Structural Bolts, Steel, Heat Treated, 120/105 Ksi Minimum Tensile Strength
Structural Bolts, Steel, Heat Treated, 120/105 Ksi Minimum Tensile Strength
F1789 Terminology for F16 Mechanical Fasteners 1, zinc coated A563-DH, zinc coated
F2329 Specification for Zinc Coating, Hot-Dip, Require-
1, coated in accordance with A563–DH coated in accor-
ments for Application to Carbon and Alloy Steel Bolts, Specification F1136, Grade dance with Specification
Screws, Washers, Nuts, and Special Threaded Fasteners 3 F1136, Grade 5
G101 Guide for Estimating the Atmospheric Corrosion
3, plain A563-C3, DH3, plain
Resistance of Low-Alloy Steels
2.2 ASME Standards:5 3.2.2 Alternatively, nuts conforming to Specification A194/
B 1.1 Unified Screw Threads A194M Gr. 2H are considered a suitable substitute for use with
B 18.2.6 Fasteners for Use in Structural Applications Specification A325 Type 1 heavy hex structural bolts.
B 18.24 Part Identification Number (PIN) Code System 3.2.3 When Specification A194/A194M Gr. 2H zinc-coated
Standard for B18 Fastener Products nuts are supplied, the zinc coating, overtapping, lubrication,
and rotational capacity testing shall be in accordance with
3. Ordering Information Specification A563.
3.1 Orders for heavy hex structural bolts under this speci- 3.3 Recommended Washers:
fication shall include the following: 3.3.1 Washers conforming to Specification F436 are the
3.1.1 Quantity (number of pieces of bolts and accessories). recommended washers for use with Specification A325 heavy
3.1.2 Size, including nominal bolt diameter, thread pitch, hex structural bolts. The washers shall have a surface finish for
and bolt length. each type of bolt as follows:
3.1.3 Name of product, heavy hex structural bolts. Bolt Type and Finish Washer Finish
3.1.4 When bolts threaded full length are required, Supple-
mentary Requirement S1 shall be specified. 1, plain (uncoated) plain (uncoated)
3.1.5 Type of bolt: Type 1 or 3. When type is not specified, 1, zinc coated zinc coated
either Type 1 or Type 3 shall be furnished at the supplier’s
option. 1, coated in accordance with coated in accordance with Speci-
Specification F1136, Grade 3 fication F1136, Grade 3
3.1.6 ASTM designation and year of issue.
3.1.7 Other components such as nuts, washers, and com- 3, plain weathering steel, plain
pressible washer-type direct-tension indicators, if required.
3.4 Other Accessories:
3.1.7.1 When such other components are specified to be
3.4.1 When compressible washer type direct tension indica-
furnished, also state “Nuts, washers, and direct tension indica-
tors are specified to be used with these bolts, they shall
tors, or combination thereof, shall be furnished by lot number.”
conform to Specification F959, Type 325.
3.1.8 Zinc Coating—Specify the zinc coating process re-
quired, for example, hot dip, mechanically deposited, Zinc/
4. Materials and Manufacture
Aluminum Corrosion Protective Coating or no preference (see
4.3). 4.1 Heat Treatment:
3.1.9 Other Finishes—Specify other protective finish, if 4.1.1 Type 1 bolts produced from medium carbon steel shall
required. be quenched in a liquid medium from the austenitizing
3.1.10 Test reports, if required (see Section 13). temperature. Type 1 bolts produced from medium carbon steel
3.1.11 Supplementary or special requirements, if required. to which chromium, nickel, molybdenum, or born were inten-
3.1.12 For establishment of a part identifying system, see tionally added shall be quenched only in oil from the austen-
ASME B 18.24. itizing temperature.
4.1.2 Type 3 bolts shall be quenched only in oil from the
NOTE 3—A typical ordering description follows: 1000 pieces 11⁄8-7 austenitizing temperature.
UNC in. dia 3 4 in. long heavy hex structural bolt, Type 1 ASTM
A325–02, each with one hardened washer, ASTM F436 Type 1, and one
4.1.3 Type 1 bolts, regardless of the steel used, and Type 3
heavy hex nut, ASTM A563 Grade DH. Each component hot-dip bolts shall be tempered by reheating to not less than 800°F.
zinc-coated. Nuts lubricated. 4.2 Threading—Threads shall be cut or rolled.
4.3 Zinc Coatings, Hot-Dip and Mechanically Deposited,
3.2 Recommended Nuts:
Zinc/Aluminum Corrosion Protective Coating:
3.2.1 Nuts conforming to the requirements of Specification
4.3.1 When zinc-coated fasteners are required, the pur-
A563 are the recommended nuts for use with Specification
chaser shall specify the zinc coating process, for example, hot
dip, mechanically deposited, Zinc/Aluminum Corrosion Pro-
5 tective Coating, or no preference.
Available from American Society of Mechanical Engineers (ASME), ASME
International Headquarters, Three Park Ave., New York, NY 10016-5990, http:// 4.3.2 When hot-dip is specified, the fasteners shall be
www.asme.org. zinc-coated by the hot-dip process and the coating shall
Copyright by ASTM Int'l (all rights reserved); Fri Sep 5 12:23:36 EDT 2014
2
Downloaded/printed by
Universidad De Chile pursuant to License Agreement. No further reproductions authorized.
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Please contact ASTM International (www.astm.org) for the latest information.
A325 – 09
conform to the coating weight/thickness and performance TABLE 1 Chemical Requirements for Type 1 Bolts
requirements of Specification F2329.
4.3.3 When mechanically deposited is specified, the fasten- Carbon Steel
Element
ers shall be zinc-coated by the mechanical deposition process Heat Product
Analysis Analysis
and the coating shall conform to the coating weight/thickness
and performance requirements of Class 55 of Specification Carbon 0.30–0.52 0.28–0.55
Manganese, min 0.60 0.57
B695. Phosphorus, max 0.040 0.048
4.3.4 When Zinc/Aluminum Corrosion Protective Coating Sulfur, max 0.050 0.058
Silicon 0.15–0.30 0.13–0.32
is specified, the coating shall conform to the coating weight/
thickness and performance requirements of Grade 3 of Speci-
fication F1136. Carbon Boron Steel
4.3.5 When no preference is specified, the supplier shall Element
Heat Product
furnish either a hot-dip zinc coating in accordance with Analysis Analysis
Specification F2329, a mechanically deposited zinc coating in Carbon 0.30–0.52 0.28–0.55
accordance with Specification B695, Class 55, or a Zinc/ Manganese, min 0.60 0.57
Aluminum Corrosion Protective Coating in accordance with Phosphorus, max 0.040 0.048
Sulfur, max 0.050 0.058
Specification F1136, Grade 3. Threaded components (bolts and Silicon 0.10–0.30 0.08–0.32
nuts) shall be coated by the same zinc-coating process and the Boron 0.0005–0.003 0.0005–0.003
supplier’s option is limited to one process per item with no
mixed processes in a lot.
Alloy Steel
4.4 Lubrication—When zinc-coated nuts are ordered with Element
the bolts, the nuts shall be lubricated in accordance with Heat Product
Analysis Analysis
Specification A563, Supplementary Requirement S1, to mini-
Carbon 0.30–0.52 0.28–0.55
mize galling. Manganese, min 0.60 0.57
4.5 Secondary Processing: Phosphorus, max 0.035 0.040
4.5.1 If any processing, which can affect the mechanical Sulfur, max 0.040 0.045
Silicon 0.15–0.35 0.13–0.37
properties or performance of the bolts, is performed after the Alloying Elements A A
Copyright by ASTM Int'l (all rights reserved); Fri Sep 5 12:23:36 EDT 2014
3
Downloaded/printed by
Universidad De Chile pursuant to License Agreement. No further reproductions authorized.
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Please contact ASTM International (www.astm.org) for the latest information.
A325 – 09
TABLE 2 Chemical Requirements for Type 3 Heavy Hex Structural BoltsA
Composition, %
Type 3 BoltsA
Element A B C D E F
Carbon:
Heat analysis 0.33–0.40 0.38–0.48 0.15–0.25 0.15–0.25 0.20–0.25 0.20–0.25
Product analysis 0.31–0.42 0.36–0.50 0.14–0.26 0.14–0.26 0.18–0.27 0.19–0.26
Manganese:
Heat analysis 0.90–1.20 0.70–0.90 0.80–1.35 0.40–1.20 0.60–1.00 0.90–1.20
Product analysis 0.86–1.24 0.67–0.93 0.76–1.39 0.36–1.24 0.56–1.04 0.86–1.24
Phosphorus:
Heat analysis 0.035 max 0.06–0.12 0.035 max 0.035 max 0.035 max 0.035 max
Product analysis 0.040 max 0.06–0.125 0.040 max 0.040 max 0.040 max 0.040 max
Sulfur:
Heat analysis 0.040 max 0.040 max 0.040 max 0.040 max 0.040 max 0.040 max
Product analysis 0.045 max 0.045 max 0.045 max 0.045 max 0.045 max 0.045 max
Silicon:
Heat analysis 0.15–0.35 0.30–0.50 0.15–0.35 0.25–0.50 0.15–0.35 0.15–0.35
Product analysis 0.13–0.37 0.25–0.55 0.13–0.37 0.20–0.55 0.13–0.37 0.13–0.37
Copper:
Heat analysis 0.25–0.45 0.20–0.40 0.20–0.50 0.30–0.50 0.30–0.60 0.20–0.40
Product analysis 0.22–0.48 0.17–0.43 0.17–0.53 0.27–0.53 0.27–0.63 0.17–0.43
Nickel:
Heat analysis 0.25–0.45 0.50–0.80 0.25–0.50 0.50–0.80 0.30–0.60 0.20–0.40
Product analysis 0.22–0.48 0.47–0.83 0.22–0.53 0.47–0.83 0.27–0.63 0.17–0.43
Chromium:
Heat analysis 0.45–0.65 0.50–0.75 0.30–0.50 0.50–1.00 0.60–0.90 0.45–0.65
Product analysis 0.42–0.68 0.47–0.83 0.27–0.53 0.45–1.05 0.55–0.95 0.42–0.68
Vanadium:
B B B B B
Heat analysis 0.020 min
B B B B B
Product analysis 0.010 min
Molybdenum:
B B B B
Heat analysis 0.06 max 0.10 max
B B B B
Product analysis 0.07 max 0.11 max
Titanium:
B B B B B
Heat analysis 0.05 max
B B B B B
Product analysis 0.06 max
A
A, B, C, D, E, and F are classes of material used for Type 3 bolts. Selection of a class shall be at the option of the bolt manufacturer.
B
These elements are not specified or required.
TABLE 3 Hardness Requirements for Bolts tested shall be axially tension tested full size and shall conform
Bolt Length,
Brinell Rockwell C to the minimum tensile load and proof load or alternate proof
Bolt Size, in. in. Min Max Min Max load specified in Table 4. Sizes 1.00 in. and smaller having a
⁄
12 to 1, incl Less than 253 319 25 34 length shorter than 2D that cannot be axially tensile tested shall
2D A be qualified on the basis of hardness.
2D and ... 319 ... 34
over 6.2.4 For bolts on which both hardness and tension tests are
11⁄8 to 11⁄2 , Less than 223 286 19 30 performed, acceptance based on tensile requirements shall take
incl 3D A
3D and ... 286 ... 30 precedence in the event of low hardness readings.
over 6.3 Rotational Capacity Test:
A
Sizes 1.00 in. and smaller having a length shorter than 2D and sizes larger
than 1.00 in. having a length shorter than 3D are subject only to minimum and
6.3.1 Definition—The rotational capacity test is intended to
maximum hardness. evaluate the presence of a lubricant, the efficiency of the
D = Nominal diameter or thread size. lubricant, and the compatibility of assemblies as represented by
the components selected for testing.
6.3.2 Requirement—Zinc-coated bolts, zinc-coated wash-
are tested by both full-size and machined specimen methods, ers, and zinc-coated and lubricated nuts tested full size in an
the full-size test shall take precedence. assembled joint or tension measuring device, in accordance
6.2.3 Sizes 1.00 in. and smaller having a length shorter than with 10.2, shall not show signs of failure when subjected to the
21⁄4 D down to 2D, inclusive, that cannot be wedge tensile nut rotation in Table 6. The test shall be performed by the
Copyright by ASTM Int'l (all rights reserved); Fri Sep 5 12:23:36 EDT 2014
4
Downloaded/printed by
Universidad De Chile pursuant to License Agreement. No further reproductions authorized.
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Please contact ASTM International (www.astm.org) for the latest information.
A325 – 09
TABLE 4 Tensile Load Requirements for Full-Size Bolts oversize, in accordance with Specification A563, shall have
Proof Load,B Alternative Class 2A threads before hot-dip or mechanically deposited zinc
Length Proof coating. After zinc coating, the maximum limits of pitch and
Bolt Size, Threads per Measure- Load,B Yield
Inch, and Series Stress Area,A Tensile Load,B ment Strength major diameter shall not exceed the Class 2A limit by more
Designation in.2 min, lbf Method Method than the following amounts:
Column 1 Column 2 Column 3 Column 4 Column 5 Oversize Limit, in.A
Hot-Dip Mechanical
⁄
12 –13 UNC 0.142 17 050 12 050 13 050 Nominal Bolt
5⁄8
Zinc Zinc
–11 UNC 0.226 27 100 19 200 20 800 Diameter (in.)
3⁄4 –10 UNC 0.334 40 100 28 400 30 700
7⁄8 –9 UNC 0.462 55 450 39 250 42 500 1⁄2 0.018 0.012
⁄
9 16 , 5⁄ 8 , 3⁄ 4 0.020 0.013
1–8 UNC 0.606 72 700 51 500 55 750 7⁄8 0.022 0.015
11⁄8 –7 UNC 0.763 80 100 56 450 61 800
1 to 11⁄4 0.024 0.016
11⁄4 –7 UNC 0.969 101 700 71 700 78 500
1 3 ⁄8 , 1 1 ⁄2 0.027 0.018
13⁄8 –6 UNC 1.155 121 300 85 450 93 550
A
11⁄2 –6 UNC 1.405 147 500 104 000 113 800 Hot-dip zinc nuts are tapped oversize after coating, and mechanical zinc-
A
coated nuts are tapped oversize before coating.
The stress area is calculated as follows:
7.2.3 The gaging limit for bolts shall be verified during
As 5 0.7854 [D 2 ~0.9743/n!# 2 manufacture. In case of dispute, a calibrated thread ring gage of
the same size as the oversize limit in 7.2.2 (Class X tolerance,
where:
As = stress area, in.2,
gage tolerance plus) shall be used to verify compliance. The
D = nominal bolt size, and gage shall assemble with hand effort following application of
n = threads per inch. light machine oil to prevent galling and damage to the gage.
These inspections, when performed to resolve controversy,
B
shall be conducted at the frequency specified in the quality
Loads tabulated are based on the following:
assurance provisions of ASME B 18.2.6.
Bolt Size, in. Column 3 Column 4 Column 5
⁄ to 1, incl
12 120 000 psi 85 000 psi 92 000 psi 8. Workmanship
11⁄8 to 11⁄2 , incl 105 000 psi 74 000 psi 81 000 psi
8.1 The allowable limits, inspection, and evaluation of the
surface discontinuities, quench cracks, forging cracks, head
bursts, shear bursts, seams, folds, thread laps, voids, tool
responsible party (see Section 14) prior to shipment after zinc marks, nicks, and gouges shall be in accordance with Specifi-
coating and lubrication of nuts (see 10.2 and Note 4). cation F788/F788M.
6.3.3 Acceptance Criterion—The bolt and nut assembly
shall be considered as non-conforming if the assembly fails to 9. Number of Tests and Retests
pass any one of the following specified requirements: 9.1 Testing Responsibility:
6.3.3.1 Inability to install the assembly to the nut rotation in 9.1.1 Each lot shall be tested by the manufacturer prior to
Table 6. shipment in accordance with the lot identification control
6.3.3.2 Inability to remove the nut after installing to the quality assurance plan in 9.2 through 9.5.
rotation specified in Table 6. 9.1.2 When bolts are furnished by a source other than the
6.3.3.3 Shear failure of the threads as determined by visual manufacturer, the Responsible Party as defined in 14 shall be
examination of bolt and nut threads following removal. responsible for assuring all tests have been performed and the
6.3.3.4 Torsional or torsional/tension failure of the bolt. bolts comply with the requirements of this specification (see
Elongation of the bolt, in the threads between the nut and bolt 4.5).
head, is to be expected at the required rotation and is not to be 9.2 Purpose of Lot Inspection—The purpose of a lot inspec-
classified as a failure. tion program is to ensure that each lot conforms to the
requirements of this specification. For such a plan to be fully
7. Dimensions effective it is essential that secondary processors, distributors,
7.1 Head and Body: and purchasers maintain the identification and integrity of each
7.1.1 The bolts shall conform to the dimensions for heavy lot until the product is installed.
hex structural bolts specified in ASME B 18.2.6. 9.3 Lot Method—All bolts shall be processed in accordance
7.1.2 The thread length shall not be changed except as with a lot identification-control quality assurance plan. The
provided in Supplementary Requirement S1. Bolts with thread manufacturer, secondary processors, and distributors shall
lengths other than those required by this specification shall be identify and maintain the integrity of each production lot of
ordered under Specification A449. bolts from raw-material selection through all processing op-
7.2 Threads: erations and treatments to final packing and shipment. Each lot
7.2.1 Uncoated—Threads shall be the Unified Coarse shall be assigned its own lot-identification number, each lot
Thread Series as specified in ASME B 1.1, and shall have Class shall be tested, and the inspection test reports for each lot shall
2A tolerances. be retained.
7.2.2 Coated—Unless otherwise specified, zinc-coated bolts 9.4 Lot Definition—A lot shall be a quantity of uniquely
to be used with zinc-coated nuts or tapped holes that are tapped identified heavy hex structural bolts of the same nominal size
Copyright by ASTM Int'l (all rights reserved); Fri Sep 5 12:23:36 EDT 2014
5
Downloaded/printed by
Universidad De Chile pursuant to License Agreement. No further reproductions authorized.
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Please contact ASTM International (www.astm.org) for the latest information.
A325 – 09
TABLE 5 Tensile Strength Requirements for Specimens Machined from Bolts
Bolt Diameter, in. Tensile Strength, min, psi (MPa) Yield Strength, min, psi (MPa) Elongation, in 4D, min, % Reduction of Area, min, %
⁄ to 1, incl.
12 120 000 (825) 92 000 (635) 14 35
Over 1 to 11⁄2 105 000 (725) 81 000 (560) 1435
TABLE 6 Rotational Capacity Test for Zinc-Coated Bolts thickness, including the washer, such that 3 to 5 full threads of
Nominal Nut Rotation, degrees the bolt are located between the bearing surfaces of the bolt
Bolt Length, in. (turn) head and nut. The hole in the joint shall have the same nominal
Up to and including 4 3 dia 240 (2⁄3) diameter as the hole in the washer. The initial tightening of the
Over 4 3 dia, but not 360 (1)
exceeding 8 3 dia nut shall produce a load in the bolt not less than 10 % of the
Over 8 3 dia, but not 420 (11⁄6) specified proof load. After initial tightening, the nut position
exceeding 12 3 dia shall be marked relative to the bolt, and the rotation shown in
Over 12 3 dia. Test not applicable
Table 6 shall be applied. During rotation, the bolt head shall be
restrained from turning. After the tightening rotation has been
applied, the assembly shall be taken apart and examined for
and length produced consecutively at the initial operation from compliance with 6.3.3.
a single mill heat of material and processed at one time, by the
same process, in the same manner so that statistical sampling is NOTE 4—Rotational capacity tests shall apply only to matched assem-
valid. The identity of the lot and lot integrity shall be bly lots that contain one A325 bolt, one A563 lubricated nut, and one F436
washer that have been zinc coated in accordance with either Specifications
maintained throughout all subsequent operations and packag- F2329 or B695. Both the bolt and nut components of the matched
ing. assembly shall be zinc coated using the same process.
9.5 Number of Tests—The minimum number of tests from
each lot for the tests specified below shall be as follows: 11. Inspection
Tests Number of Tests 11.1 If the inspection described in 11.2 is required by the
in Accordance With
purchaser, it shall be specified in the inquiry and contract or
order.
Hardness, tensile 11.2 The purchaser’s representative shall have free entry to
strength, proof load, Guide F1470
and rotational capacity
all parts of the manufacturer’s works, or supplier’s place of
business, that concern the manufacture or supply of the
Coating weight/ The referenced coating material ordered. The manufacturer or supplier shall afford the
thickness specificationA
purchaser’s representative all reasonable facilities to satisfy
Surface discontinuities Specification F788/F788M him that the material is being furnished in accordance with this
specification. All tests and inspections required by the specifi-
Dimensions and ASME B 18.2.6
thread fit
cation that are requested by the purchaser’s representative shall
A
be made before shipment, and shall be conducted as not to
Guide F1470 applies if the coating specification does not specify a testing
frequency. interfere unnecessarily with the operation of the manufactur-
er’s works or supplier’s place of business.
10. Test Methods
10.1 Tensile, Proof Load, and Hardness: 12. Rejection and Rehearing
10.1.1 Tensile, proof load, and hardness tests shall be 12.1 Disposition of nonconforming bolts shall be in accor-
conducted in accordance with Test Methods F606. dance with the Guide F1470 section titled “Disposition of
10.1.2 Tensile strength shall be determined using the Wedge Nonconforming Lots.”
or Axial Tension Testing Method of Full Size Product Method
or the Machined Test Specimens Method depending on size 13. Certification
and length as specified in 6.2.1-6.2.4. Fracture on full-size tests 13.1 When specified on the purchase order, the manufac-
shall be in the body or threads of the bolt without a fracture at turer or supplier, whichever is the responsible party as defined
the junction of the head and body. in Section 14, shall furnish the purchaser a test reports that
10.1.3 Proof load shall be determined using Method 1, includes the following:
Length Measurement, or Method 2, Yield Strength, at the 13.1.1 Heat analysis, heat number, and a statement certify-
option of the manufacturer. ing that heats having the elements listed in 5.4 intentionally
10.2 Rotational Capacity—The zinc-coated bolt shall be added were not used to produce the bolts,
placed in a steel joint or tension measuring device and 13.1.2 Results of hardness, tensile, and proof load tests,
assembled with a zinc-coated washer and a zinc-coated and 13.1.3 Results of rotational capacity tests. This shall include
lubricated nut with which the bolt is intended to be used (see the test method used (solid plate or tension measuring device);
Note 4). The nut shall have been provided with the lubricant and the statement “ Nuts lubricated” for zinc-coated nuts when
described in the last paragraph of the Manufacturing Processes shipped with zinc-coated bolts,
section of Specification A563. The joint shall be one or more 13.1.4 Zinc coating measured coating weight/thickness for
flat structural steel plates or fixture stack up with a total coated bolts,
Copyright by ASTM Int'l (all rights reserved); Fri Sep 5 12:23:36 EDT 2014
6
Downloaded/printed by
Universidad De Chile pursuant to License Agreement. No further reproductions authorized.
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Please contact ASTM International (www.astm.org) for the latest information.
A325 – 09
13.1.5 Statement of compliance of visual inspection for 15.5 Type and manufacturer’s or private label distributor’s
surface discontinuities (Section 8), identification shall be separate and distinct. The two identifi-
13.1.6 Statement of compliance with dimensional and cations shall preferably be in different locations and, when on
thread fit requirements, the same level, shall be separated by at least two spaces.
13.1.7 Lot number and purchase order number,
13.1.8 Complete mailing address of responsible party, and 16. Packaging and Package Marking
13.1.9 Title and signature of the individual assigned certi- 16.1 Packaging:
fication responsibility by the company officers. 16.1.1 Unless otherwise specified, packaging shall be in
13.2 Failure to include all the required information on the accordance with Practice D3951.
test report shall be cause for rejection. 16.1.2 When zinc coated nuts are included on the same
14. Responsibility order as zinc coated bolts, the bolts and nuts shall be shipped
in the same container.
14.1 The party responsible for the fastener shall be the 16.1.3 When special packaging requirements are required,
organization that supplies the fastener to the purchaser. they shall be defined at the time of the inquiry and order.
15. Product Marking 16.2 Package Marking:
16.2.1 Each shipping unit shall include or be plainly marked
15.1 Manufacturer’s Identification—All Type 1 and 3 bolts
with the following information:
shall be marked by the manufacturer with a unique identifier to
16.2.1.1 ASTM designation and type,
identify the manufacturer or private label distributor, as appro-
16.2.1.2 Size,
priate.
16.2.1.3 Name and brand or trademark of the manufacturer,
15.2 Grade Identification:
15.2.1 Type 1 bolts shall be marked “A325.” 16.2.1.4 Number of pieces,
15.2.2 Type 3 bolts shall be marked “A325” with the 16.2.1.5 Lot number; when nuts, washers or direct tension
“A325” underlined. The use of additional distinguishing marks indicators, or combination thereof, are ordered with A325
to indicate that the bolts are weathering steel shall be at the heavy hex structural bolts, the shipping unit shall be marked
manufacturer’s option. with the lot number in addition to the marking required by the
15.3 Marking Location and Methods—All marking shall be applicable product specification,
located on the top of the bolt head and shall be either raised or 16.2.1.6 Purchase order number, and
depressed at the manufacturer’s option. 16.2.1.7 Country of origin.
15.4 Acceptance Criteria—Bolts which are not marked in
accordance with these provisions shall be considered noncon- 17. Keywords
forming and subject to rejection. 17.1 bolts; carbon steel; steel; structural; weathering steel
SUPPLEMENTARY REQUIREMENTS
The following supplementary requirements shall apply only when specified by the purchaser in the
contract or order. Details of these supplementary requirements shall be agreed upon in writing between
the manufacturer and purchaser. Supplementary requirements shall in no way negate any requirement
of the specification itself.
S1. Bolts Threaded Full Length hand as far as the thread will permit, shall not exceed the length
S1.1 Bolts with nominal lengths equal to or shorter than of 21⁄2 threads for bolt sizes 1 in. and smaller, and 31⁄2 threads
four times the nominal bolt diameter shall be threaded full for bolt sizes larger than 1 in.
length. Bolts need not have a shoulder, and the distance from S1.2 Bolts shall be marked in accordance with Section 15,
the underhead bearing surface to the first complete (full form) except that the symbol shall be “ A325 T” instead of “A325.”
thread, as measured with a GO thread ring gage, assembled by
Copyright by ASTM Int'l (all rights reserved); Fri Sep 5 12:23:36 EDT 2014
7
Downloaded/printed by
Universidad De Chile pursuant to License Agreement. No further reproductions authorized.
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Please contact ASTM International (www.astm.org) for the latest information.
A325 – 09
SUMMARY OF CHANGES
Committee F16 has identified the location of selected changes to this standard since the last issue (A325–07a)
that may impact the use of this standard. (Approved Jan. 1, 2009)
(1) Revised—4.3 to add provision for specifying Zinc/ (2) In 8.1 deleted Note 4 in regard to non injurious bursts.
Aluminum Corrosion Protective Coating conforming to Speci-
fication F1136.
Committee F16 has identified the location of selected changes to this standard since the last issue (A325–07)
that may impact the use of this standard. (Approved Dec. 1, 2007)
Committee F16 has identified the location of selected changes to this standard since the last issue (A325–06)
that may impact the use of this standard. (Approved Sept. 15, 2007.)
ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.
This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website
(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/
COPYRIGHT/).
Copyright by ASTM Int'l (all rights reserved); Fri Sep 5 12:23:36 EDT 2014
8
Downloaded/printed by
Universidad De Chile pursuant to License Agreement. No further reproductions authorized.