    Specification: Si MN P S 0.08 0.56 1.02 0.013 0.010

    Uploaded by

    Jennylyn Daño
    N-7018 is an iron powder low hydrogen electrode containing iron powder in the coating flux. It provides high deposition rates and excellent mechanical properties, crack resistance, and X-ray quality. It has good weldability with a smooth arc and is used to weld high tensile strength steels for ships, bridges and pressure vessels. The arc length should be 1/16 inches or less to achieve good properties, and a backstep or short arc start is recommended to prevent blowholes. It has typical mechanical properties of yield strength of 510 MPa, tensile strength of 580 MPa and 30% elongation.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Specification: Si MN P S 0.08 0.56 1.02 0.013 0.010

    Uploaded by

    Jennylyn Daño
    43 views2 pages
    N-7018 is an iron powder low hydrogen electrode containing iron powder in the coating flux. It provides high deposition rates and excellent mechanical properties, crack resistance, and X-ray quality. It has good weldability with a smooth arc and is used to weld high tensile strength steels for ships, bridges and pressure vessels. The arc length should be 1/16 inches or less to achieve good properties, and a backstep or short arc start is recommended to prevent blowholes. It has typical mechanical properties of yield strength of 510 MPa, tensile strength of 580 MPa and 30% elongation.

    Original Title

    N-7018

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    N-7018 is an iron powder low hydrogen electrode containing iron powder in the coating flux. It provides high deposition rates and excellent mechanical properties, crack resistance, and X-ray quality. It has good weldability with a smooth arc and is used to weld high tensile strength steels for ships, bridges and pressure vessels. The arc length should be 1/16 inches or less to achieve good properties, and a backstep or short arc start is recommended to prevent blowholes. It has typical mechanical properties of yield strength of 510 MPa, tensile strength of 580 MPa and 30% elongation.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    43 views2 pages

    Specification: Si MN P S 0.08 0.56 1.02 0.013 0.010

    Uploaded by

    Jennylyn Daño
    N-7018 is an iron powder low hydrogen electrode containing iron powder in the coating flux. It provides high deposition rates and excellent mechanical properties, crack resistance, and X-ray quality. It has good weldability with a smooth arc and is used to weld high tensile strength steels for ships, bridges and pressure vessels. The arc length should be 1/16 inches or less to achieve good properties, and a backstep or short arc start is recommended to prevent blowholes. It has typical mechanical properties of yield strength of 510 MPa, tensile strength of 580 MPa and 30% elongation.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    10/11/2019 N-7018 - Printer Friendly Layout

    N-7018
    Specification
    AWS Specification: AWS A5.1 E7018
    JIS Specification: D5016
    Other Specification: DIN E51 53 B 10

    Description

    N-7018 is an iron powder low hydrogen type electrode containing


    large amounts of iron powder in coating flux to give higher
    deposition rates
    Deposited metal demonstrates excellent mechanical properties,
    crack resistance, and X-ray quality
    Good weldability, such as smooth and stable arc, easy slag
    removal, low spatters, and nice bead appearance

    Application

    Welding of 50 kgf/mm2 high tensile strength steels for ships, steel


    frames, bridges, and pressure vessels

    Remarks

    Require a drag to 1/16 inches maximum arc length to obtain the


    desired mechanical properties and weld quality
    An arc length of 1/8 inch or longer may result in porosity and
    serious deterioration of impact properties
    Take the backstep method or strike the arc on a small steel plate
    prepared for this particular purpose to prevent blowholes at the arc
    starting
    Polarity: Use DC (+) whenever possible with 4.0mm and smaller
    sizes

    Technical Data

    TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL DEPOSITS (%):

    C Si Mn P S
    0.08 0.56 1.02 0.013 0.010

    https://www.nihonweld.com/printerFriendlyLayout.do?itemId=1024247307&mapName=Product 1/2
    10/11/2019 N-7018 - Printer Friendly Layout
    TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSITS:

    Yield Point Tensile Strength Elongation Impact Value


    N/mm2 (KSI) N/mm2 (KSI) % °C, J (°F, Ft-Lbs)

    510 (74) 580 (84) 30 -29°, 145


    (-20°, 107)

    TYPICAL DIFFUSIBLE HYDROGEN OF WELD METAL:

    Diameter Current (amp) Re-drying Diffusible


    (mm) Condition Hydrogen Mean
    Value
    (cc./100g)

    4.0 AC 350ºC x 3.0


    0.5 hrs.

    SIZE AND RECOMMENDED CURRENT RANGE: AC, DC (+)

    DIAMETER (mm) 2.5 3.2 4.0 5.0 6.0


    LENGTH (mm) 350 350 400 450 450

    Current Flat 70 - 100 100 - 150 - 190 - 250 - 320


    Amp 140 200 240
    Vertical & 60 - 90 80 - 120 120 - 140 - -
    Overhead 160 180

    ALL POSITIONS EXCEPT VERTICAL


    Welding Positions: DOWN
    Approvals: ABS, BV, DNV, LRS, NKK

    NOTE:

    The information contained or otherwise referenced herein is presented only as “typical” without
    guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability
    incurred from any reliance thereon. Typical data and test results for mechanical properties,
    deposit, or electrode composition and other properties were obtained from a weld produced and
    tested according to prescribed standards and should not be assumed to be the expected results in
    a particular application or weldment. Actual results will vary depending on many factors, including,
    but not limited to, weld procedure, plate chemistry and temperature, weldment design, and
    fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate
    means, the suitability of any welding consumable and procedure before use in the intended
    application.