Thickness and width tolerances are as per IS: 1852/2003. Closer tolerances can also be supplied
on demand.
Packaging : Bare bundles with cross-wise steel strip. Packet weight : 7 - 18 tonnes. Marking :
Paint marked on the top sheet of the bundle OR Sticker/label on top sheet of bundle with
required details.
Common grades for Hot Rolled Coils and Sheets : IS 10748/2009 grades I-V, API 5L
Grades A, B, X42, X46, X52, X56, X60, SAIL-WTCR, IS: 11513/2011 grades O, D, DD, EDD,
IS: 1079/ 1994 grades O, D, DD, EDD, Medium Carbon Strapping Steel,
HCRS, SAE-1040, SAE – 1055, C 30, 40, 50, Medium Silicon Electrical Steel, IS: 6240/2008, SAIL
HS LPG, SAILMA, IS: 2062/2011, IS: 5986/2011 Fe 330, 360, 410, 510, SAILRIM, IS: 2062/2011
Grade with copper, SAILCOR/IRSM-41, SAE 1012, SAE 1541 Auto Chassis Grade: E 34 / E38 / 46
& SAPH 45.
Materials are also available in the following foreign specifications : For structural and
general purposes- ASTM-A 36/A 569/A 570 Grades 33/40, JISG 3101 SS400, JISG 3131 SPHC, DIN
17100 ST 37.2/ST 44.2, BS 4360 Grades 40/43A, EN 10025; For Tube-making and other grades :
JISG 3132 SPHT 1/2, DIN 1614 Pt. 1/2 ST 22/23/24, SAE 1006, SAE 1018 or equivalents, if sufficient
orders are available.
HR Sheets for Conventional LPG Cylinders
Thickness (mm) Width (mm) Length (mm)
2.9 1240 2480
2.8 1250 2500
Sheets can also be supplied in the following sizes on mutual agreement : 2.9 x 1360 x 2720 mm,
2.9 x 1270 x 2540 mm, 3.0 x 1360 x 2700 mm
Other sizes of hot rolled coils and sheets can be supplied as per mutual agreement.
NOTES:
1. Steel of these grades can be supplied with the addition of micro-alloying elements like Boron,
Titanium, Niobium and Vanadium. The micro-alloying elements shall not exceed 0.008
percent in case of Boron and 0.20 percent in case of other elements.
2. The Nitrogen content of the steel shall not be more than 0.007 percent. For Aluminium killed
or Silicon-Aluminium killed, the Nitrogen content shall not exceed 0.012 percent. This has
to be ensured by the manufacturer by occasional check analysis.
3. Grade HR4 and HR5 shall be supplied in fully Aluminium killed condition or Aluminium
with stabilising elements.
4. When the steel is Aluminium killed, the total Aluminium content shall not be less than 0.02
percent. When the steel is Silicon killed, the Silicon content shall not be less than 0.10
percent. When the steel is Aluminium-Silicon killed, the Silicon content shall not be less
than 0.03 percent and total Aluminium content shall not be less than 0.01 percent.
5. When Copper bearing steel is required the Copper content shall be between 0.20 and 0.35
percent. In case of product analysis, the Copper content shall be between 0.17 and 0.38
percent.
6. Restricted chemistry may be mutually agreed to between the purchaser and the supplier.
Chemical Composition
Grade C Mn S P Al Si MAE
max max max max min max max
HSFQ 250 0.12 1.00 0.020 0.025 0.02 0.25 -
HSFQ 350 0.12 1.20 0.020 0.025 0.02 0.25 0.03
HSFQ 450 0.12 1.40 0.020 0.025 0.02 0.40 0.05
HSFQ 500 0.12 1.50 0.020 0.025 0.02 0.50 0.10
HSFQ 550 0.12 1.60 0.020 0.025 0.02 0.50 0.15
Grade C Mn S P Al Si MAE
max max max max min max max
SAIL FORMING 250 0.12 1.40 0.025 0.030 0.02 0.30 0.04
SAIL FORMING 350 0.12 1.50 0.025 0.030 0.02 0.40 0.08
SAIL FORMING 450 0.12 1.60 0.025 0.030 0.02 0.50 0.12
MnB Steel 0.25 1.50 0.025 0.030 0.02 0.40 0.40
Chemical Composition
Specification Grade C % max Mn % max P % max S % max Si % max
IS: 10748/2004 1 0.10 0.50 0.040 0.040 For semi killed
II 0.12 0.60 0.040 0.040 Quality Si
III 0.16 1.20 0.040 0.040 content shall
IV 0.20 1.30 0.040 0.040 be 0.08% max
V 0.25 1.30 0.040 0.040
CE: 0.45 max for grades IV and V
SAIL WTCR - 0.06 0.25 0.025 0.025 0.04
SAIL SOFT - 0.06 0.25 0.025 0.04 0.05
NOTES:
1. Elements not listed in this table may not be added to the steel. All suitable arrangements are
to be made to prevent such elements being added from scrap or other materials used during
manufacture, which impair the mechanical properties and usability.
2. Steel may be supplied with the addition of micro alloying elements like niobium, titanium,
vanadiam and boron. The micro-alloying elements shall not exceed 0.10% when added
individually or in combination.
3. The nitrogen content of the steel shall not be more than 0.009%. This has to be ensured by
the manfacturer by occasional check analysis.
Mechanical Properties
IS: 1079/2009
Tensile Percentage Elongation after Fracture
Quality
Strength A, min
Rm2 t≤3 t>3
max Gauge Gauge Gauge Gauge
Desig- Old Desig- Name MPa length length length length
nation nation Lo=80 Lo=50 Lo=5.65√So Lo=50
mm mm mm mm
HR0 (New) Ordinary * * * * *
HR1 O Commercial 440 23 24 28 29
HR2 D Drawing 420 25 26 30 31
HR3 DD Deep Drawing 400 28 29 33 34
HR4 EDD Extra Deep 380 31 32 36 37
Drawing
HR5 SAILFORM 34 YS 340 400-500 * * 26 27
SAILFORM 38 YS 380 450-570 * * 24 25
SAILFORM 45 YS 450 500-620 * * 20 21
NOTES:
1. 1 MPa = 1N/mm2
2. Minimum tensile strength for qualities HR1, HR2, HR3 and HR4 would normally be expected
to be 270 MPa. Where minimum tensile strength is required, the value of 270 MPa may be
specified. All tensile strength values are determined to the nearest 10 MPa.
3. The non proportional test piece with a fixed original gauge length (50 mm) up to 6 mm
thick sheet can be used in conjunction with a conversion table. In case of dispute, however,
only the results obtained on a proportional test piece will be valid for material 3 mm and
over in thickness.
4. HR5 grade is for cold rolling only, therefore mechanical properties are not applicable.
5. Where “t” is thickness of steel sheet, in mm.
6. Tensile testing is not mandatory for HR1, unless agreed to between the purchaser and
manufacturer.
* Properties on mutual agreement between the purchaser and manufacturer.
Mechanical Properties
Specification Grade Yield Ultimate Tensile Elongation Internal diameter
Strength Strength % Std GL of bend
MPa min MPa min
SAILCOR 340 480 22
SAIL PROP SAE 1020 310-320 440 15
SAIL PRE FAB SAE 1020 345 min 450 min 21
spl.
Mechanical Properties
IS: 2062/2011
Grade Quality Tensile Yield Stress Percentage Internal Charpy
Designation Strength Min Mpa Elongation A, Bend Impact Test
Rm Min at Gauge Length, Diameter (See Note
MPa L=5.65 √S Min Min (See 3 & 4)
Note 2)
<20 20-40 >40 ≤25 >25 Temp J, Min
°C
(1) (2) (3) (4) (5) (6) (7) (8) (9) (10) (11)
A – –
E-250 BR 410 250 240 230 23 2t 3t RT 27
B0 0 27
C (-) 20 27
A – –
E-300 BR 440 300 290 280 22 2t – RT 27
B0 0 27
C (-) 20 27
A – –
E-350 BR 490 350 330 320 22 2t – RT 27
B0 0 27
C (-) 20 27
A – –
E-410 BR 540 410 390 380 20 2t – RT 25
B0 0 25
C (-) 20 25
A – –
E-450 BR 570 450 430 420 20 2.5t – RT 20
B0
C
E-550 A 650 550 530 520 12 3t – – –
BR RT 15
E 600 A 730 600 580 570 12 3.5t – – –
BR RT 15
E 650 A 780 650 630 620 12 4t – – –
BR RT 15
• For sub-quality BR, Impact test is optional.
• Impact test shall normally be carried out on products having thickness greater than or equal
to 12 mm.
Mechanical Properties - SAILMA grades
Grade YS, MPa, UTS, MPa, % El Internal Bend Charpy Impact
min min min Diameter, min Test
Std GL
≤25 >25 Temp oC J, min
mm mm
<25 25-40 >40
mm mm mm
SAILMA 300 300 290 280 440 24 2t - - -
SAILMA 300 HI 300 290 280 440 24 2t 0 40
SAILMA 350 350 330 320 490 24 2t - - -
SAILMA 350 HI 350 330 320 490 24 2t - 0 40
-20 30
SAILMA 410 410 390 380 540 22 2t - - -
SAILMA 410 HI 410 390 380 540 22 2t - 0 35
-20 25
SAILMA 450 450 430 420 570 22 2.5t - - -
SAILMA 450 HI 450 430 420 570 22 2.5t - 0 30
-20 20
SAILMA 550 550 530 520 650 14 3t - - -
SAILMA 550 HI 550 530 520 650 14 3t - 0 25
-20 15
SAILMA 600 600 580 570 730 14 3.5t - - -
Impact will be given for any one temperature. For 450 HI & above impact is for >10 mm. For <12
mm impact to be given only if specified.
Mechanical Properties
Specification Grade Yield Ultimate Tensile Elongation % Internal dia-
Strength Strength meter of bend
MPa min MPa Up to Above
3 mm 3 mm
Strapping
Quality
SAE 1541
Medium C 30 55% 500-600 21
Carbon of UTS
C 40 580-680 18
C 50 660-780 13
Med Si Elec
IS 6240/2008 240 350-450 25 t - Thickness of
GL=5.65√So test piece
SAIL HS LPG SG 255 255 400 28
GL=50 mm
JISG 3116 SG 295 295 440 26
GL=50 mm
SAIL HS LPG P245 245 360-450 26 34
P265NB 265 410-500 24 32
EN 10120 P310NB 310 460-550 21 28
SAIL SUPER JISG 3113 305 GL: 50 mm
FORM (t<6 mm) 345 (t <6 mm)
SAPH 45 SAPH 295 (t:6 440 32% (t:6-8 mm)
440 to 8 mm)
APL-5L A 207 331
% elongation
B 241-418 414-758 1.944A 0.2/U 0.9
X42 290-496 414-758 (GL : 50.8 mm)
X46 317-524 434-758 for all API Grades
A : Cross sectional
X52 359-531 455-758 area in mm2
X56 386-544 490-758 U: Minimum UTS
X60 414-565 517-758 in MPa
X65 448-600 531-758
X70 483-621 565-758
NOTES : These are pipe properties. Hot rolled plate/coil properties are to be mutually agreed
upon by producer and pipe manufacturers.
Mechanical Properties
Grade YS, MPa, min UTS, MPa, min % El min (Std GL)
HSFQ 250 250 380 30
HSFQ 350 350 400 28
HSFQ 450 450 520 25
HSFQ 500 500 560 22
HSFQ 550 550 620 18
Grade YS, MPa, min UTS, MPa, min % El min (Std GL)
SAIL FORMING 250 250 410 26
SAIL FORMING 350 350 490 24
SAIL FORMING 450 450 550 22
Mechanical Properties of high tensile flat rolled steel for lighter cylinder
(IS 15914:2011)
Grade Tensile Yield Percentage Elongation Reference Heat
Strength Stress MPa at Gauge Length = Treatment Austenitizing
MPa Min 5.65√So Min Temperature ºC
<3 mm3 3 to 5 mm3
HS 235 360-460 235 25 32 920-960
HS 265 410-510 265 22 30 890-930
HS 295 450-560 295 20 28 890-930
HS 345 490-610 345 18 24 880-920
The above properties are specified for cold formed and normalized cylinder. However tensile
properties of hot rolled plate/sheet/strip are to be mutually agreed upon by the producer and
by the cylinder manufacturer.