    MFE 711 is a non-accelerated vinyl ester resin designed for ease of fabrication using hand lay-up, spray-up, filament winding, and other techniques. It exhibits good general properties, corrosion resistance, and higher elongation for increased toughness of fiber reinforced plastics (FRP). Applications include FRP storage tanks, vessels, and on-site maintenance projects in chemical processing and pulp/paper operations. The resin complies with FDA food contact regulations when properly cured. It has a typical gel time of 10-20 minutes and physical properties including tensile strength of 85-90 MPa and heat distortion temperature of 100-106°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    TDS Mfe 711 (New)

    Uploaded by

    Wahyudi Rendiana Nyoto
    152 views2 pages
    MFE 711 is a non-accelerated vinyl ester resin designed for ease of fabrication using hand lay-up, spray-up, filament winding, and other techniques. It exhibits good general properties, corrosion resistance, and higher elongation for increased toughness of fiber reinforced plastics (FRP). Applications include FRP storage tanks, vessels, and on-site maintenance projects in chemical processing and pulp/paper operations. The resin complies with FDA food contact regulations when properly cured. It has a typical gel time of 10-20 minutes and physical properties including tensile strength of 85-90 MPa and heat distortion temperature of 100-106°C.

    Original Title

    TDS MFE 711 (NEW)

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    MFE 711 is a non-accelerated vinyl ester resin designed for ease of fabrication using hand lay-up, spray-up, filament winding, and other techniques. It exhibits good general properties, corrosion resistance, and higher elongation for increased toughness of fiber reinforced plastics (FRP). Applications include FRP storage tanks, vessels, and on-site maintenance projects in chemical processing and pulp/paper operations. The resin complies with FDA food contact regulations when properly cured. It has a typical gel time of 10-20 minutes and physical properties including tensile strength of 85-90 MPa and heat distortion temperature of 100-106°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    152 views2 pages

    TDS Mfe 711 (New)

    Uploaded by

    Wahyudi Rendiana Nyoto
    MFE 711 is a non-accelerated vinyl ester resin designed for ease of fabrication using hand lay-up, spray-up, filament winding, and other techniques. It exhibits good general properties, corrosion resistance, and higher elongation for increased toughness of fiber reinforced plastics (FRP). Applications include FRP storage tanks, vessels, and on-site maintenance projects in chemical processing and pulp/paper operations. The resin complies with FDA food contact regulations when properly cured. It has a typical gel time of 10-20 minutes and physical properties including tensile strength of 85-90 MPa and heat distortion temperature of 100-106°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    You are on page 1of 2

    Polymal

    LUXCHEM
    Vinyl Ester Resins

    Technical Information

    MFE 711
    DESCRIPTION
    MFE 711 is non accelerated vinyl ester based on bisphenol-A epoxy resin designed for ease of hand-lay
    up, spray-up and other similar processes.

    BENFITS & PROPERTIES


    • MFE 711 has good general properties, reliable molding craft and mechanical behavior and exhibits
    excellent corrosion resistance.
    • Better resistance against acid, alkali and solvent.
    • Higher elongation provides FRP with equipment with increased toughness.

    APPLICATION& FABRICATION TECHNIQUES


    • FRP storage tanks, vessels, ducts, and on-site maintenance projects, particularly in chemical
    processing and pulp and paper operations.
    • The resin is designed for ease of fabrication using hand lay-up, spray-up, filament winding,
    compression molding and resin transfer molding techniques, pultrusion and molded grating
    applications.
    • When properly formulated and cured, complies with FDA regulation 21 CFR 177.2420, covering
    materials intended for repeated use in contact with food.

    SPECIFICATION
    Typical Properties Of Liquid MFE 711 :
    Appearance : Light yellow Note
    *1) *1)
    Viscosity , mPa.s : 400 ~ 600 Brookefield:LVT,#3,60rpm@25oC
    Acid Value (mgKOH/g) : 7.0 ~ 13.0 *2) ISO 2535
    Volatile Content(%) : 42 ~ 48 ( + 0.10% 10% CO, Butanox M-50 : 1.5%
    Curing Properties*2) : Temp : 250C )
    Gel Time, min : 10 ~ 20
    Polymal
    LUXCHEM
    Vinyl Ester Resins

    TYPICAL PHYSICAL PROPERTIES OF CURED CASTING:


    Properties Unit Result Remark
    Tensile Strength MPa 85 - 90
    Tensile Modulus GPa 3.2 – 3.7 ASTM D-638
    Elongation at break % 5.0 - 6.0
    Flexural Strength MPa 120 - 150 ASTM D-790
    Flexural Modulus GPa 3.3 – 3.8
    0 ASTM D-648
    Heat Distortion Temp C 100 - 106
    Method A
    Barcol Hardness 35 - 38
    Cure schedule: 24 hours at room temp; 2 hours at 1200C

    RECOMMENDED STORAGE
    Typical storage life at temperature below 250C is 3 months. To ensure maximum stability and maintain
    optimum resin properties, avoid exposure to heat sources such as direct sunlight and steam pipes. The resin
    should be stored in closed container below 250C and properly sealed to avoid moisture pick-up and
    monomer loss.

    Disclaimer :
    The information contained in this data sheet is based on laboratory data and field experience which are
    believed to be accurate and reliable to the best of our knowledge. We do not guarantee its applicability to
    the user’s process or assume any liability for occurrences arising out of its use. Our recommendations
    should not be taken as inducements to infringe any patent or violate any law, safety code or insurance
    regulations.”

    You might also like