CHROMET 92

LOW ALLOY STEELS

MMA ALL-POSITIONAL ELECTRODE FOR JOINING P92 CREEP RESISTING STEEL
PRODUCT DESCRIPTION
Basic coated MMA electrode made on matching core wire. Moisture resistant coatings giving very low weld metal hydrogen
levels.
Recovery is approximately 120% with respect to core wire, 65% with respect to whole electrode.

SPECIFICATIONS
ASME IX QUALIFICATION
AWS A5.5M E9015-B92 H4
QW422 P-No 15E group 1
BS EN ISO 3580-A E ZCrMoWVNb 9 0.5 2 B 3 2 H5 QW432 F-No 4
APPROVALS TÜV QW442 A-No 5

WELDING POSITIONS (ISO/ASME)

PA/1G PB/2F PC/2G PF/3Gu PE/4G

CHEMICAL COMPOSITION (WELD METAL WT %)

C Mn Si S P Cr Ni Mo W Nb V N B Al Cu
min. 0.08 0.40 -- -- -- 8.0 -- 0.30 1.5 0.04 0.15 0.03 0.001 -- --
max. 0.13 1.00 0.40 0.015 0.020 9.5 0.80 0.60 2.0 0.07 0.25 0.07 0.005 0.03 0.15
Typical 0.11 0.6 0.25 0.01 0.01 9 0.6 0.45 1.7 0.05 0.2 0.05 0.003 <0.01 <0.05

ALL-WELD MECHANICAL PROPERTIES

High Temperature
PWHT 760°C / 2-4h min. typical
+550°C +600°C +650°C
Tensile strength (MPa) 620 740 511 422 340
0.2% proof strength (MPa) 530 630 419 320 229
Elongation (%) 4d 17 22 15 19.5 19.5
5d 16 19 14 18 18
Reduction of area % -- 50 64 73 80
Impact ISO-V(J) + 20°C -- 60 -- -- --
Hardness (HV) -- 230-260 -- -- --
OPERATING PARAMETERS, DC +VE OR AC (OCV: 70V MIN)
Diameter (mm) 2.5 3.2 4.0 5.0
min. A 70 80 100 140
max. A 110 140 180 240
PACKAGING DATA
Diameter (mm) 2.5 3.2 4.0 5.0
Length (mm) 300 350 350 450
kg/carton 12 14.1 13.5 16.5
Pieces/carton 762 393 267 150

STORAGE
3 hermetically sealed ring-pull metal tins per carton, with unlimited shelf life. Direct use from tin will give hydrogen <5ml/100g weld
metal during 8h working shift.
For electrodes that have been exposed:
Redry 250 – 300°C/1-2h to ensure H2 < 10ml/100g, 300 – 350°C/1-2h to ensure H2 < 5ml/100g. Maximum 420°C, 3 cycles, 10h total.
Storage of redried electrodes at 100 – 200°C in holding oven, or 50 – 150°C in heated quivers: no limit, but maximum 6 weeks
recommended.

FUME DATA
Fume composition, wt % typical
Fe Mn Ni Cr Cu Pb F OES (mg/m3)
15 5 < 0.1 <3 < 0.1 < 0.1 18 1.7

www.metrode.com DS A-20-CHROMET 92 | Rev. 01-03/16 57

 9CrWV
LOW ALLOY STEELS

SOLID WIRE FOR TIG, MIG AND SAW

PRODUCT DESCRIPTION
Solid wire, non-copper coated, for TIG, MIG and SAW

SPECIFICATIONS ASME IX QUALIFICATION

TIG MIG SAW QW422 P-No 15E group 1
AWS A5.23M -- -- EG (92) QW432 F-No 6
AWS A5.28M ER90S-G (92) ER90S-G (92) -- QW442 A-No 5
BS EN ISO 21952-A W ZCrMoWVNb 9 0.5 1.5 G ZCrMoWVNb 9 0.5 1.5 S ZCrMoWVNb 9 0.5 1.5
APPROVALS TÜV

CHEMICAL COMPOSITION (WIRE WT %)

C Mn Si S P Cr Ni Mo W Nb V N B Al Cu
min. 0.08 0.40 -- -- -- 8.0 -- 0.30 1.5 0.04 0.15 0.03 0.001 -- --
max. 0.13 0.80 0.40 0.015 0.015 9.5 0.80 0.60 2.0 0.07 0.25 0.07 0.005 0.03 0.15
Typical 0.10 0.75 0.30 0.004 0.008 9 0.5 0.45 1.7 0.06 0.2 0.05 0.003 <0.01 <0.05

ALL-WELD MECHANICAL PROPERTIES

High Temperature
PWHT 760°C / 2-4h min. typical
+550°C +600°C +650°C
Tensile strength (MPa) 620 800 455 387 312
0.2% proof strength (MPa) 440 700 374 282 200
Elongation (%) 4d 16 22 24.5 20.5 28
5d -- 19 22.5 19 25.5
Reduction of area % -- 70 82 85 89
Impact ISO-V(J) + 20°C -- 220 -- -- --
Hardness (HV) -- 265 -- -- --

PARAMETERS
Shielding Current Diameter (mm) Typical parameters
TIG Argon DC+ 2.4 100A, 12V
MIG Ar + 1-3%O2 or 5-20% CO2 DC+ 1.2 260A, 26V
SAW LA490 flux DC+ 2.4 420A, 28V, 390mm/min

PACKAGING DATA
Diameter (mm) 0.8/0.9/1.0/1.2 1.6 2.4 3.2
TIG 0.7 / 5 / 15 kg Spools to order 5 kg tube 5 kg tube 5 kg tube
MIG 15kg spool -- -- --
SAW -- -- 25kg spool 25kg spool

FUME DATA
Fume composition (wt %); TIG and SAW fume is negligible:
Fe Mn Ni Cr Mo Cu OES (mg/m3)
50 4 < 0.4 6 0.5 < 0.5 5

58 www.metrode.com DS A-20-9CrWV | Rev. 02-06/16