GATE 2018 General Aptitude (GA) Set-4

Q. 1 – Q. 5 carry one mark each.

Q.1 “When she fell down the _______, she received many _______ but little help.”

The words that best fill the blanks in the above sentence are

(A) stairs, stares (B) stairs, stairs

(C) stares, stairs (D) stares, stares

Q.2 “In spite of being warned repeatedly, he failed to correct his _________ behaviour.”

The word that best fills the blank in the above sentence is

(A) rational (B) reasonable (C) errant (D) good

Q.3 For 0 ≤ 𝑥 ≤ 2𝜋, sin 𝑥 and cos 𝑥 are both decreasing functions in the interval ________.

𝜋 𝜋 3𝜋 3𝜋
(A) (0, 2 ) (B) ( 2 , 𝜋) (C) (𝜋, ) (D) ( 2 , 2𝜋)
2

Q.4 The area of an equilateral triangle is √3. What is the perimeter of the triangle?

(A) 2 (B) 4 (C) 6 (D) 8

Q.5 Arrange the following three-dimensional objects in the descending order of their volumes:
(i) A cuboid with dimensions 10 cm, 8 cm and 6 cm
(ii) A cube of side 8 cm
(iii) A cylinder with base radius 7 cm and height 7 cm
(iv) A sphere of radius 7 cm

(A) (i), (ii), (iii), (iv)

(B) (ii), (i), (iv), (iii)
(C) (iii), (ii), (i), (iv)
(D) (iv), (iii), (ii), (i)

Q. 6 – Q. 10 carry two marks each.

Q.6 An automobile travels from city A to city B and returns to city A by the same route. The
speed of the vehicle during the onward and return journeys were constant at 60 km/h and
90 km/h, respectively. What is the average speed in km/h for the entire journey?

(A) 72 (B) 73 (C) 74 (D) 75

GA 1/2
GATE 2018 General Aptitude (GA) Set-4
Q.7 A set of 4 parallel lines intersect with another set of 5 parallel lines. How many
parallelograms are formed?

(A) 20 (B) 48 (C) 60 (D) 72

Q.8 To pass a test, a candidate needs to answer at least 2 out of 3 questions correctly. A total of
6,30,000 candidates appeared for the test. Question A was correctly answered by 3,30,000
candidates. Question B was answered correctly by 2,50,000 candidates. Question C was
answered correctly by 2,60,000 candidates. Both questions A and B were answered
correctly by 1,00,000 candidates. Both questions B and C were answered correctly by
90,000 candidates. Both questions A and C were answered correctly by 80,000 candidates.
If the number of students answering all questions correctly is the same as the number
answering none, how many candidates failed to clear the test?

(A) 30,000 (B) 2,70,000 (C) 3,90,000 (D) 4,20,000

1
Q.9 If 𝑥 2 + 𝑥 − 1 = 0 what is the value of 𝑥 4 + ?
𝑥4

(A) 1 (B) 5 (C) 7 (D) 9

Q.10 In a detailed study of annual crow births in India, it was found that there was relatively no
growth during the period 2002 to 2004 and a sudden spike from 2004 to 2005. In another
unrelated study, it was found that the revenue from cracker sales in India which remained
fairly flat from 2002 to 2004, saw a sudden spike in 2005 before declining again in 2006.
The solid line in the graph below refers to annual sale of crackers and the dashed line refers
to the annual crow births in India. Choose the most appropriate inference from the above
data.

(A) There is a strong correlation between crow birth and cracker sales.
(B) Cracker usage increases crow birth rate.
(C) If cracker sale declines, crow birth will decline.
(D) Increased birth rate of crows will cause an increase in the sale of crackers.

END OF THE QUESTION PAPER

GA 2/2
GATE 2018 Metallurgical Engineering

Q. 1 – Q. 25 carry one mark each.

Q.1 For a laminar flow of a liquid metal over a flat plate, the thicknesses of the velocity and
thermal boundary layers are 𝛿𝑣 and 𝛿𝑡 respectively. Kinematic viscosity
(viscosity/density) of liquid metal is significantly lower than its thermal diffusivity
[thermal conductivity / (density × specific heat)]. Based on this information, pick the
correct option.

(Note: The temperature of the liquid metal is different from that of the plate).

(A) 𝛿𝑣 < 𝛿𝑡 (B) 𝛿𝑣 > 𝛿𝑡

(C) 𝛿𝑣 = 𝛿𝑡 (D) Information insufficient

Q.2 What is the most-abundant anion in a 2CaO.SiO2 melt?

(A) (SiO4) 4  (B) (Si2O7) 6  (C) (Si3O10) 8  (D) (Si4O14) 10 

Q.3 Analysis of a flow phenomenon in a system requires the following variables:

i. Pressure [M L1 T 2]

ii. Velocity of the fluid [L T 1]

iii. Size of the system [L]
iv. Density of the fluid [M L3]

v. Viscosity of the fluid [M L1 T 1]

According to Buckingham Pi theorem (dimensional analysis) what is the number of

independent DIMENSIONLESS variables needed to describe this system?

(A) 2 (B) 3 (C) 4 (D) 5

MT 1/22
GATE 2018 Metallurgical Engineering

Q.4 In froth flotation, the primary purpose of adding collectors is to:

(A) make the surface of the mineral hydrophobic.

(B) make the surface of the mineral hydrophilic.
(C) stabilize the froth.
(D) adjust the pH.

Q.5 Arrange the following in the correct sequence of operations in an integrated steel plant:
i. Basic Oxygen Furnace (BOF)
ii. Blast Furnace (BF)
iii. Ruhrstahl Heraeus Degassing Process (RH)
iv. Ladle Furnace Process (LF)

(A) BOFBFLFRH (B) BFLFBOFRH

(C) RHLFBFBOF (D) BFBOFLFRH

Q.6 During decarburization in a steel bath at 1550 oC, the compositions of dissolved C (wt.%C)
and dissolved O (wt.%O) follow the relation:
(wt.%C)(wt.%O) = K
When the partial pressure of CO (𝑝𝐶𝑂 ) is 1 atm, K = 0.002.
If 𝑝𝐶𝑂 = 0.1 atm, what is the value of K, at the same temperature?
Note: Assume Henry’s law is applicable.

(A) 0.06 (B) 0.002 (C) 0.02 (D) 0.0002

MT 2/22
GATE 2018 Metallurgical Engineering

Q.7 During upset forging, and considering friction, which of the following profiles represents
the axial compressive stress?
Note: In these profiles, the absolute value of the axial compressive stress is plotted on the
y-axis.

(A) P (B) Q (C) R (D) S

Q.8 Consider the following engineering components:

P. Gas turbine blades

Q. Tungsten-based heavy alloy penetrators
R. Self-lubricating bearings
S. Engine block of an automobile

Which of the following two components are produced by powder metallurgy?

(A) P & Q (B) Q & R (C) Q & S (D) P & S

MT 3/22
GATE 2018 Metallurgical Engineering

Q.9 Which of the following materials are protected by passivation (i.e., formation of a thin
adherent film on the surface) from corrosion?

P. Aluminium alloys
Q. Mild steel
R. Stainless steel
S. Silver

(A) P & Q (B) Q & R (C) Q & S (D) P & R

Q.10 The c/a ratio of Zn (hcp) is 1.856. Slip at room temperature occurs most easily on which of
the following slip systems in Zn:

Note: In hcp metals, the ideal c/a ratio is 1.633.

(A) {11̅00} 〈112̅0〉 (B) {11̅00} 〈0002〉

(C) {0001} 〈112̅0〉 (D) {101̅1̅} 〈112̅3〉

Q.11 At equilibrium, the maximum number of phases in a three-component system at

CONSTANT PRESSURE is:

(A) 1 (B) 2 (C) 3 (D) 4

MT 4/22
GATE 2018 Metallurgical Engineering

Q.12 For a single phase system with K components, the exact differential of Gibbs free energy is
given as :
𝐾

𝑑𝐺 = −𝑆𝑑𝑇 + 𝑉𝑑𝑃 + ∑ 𝜇𝑖 𝑑𝑛𝑖

𝑖=1
Which one of the following can be derived from the above expression as a Maxwell’s
relation?

𝜕𝑆 𝜕𝑉
(A) | =− |
𝜕𝑃 𝑇,𝑛𝑖 𝜕𝑇 𝑃,𝑛𝑖

𝜕𝑆 𝜕𝑉
(B) | = |
𝜕𝑉 𝑇,𝑛𝑖 𝜕𝑇 𝑃,𝑛𝑖

𝜕𝑆 𝜕𝑉
(C) | =− |
𝜕𝑇 𝑇,𝑛𝑖 𝜕𝑃 𝑇,𝑛𝑖

𝜕𝑆 𝜕𝑉
(D) | = |
𝜕𝑃 𝑇,𝑛𝑖 𝜕𝑃 𝑇,𝑛𝑖

Q.13 For intrinsic Si at room temperature, the electron concentration = the hole
concentration = 1 × 1016 m−3 , and the electron and hole mobilities are

0.1 and 0.2 m2 . V −1 . s −1 respectively. What is the room temperature electrical

conductivity?

The charge of an electron is 1.6 × 10−19 C.

(A) 0 (.m) 1 (B) 1.6 × 10  4 (.m) 1

(C) 3.2 × 10  4 (.m) 1 (D) 4.8 × 10  4 (.m) 1

Q.14 To minimize refractory loss during BOF steel-making, slag is supersaturated with which of
the following:

(A) Al2O3 (B) Fe2O3 (C) SiO2 (D) MgO

MT 5/22
GATE 2018 Metallurgical Engineering

Q.15 Which of the following welding processes is NOT suitable for joining thin metal sheets?

(A) Gas Metal Arc Welding

(B) Electro Slag Welding
(C) Electron Beam Welding
(D) Laser Beam Welding

Q.16 Which of the following categories of materials is suitable as a filler for brazing of steel
sheets?

(A) Epoxy resins (B) Near-eutectic alloys

(C) Refractory alloys (D) Large freezing range alloys

Q.17 Arrange the following processes in INCREASING magnitude of surface roughness of the
casting.

P. Investment casting
Q. Permanent mould casting
R. Pressure die casting
S. Sand casting

(A) R < S < Q < P (B) P < S < Q < R (C) R < P < Q < S (D) Q < P < R < S

Q.18 In a Jominy end-quench test of the eutectoid plain-carbon steel, which of the following
represents the sequence of microstructures observed from the quenched end of the
specimen?

(A) Fine Pearlite, Coarse Pearlite, Martensite and Pearlite, Martensite

(B) Martensite, Martensite and Pearlite, Fine Pearlite, Coarse Pearlite
(C) Coarse Pearlite, Pearlite and Martensite, Fine Pearlite, Martensite
(D) Martensite, Martensite and Pearlite, Coarse Pearlite, Fine Pearlite

MT 6/22
GATE 2018 Metallurgical Engineering

Q.19 A long oil pipeline made of steel is suspected to have developed a scale on the inner
surface due to corrosion. Which of the following non-destructive techniques is the most
suitable for detecting and quantifying such a defect?

(A) Dye penetrant test (B) Magnetic particle inspection

(C) Ultrasonic inspection (D) Acoustic emission

Q.20 A steel is plastically worked in the temperature range below the nose of the TTT curve and
above Ms, followed by quenching to produce fine martensite. What is this process called?

(A) Martempering (B) Ausforming

(C) Inter-critical forming (D) Normalizing

Q.21 What is the requirement for equilibrium at a triple junction as shown in the schematic, with
and  as grain boundary tensions and and  as dihedral angles?

𝛾23 𝛾13 𝛾12

(A) = =
cos(𝜃1 ) cos(𝜃2 ) cos(𝜃3 )
𝛾23 𝛾13 𝛾12
(B) = =
sin(𝜃1 ) sin(𝜃2 ) sin(𝜃3 )
𝛾23 𝛾13 𝛾12
(C) = =
sin(𝜃2 ).sin(𝜃3 ) sin(𝜃1 ).sin(𝜃3 ) sin(𝜃1 ).sin(𝜃2 )

(D) 𝛾23 sin(𝜃1 ) = 𝛾13 sin(𝜃2 ) = 𝛾12 sin(𝜃3 )

MT 7/22
GATE 2018 Metallurgical Engineering

Q.22 In the A-rich end of the A-B binary eutectic phase diagram (shown below), the solidus and
liquidus are straight lines.

The freezing range of the alloy with 16% B is _________ (in oC to one decimal place)

Q.23 A vector field is given as follows:

𝑓⃗ = (−𝑥 2 𝑦 + 𝑥𝑦 2 ) 𝑖̂ + (𝑥 2 𝑦) 𝑗̂

The divergence of this field evaluated at (𝑥, 𝑦) = (2, 2) is _______________ .

Q.24 A plate of thickness h = 120 mm is cold rolled in a mill with a roll diameter of 200 mm. If
the coefficient of friction µ is 0.1, the maximum possible reduction Δh in a single pass is
________ (in mm to one decimal place)

MT 8/22
GATE 2018 Metallurgical Engineering

Q.25 A copper-aluminium diffusion couple develops a certain concentration profile after an

isothermal treatment at 600C for 10 hours. The time required to achieve the same

concentration profile at 500C is _________ (in hours to 1 decimal place)

Given: The interdiffusion coefficient for copper in aluminium at 500C and 600C are

4×1014 m2s1 and 8×1013 m2s1.

MT 9/22
GATE 2018 Metallurgical Engineering

Q. 26 – Q. 55 carry two marks each.

Q.26 The molar free energy (J mol1) of a liquid solution of a binary A-B alloy as a function of

temperature ( T ) and composition (x, the mole fraction of B) is given by:

𝐺 𝐿 (𝑇, 𝑥) = (1 − 𝑥)𝐺𝐴0,𝐿 + 𝑥𝐺𝐵0,𝐿 + 𝑅𝑇[𝑥 ln 𝑥 + (1 − 𝑥) ln(1 − 𝑥)] + 4000𝑥(1 − 𝑥).

where 𝐺𝐴0,𝐿 and 𝐺𝐵0,𝐿 are the molar free energies of pure liquid A and pure liquid B.
What is the excess molar free energy, 𝐺 𝑋𝑆,𝐿 , for an alloy with 𝑥 = 0.5 at 𝑇 = 1000 K?
Given: Gas constant R = 8.314 J K1 mol1

(A) 1000 J mol1 (B)  2000 J mol1 (C) 4763 J mol1 (D)  5763 J mol1

Q.27 Determine the correctness (or otherwise) of the following Assertion [A] and the Reason [R]

Assertion [A]: For a material exhibiting Coble creep, a reduction in grain size results in a
significant increase in creep rate
Reason [R]: Grain boundaries act as a barrier to motion of dislocations

(A) Both [A] and [R] are true and [R] is the correct reason for [A]

(B) Both [A] and [R] are true, but [R] is not the correct reason for [A]

(C) Both [A] and [R] are false

(D) [A] is true but [R] is false

MT 10/22
GATE 2018 Metallurgical Engineering

Q.28 Determine the correctness (or otherwise) of the following Assertion [A] and the Reason [R]

Assertion [A]: Refractory BCC metals like W and Mo are less ductile than FCC metals like
Ni and Pt at room temperature
Reason [R]: BCC metals have fewer independent slip systems than FCC metals

(A) Both [A] and [R] are true and [R] is the correct reason for [A]
(B) Both [A] and [R] are true, but [R] is not the correct reason for [A]
(C) Both [A] and [R] are false
(D) [A] is true but [R] is false

Q.29 A glass fibre of 5 micron diameter is subjected to a tensile stress of 20 MPa. The surface
energy and elastic modulus of this material are 0.3 Jm2 and 70 GPa, respectively. Pick the
correct answer based on the information provided above:
Note: The glass fibre contains a population of flaws of different lengths.

(A) The fibre will undergo brittle fracture

(B) The fibre will undergo plastic deformation, but not fracture

(C) The fibre will undergo elastic deformation, but not fracture

(D) The fibre will undergo buckling

MT 11/22
GATE 2018 Metallurgical Engineering

Q.30 .

Two equal and opposite point charges + Q and  Q are located as shown in the figure
above. A surface integral, 𝐹𝑖 is defined on surface 𝑆𝑖 of a sphere of radius 𝑟𝑖 as follows:

𝐹𝑖 = ∮𝑆 (𝐸⃗⃗ ∙ 𝑛̂)𝑑𝑆,
𝑖

where 𝐸⃗⃗ is the electric field, and 𝑛̂ is the unit normal to the surface of integration.
If 𝑟1 : 𝑟2 : 𝑟3 are in the ratio 1: 2: 5, use the Gauss divergence theorem to determine the ratio
𝐹1 : 𝐹2 : 𝐹3 .

(A) 1 : 2 : 5
(B) 5 : 2 : 1
(C) 1 : 1 : 0
(D) 1 : 1 : 0

MT 12/22
GATE 2018 Metallurgical Engineering

Q.31 Match
. the four tensile stress-strain curves (P,Q, R, S) with the materials listed in the box:

1. Polyester (PET)
2. High purity Copper
3. Mild Steel
4. Soda-lime Glass

(A) P-1, Q-2, R-3, S-4

(B) P-3, Q-1, R-4, S-2
(C) P-3, Q-2, R-4, S-1
(D) P-2, Q-3, R-4, S-1

Q.32 Match the metal in Group 1 with the appropriate extractive process in Group 2

Group 1 Group 2
P. Fe 1. Metallothermic Reduction
Q. Ni 2. Carbothermic reduction
R. Al 3. Matte Smelting
S. Cr 4. Fused Salt Electrolysis

(A) P-1, Q-2, R-4, S-3

(B) P-2, Q-4, R-1, S-3
(C) P-2, Q-3, R-4, S-1
(D) P-2, Q-1, R-4, S-3

MT 13/22
GATE 2018 Metallurgical Engineering

Q.33 Fe is produced in a reactor using pure Fe2O3, C and O2. For every mole of Fe produced,

2.38 moles of C is used. The exit gas from the reactor contains CO and CO2 in the molar

ratio of 1:1. How many moles of O2 is consumed for every mole of Fe produced?

(A) 1.035 (B) 2.072 (C) 0.513 (D) 4.147

Q.34 What is the voltage required to electrolytically refine impure copper of activity 𝑎𝐶𝑢 = 0.9
(Raoultian standard state) to pure copper at 300 K

Given: Gas constant R = 8.314 J mol 1 K 1, and Faraday’s constant F = 96500 C mol  1.

(A) 1.36 mV (B) 2.72 mV (C) 0 mV (D) 5.44 mV

MT 14/22
GATE 2018 Metallurgical Engineering

Q.35 Consider
. the following Ordinary Differential Equation:
𝑑 𝑑𝑐
[𝑐 ] = 0
𝑑𝑥 𝑑𝑥
In a domain 0 ≤ 𝑥 ≤ 𝑡, with boundary conditions 𝑐(0) = 0.5 and 𝑐(𝑡) = 1.0, pick the
appropriate choice for 𝑐(𝑥) from the following options:

(A) P (B) Q (C) R (D) S

MT 15/22
GATE 2018 Metallurgical Engineering

Q.36 Match the manufacturing processes in Group 1, with the types of cracks in Group 2:

Group 1 Group 2
P. Arc welding 1. Edge crack
Q. Extrusion 2. Chevron crack
R. Drawing 3. Surface crack
S. Rolling 4. Liquation crack

(A) P-1, Q-2, R-3, S-4

(B) P-1, Q-3, R-4, S-2
(C) P-4, Q-3, R-2, S-1
(D) P-4, Q-2, R-1, S-3

MT 16/22
GATE 2018 Metallurgical Engineering

Q.37 Consider
. a dilute substitutional solid solution of X in a metal A. The powder diffraction
pattern of this alloy reveals that all the peaks have shifted to the left when compared to
those for pure A (with no splitting of peaks). If such a solute interacts and segregates to an
edge dislocation, which of the following positions around the dislocation will it
preferentially occupy?

(A) P (B) Q (C) R (D) S

Q.38 A classroom of 20 students can be categorized on the basis of blood-types: 5 students each
with “A”, “B”, “AB”, and “O” blood-types. If four students are selected at random from
this class, what is the probability that each student has a different blood-type?

(A) 0.2500 (B) 0.1289 (C) 0.0625 (D) 0.0156

Q.39 If the solid-liquid interfacial energy increases by 10%, the energy barrier for homogeneous
nucleation of a spherical solid from the liquid, will change by:

(A) 21% (B) 33% (C) 10% (D) 46%

MT 17/22
GATE 2018 Metallurgical Engineering

Q.40 Consider the following stress state imposed on a material:

90 50 0
𝜎 = [50 −20 0 ] MPa.
0 0 140
If the material responds elastically with a volumetric strain 𝛥 = 3.5 × 10−4 , what is its
bulk modulus?

(A) 150 GPa (B) 350 GPa (C) 200 GPa (D) 400 GPa

Q.41 A continuous and aligned carbon-fiber composite consists of 25 vol. % of fibers in an

epoxy matrix. The Young’s modulus of fiber and matrix, respectively are 𝐸𝑓 = 250 GPa
and 𝐸𝑚 = 2.5 GPa.

If the composite is subjected to longitudinal loading (iso-strain condition and assuming

elastic response), the fraction of load borne by the reinforcement is ________ (to two
decimal places)

Q.42 Pure iron transforms from body centered cubic (BCC) to face centered cubic (FCC) crystal
structure at 912 C. If the lattice parameter of the BCC phase is 0.293 nm and that of the
FCC phase is 0.363 nm, the associated volume change is _______ (in % to one decimal
place)

MT 18/22
GATE 2018 Metallurgical Engineering

Q.43 As shown in schematic below, an alloy is cast as a rectangular slab between two thick
mould walls that differ in their thermal conductivities. Shrinkage defects are found at a
distance L1 from Mould-1 with thermal conductivity 𝑘1 and distance L2 from Mould-2
with thermal conductivity 𝑘2 . If the ratio L1:L2 = 3:2, and assuming 1-D heat transfer, the
𝑘
ratio ( 1⁄𝑘 ) is ________ (to two decimal places)
2

Q.44 The temperature profile (T in Kelvin) of an arc weld across its width is given as
𝑇 = 2000 exp(−0.3𝑥 2 ) where 𝑥 (in mm) is the distance from the weld centre. The
melting point of the base material is 1500 K. The width of the fusion zone is _______ (in
mm to two decimal places).

Q.45 The terminal velocity (𝑣) of a spherical inclusion of diameter D = 50 micrometers rising in

liquid steel is __________ (in mm s1 to two decimal places)

Assume Stokes law; i.e., drag force 𝐹𝑑 = 3𝜋𝜇𝐷𝑣, where 𝜇 is the viscosity of steel.
Given: Density of liquid steel = 7900 kg m3; Viscosity of liquid steel = 0.0079 Pa s;

Density of the inclusion = 2500 kg m3; Acceleration due to gravity = 9.8 m s2

MT 19/22
GATE 2018 Metallurgical Engineering

Q.46 A single crystal of aluminium is subjected to 10 MPa tensile stress along the [321]
crystallographic direction. The resolved shear stress on the (111̅) [101] slip system is
______ (in MPa to two decimal places)

Q.47 If the net magnetic moment of an Fe atom in BCC structure is 2 𝜇𝐵 , then the saturation

magnetization of Fe is ___________ (kA m1 to one decimal place)

Given: 𝜇𝐵 = 9.273 × 10 24 A m2; Lattice parameter of BCC iron is 0.287 nm

Note: kA is kiloAmperes

Q.48 If 2 moles of Au and 3 moles of Ag are mixed to form a single-phase ideal solid solution,
the total entropy of mixing is __________ (on J K1 to one decimal place )

Given: Gas constant R = 8.314 J K1 mol1

Q.49 A spherical liquid metal droplet of diameter 1 mm is solidified in a stream of gas at 300 K.
Assuming that the metal droplet remains at its melting point of 900 K and neglecting
radiative losses, the time to complete the solidification is __________ (in seconds to one
decimal place).
Given: The enthalpy of fusion for the metal is 4000 kJ kg1; The gas-droplet convective

heat transfer coefficient is 200 W m2 K1; Density of liquid metal is 2700 kg m3.

MT 20/22
GATE 2018 Metallurgical Engineering

Q.50 At a temperature of 710 K, the vapour pressure of pure liquid Zn is given by:
𝑝𝑍𝑛 (𝑋𝑧𝑛 = 1.0) = 3.6 × 10−4 atm.
The Raoultian activity coefficient (𝛾𝑍𝑛 ) of Zn in Zn-Cd alloy liquid at 710 K is
approximated by:
ln(𝛾𝑍𝑛 ) = 0.875(1 − 𝑋𝑍𝑛 )2
𝑝𝑍𝑛 (𝑋𝑧𝑛 =0.7)
The ratio [ ] for a liquid alloy with 𝑋𝑧𝑛 = 0.7 is __________ (to two
𝑝𝑍𝑛 (𝑋𝑧𝑛 =1.0)
decimal places).

Q.51 For the reaction: 4Ag(s, pure) + O2 (g) ⟶ 2Ag 2 O(s, pure), the standard enthalpy change,
∆𝐻 0 = − 61080 J, and the standard entropy change, ∆𝑆 0 = − 132.22 J K −1, in the
temperature range from 298 K to 500 K.
The temperature above which Ag 2 O decomposes in an atmosphere containing oxygen at a
partial pressure 𝑝𝑂2 = 0.3 atm is __________ (in K to one decimal place).

Given: Gas constant R = 8.314 J K1 mol1

Q.52 In a powder diffraction experiment on BCC iron, the first peak occurs at 2𝜃 = 68.7. The

wavelength of X-rays is _________ (in nm to three decimal places).

Given: The lattice parameter of iron = 0.287 nm

Q.53 A 1 mol piece of copper at 400 K is brought in contact with another 1 mol piece of copper
at 300 K, and allowed to reach thermal equilibrium. The entropy change for this process is
__________ (in J K1 to three decimal places)

Given: Specific heat capacity of copper (between 250 K and 500 K) is 22.6 J K1mol1.
Assume that the system containing the two pieces of copper remains isolated during this
process.

MT 21/22
GATE 2018 Metallurgical Engineering

Q.54 Using the trapezoidal rule with two equal intervals (n = 2, Δ𝑥 = 1), the definite integral
4 1
∫2 𝑑𝑥 =______________ (to two decimal places).
ln(𝑥)

Q.55 The ideal plastic work involved in extruding a cylindrical billet of length 100 mm, from an
initial diameter of 20 mm to a final diameter of 16 mm is __________ (in J to one decimal
place).

The flow stress in compression is 40 MPa, and remains constant throughout the process.

END OF THE QUESTION PAPER