Catalogue - Updated - November, 2009 Page 1 of 8

RIVA ACCIAIO
Drawn Square Steel Bars

Drawn Square Steel Bars

Viale Certosa, 249 - 20151 Milano

Tel: +39 02 30 700 - Fax: +39 02 38000 346 - Mail: commerciale.riva@rivagroup.com

Production Units:
Malegno (BS), Italy
 Catalogue - Updated - November, 2009 Page 2 of 8

RIVA ACCIAIO

Drawn Square Steel Bars

Products
STRUCTURAL AND GENERAL USE NON-ALLOY STEEL EN 10025-04
EN 10277-2
EN 10083-2
NON-ALLOY STEEL FOR HIGH SPEED MACHINING UNI 4838
CASE-HARDENING ALLOY STEEL EN 10084/08
EN 10277-4/07
QUENCHED AND TEMPERED SPECIAL CARBON STEEL EN 10083-2/06
EN 10277-5/07
QUENCHED AND TEMPERED SPECIAL ALLOYED STEEL EN 10083-3/06
EN 10277-5/07
MICRO-ALLOYED STEEL ACCORDING TO CUSTOMER SPECIFICATIONS

STANDARD DIMENSIONS
28 - 30 - 30,30 - 31,75 - 32 - 33 - 35 - 36 - 37 - 38 - 38,10 - 40 - 40,30 - 41 - 42 - 43 - 44,45 - 45 - 47 - 48 - 50 - 50,30 - 50,80 - 52 - 54 - 55 - 57 - 57,15
- 57,20 - 58 - 59 - 60 - 63 - 63,50 - 64 - 65 - 69 - 70 - 75 - 76,20 - 78 - 80 - 82,55 - 88 - 88,90 - 90 - 95 - 95,25 - 100 - 101,60 mm

OUT OF STANDARD DIMENSIONS

with 0,5 mm progression in the range 30÷100 mm

BAR LENGTH
3÷7m
standard 3 ÷ 4 and 6 ÷ 7 m

SIZE TOLERANCE
SIDE - h11 - h10 - k11 - k10 - a108 (according to ASTM)
- commercial up to 1 m
LENGTH - fixed standard  50 mm
- fixed out of standard  20 mm

BRIGHT LONG PRODUCTS SIZE TOLLERANCES

Nominal Class of Tolerances EN 20286-2
Dimension
(mm) h6 g6 h7 k7 h8 k8 h9 k9 h10 k10 h11 k11 h12 h13
+0 -0,005 +0 +0,016 +0 +0,022 +0 +0,036 +0 +0,058 +0 +0,090 +0 +0
> 6÷10
-0,009 -0,014 -0,015 +0,001 -0,022 -0 -0,036 -0 -0,058 -0 -0,090 -0 -0,150 -0,220
+0 -0,006 +0 +0,019 +0 +0,027 +0 +0,043 +0 +0,070 +0 +0,110 +0 +0
> 10÷18
-0,011 -0,017 -0,018 +0,001 -0,027 -0 -0,043 -0 -0,070 -0 -0,110 -0 -0,180 -0,270
+0 -0,007 +0 +0,023 +0 +0,033 +0 +0,052 +0 +0,084 +0 +0,130 +0 +0
> 18÷30
-0,013 -0,020 -0,021 +0,002 -0,033 -0 -0,052 -0 -0,084 -0 -0,130 -0 -0,210 -0,330
+0 -0,009 +0 +0,027 +0 +0,039 +0 +0,062 +0 +0,100 +0 +0,160 +0 +0
> 30÷50
-0,016 -0,025 -0,025 +0,002 -0,039 -0 -0,062 -0 -0,100 -0 -0,160 -0 -0,250 -0,390
+0 -0,010 +0 +0,032 +0 +0,046 +0 +0,074 +0 +0,120 +0 +0,190 +0 +0
> 50÷80
-0,019 -0,029 -0,030 +0,002 -0,046 -0 -0,074 -0 -0,120 -0 -0,190 -0 -0,300 -0,460
+0 -0,012 +0 +0,038 +0 +0,054 +0 +0,087 +0 +0,140 +0 +0,220 +0 +0
>80÷120
-0,022 -0,034 -0,035 +0,003 -0,054 -0 -0,087 -0 -0,140 -0 -0,220 -0 -0,350 -0,540
 Catalogue - Updated - November, 2009 Page 3 of 8

RIVA ACCIAIO

Drawn Square Steel Bars

STRAIGHTNESS
STANDARD:
- wave  1,5‰ L for C content  0,25% and  1,0‰ for C content < 0,25%

TWIST
-  4° /m

SURFACE FINISH
- Ra  3,2 µm

ENDS APPEARANCE
- cold saw cutting for > 60 mm
- cold shearing for  60 mm

SURFACE APPEARANCE
DEFECTS DEPTH:
-  0,01 , equivalent to: class 3 EN 10277-1 standard and class 1 UNI 10233-1 standard.
 Catalogue - Updated - November, 2009 Page 4 of 8

RIVA ACCIAIO

Drawn Square Steel Bars

STRUCTURAL AND GENERAL USE NON-ALLOY STEEL

EN 10025-04 (S235JR, E295GC, E335GC, S355J2G3C)
EN 10277-2 (C10, C15, C16)
EN 10083-2 (C35, C40, C45, C50, C60)

DESCRIPTION AND APPLICATIONS

Base and non-alloy steel quality suitable for construction of structural elements, as welded, bolted, riveted structures for room temperature applications.
Non-alloy quality steel, for heat treating, suitable for mechanical applications.

HEAT CHEMICAL COMPOSITION

Si % P% S% N% Cr % Mo % Ni % Cr+Mo+Ni %
Quality N° C% Mn %
Max Max Max Max Max Max Max Max
S235JRC 1.0122  0,17  1,40 - 0,040 0,040 0,012 - - - -
E295GC 1.0533 - - - 0,045 0,045 0,012 - - - -
E335GC 1.0543 - - - 0,045 0,045 0,012 - - - -
S355J2C 1.0579  0,20  1,60 0,55 0,030 0,030 - - - - -
C10 1.0301 0,07 ÷ 0,13 0,30 ÷ 0,60 0,40 0,045 0,045 - - - - -
C15 1.0401 0,12 ÷0,18 0,30 ÷ 0,80 0,40 0,045 0,045 - - - - -
C16 1.0407 0,12 ÷ 0,18 0,60 ÷ 0,90 0,40 0,045 0,045 - - - - -
C35 1.0501 0,32 ÷ 0,39 0,50 ÷ 0,80 0,40 0,045 0,045 - 0,40 0,10 0,40 0,63
C40 1.0511 0,37 ÷ 0,44 0,50 ÷ 0,80 0,40 0,045 0,045 - 0,40 0,10 0,40 0,63
C45 1.0503 0,42 ÷ 0,50 0,50 ÷ 0,80 0,40 0,045 0,045 - 0,40 0,10 0,40 0,63
C55 1.0535 0,52 ÷ 0,60 0,60 ÷ 0,90 0,40 0,045 0,045 - 0,40 0,10 0,40 0,63
C60 1.0601 0,57 ÷ 0,65 0,60 ÷ 0,90 0,40 0,045 0,045 - 0,40 0,10 0,40 0,63

MECHANICAL PROPERTIES ON DRAWN PRODUCTS (+C)

Rp0,2 (N/mm2) Min Rm (mm2) *
A5 %
Min
Nominal Thickness (mm) Nominal Thickness (mm)
Quality
>5 >10 >16 >40 >63 >5 >10 >16 >40 >63 >5 > 10 > 16 > 40 > 63
10 16 40 63 100 10 16  40 63 100 100  16  40  63  100
S235JRC 355 300 260 235 215 470÷840 420÷770 390÷730 380÷670 360÷640 8 9 10 11 11
E295GC 510 420 320 300 255 650÷950 600÷900 550÷850 520÷770 470÷740 6 7 8 9 9
E335GC 540 480 390 340 295 700÷1050 680÷970 640÷930 620÷870 570÷810 5 6 7 8 8
S355J2C 520 450 350 335 315 630÷950 580÷880 530÷850 500÷770 470÷740 6 7 8 9 9
C10 350 300 250 200 180 460÷760 430÷730 400÷700 350÷640 320÷580 8 9 10 12 12
C15 380 340 280 240 215 500÷800 480÷780 430÷730 380÷670 340÷600 7 8 9 11 12
C16 400 360 300 260 235 520÷820 500÷800 450÷750 400÷690 360÷620 7 8 9 11 12
C35 510 420 320 300 270 650÷1000 600÷950 580÷880 550÷840 520÷800 6 7 8 9 9
C40 540 460 365 330 290 700÷1000 650÷980 620÷920 590÷840 550÷820 6 7 8 9 9
C45 565 500 410 360 310 750÷1050 710÷1030 650÷1000 630÷900 580÷850 5 6 7 8 8
C55 590 520 440 390 - 770÷1100 730÷1080 690÷1050 650÷1030 - 5 6 7 8 -
C60 630 550 480 - - 800÷1150 780÷1130 735÷1100 - - 5 5 6 - -

NOTE: The mechanical properties of the table satisfy the prescriptions of DIN 1652-2-3-4 and UNI 10233-3 standards too.
 Catalogue - Updated - November, 2009 Page 5 of 8

RIVA ACCIAIO

Drawn Square Steel Bars

NON-ALLOY STEEL FOR HIGH SPEED MACHINING

UNI 4838

HEAT CHEMICAL COMPOSITION

Quality C% Mn % Si % Max P % Max S%
CF35SMn10 0,32 ÷ 0,39 1,35 ÷ 1,65 0,30 0,040 0,080 ÷ 0,130

MECHANICAL PROPERTIES (ON DRAWN PRODUCT)

Thickness Rm Rp0,2 Min A5 Min
Quality
mm N/mm2 N/mm2 %
CF35SMn10 > 5  10  700 550 6
CF35SMn10 > 10  16 680 ÷ 930 530 6
CF35SMn10 > 16  25 660 ÷ 910 510 7
CF35SMn10 > 25  40 640 ÷ 890 490 8
CF35SMn10 > 40  870 - 9

NOTE: The mechanical properties of the table satisfy the prescription of UNI 10233-4 standard.
 Catalogue - Updated - November, 2009 Page 6 of 8

RIVA ACCIAIO

Drawn Square Steel Bars

CASE-HARDENING ALLOY STEEL

EN 10084/08
EN 10277-4/07

HEAT CHEMICAL COMPOSITION

Si % P%
Quality N° C% Mn % S% Cr % Ni % Mo %
Max Max
16MnCrS5 1.7139 0,14 ÷ 0,19 1,00 ÷ 1,30 0,40 0,025 0,020 ÷ 0,040 0,80 ÷ 1,10 - -
20MnCrS5 1.7149 0,17 ÷ 0,22 1,10 ÷ 1,40 0,40 0,025 0,020 ÷ 0,040 1,00 ÷ 1,30 - -
16NiCrS4 1.5715 0,13 ÷ 0,19 0,70 ÷ 1,00 0,40 0,025 0,020 ÷ 0,040 0,60 ÷ 1,00 0,80 ÷ 1,10 -
20NiCrMoS2.2 1.6526 0,17 ÷ 0,23 0,65 ÷ 0,95 0,40 0,025 0,020 ÷ 0,040 0,35 ÷ 0,70 0,40 ÷ 0,70 0,15 ÷ 0,25

MECHANICAL PROPERTIES
Brinell Hardness on Annealed and Drawn Product (+A+C)

Quality Nominal Thickness (mm)

> 5  10 > 10  16 > 16  40 > 40  63 > 63  100

16MnCrS5 260 250 245 240 240
20MnCrS5 270 260 255 250 250
16NiCrS4 270 260 255 255 255
20NiCrMoS2.2 270 260 255 255 255

NOTE: The hardnesses of the table satisfy the prescriptions of UNI 10233-5 and DIN 1652-3 standards too (qualities 16MnCrS5, 20MnCrS5 and
20NiCrMoS2.2).
 Catalogue - Updated - November, 2009 Page 7 of 8

RIVA ACCIAIO

Drawn Square Steel Bars

QUENCHED AND TEMPERED SPECIAL CARBON STEEL

EN 10083-2/06
EN 10277-5/07

HEAT CHEMICAL COMPOSITION

Si % P% Cr+Mo+Ni
Quality N° C% Mn % S% Cr % Mo % Ni %
Max Max %
C35E 1.1181 0,32 ÷ 0,39 0,50 ÷ 0,80 0,40 0,030  0,035  0,40  0,10  0,40  0,63
C35R 1.1180 0,32 ÷ 0,39 0,50 ÷ 0,80 0,40 0,030 0,020 ÷ 0,040  0,40  0,10  0,40  0,63
C40E 1.1186 0,37 ÷ 0,44 0,50 ÷ 0,80 0,40 0,030  0,035  0,40  0,10  0,40  0,63
C40R 1.1189 0,37 ÷ 0,44 0,50 ÷ 0,80 0,40 0,030 0,020 ÷ 0,040  0,40  0,10  0,40  0,63
C45E 1.1191 0,42 ÷ 0,50 0,50 ÷ 0,80 0,40 0,030  0,035  0,40  0,10  0,40  0,63
C45R 1.1201 0,42 ÷ 0,50 0,50 ÷ 0,80 0,40 0,030 0,020 ÷ 0,040  0,40  0,10  0,40  0,63
C50E 1.1206 0,47 ÷ 0,55 0,60 ÷ 0,90 0,40 0,030  0,035  0,40  0,10  0,40  0,63
C50R 1.1241 0,47 ÷ 0,55 0,60 ÷ 0,90 0,40 0,030 0,020 ÷ 0,040  0,40  0,10  0,40  0,63
C60E 1.1221 0,57 ÷ 0,65 0,60 ÷ 0,90 0,40 0,030  0,035  0,40  0,10  0,40  0,63
C60R 1.1223 0,57 ÷ 0,65 0,60 ÷ 0,90 0,40 0,030 0,020 ÷ 0,040  0,40  0,10  0,40  0,63

MECHANICAL PROPERTIES ON THE DRAWN PRODUCT (+C)

Rp0,5(N/mm2) Min Rm (N/mm2) *
A5 % Min
Nominal Thickness (mm) Nominal Thickness (mm)
Quality
>5 >10 >16 >40 >63 >5 >10 >16 >40 >63 >5 >10 >16 >40 >63
10 16 40 63 100 10 16 40 63 100 10 16 40 63 100
C35E
510 420 320 300 270 650÷1000 600÷950 580÷880 550÷840 520÷800 6 7 8 9 9
C35R
C40E
540 460 365 330 290 700÷1000 650÷980 620÷920 590÷840 550÷820 6 7 8 9 9
C40R
C45E
565 500 410 360 310 750÷1050 710÷1030 650÷1000 630÷900 580÷850 5 6 7 8 8
C45R
C50E
390 520 440 390 - 770÷1100 730÷1080 690÷1050 650÷1030 - 5 6 7 8 -
C50R
C60E
630 550 480 - - 800÷1150 780÷1130 730÷1100 - - 5 5 6 - -
C60R

NOTE: The mechanical properties of the table satisfy the prescriptions of DIN 1652-4 and UNI 10233-3 standards too.
 Catalogue - Updated - November, 2009 Page 8 of 8

RIVA ACCIAIO

Drawn Square Steel Bars

QUENCHED AND TEMPERED SPECIAL ALLOYED STEEL

EN 10083-3/06
EN 10277-5/07

HEAT CHEMICAL COMPOSITION

Quality N° C% Mn % Si % Max P % Max S% Cr % Mo % V%
34CrS4 1.7037 0,30 ÷ 0,37 0,60 ÷ 0,90 0,40 0,025 0,020 ÷ 0,040 0,90 ÷ 1,20 - -
41CrS4 1.7039 0,38 ÷ 0,45 0,60 ÷ 0,90 0,40 0,025 0,020 ÷ 0,040 0,90 ÷ 1,20 - -
25CrMoS4 1.7213 0,22 ÷ 0,29 0,60 ÷ 0,90 0,40 0,025 0,020 ÷ 0,040 0,90 ÷ 1,20 0,15 ÷ 0,30 -
42CrMoS4 1.7227 0,38 ÷ 0,45 0,60 ÷ 0,90 0,40 0,025 0,020 ÷ 0,040 0,90 ÷ 1,20 0,15 ÷ 0,30 -
51CrV4 1.8159 0,47 ÷ 0,55 0,70 ÷ 1,10 0,40 0,025  0,035 0,90 ÷ 1,20 - 0,10 ÷ 0,25

MECHANICAL PROPERTIES
Brinell Hardness HB Max on Annealed and Drawn (+A+C)

Quality Nominal Thickness (mm)

> 5  10 > 10  16 > 16  40 > 40  63 > 63  100

34CrS4 284 275 270 265 265
41CrS4 295 285 280 270 270
25CrMoS4 270 260 255 250 250
42CrMoS4 300 290 285 280 280
51CrV4 308 298 293 288 288

IMPORTANT: Hardnesses of the table satisfy DIN 1652-4 and UNI 10233-5 standards too.