Observation by SANS and PNR of pure Néel-type domain wall profiles and skyrmion suppression below room temperature in magnetic [Pt/CoFeB/Ru]$_{10}$ multilayers
Authors:
Victor Ukleev,
Fernando Ajejas,
Anton Devishvili,
Alexei Vorobiev,
Nina-Juliane Steinke,
Robert Cubitt,
Chen Luo,
Radu-Marius Abrudan,
Florin Radu,
Vincent Cros,
Nicolas Reyren,
Jonathan S. White
Abstract:
We report investigations of the magnetic textures in periodic [Pt(1 nm)/(CoFeB(0.8 nm)/Ru(1.4 nm)]$_{10}$ multilayers using polarised neutron reflectometry (PNR) and small-angle neutron scattering (SANS). The multilayers are known to host skyrmions stabilized by Dzyaloshinskii-Moriya interactions induced by broken inversion symmetry and spin-orbit coupling at the asymmetric interfaces. From depth-…
▽ More
We report investigations of the magnetic textures in periodic [Pt(1 nm)/(CoFeB(0.8 nm)/Ru(1.4 nm)]$_{10}$ multilayers using polarised neutron reflectometry (PNR) and small-angle neutron scattering (SANS). The multilayers are known to host skyrmions stabilized by Dzyaloshinskii-Moriya interactions induced by broken inversion symmetry and spin-orbit coupling at the asymmetric interfaces. From depth-dependent PNR measurements, we observe well-defined structural features, and obtain the layer-resolved magnetization profiles. The in-plane magnetization of the CoFeB layers calculated from fitting of the PNR profiles is found to be in excellent agreement with magnetometry data. Using SANS as a bulk probe of the entire multilayer, we observe long-period magnetic stripe domains and skyrmion ensembles with full orientational disorder at room temperature. No sign of skyrmions is found below 250\,K, which we suggest is due to an increase of a effective magnetic anisotropy in the CoFeB layer on cooling that suppresses skyrmion stability. Using polarised SANS at room temperature, we prove the existence of pure Néel-type windings in both stripe domain and skyrmion regimes. No Bloch-type winding admixture, i.e. an indication for hybrid windings, is detected within the measurement sensitivity, in good agreement with expectations according to our micromagnetic modelling of the multilayers. Our findings using neutron techniques offer valuable microscopic insights into the rich magnetic behavior of skyrmion-hosting multilayers, which are essential for the advancement of future skyrmion-based spintronic devices.
△ Less
Submitted 29 January, 2024; v1 submitted 10 November, 2023;
originally announced November 2023.
-
Role of gallium diffusion in the formation of a magnetically dead layer at Y3Fe5O12 / Gd3Ga5O12 epitaxial interface
Authors:
S. M. Suturin,
A. M. Korovin,
V. E. Bursian,
L. V. Lutsev,
V. Bourobina,
N. L. Yakovlev,
M. Montecchi,
L. Pasquali,
V. Ukleev,
A. Vorobiev,
A. Devishvili,
N. S. Sokolov
Abstract:
We have clarified the origin of magnetically dead interface layer formed in yttrium iron garnet (YIG) films grown at above 700°C onto gadolinium gallium garnet (GGG) substrate by means of laser molecular beam epitaxy. The diffusion-assisted formation of a Ga-rich region at the YIG / GGG interface is demonstrated by means of composition depth profiling performed by X-ray photoelectron spectroscopy,…
▽ More
We have clarified the origin of magnetically dead interface layer formed in yttrium iron garnet (YIG) films grown at above 700°C onto gadolinium gallium garnet (GGG) substrate by means of laser molecular beam epitaxy. The diffusion-assisted formation of a Ga-rich region at the YIG / GGG interface is demonstrated by means of composition depth profiling performed by X-ray photoelectron spectroscopy, secondary ion mass spectroscopy and X-ray and neutron reflectometry. Our finding is in sharp contrast to the earlier expressed assumption that Gd acts as a migrant element in the YIG/GGG system. We further correlate the presence of Ga-rich transition layer with considerable quenching of ferromagnetic resonance and spin wave propagation in thin YIG films. Finally, we clarify the origin of the enigmatic low-density overlayer that is often observed in neutron and X-ray reflectometry studies of the YIG / GGG epitaxial system.
△ Less
Submitted 6 November, 2018; v1 submitted 4 November, 2018;
originally announced November 2018.
-
The viscoelastic signature underpinning polymer deformation under shear flow
Authors:
Airidas Korolkovas,
Sylvain Prévost,
Maciej Kawecki,
Anton Devishvili,
Franz A. Adlmann,
Philipp Gutfreund,
Max Wolff
Abstract:
Entangled polymers are deformed by a strong shear flow. The shape of the polymer, called the form factor, is measured by small angle neutron scattering. However, the real-space molecular structure is not directly available from the reciprocal-space data, due to the phase problem. Instead, the data has to be fitted with a theoretical model of the molecule. We approximate the unknown structure using…
▽ More
Entangled polymers are deformed by a strong shear flow. The shape of the polymer, called the form factor, is measured by small angle neutron scattering. However, the real-space molecular structure is not directly available from the reciprocal-space data, due to the phase problem. Instead, the data has to be fitted with a theoretical model of the molecule. We approximate the unknown structure using piecewise straight segments, from which we derive an analytical form factor. We fit it to our data on a semi-dilute entangled polystyrene solution under in situ shear flow. The character of the deformation is shown to lie between that of a single ideal chain (viscous) and a cross-linked network (elastic rubber). Furthermore, we use the fitted structure to estimate the mechanical stress, and find a fairly good agreement with rheology literature.
△ Less
Submitted 6 December, 2018; v1 submitted 22 May, 2018;
originally announced May 2018.
-
Structural and magnetic properties of Co-N thin films deposited using magnetron sputtering at 523 K
Authors:
Nidhi Pandey,
Mukul Gupta,
Rachana Gupta,
Sujay Chakravarty,
Neeraj Shukla,
Anton Devishvili
Abstract:
In this work, we studied cobalt nitride (Co-N) thin films deposited using a dc magnetron sputtering method at a substrate temperature (\Ts) of 523\,K. We find that independent of the reactive gas flow (\pn) used during sputtering, the phases of Co-N formed at this temperature seems to be identical having N \pat~$\sim$5. This is contrary to Co-N phases formed at lower \Ts. For \Ts$\sim$300\,K, an e…
▽ More
In this work, we studied cobalt nitride (Co-N) thin films deposited using a dc magnetron sputtering method at a substrate temperature (\Ts) of 523\,K. We find that independent of the reactive gas flow (\pn) used during sputtering, the phases of Co-N formed at this temperature seems to be identical having N \pat~$\sim$5. This is contrary to Co-N phases formed at lower \Ts. For \Ts$\sim$300\,K, an evolution of Co-N phases starting from Co(N)$\rightarrow$\tcn$\rightarrow$Co$_3$N$\rightarrow$CoN can be seen as \pn increases to 100\p, whereas when the substrate temperature increases to 523\,K, the phase formed is a mixture of Co and \tcn, independent of the {\pn} used during sputtering. We used x-ray diffraction (XRD) to probe long range ordering, x-ray absorption spectroscopy (XAS) at Co absorption edge for the local structure, Magneto-optical Kerr e ffect (MOKE) and polarized neutron reflectivity (PNR) to measure the magnetization of samples. Quantification of N \pat~was done using secondary ion mass spectroscopy (SIMS). Measurements suggest that the magnetic moment of Co-N samples deposited at 523\,K is slightly higher than the bulk Co moment and does not get affected with the \pn~used for reactive sputtering. Our results provide an important insight about the phase formation of Co-N thin films which is discussed in this work.
△ Less
Submitted 29 July, 2016;
originally announced July 2016.
-
On the Explanation of the Paramagnetic Meissner Effect in Superconductor/Ferromagnet Heterostructures
Authors:
B. Nagy,
Yu. Khaydukov,
D. Efremov,
A. S. Vasenko,
L. Mustafa,
J. -H. Kim,
T. Keller,
K. Zhernenkov,
A. Devishvili,
R. Steitz,
B. Keimer,
L. Bottyan
Abstract:
An increase of the magnetic moment in superconductor/ferromagnet (S/F) bilayers V(40nm)/F [F$=$Fe(1,3nm), Co(3nm), Ni(3nm)] was observed using SQUID magnetometry upon cooling below the superconducting transition temperature Tc in magnetic fields of 10 Oe to 50 Oe applied parallel to the sample surface. A similar increase, often called the paramagnetic Meissner effect (PME), was observed before in…
▽ More
An increase of the magnetic moment in superconductor/ferromagnet (S/F) bilayers V(40nm)/F [F$=$Fe(1,3nm), Co(3nm), Ni(3nm)] was observed using SQUID magnetometry upon cooling below the superconducting transition temperature Tc in magnetic fields of 10 Oe to 50 Oe applied parallel to the sample surface. A similar increase, often called the paramagnetic Meissner effect (PME), was observed before in various superconductors and superconductor/ferromagnet systems. To explain the PME effect in the presented S/F bilayers a model based on a row of vortices located at the S/F interface is proposed. According to the model the magnetic moment induced below Tc consists of the paramagnetic contribution of the vortex cores and the diamagnetic contribution of the vortex-free region of the S layer. Since the thickness of the S layer is found to be 3-4 times less than the magnetic field penetration depth, this latter diamagnetic contribution is negligible. The model correctly accounts for the sign, the approximate magnitude and the field dependence of the paramagnetic and the Meissner contributions of the induced magnetic moment upon passing the superconducting transition of a ferromagnet/superconductor bilayer.
△ Less
Submitted 8 October, 2016; v1 submitted 25 July, 2016;
originally announced July 2016.
-
Neutron reflectometry on highly absorbing films and its application to 10B4C-based neutron detectors
Authors:
F. Piscitelli,
A. Khaplanov,
A. Devishvili,
S. Schmidt,
C. Höglund,
J. Birch,
A. J. C. Dennison,
P. Gutfreund,
R. Hall-Wilton,
P. Van Esch
Abstract:
Neutron reflectometry is a powerful tool used for studies of surfaces and interfaces. In general the absorption in the typical studied materials can be neglected and this technique is limited to the measurement of the reflectivity only. In the case of strongly absorbing nuclei the number of neutrons is not conserved and the absorption can be directly measured by using the neutron-induced fluoresce…
▽ More
Neutron reflectometry is a powerful tool used for studies of surfaces and interfaces. In general the absorption in the typical studied materials can be neglected and this technique is limited to the measurement of the reflectivity only. In the case of strongly absorbing nuclei the number of neutrons is not conserved and the absorption can be directly measured by using the neutron-induced fluorescence technique which exploits the prompt particle emission of absorbing isotopes. This technique is emerging from soft matter and biology where highly absorbing nuclei, generally in very small quantities, are used as a label for buried layers. Nowadays the importance of highly absorbing layers is rapidly increasing, partially because of their application in neutron detection; a field that has become more and more active also due to the 3He-shortage. In this manuscript we extend the neutron-induced fluorescence technique to the study of thick layers of highly absorbing materials; in particular 10B4C. The theory of neutron reflectometry is a commonly studied topic, however the subtle relationship between the reflection and the absorption of neutrons is not widely known, in particular when a strong absorption is present. The theory for a general stack of absorbing layers has been developed and compared to measurements. This new technique has potential as a tool for characterization of highly absorbing layers. We also report on the requirements that a 10B4C layer must fulfill in order to be employed as a converter in neutron detection.
△ Less
Submitted 5 October, 2015;
originally announced October 2015.
-
Depth profile of the ferromagnetic order in a YBa$_2$Cu$_3$O$_7$ / La$_{2/3}$Ca$_{1/3}$MnO$_3$ superlattice on a LSAT substrate: a polarized neutron reflectometry study
Authors:
M. A. Uribe-Laverde,
D. K. Satapathy,
I. Marozau,
V. K. Malik,
S. Das,
K. Sen,
J. Stahn,
A. Rühm,
J. -H. Kim,
T. Keller,
A. Devishvili,
B. P. Toperverg,
C. Bernhard
Abstract:
Using polarized neutron reflectometry (PNR) we have investigated a YBa2Cu3O7(10nm)/La2/3Ca1/3MnO3(9nm)]10 (YBCO/LCMO) superlattice grown by pulsed laser deposition on a La0.3Sr0.7Al0.65Ta0.35O3 (LSAT) substrate. Due to the high structural quality of the superlattice and the substrate, the specular reflectivity signal extends with a high signal-to-background ratio beyond the fourth order superlatti…
▽ More
Using polarized neutron reflectometry (PNR) we have investigated a YBa2Cu3O7(10nm)/La2/3Ca1/3MnO3(9nm)]10 (YBCO/LCMO) superlattice grown by pulsed laser deposition on a La0.3Sr0.7Al0.65Ta0.35O3 (LSAT) substrate. Due to the high structural quality of the superlattice and the substrate, the specular reflectivity signal extends with a high signal-to-background ratio beyond the fourth order superlattice Bragg peak. This allows us to obtain more detailed and reliable information about the magnetic depth profile than in previous PNR studies on similar superlattices that were partially impeded by problems related to the low temperature structural transitions of the SrTiO3 substrates. In agreement with the previous reports, our PNR data reveal a strong magnetic proximity effect showing that the depth profile of the magnetic potential differs significantly from the one of the nuclear potential that is given by the YBCO and LCMO layer thickness. We present fits of the PNR data using different simple block-like models for which either a ferromagnetic moment is induced on the YBCO side of the interfaces or the ferromagnetic order is suppressed on the LCMO side. We show that a good agreement with the PNR data and with the average magnetization as obtained from dc magnetization data can only be obtained with the latter model where a so-called depleted layer with a strongly suppressed ferromagnetic moment develops on the LCMO side of the interfaces. The models with an induced ferromagnetic moment on the YBCO side fail to reproduce the details of the higher order superlattice Bragg peaks and yield a wrong magnitude of the average magnetization. We also show that the PNR data are still consistent with the small, ferromagnetic Cu moment of 0.25muB that was previously identified with x-ray magnetic circular dichroism and x-ray resonant magnetic reflectometry measurements on the same superlattice.
△ Less
Submitted 5 December, 2012;
originally announced December 2012.
-
Magnetic proximity effect in $\mathbf{YBa_2Cu_3O_7/La_{2/3}Ca_{1/3}MnO_3}$ and $\mathbf{YBa_2Cu_3O_7/LaMnO_{3+δ}}$ superlattices
Authors:
D. K. Satapathy,
M. A. Uribe-Laverde,
I. Marozau,
V. K. Malik,
S. Das,
Th. Wagner,
C. Marcelot,
J. Stahn,
S. Brück,
A. Rühm,
S. Macke,
T. Tietze,
E. Goering,
A. Frañó,
J. -H. Kim,
M. Wu,
E. Benckiser,
B. Keimer,
A. Devishvili,
B. P. Toperverg,
M. Merz,
P. Nagel,
S. Schuppler,
C. Bernhard
Abstract:
Using neutron reflectometry and resonant x-ray techniques we studied the magnetic proximity effect (MPE) in superlattices composed of superconducting YBa$_2$Cu$_3$O$_7$ (YBCO) and ferromagnetic-metallic (FM-M) La$_{0.67}$Ca$_{0.33}$MnO$_{3}$ (LCMO) or ferromagnetic-insulating (FM-I) LaMnO$_{3+δ}$ (LMO). We find that the MPE strongly depends on the electronic state of the manganite layers, being pr…
▽ More
Using neutron reflectometry and resonant x-ray techniques we studied the magnetic proximity effect (MPE) in superlattices composed of superconducting YBa$_2$Cu$_3$O$_7$ (YBCO) and ferromagnetic-metallic (FM-M) La$_{0.67}$Ca$_{0.33}$MnO$_{3}$ (LCMO) or ferromagnetic-insulating (FM-I) LaMnO$_{3+δ}$ (LMO). We find that the MPE strongly depends on the electronic state of the manganite layers, being pronounced for the FM-M LCMO and almost absent for FM-I LMO. We also detail the change of the magnetic depth profile due to the MPE and provide evidence for its intrinsic nature.
△ Less
Submitted 7 June, 2012; v1 submitted 24 November, 2011;
originally announced November 2011.