomb stability diagrams were obtained by plotting the differential conductance, dI/dVSD, as a function of VSD and VG, as shown in Fig. 2.
Coulomb stability diagrams for various CQD sizes
Figure 2 shows Coulomb stability diagrams obtained for three samples with different CQD sizes (see also Supplementary Fig. S1 for more data). The dark-colored diamond-shaped areas (Coulomb diamonds) correspond to the Coulomb blockade regions. Each Coulomb diamond is associated with a well-defined number of confined electrons, n, in the CQD. Although the number of electrons in the CQD could not be determined, we can tell the parity of n from the size of the Coulomb diamonds. Especially in samples A and B, the Coulomb diamond for nâ=âNâ+â1 electrons is notably larger than that for nâ=âN and Nâ+â2. The (Nâ+â1) diamond contains an even number of electrons and has a larger addition energy, Eadd, which consists of the Coulomb charging energy, EC, and difference in orbital quantization energy, ÎE, in the CQD. The diamonds labeled N and Nâ+â2 are smaller because the addition energies are only due to EC. Therefore, N is an odd number in these samples. In large CQDs (sample C, dâ~â8.7ânm), such even-odd behavior of the Coulomb diamonds is not clearly observed, as shown in Fig. 2c, most likely because of the very different numbers of electrons n in large CQDs; a larger PbS CQD has a narrower bandgap, as well as smaller EC and ÎE, leading to electrical access to the larger n regime. In Fig. 2a, b and Supplementary Fig. S1a, the sizes of the Coulomb diamonds for nâ=âN and Nâ+â2 are not the same and significantly differ, indicating that EC strongly depends on the number of electrons in these samples. Since similar even-odd behavior of the Coulomb diamonds and n-dependent charging energy are reported in many other few-electron quantum dot systems9,10,11,12,49, samples A, B, and D are in the few-electron regime, while samples C and E are in the many-electron regime.
Charge addition energy and conductance
In Fig. 3a, we plot the Eadd of electrons for each sample as a function of the number of electrons labeled in Fig. 2 and Supplementary Fig. S1. In small CQD samples (samples A, B, and D), Eadd for nâ=âN (odd) is slightly larger than that for nâ=âNâ+â2 (odd), indicating that EC decreases with increasing n. These results indicate that the electron wavefunction in the PbS CQD becomes more extended in space with increasing n, leading to larger capacitive coupling with the electrodes and reduced electron-electron Coulomb repulsion in the CQDs. Such an n dependence of Eadd is not clear for large CQD samples with dâ~â8.7ânm; Eadd shows much smaller and almost constant values in samples C and E, indicating that the spatial size of the electron wavefunction in the PbS CQDs does not significantly change and that the quantized energy levels are almost degenerate. The large peak in Eadd at nâ=âNâ+â1 for sample D reflects a large orbital quantization energy difference ÎE, which strongly depends on n as well as the size and shape of the measured single PbS CQDs50. The number of electrons in sample D might be slightly different from those in samples A and B (i.e., sample D might be probing different quantized states).
Figure 3b shows the CQD size dependence of the experimentally obtained EC. Here, EC is plotted as the average of all Eadd for n = odd in each sample. The calculated EC for a metal sphere quantum dot is shown as a solid line in Fig. 3b. The self-capacitance of a metal sphere quantum dot surrounded by oleic acid is given by Cdotâ=â4Ïε0εrr, where ε0 is the vacuum permittivity, εrâ~â2.5 is the relative permittivity of oleic acid51,52, and r is the radius of the sphere. Then, EC is calculated as ECâ=âe2/2Cdot, where e is the elementary charge. The experimentally obtained EC is found to be in reasonable agreement with the simple metal sphere quantum dot model. The observation of a large EC of ~150âmeV in small CQDs suggests that devices with small CQDs operate as SETs even at room temperature. Figure 3c and Supplementary Fig. S2 show Coulomb stability diagrams for three different devices (samples F, G, and H) with dâ~â4.8ânm measured at room temperature. The temperature dependence of the Coulomb stability diagram for sample F is also shown in Supplementary Fig. S3. While there is a tendency for the noise to increase at higher temperatures, we still obtained diamond-like Coulomb stability diagrams for samples F, G, and H, confirming that the devices operate as SETs even at room temperature. It is known that the criterion for the high-temperature operation of SETs is Eaddâ>â~ 4kBT, considering thermal broadening in the single-level tunneling regime53, where kB is the Boltzmann constant. Given that Eaddâ>â120âmeV for CQDs with dâ~â4.8ânm, which exceeds 4kBT at Tâ=â300âK, it is reasonable to observe Coulomb diamonds even at room temperature. To date, various SET devices, such as Si-based SET structures54,55,56,57, carbon nanotubes58, graphene quantum dots59, and metal nanoparticles60, have been demonstrated to operate at room temperature. This is the demonstration of room-temperature SET operation in semiconductor nanocrystal systems. Considering that PbS CQDs are excellent emitters and absorbers of light, our device is a platform for room-temperature SETs with good optical properties, increasing the functionality and versatility of single-electron devices.
Next, we discuss the magnitude of the tunneling conductance. Figure 3d shows the differential conductance taken at VSDâ=â0âV as a function of VG plotted for samples with dâ=â4.8ânm (i.e., samples B and D), exhibiting clear Coulomb oscillation peaks. The conductance at the Coulomb peaks shows a strong dependence on n. The two paired N-th and (Nâ+â1)th Coulomb peaks exhibit almost the same conductance and one order of magnitude lower conductance than the other paired (Nâ+â2)-th and (Nâ+â3)-th peaks located in the high VG region (this tendency is clearer in sample D). These results strongly suggest that the N and (Nâ+â1) electrons ((Nâ+â2) and (Nâ+â3) electrons) in these CQDs are in spin-up and spin-down states while occupying the same orbital. As mentioned in the previous paragraph, the spatial size of the electron wavefunction becomes larger for higher orbitals. These facts lead to the conclusion that the tunneling barrier in the present metal electrode-CQD system is formed not only by the capping materials (oleic acid) but also by the intrinsic gaps between the metal electrodes and the electron wavefunction in the CQD, as schematically illustrated in Fig. 3e. Since the tunneling conductance exponentially depends on the tunneling gap, even a small change in the size of the electron wavefunction gives rise to a large difference in the tunneling conductance.
Kondo effect in PbS CQDs
Next, let us examine the spin-dependent carrier transport observed in single PbS CQDs. Figure 4a shows a Coulomb stability diagram for a high-conductance sample with dâ~â4.8ânm (sample I) measured at 4âK. One can only observe the data near the charge degeneracy point of the Coulomb stability diagram for the addition of the N-th electron owing to the poor gate modulation efficiency in this sample. The Coulomb diamond for nâ=âN shows a clear resonant enhancement of the zero-bias conductance. This behavior arises from the formation of a spin singlet state between an unpaired electron in the CQD and an electron with the opposite spin in the electrodes, i.e., the spin-half Kondo effect61,62. The spin-half Kondo effect only appears in n = odd Coulomb diamonds, suggesting that N is an odd number in Fig. 4a.
In Fig. 4b, dI/dVSD is plotted as a function of VSD at VGâ=â25âV for various temperatures. The Kondo peak at VSDâ=â0âV grows with decreasing temperature. Figure 4c shows the temperature dependence of dI/dVSD at VSDâ=â0âV (i.e., at the Kondo peak) for various VG values. With increasing temperature, dI/dVSD at VSDâ=â0âV decreases up to ~30âK because of the weakened Kondo effect and then begins to increase at Tâ>â30âK due to the increased background conductance induced by the thermal broadening of the adjacent tunneling peak. Although the background conductance due to the falling edges of the adjacent tunneling peaks hinders precise determination of the full-width at half-maximum of the Kondo peak, w, it is roughly estimated to be ewâ~â3âmeV. The Kondo temperature, TK, is expressed as kBTK ~ ew61,63,64. From this relation, TK in this sample is determined to be TKâ~â30âK, which is consistent with the enhanced conductance at VSDâ=â0âV for Tâ<â30âK in Fig. 4c.
Discussion
In sample A, the slopes of the Coulomb diamond boundaries are not constant and depend on VG and VSD (see Fig. 2a and Supplementary Fig. S4a), indicating that the electron density profile in the CQD is affected by the potential gradient induced by VG and VSD. In this sample, the noise level is low enough to identify the excited-state lines in the Coulomb stability diagram65. Clear excited-state lines are observed, from which the orbital quantization energy differences for n electrons, ÎE(n), are determined to be ÎE(N)â=â50âmeV, ÎE(Nâ+â1)lowâ=â80âmeV from the low VG region of the (Nâ+â1) Coulomb diamond, ÎE(Nâ+â1)highâ=â90âmeV from the high VG region of the (Nâ+â1) Coulomb diamond, and ÎE(Nâ+â2)â=â35âmeV (see Supplementary Fig. S4). We simulated ÎE for cubic PbS quantum dots with similar volumes in the few-electron regime using the software QTCAD from Nanoacademic Technologies66 and found a ÎE of 10-100âmeV, which is in reasonable agreement with the experimentally observed ÎE(n). Although the observed ÎE(Nâ+â1)high and ÎE(Nâ+â1)low originate from the same excited state, ÎE(Nâ+â1)high is larger than ÎE(Nâ+â1)low, indicating stronger confinement of electrons at higher VG. Furthermore, ÎE(N) significantly increases with increasing VG (see Supplementary Fig. S4 and Note 1), which again indicates stronger confinement of electrons in the CQD at higher VG. These results indicate the strong influence of the external electric field induced by VG and VSD on the confinement potential of electrons in single PbS CQDs, suggesting the tunability of the effective confinement size of electrons and the bandgap in CQDs by the external electric field.
Regarding the Kondo effect, we found a sample (sample J, dâ~â4.8ânm) that has higher conductance than sample I, as shown in Supplementary Fig. S5. The width of the Kondo peak in sample J is ewâ~â7âmeV at VGâ=â40âV, suggesting a very high Kondo temperature of TKâ~â80âK. The TK in a SET is described by \({k}_{{{{{{\rm{B}}}}}}}{T}_{{{{{{\rm{K}}}}}}} \sim {({E}_{{{{{{\rm{C}}}}}}}{\it\Gamma })}^{\frac{1}{2}}\) exp[-Ï(μ-ε0)/2Î], where Î is the tunnel coupling energy between the quantum dot and the source-drain electrodes, μ is the electrochemical potential of the source-drain electrodes at VSDâ=â0âV, and ε0 is a spin-degenerate energy level in the quantum dot occupied by a single electron61. Therefore, TK is limited by both EC and Î. Considering the large charging energy ECâ~â120âmeV (corresponding to a thermal energy of 1400âK) in PbS CQDs with dâ~â4.8ânm, the small Î limits the TK in samples I and J; this is reasonable because oleic acid (~2ânm long ligand) is known as a long-chain insulating ligand that blocks charge carrier transport through CQDs44. The observation of a high TK in oleic acid-capped PbS CQDs suggests the feasibility of realizing a much higher TK up to room temperature by replacing oleic acid with short-chain ligands, which may add the Kondo effect as one of the carrier transport mechanisms in CQD assemblies operated at room temperature.
In summary, we have demonstrated single-CQD transistors based on commercially available high-quality PbS CQDs with oleic acid as a ligand. The transport characteristics strongly depend on the quantum dot size; a few-electron regime is observed in small PbS CQDs, while a many-electron regime is observed in large CQDs. From the n dependence of EC and the conductance, we demonstrated that the tunneling barrier in this system is formed not only by the capping material but also by the intrinsic gap between the electron wavefunction in the CQDs and electrodes. Analysis of the excited states indicates that the confinement potential of electrons in CQDs is strongly affected by the external electric field induced by VG and VSD. The Kondo effect is also observed in a single-CQD system; this indicates strong coupling between the electrodes and the CQDs despite the use of a long-chain insulating oleic acid ligand. These results provide nanoscopic insight into carrier transport through CQDs at the single quantum dot level, which is essential for developing CQD applications in optoelectronic devices, such as solar cells and photodetectors. Furthermore, the large charging energy in small CQDs enables SET operation even at room temperature. Considering that PbS CQDs are excellent emitters and absorbers of light, our device is a platform for room-temperature SETs with good optical properties, increasing the functionality and versatility of single-electron devices. This will bring about innovation in quantum information technology.
Methods
Sample preparation
We first formed thin gold nanojunctions on a 100-nm-thick SiO2 layer grown on a p-type Si substrate. The thickness and width of the gold nanojunctions were ~ 10ânm and ~60ânm, respectively. The p-type Si substrate was used as a back-gate electrode. Then, nanogap source-drain electrodes with gap sizes of 3-10ânm were fabricated using the electrical break junction (EBJ) method67,68 (see Supplementary Fig. S6). The gap sizes of the fabricated nanogap electrodes were characterized by scanning electron microscopy (SEM): approximately 10% of them have a nanogap size of <5ânm, and 50% of them have a gap size of 5-10ânm, as shown in Supplementary Fig. S6c. These gap sizes are suitable for detecting a current through single PbS CQDs in this study. The formation of thin gold nanojunctions, wire bonding, and fabrication of nanogap source-drain electrodes using the EBJ method were all performed in ambient air. After nanogap formation, we placed the devices with nanogap electrodes into a glovebox or a glove bag filled with nitrogen gas and drop-casted a solution of PbS CQDs (10âmg/mL) onto the nanogap electrodes, followed by blowing off of the excess solution using dry nitrogen gas. We then mounted the samples in a cryostat insert under a nitrogen gas atmosphere. We introduced them into a top-loading 4âK cryostat while maintaining a nitrogen gas environment. After introducing the samples into the cryostat, we replaced the nitrogen gas with helium gas and conducted measurements in a helium gas environment. During these procedures, we paid particular attention to not exposing PbS CQDs to air to avoid physisorption of water/moisture and oxygen69. The fabrication yield of single PbS transistors is very low and typically a few %. An SEM image of a typical PbS CQD sample is shown in Fig. 1b and Supplementary Fig. S7. One can observe PbS CQDs around and between the nanogap source-drain electrodes. PbS CQDs are also distributed on the Au electrodes but cannot be observed due to the off-focus and low contrast.
Transport measurements were performed mostly at cryogenic temperatures on three types of commercial PbS CQDs (Supplementary Fig. S8): oleic acid-capped PbS CQDs with 1100ânm peak emission (dâ~â3.6â±â0.7ânm), oleic acid-capped PbS CQDs with 1500ânm peak emission (dâ~â4.8â±â0.6ânm), both in toluene solution from SigmaâAldrich Co. LLC, and oleic acid-capped PbS CQDs with 2000ânm peak absorption (dâ~â8.7â±â1.2ânm), in octane solution from Quantum Solutions. In this paper, we introduce eleven PbS CQD samples: a PbS CQD with dâ~â3.6ânm (sample A), eight CQDs with dâ~â4.8ânm (samples B, D, F, G, H, I, J, and K), and two CQDs with dâ~â8.7ânm (samples C and E).
Determination of the charge addition energies and the charging energies
From Fig. 2 and Supplementary Fig. S1, we derived Eadd for each n through the following procedures. The difference in the electrochemical potential between the source and drain electrodes where the tunneling-in and tunneling-out lines of a Coulomb diamond cross (i.e., eâ|âVSD (apex)| at the apex of each Coulomb diamond in Supplementary Fig. S9) is equal to the addition energy. When |VSD (apex)| was polarity dependent, the size of the Coulomb diamonds was determined as the average of the two values. EC was determined from the addition energy for n = odd. In Fig. 3b, EC was determined by the average of all Eadd for n = odd.
For most of the samples, the Coulomb stability diagrams appear noisy, probably because of a sudden change in the electrostatic environment of the measured CQDs induced by the charge fluctuations in neighboring CQDs. We observed larger noise in larger CQDs, probably because of the frequent trapping/detrapping of electrons in the surrounding CQDs due to the smaller EC and ÎE in larger CQDs. Therefore, we could not discuss Eadd in detail for large CQD samples (i.e., samples C and E). We observed clear charge degeneracy points in the Coulomb stability diagrams, which contradicts the previously reported results for large PbS CQDs3; the reason for the contradiction is unknown but seemingly caused by electron transport through serially coupled double CQDs in ref. 3.
In our samples, the CQD, acting as a Coulomb island, is surrounded by other CQDs and electrodes as shown in Fig. 1b and Supplementary Fig. S7. In this configuration, the actual capacitance should always be larger than the self-capacitance of a metal sphere quantum dot because the Coulomb island is capacitively coupled with the electrodes and the surrounding CQDs, leading to screening of the electric field70. This could result in a charging energy smaller than that of the metal sphere model. However, in the few-electron regime of small CQD samples, the spatial extension of electron wavefunctions is smaller than the geometrical CQD size estimated from the SEM images, as illustrated in Fig. 3e. Therefore, the agreement between the experimentally obtained EC in small CQDs and the metal sphere model could be the result of the compensation of both the screening effect of the surroundings and the reduced effective CQD size in the few-electron regime. In connection with this discussion, we elaborate on the contribution of ligands. In this study, the CQDs are capped with long-chain insulating oleic acid (length â¼ 2ânm) as an organic ligand, which results in weak interactions (weak capacitive coupling) with neighboring electrodes/CQDs and minimal wavefunction overlap with the neighboring electrodes/CQDs, leading to more isolated CQDs that can be explained by the almost isolated metal sphere model.
Analysis of Coulomb stability diagrams for samples C and E (dâ~â8.7ânm)
The Coulomb diamond signatures appear particularly unclear in Fig. 2c and Supplementary Fig. S1b (i.e., samples C and E). While some Coulomb diamonds do not close, suggesting the possibility of multi-dot behavior, the possibility that in this system, the significant noise and instability of the characteristics may be influenced by the charge fluctuations in the surrounding CQDs should also be considered. By observing the structure of the devices for samples C and E using SEM, we found that the gap size of the nanogap electrode in both samples was approximately 10ânm. Considering the dot size of d â¼8.7ânm (~12ânm including oleic acid ligand), parallel quantum dot conduction is more likely to be detected than serial quantum dot conduction in this situation. In the case of parallel quantum dot arrangements, we would observe overlap of two types of Coulomb diamonds. However, such behavior is not clearly observed in Fig. 2c and Supplementary Fig. S1b. Therefore, we think that the unclear Coulomb diamonds are likely due to the significant charge fluctuations in the surrounding CQDs.
As mentioned in the main text, we believe the results for samples C and E correspond to measurements of the many-electron regime. In general, single-electron transport in the many-electron regime is well described by the constant interaction model9. Therefore, in the analysis of Coulomb diamonds in Fig. 2c, we arranged the lines forming the boundaries of the diamonds (two types of lines with positive and negative slopes) such that they exhibit a gate-independent constant slope, allowing us to determine the size of the diamonds.
Observed carrier type
In samples B and D, EC decreases while the conductance increases with increasing VG (see Fig. 2b and Supplementary Fig. S1a), which is typical for SETs in the few-electron transport regime9,10,11,12,49. We also observed a bandgap region near the conduction band edge in sample K (see Supplementary Fig. S10). These results suggest that we are measuring electron transport in the conduction band and that electrons are being added to the conduction band of the PbS CQDs with increasing VG. Only in sample A does the conductance slightly decrease, while EC decreases with increasing VG. The reason for this behavior of the conductance in sample A is unknown thus far.
Data availability
The measurement and analyses data generated in this study have been deposited in the Figshare database under accession code https://doi.org/10.6084/m9.figshare.24311608. They are also available from the corresponding author upon reasonable request.
References
Yin, Y. & Alivisatos, A. Colloidal nanocrystal synthesis and the organicâinorganic interface. Nature 437, 664â670 (2005).
Klein, D. L., Roth, R., Lim, A. K. L., Alivisatos, A. P. & McEuen, P. L. A single-electron transistor made from a cadmium selenide nanocrystal. Nature 389, 699â701 (1997).
Wang, H. et al. Effects of electron-phonon interactions on the electron tunneling spectrum of PbS quantum dots. Phys. Rev. B 92, 041403(R) (2015).
Wang, H. et al. Transport in a single self-doped nanocrystal. ACS Nano 11, 1222â1229 (2017).
Kobo, M., Yamamoto, M., Ishii, H. & Noguchi, Y. Observation of charge transport through CdSe/ZnS quantum dots in a single-electron transistor structure. J. Appl. Phys. 120, 164306 (2016).
Koppens, F. H. L. et al. Driven coherent oscillations of a single electron spin in a quantum dot. Nature 442, 766â771 (2006).
Nowack, K. C., Koppens, F. H. L., Nazarov, Y. U. V. & Vandersypen, L. M. K. Coherent control of a single electron spin with electric fields. Science 318, 1430â1433 (2007).
Petta, J. R. et al. Coherent manipulation of coupled electron spins in semiconductor quantum dots. Science 309, 2180â2184 (2005).
Kouwenhoven, L. P., Austing, D. G. & Tarucha, S. Few-electron quantum dots. Rep. Prog. Phys. 64, 701â736 (2001).
Jung, M. et al. Shell structures in self-assembled InAs quantum dots probed by lateral electron tunneling structures. Appl. Phys. Lett. 87, 203109 (2005).
Kita, T., Chiba, D., Ohno, Y. & Ohno, H. A few-electron vertical In0.56Ga0.44As quantum dot with an insulating gate. Appl. Phys. Lett. 91, 232101 (2007).
Shibata, K. et al. Electron magneto-tunneling through single self-assembled InAs quantum dashes. Appl. Phys. Express 7, 045001 (2014).
Mittag, C. et al. Few-electron single and double quantum dots in an InAs two-dimensional electron gas. PRX Quantum 2, 010321 (2021).
Hao, X., Ruskov, R., Xiao, M., Tahan, C. & Jiang, H. W. Electron spin resonance and spinâvalley physics in a silicon double quantum dot. Nat. Commun. 5, 3860 (2014).
Horibe, K., Kodera, T. & Oda, S. Lithographically defined few-electron silicon quantum dots based on a silicon-on-insulator substrate. Appl. Phys. Lett. 106, 083111 (2015).
Shaji, N. et al. Spin blockade and lifetime-enhanced transport in a few-electron Si/SiGe double quantum dot. Nat. Phys. 4, 540â544 (2008).
Maune, B. M. et al. Coherent singlet-triplet oscillations in a silicon-based double quantum dot. Nature 481, 344â347 (2012).
Kawakami, E. et al. Electrical control of a long-lived spin qubit in a Si/SiGe quantum dot. Nat. Nanotech. 9, 666 (2014).
Likharev, K. K. Single-electron devices and their applications. Proc. IEEE 87, 606â632 (1999).
GarcÃa de Arquer, F. P. et al. Semiconductor quantum dots: technological progress and future challenges. Science 373, eaaz8541 (2021).
Kagan, C. R., Bassett, L. C., Murray, C. B. & Thompson, S. M. Colloidal quantum dots as platforms for quantum information science. Chem. Rev. 121, 3186â3233 (2021).
Press, D., Ladd, T. D., Zhang, B. & Yamamoto, Y. Complete quantum control of a single quantum dot spin using ultrafast optical pulses. Nature 456, 218â221 (2008).
Warburton, R. J. Single spins in self-assembled quantum dots. Nat. Mater. 12, 483â493 (2013).
Talapin, D. V. & Murray, C. B. PbSe Nanocrystal solids for n- and p-channel thin film field-effect transistors. Science 310, 86â89 (2005).
Kovalenko, M. V. Opportunities and challenges for quantum dot photovoltaics. Nat. Nanotechnol. 10, 994â997 (2015).
McDonald, S. A. et al. Solution-processed PbS quantum dot infrared photodetectors and photovoltaics. Nat. Mater. 4, 138â142 (2005).
Szendrei, K. et al. Solution-processable near-IR photodetectors based on electron transfer from PbS nanocrystals to fullerene derivatives. Adv. Mater. 21, 683â687 (2009).
Rauch, T. et al. Near-infrared imaging with quantum-dot-sensitized organic photodiodes. Nat. Photon. 3, 332â336 (2009).
GarcÃa de Arquer, F. P., Armin, A., Meredith, P. & Sargent, E. H. Solution-processed semiconductors for next-generation photodetectors. Nat. Rev. Mater. 2, 16100 (2017).
Lee, J., Sundar, V. C., Heine, J. R., Bawendi, M. G. & Jensen, K. F. Full color emission from IIâVI semiconductor quantum dotâpolymer composites. Adv. Mater. 12, 1102â1105 (2000).
Nurmikko, A. What future for quantum dot-based light emitters? Nat. Nanotechnol. 10, 1001â1004 (2015).
Yu, D., Wang, C. & Guyot-Sionnest, P. n-Type conducting CdSe nanocrystal solids. Science 300, 1277â1280 (2003).
Vanmaekelbergh, D. & Liljeroth, P. Electron-conducting quantum dot solids: novel materials based on colloidal semiconductor nanocrystals. Chem. Soc. Rev. 34, 299â312 (2005).
Nag, A. et al. Metal-free inorganic ligands for colloidal nanocrystals: S2â, HSâ, Se2â, HSeâ, Te2â, HTeâ, TeS32â, OHâ, and NH2â as surface ligands. J. Am. Chem. Soc. 133, 10612â10620 (2011).
Balazs, D. M. et al. Counterion-mediated ligand exchange for PbS colloidal quantum dot superlattices. ACS Nano 9, 11951â11959 (2015).
Kang, M. S., Lee, J., Norris, D. J. & Frisbie, C. D. High carrier densities achieved at low voltages in ambipolar PbSe nanocrystal thin-film transistors. Nano Lett. 9, 3848â3852 (2009).
Liu, Y. et al. Dependence of carrier mobility on nanocrystal size and ligand length in PbSe nanocrystal solids. Nano Lett. 10, 1960â1969 (2010).
Bisri, S. Z., Piliego, C., Yarema, M., Heiss, W. & Loi, M. A. Low driving voltage and high mobility ambipolar field-effect transistors with PbS colloidal nanocrystals. Adv. Mater. 25, 4309â4314 (2013).
Bisri, S. Z. et al. Determination of the electronic energy levels of colloidal nanocrystals using field-effect transistors and ab-Initio calculations. Adv. Mater. 26, 5639â5645 (2014).
Lhuillier, E. et al. Electrolyte-gated field effect transistor to probe the surface defects and morphology in films of thick CdSe colloidal nanoplatelets. ACS Nano 8, 3813â3820 (2014).
Lan, X. et al. Quantum dot solids showing state-resolved band-like transport. Nat. Mater. 19, 323â329 (2020).
Swart, I., Liljeroth, P. & Vanmaekelbergh, D. Scanning probe microscopy and spectroscopy of colloidal semiconductor nanocrystals and assembled structures. Chem. Rev. 116, 11181â11219 (2016).
Notot, V. et al. Quantum dot acceptors in two-dimensional epitaxially fused PbSe quantum dot superlattices. ACS Nano 16, 3081â3091 (2022).
Liu, L. et al. Ligand and solvent effects on hole transport in colloidal quantum dot assemblies for electronic devices. ACS Appl. Nano Mater. 1, 5217â5225 (2018).
Liu, L. et al. Evidence of band filling in PbS colloidal quantum dot square superstructures. Nanoscale 13, 14001â14007 (2021).
Septianto, R. D. et al. Enabling metallic behaviour in two-dimensional superlattice of semiconductor colloidal quantum dots. Nat. Commun. 14, 2670 (2023).
Liu, L., Bisri, S. Z., Ishida, Y., Aida, T. & Iwasa, Y. Tunable electronic properties by ligand coverage control in PbS nanocrystal assemblies. Nanoscale 11, 20467â20474 (2019).
Septianto, R. D. et al. On-demand tuning of charge accumulation and carrier mobility in quantum dot solids for electron transport and energy storage devices. NPG Asia Mater. 12, 33 (2020).
Nilsson, H. A. et al. Giant, level-dependent g factors in InSb nanowire quantum dots. Nano Lett. 9, 3151â3156 (2009).
Choi, H., Ko, J.-H., Kim, Y.-H. & Jeong, S. Steric-hindrance-driven shape transition in PbS quantum dots: understanding size-dependent stability. J. Am. Chem. Soc. 135, 5278â5281 (2013).
Ferreira de Sousa, F., Moreira, S. G. C., Santos da Silva, S. J., Del Nero, J. & Alcantara, P. Jr. Dielectric properties of oleic acid in liquid phase. J. Bionanosci. 3, 1â4 (2010).
Lizhi, H., Toyoda, K. & Ihara, I. Dielectric properties of edible oils and fatty acids as a function of frequency, temperature, moisture and composition. J. Food Eng. 88, 151â158 (2008).
Ihn, T. Semiconductor Nanostructures: Quantum States and Electronic Transport (Oxford University Press, 2010).
Takahashi, Y. et al. Fabrication technique for Si single-electron transistor operating at room temperature. Electron. Lett. 31, 136â137 (1995).
Shin, S. J. et al. Si-based ultrasmall multiswitching single-electron transistor operating at room-temperature. Appl. Phys. Lett. 97, 103101 (2010).
Lee, S., Lee, Y., Song, E. B. & Hiramoto, T. Observation of single electron transport via multiple quantum states of a silicon quantum dot at room temperature. Nano Lett. 14, 71â77 (2014).
Lavieville, R. et al. Quantum dot made in metal oxide silicon-nanowire field effect transistor working at room temperature. Nano Lett. 15, 2958â2964 (2015).
Postma, H. W. C., Teepen, T., Yao, Z., Grifoni, M. & Dekker, C. Carbon nanotube single-electron transistors at room temperature. Science 293, 76â79 (2001).
Barreiro, A., van der Zant, H. S. J. & Vandersypen, L. M. K. Quantum dots at room temperature carved out from few-layer graphene. Nano Lett. 12, 6096â6100 (2012).
Zharinov, V. S., Picot, T., Scheerder, J. E., Janssens, E. & de Vondel, J. V. Room temperature single electron transistor based on a size-selected aluminium cluster. Nanoscale 12, 1164â1170 (2020).
Cronenwett, S. M., Oosterkamp, T. H. & Kouwenhoven, L. P. A tunable Kondo effect in quantum dots. Science 281, 540â544 (1998).
Goldhaber-Gordon, D. et al. Kondo effect in a single-electron transistor. Nature 391, 156â159 (1998).
Liang, W., Shores, M. P., Bockrath, M., Long, J. R. & Park, H. Kondo resonance in a single-molecule transistor. Nature 417, 725â729 (2002).
Yu, L. H. & Natelson, D. The Kondo effect in C60 single-molecule transistors. Nano Lett. 4, 79â83 (2004).
Hanson, R., Kouwenhoven, L. P., Petta, J. R., Tarucha, S. & Vandersypen, L. M. K. Spins in few-electron quantum dots. Rev. Mod. Phys. 79, 1217â1265 (2007).
Beaudoin, F. et al. Robust technology computer-aided design of gated quantum dots at cryogenic temperature. Appl. Phys. Lett. 120, 264001 (2022).
Park, H., Lim, A., Alivisatos, A., Park, J. & McEuen, P. L. Fabrication of metallic electrodes with nanometer separation by electromigration. Appl. Phys. Lett. 75, 301â303 (1999).
Strachan, D. et al. Controlled fabrication of nanogaps in ambient environment for molecular electronics. Appl. Phys. Lett. 86, 043109 (2005).
Balazs, D. M. et al. Reducing charge trapping in PbS colloidal quantum dot solids. Appl. Phys. Lett. 104, 112104 (2014).
Duan, C. et al. Controllability of the Coulomb charging energy in close-packed nanoparticle arrays. Nanoscale 5, 10258â10266 (2013).
Acknowledgements
K.S. thanks Thomas Ihn (ETH Zurich) for valuable comments and Rikima Ono (RIEC, Tohoku University), Mayumi Abe, and Kouki Saito (Tohoku Institute of Technology) for technical support. This work was partly carried out at the Fundamental Technology Center and the Laboratory for Nanoelectronics and Spintronics, Research Institute of Electrical Communication, Tohoku University. This work was partly supported by the Cooperative Research Projects of RIEC (Grant no. R04/A06) (K.S. and T.O.), JKA and its promotion funds from KEIRIN RACE (Grant no. 2023M-380) (K.S.), and Grants-in-Aid for Scientific Research (S) (Grant no. JP20H05660) (K.H.), Scientific Research (C) (Grant no. JP21K04815) (S.Z.B.), and Scientific Research (C) (Grant no. JP21K04820) (K.S.) from The Japan Society for the Promotion of Science (JSPS).
Author information
Authors and Affiliations
Contributions
K.S., M.Y., K.H., T.O., and S.Z.B. performed the fabrication of PbS CQD transistors. K.S. and M.Y. performed transport measurements. K.S. and S.Z.B. analyzed the data presented in the paper and Supplementary Information. K.S. and S.Z.B. wrote the manuscript. The whole project was supervised by K.S., S.Z.B., and Y.I. All the authors read and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisherâs note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the articleâs Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the articleâs Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Shibata, K., Yoshida, M., Hirakawa, K. et al. Single PbS colloidal quantum dot transistors. Nat Commun 14, 7486 (2023). https://doi.org/10.1038/s41467-023-43343-7