Lecture 15
Lecture 15
Lecture 15
Cast Iron
Knowledge &
Knowledge about different Cast Irons
Understanding
Skills & Abilities Ability to know the character and potential use of Cast Irons
Values &
Aware of the importance and limitation of use of Cast Irons
Attitudes
Resources
1. S H Avner (1974), “Introduction to physical metallurgy,” Tata McGraw-Hill, Ch-09.
2. R A Higgins (1977), “Materials for the engineering technicians,” Arnold, Ch-13.
Outline of this lecture
Cast Iron
Classification of Cast Iron
Introduction
Cast iron is mainly an alloy of Fe and C with addition of Si.
High C brittleness
However, they melt readily and can be cast into complicated shapes .
Casting is the only suitable process applied to these alloys, they are known
as cast irons.
4
Introduction
Cast irons are the largest tonnage of cast-to-shape products of foundry
industry in the world
5
Uses of Cast Irons
6
Forms of Carbon in Fe-C alloys
C can be said to be in a combined form such as intermetallic iron carbide
compound
Carbon can also be present in either graphitic form (pure C, hexagonal
structure)
7
Solidification process 1. liquid to austenite (A) dendrites
transformation begins
L E (A + G) grey/nodular iron
L E (A + C) white iron
A + G grey/nodular iron
A + C white iron
•between 3 and 4, ppt. of carbon (as G or C)
from austenite takes place
9
Chemical Composition of Cast Irons
Influence of chemical composition on properties and uses of cast irons is
largely related to the two alloying elements, carbon and silicon, and their
influence on the process of graphitization.
Fe3C = Fe + 3C
Presence of C, especially above 2.0%, increases the graphitization process
Presence of Si causes cementite to become less stable (thus promotes
graphite formation)
Other elements helping graphitization process (graphite stabilizers): Cu, Ni
Elements inhibiting graphitizing process (carbide stabilizers): Mn, S, P, Cr, V,
Mo
Elements having dual effects: Al, Ti (actual effect depends upon composition)
Elements other than C and Si (e.g., Mn, Cu, Ni, Cr, Mo) added mainly to
control the matrix microstructure; have small effects on solidification
microstructures
Chemical Composition of Cast Irons
Composition of cast irons are described
in terms of both carbon and silicon
percentages.
Thus the term carbon equivalent, CE,
has been adopted.
CE = %C + %Si/3
CE > 4.3% hypereutectic alloy
(ductile irons)
CE < 4.3% hypoeutectic alloy (grey,
white, malleable irons)
11
Role of Si and Other Alloyants
12
Role of Si and Other Alloyants
13
Role of Si and Other Alloyants
Manganese (Mn)
In presence of Mn, MnS or complex manganese-iron-sulphides forms
are, usually randomly distributed.
Mn above that necessary to react with the sulphur will help in retaining
the pearlitic microstructure.
In view of attaining desired microstructure, the sulphur-manganese
relationship is expressed as below:
a) % S x 1.7 = % Mn; Chemically equivalent S and Mn percentage to form
MnS considering no effect from iron.
b) % S x 1.7 + 0.15 = Mn; the Mn percentage which will promote a
maximum of ferrite and a minimum of pearlite.
c) % S x 3 + 0.35 = Mn; the manganese percentage which will develop a
pearlitic microstructure.
14
Role of Si and Other Alloyants
Phosphorus (P)
15
Cast iron microstructures
Type of cast iron (white / nodular / grey) is largely established during the freezing
process.
The room-temperature microstructure reflects the entire freezing and cooling of the
iron.
16
White cast iron
All of its carbon is present in a chemically combined form as
cementite(iron carbide).
White iron presents a white crystalline surface when fractured.
17
Malleable Cast Iron
Carbon is present as irregular nodular-shaped aggregates of graphite,
called tempered carbon
It is produced by heat-treating (malleableizing) white iron of suitable
composition to impart ductility, or malleability in the casting
If conditions are suitable cementite breaks up into iron and graphite
Fe3C Fe (α) + C (graphite)
Malleable iron showing Pearlitic malleable iron showing Ferritic malleable iron
tempered carbon. tempered carbon in ferrite- showing tempered carbon in
Unetched pearlitic matrix. Etched ferrite matrix. Etched 18
Malleable Cast Iron
19
Malleable Cast Iron
20
Malleable Cast Iron
0-1 denotes slow heating period.
On heating, pearlite and part of cementite transform to austenite.
During long time holding period (1-2) cementite phase is converted to
graphite, which exists in the form of clusters or rosettes around austenite.
In the next step when this structure is cooled, where cluster form of graphite
does not change, but the austenite transforms to either pearlite or ferrite
depending on cooling rates.
For faster cooling (2-3), pearlitic malleable cast iron is formed.
if the cooling rate is very slow (2-3‟), more carbon from austenite will come
out and rest of the austenite transforms to ferrite, which is called ferritic
malleable cast iron.
21
Gray Cast Iron
A large portion of its carbon is
distributed throughout the
casting as free or graphitic
carbon in flake form.
22
Ferritic and Pearlitic Gray Cast Iron
Alloy Addition
Silicon
Fluidity
Changes diagram
Relation of structure
23
Heat Treatment of Gray Cast Iron
24
Heat Treatment of Gray Cast Iron
Annealing of Gray cast iron
Temperature 740-780 0 C
Slow cooling
Iron carbide to ferrite and graphite
Normalizing of Gray cast iron
Temperature 900-1000 0 C
Air cooling
Pearlitic Gray Cast Iron
Quenching of Gray cast iron
Temperature 900-1000 0 C
Fast/Rapid Cooling (Quenching), Martensite matrix forms
Tempering
25
Nodular Cast Iron
Also known as ductile cast iron, or spheroidal graphite cast iron
A large proportion of its carbon to occur as regular spheroids or
nodules.
Small percentage of magnesium, cerium, or other agent is added in a
specially prepared liquid iron (spherodizing) to form graphite
spheroids
Ductility is the highest in these types of cast irons
When fractured, it presents a bright steely surface
26
Nodular Cast Iron
27
Nodular Cast Iron
Well-known functions of Mg:
1. Acts as deoxdiser and desulphuriser of molten metal
2. Promotes the development of graphite as nodules
3. Prevent nucleation of graphite as flake during freezing
Actual amount of Mg required depends on S and O2 content of base
iron. Desulphurization of the melt before casting is critical.
It is critical in making ductile iron that the amount of residual
magnesium present in the melt during solidification be in the range
0.03 to 0.05 weight percent.
Magnesium contents less than this amount will result in graphite flakes, and
amounts more than this results in the appearance of so called exploded graphites.
Either type contributes to a degradation in the ductility of the cast iron produced
28
Malleable Iron vs. Ductile Iron
Malleable iron, like ductile iron, possesses considerable ductility and
toughness because of its combination of nested graphite and a low-carbon
metallic matrix.
Consequently, malleable iron and ductile iron are suitable for some of the
same applications requiring good ductility and toughness and the choice
between them is based on economy rather than properties.
However, because ductile iron castings have similar properties to malleable
iron castings, and do not require the long and expensive heat treatment,
malleable iron production has fallen to very low levels, and only a few thin
section castings are made this way today.
Because solidification of white iron throughout a section is essential in the
production of malleable iron, ductile iron also has a clear advantage when
the section is too thick to permit solidification as white iron.
Malleable iron castings are produced in thin section thicknesses ranging
from about 1.5 to 100 mm and in weight from less than 30 g to 180 kg or
more.
29
Next Class
MME291: Lecture 8
Stainless Steels