    LH 210 SF is a flexible flux-coated brass brazing alloy rod that can be directly applied without separate flux. It has good strength up to 45 kgf/mm2 and melts between 890-900°C. It can be used to join steel, cast iron, copper, brass and other dissimilar metals through capillary action or by melting the rod into a V-groove joint. Proper joint preparation and a neutral flame heat source are required.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    210 SF

    Uploaded by

    Antony Joshwa
    76 views1 page
    LH 210 SF is a flexible flux-coated brass brazing alloy rod that can be directly applied without separate flux. It has good strength up to 45 kgf/mm2 and melts between 890-900°C. It can be used to join steel, cast iron, copper, brass and other dissimilar metals through capillary action or by melting the rod into a V-groove joint. Proper joint preparation and a neutral flame heat source are required.

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    LH 210 SF is a flexible flux-coated brass brazing alloy rod that can be directly applied without separate flux. It has good strength up to 45 kgf/mm2 and melts between 890-900°C. It can be used to join steel, cast iron, copper, brass and other dissimilar metals through capillary action or by melting the rod into a V-groove joint. Proper joint preparation and a neutral flame heat source are required.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    76 views1 page

    210 SF

    Uploaded by

    Antony Joshwa
    LH 210 SF is a flexible flux-coated brass brazing alloy rod that can be directly applied without separate flux. It has good strength up to 45 kgf/mm2 and melts between 890-900°C. It can be used to join steel, cast iron, copper, brass and other dissimilar metals through capillary action or by melting the rod into a V-groove joint. Proper joint preparation and a neutral flame heat source are required.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    LOW-HEAT INPUT WELDING ALLOYS

    LH 210 SF Flexible coated special brass brazing alloy with good


    strength

    ALLOY BASIS
    Cu, Zn, Additives

    PROPERTIES
    LH 210 SF is a flexible flux coated rod which can be used directly on the job without
    separate application of flux. The operation becomes very fast and economical. The flux is
    so flexible and thin that on bending the rod through 180 0 the flux coating does not peel off.
    Hence it has an extended life span.

    TECHNICAL DATA
    UTS : up to 45 kgf/mm2
    Melting temperature : 890-900 0C

    TYPICAL APPLICATIONS
    Joining and surfacing of steel, cast iron, copper,
    brass. Also for galvanised iron, joins dissimilar
    metals like steel to cast iron, steel to copper and
    copper-alloys and cast iron to copper and copper
    alloys. Excellent for sheet metal assembly and
    repair. Well suited for repair of car bodies and car
    silencer assembly where it can be used on
    overhead position without dismantling.

    PROCEDURE
    In steel, copper and its alloys where thickness is more than 5 mm make a V-groove of 750.
    Clean the joint thoroughly. Use neutral flame. Preheat a broad area and then heat locally
    until flux melts. Then apply the rod and melt it into the joint. For capillary joints melt the rod
    and draw with the flame along the joint. In case of cast iron, preheat the entire casting to
    450 0C and maintain this preheat until the operation is completed.
    Cleaning: Remove flux residues mechanically or chemically (using 10% hydrochloric acid
    for ferrous metals and 10% sulphuric acid for copper and its alloys) followed by rinsing in
    running water.
    Heat Source: Acetylene torch, furnace, high frequency induction.

    AVAILABILITY
    Size (∅ mm)/Length : 1.6x500 2.5x500 3.2x500 4.0x500

    Ador Fontech Limited