FEDERAL SUPPLY CLASS

REV.
3120

B NOTICE

THE REQUIREMENTS FOR ACQUIRING THE PRODUCT(S) DESCRIBED HEREIN SHALL CONSIST OF THIS
AEROSPACE STANDARD SHEET AND THE ISSUE OF THE FOLLOWING STANDARD LISTED IN THE DODISS
SPECIFIED IN THE PROCUREMENT DOCUMENT: SAE AS81820.
AS14101

THIS DOCUMENT INCLUDES CADMIUM AS A PLATING MATERIAL. THE USE OF CADMIUM HAS BEEN
RESTRICTED AND/OR BANNED FOR USE IN MANY COUNTRIES DUE TO ENVIRONMENTAL AND HEALTH
CONCERNS. THE USER SHOULD CONSULT WITH LOCAL OFFICIALS ON APPLICABLE HEALTH AND
ENVIRONMENTAL REGULATIONS REGARDING ITS USE.

FIGURE 1

TABLE 1 - DIMENSIONS AND STRENGTHS

NO-LOAD
ROTATIONAL
STATIC LIMIT OSCIL- BREAKAWAY TORQUE WT
φB φD** P W φE LOAD LATING IN-LB LB
PART +.0000 +.0000 H** φM +.000 Q* +.000 +.000 RADIAL AXIAL LOAD * MAX
NO. −.0005 −.0005 ±.005 MIN −.010 (REF) −.002 −.008 LB LB LB STANDARD "K" TYPE (REF)
MS14101- 3 .1900 .5625 .218 .293 .025 10 .281 .500 3975 150 1500 0.25- 5.0 0-0.5 .020
MS14101- 4 .2500 .6562 .250 .364 .025 10 .343 .594 6040 430 3320 0.25- 5.0 0-0.5 .020
MS14101- 5 .3125 .7500 .281 .419 .035 10 .375 .650 8750 700 5460 0.25- 8.0 0-1.0 .030

REVISED 2004-11
MS14101-5A .3125 .7500 .281 .419 .035 10 .375 .660 8750 700 5460 0.25- 8.0 0-1.0 .030
MS14101- 6 .3750 .8125 .312 .475 .035 9 .406 .712 10540 1100 6600 0.25- 8.0 0-1.0 .040
MS14101- 7 .4375 .9062 .343 .530 .035 8 .437 .806 13200 1400 8050 0.25- 8.0 0-1.0 .050
MS14101- 8 .5000 1.0000 .390 .600 .055 8 .500 .876 17900 2100 10400 0.25- 8.0 0-1.0 .070
MS14101- 9 .5625 1.0937 .437 .670 .055 8 .562 .970 23200 3680 13000 0.25- 8.0 0-1.0 .090
MS14101-10 .6250 1.1875 .500 .739 .055 8 .625 1.063 30500 4720 16450 0.25- 8.0 0-1.0 .120
MS14101-12 .7500 1.4375 .593 .920 .055 8 .750 1.313 46400 6750 23600 0.25- 8.0 0-1.0 .210
MS14101-14 .8750 1.5625 .703 .980 .055 8 .875 1.438 62200 9350 30250 0.25-12.0 0-2.0 .270
MS14101-16 1.0000 1.7500 .797 1.118 .055 9 1.000 1.626 82200 12160 38000 0.25-12.0 0-2.0 .390

* SEE REQUIREMENT 5 "NO-LOAD TORQUE" AND NOTE 8.

ISSUED 1998-07

**SEE NOTE 7.

MS14101-5 INACTIVE FOR NEW DESIGN

THIRD ANGLE PROJECTION

CUSTODIAN: SAE AIRFRAME CONTROL BEARINGS GROUP

AEROSPACE STANDARD REV.

BEARING, PLAIN, SELF-LUBRICATING,
AS14101
SELF-ALIGNING, LOW SPEED, NARROW, SHEET 1 OF 3 B
GROOVED RACE, -65 TO 325 °F
Copyright © 2004 SAE International
All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying,
recording, or otherwise, without the prior written permission of SAE.
TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: 724-776-4970 (outside USA)
Fax: 724-776-0790 Email: custsvc@sae.org SAE WEB ADDRESS: http://www.sae.org
REV.
B TABLE 2 - OVERSIZE BEARING DIMENSIONS 1/ 2/
RESTRICTED USAGE FOR REPAIR WORK ONLY
.010 AND .020 OVERSIZE OUTSIDE DIAMETER FOR
REPLACEMENT OF BEARINGS SHOWN ON SHEET 1
AS14101

1ST 2ND
PART NOMINAL OVERSIZE PART NOMINAL OVERSIZE
NO. SIZE (.010) φD NO. SIZE (.020) φD
MS14101- 3T .1875 .5725 MS14101- 3U .1875 .5825
MS14101- 4T .2500 .6662 MS14101- 4U .2500 .6762
MS14101- 5(A)T .3125 .7600 MS14101- 5(A)U .3125 .7700
MS14101- 6T .3750 .8225 MS14101- 6U .3750 .8325
MS14101- 7T .4375 .9162 MS14101- 7U .4375 .9262
MS14101- 8T .5000 1.0100 MS14101- 8U .5000 1.0200
MS14101- 9T .5625 1.1037 MS14101- 9U .5625 1.1137
MS14101-10T .6250 1.1975 MS14101-10U .6250 1.2075
MS14101-12T .7500 1.4475 MS14101-12U .7500 1.4575
MS14101-14T .8750 1.5725 MS14101-14U .8750 1.5825
MS14101-16T 1.0000 1.7600 MS14101-16U 1.0000 1.7700

1/ BEFORE INITIATING A REPAIR PROCEDURE TO USE AN OVERSIZE BEARING,

APPROVAL FOR MODIFYING AND REIDENTIFYING THE BEARING HOUSING MUST
BE OBTAINED FROM THE COGNIZANT ENGINEERING AUTHORITY.
2/ REFER TO NAS0331 FOR INSTALLATION PROCEDURE AND STAKING FORCES.

REQUIREMENTS:

1. MATERIAL: BALL, 440C (AMS 5630, AMS 5880, OR AMS 5618) OR PH13-8Mo AMS 5629 H1000 (SEE NOTE 8a).
RACE, AMS 5643 (17-4PH).
LINER, PTFE SHALL BE INCLUDED IN THE LINER.

2. SURFACE TEXTURE: BALL DIA Ra 8 MAX; BALL FACES, BALL BORE AND RACE DIA Ra 32 MAX; ALL OTHER
METALLIC SURFACES Ra 125 MAX. LINER SURFACES ARE EXEMPT FROM SURFACE TEXTURE
MEASUREMENTS.

3. HARDNESS: BALL, 440C Rc 55-62 OR PH13-8Mo Rc 43 MIN; RACE; Rc 28 MIN/Rc 37 MAX BEFORE SWAGING.

4. SURFACE FINISH:

RACE: PLATING, WHEN SPECIFIED, SHALL BE ZINC-NICKEL PLATING PER AMS 2417, TYPE 2, OR CADMIUM
PLATING PER AMS-QQ-P-416, TYPE II, CLASS 2, WITH A THICKNESS RANGE OF 0.0003 TO 0.0006
INCHES. PLATE ON THE OUTSIDE DIAMETER SURFACE AND ON THE FLAT BETWEEN THE OUTSIDE
DIAMETER AND THE GROOVE. PLATING RUNOUT MAY OCCUR EITHER IN THE GROOVE OR IN THE
AREA BETWEEN THE GROOVE AND THE BALL.

BALL: PH13-8Mo, PASSIVATE PER AMS-QQ-P-35 OR ASTM A 967; 440C, PASSIVATE PER AMS-QQ-P-35 OR
ASTM A 967, OPTIONAL.

5. NO-LOAD TORQUE: WHEN THE LETTER “K” IS PRESENT IN THE PART NUMBER, LOWER VALUES OF
NO-LOAD TORQUE ARE SPECIFIED PER TABLE 1. IF THE MEASURED TORQUE OF A “K” TYPE BEARING IS
LESS THAN 0.1 INCH-POUND, THE INTERNAL RADIAL PLAY SHALL BE MEASURED AND SHALL NOT EXCEED
THE FOLLOWING:

DASH NO. MAXIMUM RADIAL PLAY MAXIMUM AXIAL PLAY

-3K THRU -12K 0.0007 INCH 0.0028 INCH
-14K THRU -16K 0.0010 INCH 0.0040 INCH

THE INTERNAL AXIAL PLAY SHALL BE MEASURED FOR ALL "K" TYPE BEARINGS.

AEROSPACE STANDARD REV.

BEARING, PLAIN, SELF-LUBRICATING,
AS14101
SELF-ALIGNING, LOW SPEED, NARROW, SHEET 2 OF 3 B
GROOVED RACE, -65 TO 325 °F
REV.
B NOTES:

1. DIMENSIONS ARE IN INCHES. UNLESS OTHERWISE SPECIFIED, TOLERANCES ARE; DECIMALS ±.010 AND
ANGLES ±0.5°.
AS14101

2. BREAK SHARP EDGES AND CORNERS AND REMOVE ALL BURRS AND SLIVERS.

3. THE -3 SIZE BEARING IS EXEMPT FROM THE "RADIAL STATIC LIMIT LOAD" TEST BECAUSE THE LOAD
CAPACITY OF THE BEARING IS PIN CRITICAL.

4. WHEN TESTED TO THE FLUID CONTAMINATION AND SUB-ZERO TEMPERATURE REQUIREMENTS OF THE
PROCUREMENT SPECIFICATION, THE OSCILLATING LOAD SHALL BE DECREASED TO 75% OF THE SPECIFIED
LOAD.

5. WHEN FLUIDS AND ELEVATED TEMPERATURES (ABOVE 200 °F) ARE BOTH PRESENT IN AN APPLICATION,
THEN REDUCTIONS IN OPERATING LOADS OR BEARING LIFE MAY BE REQUIRED.

6. DASH NUMBER DESIGNATES NOMINAL BORE DIA IN SIXTEENTHS OF AN INCH.

7. DIMENSION “øD” TO BE MET AFTER PLATING. DIMENSION "H" TO BE MET BEFORE PLATING WHEN
APPLICABLE.

8. EXAMPLE OF PART NO.

8a. BALL MATERIAL SHALL BE 440C (AMS 5630, AMS 5880, OR AMS 5618) UNLESS "C" CALLOUT IS PRESENT IN
PART NUMBER. "C" INDICATES PH13-8Mo AMS 5629 H1000.

9. IN THE EVENT OF A CONFLICT BETWEEN THE TEXT OF THIS STANDARD AND THE REFERENCES CITED
HEREIN, THE TEXT OF THIS STANDARD SHALL TAKE PRECEDENCE.

10. REFERENCED GOVERNMENT (OR NON-GOVERNMENT) DOCUMENTS OF THE ISSUE LISTED IN THAT ISSUE
OF THE DEPARTMENT OF DEFENSE INDEX OF SPECIFICATIONS AND STANDARDS DODISS SPECIFIED IN THE
SOLICITATION FORM A PART OF THIS STANDARD TO THE EXTENT SPECIFIED HEREIN.

11. THE CHANGE BAR ( l ) LOCATED IN THE LEFT MARGIN IS FOR THE CONVENIENCE OF THE USER IN
LOCATING AREAS WHERE TECHNICAL REVISIONS, NOT EDITORIAL CHANGES, HAVE BEEN MADE TO THE
PREVIOUS ISSUE OF THIS DOCUMENT. AN (R) SYMBOL TO THE LEFT OF THE DOCUMENT TITLE INDICATES
A COMPLETE REVISION OF THE DOCUMENT.

AEROSPACE STANDARD REV.

BEARING, PLAIN, SELF-LUBRICATING,
AS14101
SELF-ALIGNING, LOW SPEED, NARROW, SHEET 3 OF 3 B
GROOVED RACE, -65 TO 325 °F