    Böhler Fox CM 2 KB: Classifi Cations

    Uploaded by

    Branko Ferenčak
    This document summarizes welding consumables for creep resistant steels, specifically the BÖHLER FOX CM 2 Kb stick electrode. It is a basic coated, core wire alloyed stick electrode for welding 2.25% Cr 1% Mo alloyed steels, with an approved service temperature up to 600°C. The electrode provides reliable creep rupture properties, crack resistance, and ductile deposits with high creep rupture strength and low hydrogen content. It is suitable for welding high temperature steels and similar alloyed cast steels in all positions except vertical down.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Böhler Fox CM 2 KB: Classifi Cations

    Uploaded by

    Branko Ferenčak
    201 views1 page
    This document summarizes welding consumables for creep resistant steels, specifically the BÖHLER FOX CM 2 Kb stick electrode. It is a basic coated, core wire alloyed stick electrode for welding 2.25% Cr 1% Mo alloyed steels, with an approved service temperature up to 600°C. The electrode provides reliable creep rupture properties, crack resistance, and ductile deposits with high creep rupture strength and low hydrogen content. It is suitable for welding high temperature steels and similar alloyed cast steels in all positions except vertical down.

    Original Description:

    CM2

    Original Title

    FOX CM2-Kb

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document summarizes welding consumables for creep resistant steels, specifically the BÖHLER FOX CM 2 Kb stick electrode. It is a basic coated, core wire alloyed stick electrode for welding 2.25% Cr 1% Mo alloyed steels, with an approved service temperature up to 600°C. The electrode provides reliable creep rupture properties, crack resistance, and ductile deposits with high creep rupture strength and low hydrogen content. It is suitable for welding high temperature steels and similar alloyed cast steels in all positions except vertical down.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    201 views1 page

    Böhler Fox CM 2 KB: Classifi Cations

    Uploaded by

    Branko Ferenčak
    This document summarizes welding consumables for creep resistant steels, specifically the BÖHLER FOX CM 2 Kb stick electrode. It is a basic coated, core wire alloyed stick electrode for welding 2.25% Cr 1% Mo alloyed steels, with an approved service temperature up to 600°C. The electrode provides reliable creep rupture properties, crack resistance, and ductile deposits with high creep rupture strength and low hydrogen content. It is suitable for welding high temperature steels and similar alloyed cast steels in all positions except vertical down.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    You are on page 1of 1

    Welding consumables for creep resistant steels

    BÖHLER FOX CM 2 Kb
    SMAW

    Stick electrode, low-alloyed, creep resistant


    Classifications
    EN ISO 3580-A AWS A5.5 / SFA-5.5
    E CrMo2 B 4 2 H5 E9018-B3 H4 R
    Characteristics and typical fields of application
    Basic coated, core wire alloyed stick electrode for welding 2.25% Cr 1% Mo alloyed steels. Approved in long-term condition up to +600°C
    service temperature. Applicable for welds in refineries, boiler construction, and thermal power plants. Core wire alloyed electrode which
    will provide reliable creep rupture properties. Crack resistant and ductile deposit, high creep rupture strength, low hydrogen content (acc.
    AWS condition HD < 4 ml/100 g). Good weldability in all positions except vertical down. Deposit is nitride-able and heat treatable. Metal
    recovery approximately 110%. Suitable for Step Cooling.

    Base materials
    high temperature steels and similar alloyed cast steels, QT-steels similar alloyed up to 980 MPa tensile strength, similar alloyed case
    hardening steels, nitriding steels
    1.7380 10CrMo9-10, 1.7276 10CrMo11, 1.7281 16CrMo9-3, 1.7383 11CrMo9-10, 1.7379 G17CrMo9-10, 1.7382 G19CrMo9-10
    ASTM A 182 Gr. F22; A 213 Gr. T22; A 234 Gr. WP22; 335 Gr. P22; A 336 Gr. F22; A 426 Gr. CP22

    Typical analysis of all-weld metal


    C Si Mn Cr Mo P Sb Sn As
    wt.-% 0.08 0.3 0.7 2.2 1.0 ≤ 0.010 ≤ 0.005 ≤ 0.006 ≤ 0.005
    Mechanical properties of all-weld metal - typical values (min. values)
    Condition Yield strength Rp0.2 Tensile strength Rm Elongation A (L0=5d0) Impact values ISO-V KV J
    MPa MPa % 20°C
    a1 580 (≥ 400) 680 (≥ 500) 19 (≥ 18) 150 (≥ 47)
    a2 530 (≥ 400) 630 (≥ 500) 20 (≥ 18) 180
    v 490 (≥ 400) 600 (≥ 500) 21 180
    a1 annealed, 720 °C/1h / furnace down to 300 °C / air
    a2 annealed, 720 °C/2h / furnace down to 200 °C / air
    v quenched/tempered 930 °C/0.5 h/ air + 680 °C/15 h / air
    Operating data
    Polarity DC+ Dimension mm Current A
    Electrode 2.5 × 250 80 – 110
    FOX CM 2 Kb 9018-B3 E CrMo2 B 3.2 × 350 100 – 140
    identification
    4.0 × 350 130 – 180
    Redrying 300-350°C/2h 4.0 × 450 130 – 180
    5.0 × 450 180 – 230
    Preheating and interpass temperatures 200 – 350ºC. post-weld annealing at 700 – 750ºC at least 1 hour followed by cooling in furnace
    down to 300ºC and still air.

    Approvals
    TÜV (00722), DB (10.014.81), ABS, DNV GL, CE, NAKS (Ø 3,2; Ø 4,0 mm)