An American National Standard

Designation: D2241 09

Standard Specification for

Poly(Vinyl Chloride) (PVC) Pressure-Rated Pipe (SDR
Series)1
This standard is issued under the fixed designation D2241; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon () indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.

1. Scope* of this standard to establish appropriate safety and health

1.1 This specification covers poly(vinyl chloride) (PVC) practices and determine the applicability of regulatory limita-
pipe made in standard thermoplastic pipe dimension ratios and tions prior to use. A specific precautionary statement is given
pressure rated for water (see appendix). Included are criteria in Note 7.
for classifying PVC plastic pipe materials and PVC plastic NOTE 3CPVC plastic pipe (SDR-PR), which was formerly included
pipe, a system of nomenclature for PVC plastic pipe, and in this specification, is now covered by Specification F442/F442M.
requirements and test methods for materials, workmanship,
dimensions, sustained pressure, burst pressure, flattening, and NOTE 4The sustained and burst pressure test requirements, and the
extrusion quality. Methods of marking are also given. pressure ratings in the appendix, are calculated from stress values obtained
from tests made on pipe 4 in. (100 mm) and smaller. However, tests
1.2 The products covered by this specification are intended conducted on pipe as large as 24 in. (600 mm) in diameter have shown
for use with the distribution of pressurized liquids only, which these stress values to be valid for larger diameter PVC pipe.
are chemically compatible with the piping materials. Due to
inherent hazards associated with testing components and sys- NOTE 5PVC pipe made to this specification is often belled for use as
tems with compressed air or other compressed gases, some line pipe. For details of the solvent cement bell, see Specification D2672
manufacturers do not allow pneumatic testing of their products. and for details of belled elastomeric joints, see Specifications D3139 and
D3212.
Consult with specific product/component manufacturers for
their specific testing procedures prior to pneumatic testing. 2. Referenced Documents
NOTE 1Pressurized (compressed) air or other compressed gases 2.1 ASTM Standards:2
contain large amounts of stored energy which present serious safety D618 Practice for Conditioning Plastics for Testing
hazards should a system fail for any reason. D1598 Test Method for Time-to-Failure of Plastic Pipe
NOTE 2This standard specifies dimensional, performance and test
requirements for plumbing and fluid handling applications, but does not
Under Constant Internal Pressure
address venting of combustion gases. D1599 Test Method for Resistance to Short-Time Hydraulic
Pressure of Plastic Pipe, Tubing, and Fittings
1.3 The text of this specification references notes, footnotes,
D1600 Terminology for Abbreviated Terms Relating to
and appendixes which provide explanatory material. These
Plastics
notes and footnotes (excluding those in tables and figures) shall
D1784 Specification for Rigid Poly(Vinyl Chloride) (PVC)
not be considered as requirements of the specification.
Compounds and Chlorinated Poly(Vinyl Chloride)
1.4 The values stated in inch-pound units are to be regarded
(CPVC) Compounds
as standard. The values given in parentheses are mathematical
D2122 Test Method for Determining Dimensions of Ther-
conversions to SI units that are provided for information only
moplastic Pipe and Fittings
and are not considered standard.
D2152 Test Method for Adequacy of Fusion of Extruded
1.5 The following safety hazards caveat pertains only to the
Poly(Vinyl Chloride) (PVC) Pipe and Molded Fittings by
test methods portion, Section 8, of this specification: This
Acetone Immersion
standard does not purport to address all of the safety concerns,
D2444 Test Method for Determination of the Impact Resis-
if any, associated with its use. It is the responsibility of the user
tance of Thermoplastic Pipe and Fittings by Means of a
Tup (Falling Weight)
1
This specification is under the jurisdiction of ASTM Committee F17 on Plastic
Piping Systems and is the direct responsibility of Subcommittee F17.25 on Vinyl
2
Based Pipe. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Dec. 1, 2009. Published December 2009. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1964. Last previous edition approved in 2005 as D2241 05. DOI: Standards volume information, refer to the standards Document Summary page on
10.1520/D2241-09. the ASTM website.

*A Summary of Changes section appears at the end of this standard.

Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
Copyright by ASTM Int'l (all rights reserved); Fri Jul 1 12:36:10 EDT 2011
1
Downloaded/printed by
Jalusa Soares (Tigre+S.A+-+Tubos+e+Conexoes) pursuant to License Agreement. No further reproductions authorized.
 D2241 09
D2672 Specification for Joints for IPS PVC Pipe Using 3.2.5 standard thermoplastic pipe materials designation
Solvent Cement codeThe pipe materials designation code shall consist of the
D2837 Test Method for Obtaining Hydrostatic Design Basis abbreviation PVC for the type of plastic, followed by the
for Thermoplastic Pipe Materials or Pressure Design Basis ASTM type and grade in Arabic numerals and the design stress
for Thermoplastic Pipe Products in units of 100 psi (0.7 MPa) with any decimal figures dropped.
D3139 Specification for Joints for Plastic Pressure Pipes When the design stress code contains less than two figures, a
Using Flexible Elastomeric Seals cipher shall be used before the number, thus a complete
D3212 Specification for Joints for Drain and Sewer Plastic material code shall consist of three letters and four figures for
Pipes Using Flexible Elastomeric Seals PVC plastic pipe materials.
F412 Terminology Relating to Plastic Piping Systems
F442/F442M Specification for Chlorinated Poly(Vinyl 4. Classification
Chloride) (CPVC) Plastic Pipe (SDRPR) 4.1 GeneralThis specification covers PVC pipe made and
2.2 NSF Standards:3 marked with one of six Type/Grade/Design Stress designations
Standard No. 14 for Plastic Piping Components and Related (see X1.2) in eleven standard dimension ratios.
Materials 4.2 Standard Thermoplastic Pipe Dimension Ratios
Standard No. 61 for Drinking Water Systems (SDR)This specification covers PVC pipe in eleven standard
ComponentsHealth Effects dimension ratios, namely, 13.5, 17, 21, 26, 32.5, 41, and 64 (in
the body of the document) and 11, 35, 51 and 81 (in Annex
3. Terminology A1.) Standard dimension ratios are uniform for all nominal
3.1 DefinitionsDefinitions are in accordance with Termi- pipe sizes for each material and pressure rating. These are
nology F412, and abbreviations are in accordance with Termi- referred to as SDR 11, SDR13.5, SDR17, SDR21, SDR26,
nology D1600, unless otherwise specified. The abbreviation for SDR32.5, SDR35, SDR41, SDR51, SDR64, and SDR81,
poly(vinyl chloride) plastic is PVC. respectively. The pressure rating is uniform for all nominal
3.2 Definitions of Terms Specific to This Standard: pipe sizes for a given PVC pipe material and SDR (see Table
3.2.1 hydrostatic design stressthe estimated maximum X1.1).
tensile stress the material is capable of withstanding continu- 4.3 Hydrostatic Design StressesThis specification covers
ously with a high degree of certainty that failure of the pipe pipe made from PVC plastics defined by four hydrostatic
will not occur. This stress is circumferential when internal design stresses developed on the basis of long-term tests
hydrostatic water pressure is applied. (appendix).
3.2.2 pressure rating (PR)the estimated maximum water
pressure the pipe is capable of withstanding continuously with 5. Materials
a high degree of certainty that failure of the pipe will not occur. 5.1 GeneralPoly(vinyl chloride) plastics used to make
3.2.3 relation between standard dimension ratio, hydro- pipe meeting the requirements of this specification are catego-
static design stress, and pressure ratingThe following ex- rized by means of two criteria, namely, (1) short-term strength
pression, commonly known as the ISO equation,4 is used in tests, and (2) long-term strength tests.
this specification to relate standard dimension ratio, hydrostatic NOTE 6The PVC pipe intended for use in the transport of potable
design stress, and pressure rating: water should be evaluated and certified as safe for this purpose by a testing
2S/P 5 R 2 1 or 2 S/P 5 ~D0/t! 2 1 (1) agency acceptable to the local health authority. The evaluation should be
in accordance with requirements for chemical extraction, taste, and odor
where: that are no less restrictive than those included in NSF Standard No. 14.
S = hydrostatic design stress, psi (or MPa), The seal or mark of the laboratory making the evaluation should be
P = pressure rating, psi (or MPa), included on the pipe. See pipe marking requirement for reclaimed water
D0 = average outside diameter, in. (or mm), systems.
t = minimum wall thickness, in. (or mm), and 5.2 Basic MaterialsThis specification covers pipe made
R = standard thermoplastic pipe dimension ratio (D0/t for from PVC plastics having certain physical and chemical
PVC pipe), also known as SDR. properties as described in Specification D1784.
3.2.4 standard thermoplastic pipe dimension ratio (SDR) 5.3 CompoundThe PVC compounds used for this pipe
the ratio of pipe diameter to wall thickness. For PVC pipe it is shall equal or exceed one of the following classes described in
calculated by dividing the average outside diameter of the pipe Specification D1784: PVC 12454 or 14333.
in inches or millimetres by the minimum wall thickness in 5.4 Rework MaterialThe manufacturer shall use only his
inches or millimetres. If the wall thickness calculated by this own clean rework pipe material and the pipe produced shall
formula is less than 0.060 in. (1.52 mm), it shall be arbitrarily meet all the requirements of this specification.
increased to 0.060in. (1.52 mm). The SDR values shall be
rounded to the nearest 0.5. 6. Requirements Requirements
6.1 Dimensions and Tolerances:
3
6.1.1 Outside DiametersThe outside diameters and toler-
Available from NSF International, P.O. Box 130140, 789 N. Dixboro Rd., Ann
ances shall be as shown in Table 1 when measured in
Arbor, MI 48113-0140, http://www.nsf.org.
4
ISO R1611960, Pipes of Plastics Materials for the Transport of Fluids accordance with Test Method D2122. The tolerances for
(Outside Diameters and Nominal Pressures) Part 1, Metric Series. out-of-roundness shall apply only on pipe prior to shipment.

Copyright by ASTM Int'l (all rights reserved); Fri Jul 1 12:36:10 EDT 2011
2
Downloaded/printed by
Jalusa Soares (Tigre+S.A+-+Tubos+e+Conexoes) pursuant to License Agreement. No further reproductions authorized.
 D2241 09
TABLE 1 IPS PVC PipeOutside Diameters and Tolerances
Tolerances, in. (mm)
Maximum Out-of-Roundness
(Maximum Minimum Diameter)
Nominal Pipe Average Outside Diameter,
SDR64,
Size, in. in. (mm) For Average SDR41,
SDR17,
SDR32.5,
SDR13.5
SDR26,
SDR21

18 0.405 (10.29) 60.004 (0.10) 0.030 (0.76) 0.016 (0.41)

14 0.540 (13.72) 60.004 (0.10) 0.030 (0.76) 0.016 (0.41)
3 8 0.675 (17.14) 60.004 (0.10) 0.030 (0.76) 0.016 (0.41)
1 2 0.840 (21.34) 60.004 (0.10) 0.030 (0.76) 0.016 (0.41)

3 4 1.050 (26.67) 60.004 (0.10) 0.030 (0.76) 0.020 (0.51)

1 1.315 (33.40) 60.005 (0.13) 0.030 (0.76) 0.020 (0.51)
1 1 4 1.660 (42.16) 60.005 (0.13) 0.030 (0.76) 0.024 (0.61)
1 1 2 1.900 (48.26) 60.006 (0.15) 0.060 (1.52) 0.024 (0.61)

2 2.375 (60.32) 60.006 (0.15) 0.060 (1.52) 0.024 (0.61)

2 1 2 2.875 (73.02) 60.007 (0.18) 0.060 (1.52) 0.030 (0.76)
3 3.500 (88.90) 60.008 (0.20) 0.060 (1.52) 0.030 (0.76)
3 1 2 4.000 (101.60) 60.008 (0.20) 0.100 (2.54) 0.030 (0.76)

4 4.500 (114.30) 60.009 (0.23) 0.100 (2.54) 0.030 (0.76)

5 5.563 (141.30) 60.010 (0.25) 0.100 (2.54) 0.060 (1.52)
6 6.625 (168.28) 60.011 (0.28) 0.100 (2.54) 0.070 (1.78)
8 8.625 (219.08) 60.015 (0.38) 0.150 (3.81) 0.090 (2.29)

10 10.750 (273.05) 60.015 (0.38) 0.150 (3.81) 0.100 (2.54)

12 12.750 (323.85) 60.015 (0.38) 0.150 (3.81) 0.120 (3.05)
14 14.000 (355.60) 60.015 (0.38) 0.200 (5.08) 0.150 (3.81)
16 16.000 (406.40) 60.019 (0.48) 0.320 (8.13) 0.160 (4.06)

18 18.000 (457.20) 60.019 (0.48) 0.360 (9.14) 0.180 (4.57)

20 20.000 (508.00) 60.023 (0.58) 0.400 (10.2) 0.200 (5.08)
24 24.000 (609.60) 60.031 (0.79) 0.480 (12.2) 0.240 (6.10)
30 30.000 (762.00) 60.041 (1.04) 0.600 (15.2) 0.300 (7.62)
36 36.000 (914.40) 60.050 (1.27) 0.720 (18.3) 0.360 (9.14)

6.1.2 Wall ThicknessThe wall thicknesses and tolerances 6.6 Impact ResistanceThe minimum impact resistance for
shall be as shown in Table 2 when measured in accordance PVC plastic pipe shall be as given in Table 5, when determined
with Test Method D2122. in accordance with 8.7.
6.2 Sustained PressureThe pipe shall not fail, balloon, NOTE 7The impact resistance test is intended for use only as a quality
burst, or weep as defined in Test Method D1598 at the test control test, not as a simulated service test. This test has been found to
pressures given in Table 3 when tested in accordance with 8.4. have no quality control significance in sizes over 12 in. (305 mm).
6.2.1 Accelerated Regression TestThe accelerated regres-
sion test shall be used in place of both the sustained and burst 7. Workmanship, Finish, and Appearance
pressure tests, at the option of the manufacturer. The test shall 7.1 The pipe shall be homogeneous throughout and free
be conducted in accordance with 8.4.1. The pipe shall demon- from visible cracks, holes, foreign inclusions, or other defects.
strate a hydrostatic design basis projection at the 100 000-h The pipe shall be as uniform as commercially practicable in
intercept that meets the hydrostatic design basis category color, opacity, density, and other physical properties.
requirement (see the table for Hydrostatic Design Basis NOTE 8Color and transparency or opacity should be specified in the
Categories of Test Method D2837) for the PVC material used contract or purchase order.
in its manufacture. ( Example: PVC 1120 pipe must have a
minimum 100 000-h projection of 3830 psi and 85 % lower 8. Test Methods
confidence limit (LCL).) 8.1 Conditioning Unless otherwise specified in the appli-
6.3 Burst PressureThe minimum burst pressures for PVC cable test method, condition the test specimens at 73.4 6 3.6F
plastic pipe shall be as given in Table 4, when determined in (23 6 2C) and 50 6 5 % relative humidity for not less than 40
accordance with 8.5. h prior to test in accordance with Procedure A of Practice D618
6.4 FlatteningThere shall be no evidence of splitting, for those tests where conditioning is required.
cracking, or breaking when the pipe is tested in accordance 8.2 Test ConditionsConduct the tests in the standard
with 8.6. laboratory atmosphere of 73.4 6 3.6F (23 6 2C) and 50 6
6.5 Extrusion QualityThe pipe shall not flake or disinte- 5 % relative humidity, unless otherwise specified in the test
grate when tested in accordance with Test Method D2152. methods or in this specification.

Copyright by ASTM Int'l (all rights reserved); Fri Jul 1 12:36:10 EDT 2011
3
Downloaded/printed by
Jalusa Soares (Tigre+S.A+-+Tubos+e+Conexoes) pursuant to License Agreement. No further reproductions authorized.
 D2241 09
TABLE 2 Wall Thicknesses and Tolerances for PVC Plastic Pipe with IPS Outside Diameters
Wall Thickness,A in.B
Nominal
SDR64 SDR41 SDR32.5 SDR26 SDR21 SDR17 SDR13.5
Pipe
Size, in. Mini- Toler- Mini- Toler- Mini- Toler- Mini- Toler- Mini- Toler- Mini- Toler- Mini- Toler-
mum ance mum ance mum ance mum ance mum ance mum ance mum ance

18 ... ... ... ... ... ... ... ... ... ... ... ... 0.060 +0.020

14 ... ... ... ... ... ... ... ... ... ... ... ... 0.060 +0.020
3 8 ... ... ... ... ... ... ... ... ... ... ... ... 0.060 +0.020
1 2 ... ... ... ... ... ... ... ... ... ... ... ... 0.062 +0.020
3 4 ... ... ... ... ... ... ... ... 0.060 +0.020 0.062 +0.020 0.078 +0.020
1 ... ... ... ... ... ... 0.060 +0.020 0.063 +0.020 0.077 +0.020 0.097 +0.020
1 1 4 ... ... ... ... 0.060 +0.020 0.064 +0.020 0.079 +0.020 0.098 +0.020 0.123 +0.020
1 1 2 ... ... ... ... 0.060 +0.020 0.073 +0.020 0.090 +0.020 0.112 +0.020 0.141 +0.020
2 ... ... ... ... 0.073 +0.020 0.091 +0.020 0.113 +0.020 0.140 +0.020 0.176 +0.020
2 1 2 ... ... ... ... 0.088 +0.020 0.110 +0.020 0.137 +0.020 0.169 +0.020 0.213 +0.026
3 ... ... 0.085 +0.020 0.108 +0.020 0.135 +0.020 0.167 +0.020 0.206 +0.025 0.259 +0.031
3 1 2 ... ... 0.098 +0.020 0.123 +0.020 0.154 +0.020 0.190 +0.023 0.235 +0.028 0.296 +0.036
4 0.070 +0.020 0.110 +0.020 0.138 +0.020 0.173 +0.020 0.214 +0.026 0.265 +0.032 0.333 +0.040
5 0.087 +0.020 0.136 +0.020 0.171 +0.021 0.214 +0.027 0.265 +0.032 0.327 +0.039 0.412 +0.049
6 0.104 +0.020 0.162 +0.020 0.204 +0.024 0.255 +0.031 0.316 +0.038 0.390 +0.047 0.491 +0.059
8 0.135 +0.020 0.210 +0.025 0.265 +0.032 0.332 +0.040 0.410 +0.049 0.508 +0.061 ... ...
10 0.168 +0.020 0.262 +0.031 0.331 +0.040 0.413 +0.050 0.511 +0.061 0.632 +0.076 ... ...
12 0.199 +0.024 0.311 +0.037 0.392 +0.047 0.490 +0.059 0.606 +0.073 0.750 +0.090 ... ...
14 ... ... 0.341 +0.048 0.430 +0.052 0.538 +0.064 0.666 +0.080 0.823 +0.099 ... ...
16 ... ... 0.390 +0.055 0.492 +0.059 0.615 +0.074 0.762 +0.091 0.941 +0.113 ... ...
18 ... ... 0.439 +0.061 0.554 +0.066 0.692 +0.083 0.857 +0.103 1.059 +0.127 ... ...
20 ... ... 0.488 +0.068 0.615 +0.074 0.769 +0.092 0.952 +0.114 1.176 +0.141 ... ...
24 ... ... 0.585 +0.082 0.738 +0.088 0.923 +0.111 1.143 +0.137 1.412 +0.169 ... ...
30 ... ... 0.732 +0.102 0.923 +0.111 1.154 +0.138 1.428 +0.171 1.765 +0.212 ... ...
36 ... ... 0.878 +0.123 1.108 +0.133 1.385 +0.166 1.714 +0.205 2.118 +0.254 ... ...
A
The minimum is the lowest wall thickness of the pipe at any cross section. The maximum permitted wall thickness, at any cross section, is the minimum wall thickness
plus the stated tolerance. All tolerances are on the plus side of the minimum requirement.
B
1 in. = 25.4 mm (exact).

TABLE 3 Sustained Pressure Test Conditions for Water at 73F (23C) for PVC Plastic Pipe
PressureA Required for Test
PVC 1120,
SDR PVC 1220,
PVC 2120 PVC 2116 PVC 2112 PVC 2110
psi MPa (bar) psi MPa (bar) psi MPa (bar) psi MPa (bar)
13.5 670 4.62 (46.2) 540 3.72 (37.2) 450 3.10 (31.0) 370 2.55 (25.5)
17 530 3.65 (36.5) 420 2.90 (29.0) 350 2.41 (24.1) 290 2.00 (20.0)
21 420 2.90 (29.0) 340 2.34 (23.4) 280 1.93 (19.3) 230 1.59 (15.9)
26 340 2.34 (23.4) 270 1.86 (18.6) 220 1.52 (15.2) 180 1.24 (12.4)
32.5 270 1.86 (18.6) 210 1.45 (14.5) 180 1.24 (12.4) 150 1.03 (10.3)
41 210 1.45 (14.5) 170 1.17 (11.7) 140 0.97 (9.7) 120 0.83 (8.3)
64 130 0.90 (9.0) 110 0.76 (7.6) 90 0.62 (6.2) 70 0.48 (4.8)
A
The fiber stresses used to derive these test pressures are as follows:
psi MPa (bar)
PVC 1120, PVC 1220, PVC 2120 4200 29.0 (290)
PVC 2116 3360 23.2 (232)
PVC 2112 2800 19.3 (193)
PVC 2110 2300 15.9 (159)

Some minor adjustments have been made to keep the test pressures uniform to simplify testing.

8.3 SamplingThe selection of the sample or samples of ten times the nominal diameter in length, but not less than 10
pipe shall be as agreed upon by the purchaser and the seller. In in. (250 mm) or more than 3 ft (1000 mm) between end
case of no prior agreement, any sample selected by the testing closures and bearing the permanent marking on the pipe.
laboratory shall be deemed adequate. Maintain the specimens at the pressure indicated for a period of
8.3.1 Test SpecimensNot less than 50 % of the test speci- 1000 h. Hold the pressure as closely as possible, but within
mens required for any pressure test shall have at least a part of 610 psi (670 kPa). Condition the specimens at the test
the marking in their central sections. The central section is that temperature of 73.4F (23C) to within 63.6F (2C). Main-
portion of pipe which is at least one pipe diameter away from tain the test temperature at 73.4 6 3.6F (23 6 2C). Test in
an end closure. accordance with Test Method D1598, except maintain the
8.4 Sustained Pressure TestSelect the test specimens at pressure at the values given in Table 3 for 1000 h. Failure of
random. Test individually with water at the internal pressures two of the six specimens tested shall constitute failure in the
given in Table 3, six specimens of pipe, each specimen at least test. Failure of one of the six specimens tested is cause for

Copyright by ASTM Int'l (all rights reserved); Fri Jul 1 12:36:10 EDT 2011
4
Downloaded/printed by
Jalusa Soares (Tigre+S.A+-+Tubos+e+Conexoes) pursuant to License Agreement. No further reproductions authorized.
 D2241 09
TABLE 4 Burst Pressure Requirements for Water at 73F (23C) the compression is completed within 2 to 5 min. On removal of
for PVC Plastic Pipe the load, examine the specimens for evidence of splitting,
Minimum Burst PressureA cracking, or breaking.
PVC 1120, PVC 2116, 8.7 Impact ResistanceDetermine the impact resistance in
SDR PVC 1220, PVC 2112, accordance with the specification requirement section of Test
PVC 2120 PVC 2110
Method D2444. Test at 73.4 6 3.6F (236 2C) using a Tup B
psi MPa (bar) psi MPa (bar)
and flat plate support. Use a 20-lb (9-kg) tup.
13.5 1000 6.89 (68.9) 800 5.52 (55.2) 8.7.1 Test SpecimensSpecimens of pipe for impact testing
17 800 5.52 (55.2) 630 4.34 (43.4)
21 630 4.34 (43.4) 500 3.45 (34.5) shall be cut to lengths required in Test Method D2444.
26 500 3.45 (34.5) 400 2.76 (27.6) 8.7.2 Test Requirements (14 to 12 in.)For pipe sizes 14
32.5 400 2.76 (27.6) 315 2.17 (21.7) in. (6 mm) through 12 in. (300 mm), ten specimens shall be
41 315 2.17 (21.7) 250 1.72 (17.2)
64 200 1.38 (13.8) 160 1.10 (11.0) tested. If nine or more pass, the lot passes. If two or more fail,
A
The fiber stresses used to derive these test the lot fails.
pressures are as follows:
psi MPa (bar) 9. Retest and Rejection
PVC 1120, PVC 1220, PVC 2120 6400 44.1 (441) 9.1 If the results of any test(s) do not meet the requirements
PVC 2116, PVC 2112, PVC 2110 5000 34.5 (345)
of this specification, the test(s) shall be conducted again only
by agreement between the purchaser and seller. Under such
TABLE 5 Impact Resistance at 73F (23C) for PVC Plastic Pipe agreement, minimum requirements shall not be lowered,
changed, or modified, nor shall specification limits be changed.
Impact Resistance, Impact Resistance,
Size, in.
ftlbf (J) All SDRs
Size, in.
ftlbf (J) All SDRs If upon retest, failure occurs, the quantity of product repre-

14 10 (13.6) 212 40 (54.2)
sented by the test(s) does not meet the requirements of this

12 10 (13.6) 3 60 (81.3) specification.
3 4 15 (20.3) 312 70 (94.9)
1 20 (27.1) 4 90 (122.0) 10. Product Marking
1 1 4 20 (27.1) 5 100 (135.6)
1 1 2 30 (40.7) 6 120 (162.7) 10.1 Marking on the pipe shall include the following,
2 30 (40.7) 8 or larger 160 (216.9) spaced at intervals of not more than 5 ft (1.5 m):
10.1.1 Nominal pipe size (for example, 2 in. (50 mm)),
10.1.2 The outside diameter system (IPS or PIP) on sizes 14
retest of six additional specimens. Failure of one of the six in. (350 mm) and over (for example, IPS 14 in. (350 mm) or
specimens tested in retest shall constitute failure in the test. PIP 21 in. (500 mm)),
Evidence of failure of the pipe shall be as defined in Test 10.1.3 Type of plastic pipe material in accordance with the
Method D1598. designation code given in 3.2.5 (for example, PVC1120),
8.4.1 Accelerated Regression TestTest in accordance with 10.1.4 Standard thermoplastic pipe dimension ratio in ac-
procedures in Test Method D1598, using either free end or cordance with the designation code given in 3.2.4 (for ex-
restrained end fittings. A minimum of six specimens shall be ample, SDR21), or the pressure rating in pounds per square
tested. Test three specimens at a single pressure that result in inch for water at 73F (23C) shown as the number followed
failures at or below 0.10 h. Test an additional three specimens by psi (for example, 200 psi (1.4 MPa)), except that when
at a single pressure that will result in failures at about 200 h. intended for pressure applications, the pressure rating shall be
Generating additional data points to improve the LTHS or shown (for example, 200 psi (1.4 MPa)). When the indicated
LCL, or both, is acceptable. No points shall be excluded unless pressure rating is lower than that calculated in accordance with
an obvious defect is detected in the failure area of the test 3.2.3 (see appendix), the SDR shall also be included in the
sample, or there was a malfunction of test equipment. Charac- marking code,
terize the data using the least squares regression described in 10.1.5 ASTM designation D2241, with which the pipe
Test Method D2837. complies,
8.5 Burst PressureDetermine the minimum burst pressure 10.1.6 Manufacturers name (or trademark),
with at least five specimens in accordance with Test Method 10.1.7 Production code with which the manufacturer can
D1599, having the lengths specified in 8.4. The time of testing trace the year, month, day shift, plant and extruder of manu-
of each specimen shall be not less than 60 s. facture for this product, and
NOTE 9Times greater than 60 s may be needed to bring large size 10.1.8 Pipe intended for the transport of potable water shall
specimens to the burst pressure. The test is more difficult to pass using also include the seal or mark of the laboratory making the
greater pressurizing times. evaluation for this purpose, spaced at intervals specified by the
8.6 FlatteningFlatten three specimens of the pipe, 2 in. laboratory.
(50 mm) long, between parallel plates in a suitable press until NOTE 10Manufacturers using the seal or mark of a laboratory must
the distance between the plates is 40 % of the outside diameter obtain prior authorization from the laboratory concerned.
of the pipe. The rate of loading shall be uniform and such that

Copyright by ASTM Int'l (all rights reserved); Fri Jul 1 12:36:10 EDT 2011
5
Downloaded/printed by
Jalusa Soares (Tigre+S.A+-+Tubos+e+Conexoes) pursuant to License Agreement. No further reproductions authorized.
 D2241 09
11. Quality Assurance 12. Keywords
11.1 When the product is marked with this designation, 12.1 pressure pipe; pressure rated; PVC; SDR
D2241, the manufacturer affirms that the product was manu-
factured, inspected, sampled, and tested in accordance with this
specification and has been found to meet the requirements of
this specification.

SUPPLEMENTARY REQUIREMENTS

This requirement applies whenever a regulatory authority or user calls for product to be used to
convey or to be in contact with potable water.

S1. Potable Water RequirementProducts intended for the health effects portion of NSF Standard No. 14 by an
contact with potable water shall be evaluated, tested, and acceptable certifying organization when required by the regu-
certified for conformance with ANSI/NSF Standard No. 61 or latory authority having jurisdiction.

This requirement applies only to pipe to be used in systems that have not established other provisions for identification.

S2. Pipe Marking Requirement for Reclaimed Water stripes printed lengthwise on opposite sides of the pipe. The
SystemsColor Identification of pipe shall be by: (1) use of pipe shall be marked RECLAIMED WATER at intervals of 5
purple (violet) PVC material or (2) by use of continuous purple ft. or less.

ANNEX

(Mandatory Information)

A1. PVC PRESSURE RATED PIPES HAVING OTHER THAN IPS OUTSIDE DIAMETERS

A1.1 As the use of PVC pipe has expanded, a need for pipe TABLE A1.2 PIP Outside Diameters and Tolerance for PVC
diameters and dimension ratios other than those listed in the Plastic Pipe
main body of this specification has developed. These include Tolerances, in. (mm)
Nominal Tube Average Outside
small diameter (2-in. and under) CTS sizes and larger diameter Size, in. Diameter, in. (mm) Average
Maximum
(6 in. and over) PIP sizes. The IPS outside diameter pipes and Out-of-Roundness

the standard dimension ratios included in the body of this 6 6.140 (155.96) 60.011 (0.28) 0.100 (2.54)
8 8.160 (207.26) 60.15 (0.38) 0.150 (3.81)
specification provide the format onto which these additional 10 10.200 (259.08) 60.15 (0.38) 0.150 (3.81)
sizes are fitted. 12 12.240 (310.90) 60.15 (0.38) 0.150 (3.81)
15 15.300 (388.62) 6 .016 (0.41) 0.294 (7.46)
A1.2 Pipe sizes listed in this Annex shall be tested to verify 18 18.701 (475.00) 6 .020 (0.51) 0.360 (9.14)
21 22.047 (559.99) 6 .025 (0.64) 0.420 (10.66)
they meet the requirements shown in Tables A1.1-A1.7 and all 24 24.803 (629.99) 6 .032 (0.81) 0.480 (12.20)
other requirements of the specification. 27 27.953 (710.00) 6 .038 (0.96) 0.540 (13.72)

TABLE A1.1 CTS Outside Diameters and Tolerance for PVC

Plastic Pipe
Tolerances, in. (mm)
Nominal Tube Average Outside
Size, in. Diameter, in. (mm) Maximum
Average TABLE A1.3 Sustained Pressure Test Conditions for Water
Out-of-Roundness
73.4F (23C) for PVC Plastic PipeA

12 0.625 (15.9) 6 0.003 (0.08) 0.008 (0.20)

34 0.875 (22.2) 6 0.003 (0.08) 0.010 (0.26) Pressure Required for TestPVC 1120
1 1.125 (28.6) 6 0.003 (0.08) 0.012 (0.30) SDR psi MPa Bars
1 14 1.375 (34.9) 6 0.003 (0.08) 0.014 (0.36)
11 840 5.79 57.9
1 12 1.625 (41.3) 6 0.004 (0.10) 0.016 (0.40)
35 247 1.70 17.0
2 2.125 (54.0) 6 0.004 (0.10) 0.020 (0.50)
51 168 1.16 11.6
81 105 0.725 7.25
A
The fiber stress used to derive this test was 4200 psi (29.0 MPa).

Copyright by ASTM Int'l (all rights reserved); Fri Jul 1 12:36:10 EDT 2011
6
Downloaded/printed by
Jalusa Soares (Tigre+S.A+-+Tubos+e+Conexoes) pursuant to License Agreement. No further reproductions authorized.
 D2241 09
TABLE A1.4 Burst Pressure Test Conditions for Water at 73.4F
(23C) for PVC Plastic PipeA
Pressure Required for TestPVC 1120
SDR psi MPa Bars
11 1280 8.82 88.2
35 380 2.62 26.2
51 260 1.79 17.9
81 160 1.085 10.85
A
The fiber stress used to derive this test was 6400 psi (44.1 MPa).

TABLE A1.5 Water Pressure Ratings (PR) at 73F (23C) for

Nonthreaded PVC Plastic Pipe
PVC 1120
PVC 1220
SDR PVC 2120
psi MPa Bars
11 400 2.75 27.5
35 118 0.81 8.1
51 80 0.55 5.5
81 50 0.34 3.4

TABLE A1.6 Wall Thicknesses and Tolerances for PVC Plastic pipe with CTS Outside DiametersA
Wall Thickness, in. (mm)B
Nominal Tube
SDR 21 SDR 17 SDR 13.5 SDR 11
Size, in.
Minimum Tolerance Minimum Tolerance Minimum Tolerance Minimum Tolerance
12 ... ... ... ... 0.060 +0.020 0.060 +0.020
34 ... ... 0.060 +0.020 0.065 +0.020 0.080 +0.020
1 0.060 +0.020 0.066 +0.020 0.083 +0.020 0.102 +0.020
1 1 4 0.065 +0.020 0.081 +0.020 0.102 +0.020 0.125 +0.020
1 1 2 0.077 +0.020 0.096 +0.020 0.120 +0.020 0.148 +0.020
2 0.101 +0.023 0.125 +0.023 0.157 +0.023 0.193 +0.023
A
The minimum is the lowest wall thickness of the pipe at any cross section. The maximum permitted wall thickness, at any cross-section, is the minimum wall thickness
plus the stated tolerance. All tolerances are on the plus side of the minimum tolerance.
B
1 in. = 25.4 mm (exact).

TABLE A1.7 Wall Thicknesses and Tolerances for PVC Plastic Pipe with PIP Outside DiametersA
Wall Thickness, in. (mm)B
Nominal
SDR81 SDR51 SDR41 SDR35 SDR32.5 SDR26 SDR21
Pipe
Size, in. Mini- Toler- Mini- Toler- Mini- Toler- Mini- Toler- Mini- Toler- Mini- Toler- Mini- Toler-
mum ance mum ance mum ance mum ance mum ance mum ance mum ance
6 0.076 +0.020 0.120 +0.020 0.150 +0.020 ... ... 0.189 +0.023 ... ... ... ...
8 0.101 +0.020 0.160 +0.020 0.199 +0.024 ... ... 0.251 +0.030 ... ... ... ...
10 0.126 +0.020 0.200 +0.024 0.249 +0.030 ... ... 0.314 +0.038 ... ... ... ...
12 0.151 +0.020 0.240 +0.029 0.299 +0.036 ... ... 0.377 +0.045 ... ... ... ...
15 0.189 +0.023 0.300 +0.042 0.373 +0.052 0.437 +0.052 0.471 +0.056 0.588 +0.070 0.728 +0.087
18 ... ... 0.366 +0.051 0.456 +0.064 0.534 +0.064 0.575 +0.069 0.719 +0.086 ... ...
21 ... ... 0.432 +0.060 0.538 +0.075 0.630 +0.076 0.678 +0.081 0.848 +0.102 ... ...
24 ... ... 0.486 +0.068 0.605 +0.085 0.709 +0.085 0.763 +0.092 0.954 +0.115 ... ...
27 ... ... 0.548 +0.077 0.682 +0.095 0.799 +0.096 0.860 +0.103 1.075 +0.129 ... ...
A
1 in. = 25.4 mm (exact).
B
The minimum is the lowest wall thickness of the pipe at any cross section. The maximum permitted wall thickness, at any cross section, is the minimum wall thickness
plus the stated tolerance. All tolerances are on the plus side of the minimum requirement.

Copyright by ASTM Int'l (all rights reserved); Fri Jul 1 12:36:10 EDT 2011
7
Downloaded/printed by
Jalusa Soares (Tigre+S.A+-+Tubos+e+Conexoes) pursuant to License Agreement. No further reproductions authorized.
 D2241 09
APPENDIX

(Nonmandatory Information)

X1. SOURCE OF HYDROSTATIC DESIGN STRESSES

TABLE X1.1 Standard Thermoplastic Pipe Dimension Ratios (SDR) and Water Pressure Ratings (PR) at 73F (23C) for Nonthreaded
PVC Plastic PipeA
Pressure Rating of PVC Pipe MaterialsA
SDR PVC 1120, PVC 2116 PVC 2112 PVC 2110
PVC 1220,
PVC 2120
psi MPa (bar) psi MPa (bar) psi MPa (bar) psi MPa (bar)
13.5 315 2.17 (21.7) 250 1.72 (17.2) 200 1.38 (13.8) 160 1.10 (11.0)
17 250 1.72 (17.2) 200 1.38 (13.8) 160 1.10 (11.0) 125 0.86 (8.6)
21 200 1.38 (13.8) 160 1.10 (11.0) 125 0.86 (8.6) 100 0.69 (6.9)
26 160 1.10 (11.0) 125 0.86 (8.6) 100 0.69 (6.9) 80 0.55 (5.5)
32.5 125 0.86 (8.6) 100 0.69 (6.9) 80 0.55 (5.5) 63 0.43 (4.3)
41 100 0.69 (6.9) 80 0.55 (5.5) 63 0.43 (4.3) 50 0.34 (3.4)
64 63 0.43 (4.3) 50 0.34 (3.4) NPRC NPRC NPRC NPRC
Pressure RatingABC Standard Dimension Ratio of PVC Pipe Materials
psi MPa (bar) PVC 1120, PVC 2116 PVC 2112 PVC 2110
PVC 1220,
PVC 2120
315 27.17 (21.7) 13.5 ... ... ...
250 1.72 (17.2) 17 13.5 ... ...
200 1.38 (13.8) 21 17 13.5 ...
160 1.10 (11.0) 26 21 17 13.5
125 0.86 (8.6) 32.5 26 21 17
100 0.69 (6.9) 41 32.5 26 21
80 0.55 (5.5) ... 41 32.5 26
63 0.43 (4.3) 64 ... 41 32.5
50 0.34 (3.4) ... 64 ... 41
A
These pressures ratings do not apply for threaded pipe.
B
See 3.2.5 and 5.3 for code designation.
C
NPR = not pressure rated.

X1.1 The hydrostatic design stresses recommended by the for thermoplastic pipe materials is Test Method D2837. Addi-
Plastics Pipe Institute are used to pressure rate PVC plastic tional information regarding the criteria used in developing
pipe. These hydrostatic design stresses are 2000 psi (14 MPa), these hydrostatic design stresses may be obtained from the
1600 psi (11.0 MPa), 1250 psi (8.6 MPa), and 1000 psi (6.9 Plastics Pipe Institute.5 These hydrostatic design stresses may
MPa) for water at 73.4F (23C). These hydrostatic design not be suitable for materials that show a wide departure from
stresses apply only to pipe meeting all the requirements of this a straight line plot of log stress versus log time to failure. All
specification. the data available to date on PVC pipe materials made in the
United States exhibit a straight-line plot under these plotting
X1.2 Six PVC pipe materials are included based on the
conditions.
requirements of Specification D1784 and the PPI-
recommended hydrostatic design stresses as follows: X1.4 The pipe is rated for use with water in 73F (23C) at
X1.2.1 Type I, Grade 1 (12454-B), with a hydrostatic design the maximum internal pressures shown in Table X1.1. Lower
stress of 2000 psi (14 MPa), designated as PVC1120. pressure ratings than those calculated in accordance with 3.2.3
X1.2.2 Type I, Grade 2 (12454-C), with a hydrostatic design may be recommended, at the option of the pipe manufacturer,
stress of 2000 psi (14 MPa), designated as PVC1220. in which case the SDR shall be included in the marking.
X1.2.3 Type II, Grade 1 (14333-D), with a hydrostatic Experience of the industry indicates that PVC plastic pipe
design stress of 2000 psi (14 MPa), designated as PVC2120. meeting the requirements of this specification give satisfactory
X1.2.4 Type II, Grade 1 (14333-D), with a hydrostatic service under normal conditions for a long period at these
design stress of 1600 psi (11.0 MPa), designated as PVC2116. pressure ratings. The sustained pressure requirements (6.3) are
X1.2.5 Type II, Grade 1 (14333-D), with a hydrostatic related to these ratings through the slopes of the strength-time
design stress of 1250 psi (8.6 MPa), designated as PVC2112. plots of these materials in pipe form.
X1.2.6 Type II, Grade 1 (14333-D), with a hydrostatic 5
Available from Plastics Pipe Institute (PPI), 105 Decker Court, Suite 825,
design stress of 1000 psi (7 MPa), designated as PVC2110. Irving, TX 75062, http://www.plasticpipe.org.
X1.3 The standard method for obtaining hydrostatic basis

Copyright by ASTM Int'l (all rights reserved); Fri Jul 1 12:36:10 EDT 2011
8
Downloaded/printed by
Jalusa Soares (Tigre+S.A+-+Tubos+e+Conexoes) pursuant to License Agreement. No further reproductions authorized.
 D2241 09
X1.5 The hydrostatic design stresses recommended by the
Plastic Pipe Institute are based on tests made on pipe ranging
in size from 12 to 212 in. (12.5 to 50 mm).

SUMMARY OF CHANGES

Committee F17 has identified the location of selected changes to this standard since the last issue (D224105)
that may impact the use of this standard.

(1) Inserted the phrase, Unless otherwise specified in the

applicable test method... into 8.1.

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.

This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website
(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/
COPYRIGHT/).

Copyright by ASTM Int'l (all rights reserved); Fri Jul 1 12:36:10 EDT 2011
9
Downloaded/printed by