Defects/imperfections in Welds - Reheat Cracking: Identification

TWI main site Technical Capabilities Industrial Membership Training and Examinations
Accessibility Careers Text Only Site Map Global websites
> Technical Knowledge > Job Knowledge > Defects / imperfections in welds - reheat cracking
Share:
Defects/imperfections in welds - reheat cracking

Job Knowledge 48
The characteristic features and principal causes of reheat

cracking are described. General guidelines on best practice
are given so that welders can minimise the risk of reheat
cracking in welded fabrications.
Identification
Visual appearance
Reheat cracking may occur in low alloy steels containing

alloying additions of chromium and molybdenum or
Location of reheat cracks in a nuclear pressure vessel steel
chromium, molybdenum and vanadium when the welded
component is being subjected to post weld heat treatment, such as stress relief heat treatment, or has been subjected
to high temperature service (typically in the range 350 to 550°C).
Cracking is almost exclusively found in the coarse grained regions of the heat affected zone (HAZ) beneath the weld,
or cladding, and in the coarse grained regions within the weld metal. The cracks can often be seen visually, usually
associated with areas of stress concentration such as the weld toe.
Cracking may be in the form of coarse macro-cracks or colonies of micro-cracks.
A macro-crack will appear as a 'rough' crack, often with branching, following the coarse grain region, (Fig. 1a).
Cracking is always intergranular along the prior austenite grain boundaries (Fig. 1b). Macro-cracks in the weld metal
can be oriented either longitudinal or transverse to the direction of welding. Cracks in the HAZ, however, are always
parallel to the direction of welding.
Fig.1a. Cracking associated with the coarse grained

heat affected zone
Fig.1b. Intergranular morphology of reheat cracks
Micro-cracking can also be found both in the HAZ and within the weld metal. Micro-cracks in multipass welds will be
found associated with the grain coarsened regions which have not been refined by subsequent passes.
Causes
The principal cause is that when heat treating susceptible steels, the grain interior becomes strengthened by carbide
precipitation, forcing the relaxation of residual stresses by creep deformation at the grain boundaries.
The presence of impurities which segregate to the grain boundaries and promote temper embrittlement, e.g.
antimony, arsenic, tin, sulphur and phosphorus, will increase the susceptibility to reheat cracking.
The joint design can increase the risk of cracking. For example, joints likely to contain stress concentration, such as
partial penetration welds, are more liable to initiate cracks.
The welding procedure also has an influence. Large weld beads are undesirable, as they produce coarse columnar
grains within the weld metal and a coarse grained HAZ which is less likely to be refined by the subsequent pass, and
therefore will be more susceptible to reheat cracking.
Best practice in prevention
The risk of reheat cracking can be reduced through the choice of steel, specifying the maximum impurity level and by
adopting a more tolerant welding procedure / technique.
Steel choice
If possible, avoid welding steels known to be susceptible to reheat cracking. For example, A 508 Class 2 is known to
be particularly susceptible to reheat cracking, whereas cracking associated with welding and cladding in A508 Class 3
is largely unknown. The two steels have similar mechanical properties, but A508 Class 3 has a lower Cr content and a
higher manganese content.
Similarly, in the higher strength, creep-resistant steels, an approximate ranking of their crack susceptibility is as
follows:
5 Cr 1Mo lower risk

2.25Cr 1 Mo ↓
0.5Mo B ↓
0.5Cr 0.5Mo 0.25V higher risk
Thus, in selecting a creep-resistant, chromium molybdenum steel, 0.5Cr 0.5Mo 0.25V steel is known to be susceptible
to reheat cracking but the 2.25Cr 1Mo which has a similar creep resistance, is significantly less susceptible.
Unfortunately, although some knowledge has been gained on the susceptibility of certain steels, the risk of cracking
cannot be reliably predicted from the chemical composition. Various indices, including ΔG1, PSR and Rs, have been
used to indicate the susceptibility of steel to reheat cracking. Steels which have a value of ΔG1 of less than 2, PSR less
than zero or Rs less than 0.03, are less susceptible to reheat cracking
ΔG1 = 10C + Cr + 3.3Mo + 8.1V - 2
PSR = Cr +Cu + 2Mo + 10V +7Nb + 5Ti - 2
Rs = 0.12Cu +0.19S +0.10As + P +1.18Sn + 1.49Sb
Irrespective of the steel type, it is important to purchase steels specified to have low levels of impurity elements
(antimony, arsenic, tin, bismuth, sulphur and phosphorus). To avoid weld metal reheat cracking, it is necessary to
ensure that welding consumables deposit weld metal with appropriately low levels of these impurities, and preferably
to avoid coarse columnar grains. Following several instances of weld metal reheat cracking in thick-wall 2.25%Cr-
1%Mo-0.25%V reactor vessels, impurities in the flux were identified as being responsible for the cracking, and an
equation given for the desired upper limit of these additional impurities.
K = Pb + Bi + 0.03Sb (ppm)
The compositional factor K must be less than 1.5 to achieve freedom from this form of cracking.
Welding procedure and technique
The welding procedure can be used to minimise the risk of reheat cracking by
Producing the maximum refinement of the coarse grain HAZ

Limiting the degree of austenite grain growth
Eliminating stress concentrations
The procedure should aim to refine the coarse grained HAZ by subsequent passes. In butt welds, maximum
refinement can be achieved by using a steep-sided joint preparation with a low angle of attack to minimise
penetration into the side-wall, ( Fig 2a). In comparison, a larger angle V preparation produces a wider HAZ, limiting
the amount of refinement achieved by subsequent passes, ( Fig 2b). Narrow joint preparations, however, are more
difficult to weld, due to the increased risk of lack of side-wall fusion.
Fig.2a. Welding in the flat position - high

degree of HAZ refinement
Fig.2b. Welding in the horizontal/vertical
position - low degree of HAZ refinement
Refinement of the HAZ can be promoted by first buttering the surface of the susceptible plate with a thin weld metal
layer using a small diameter (3.2mm) electrode. The joint is then completed using a larger diameter (4 - 4.8mm)
electrode, which is intended to generate sufficient heat to refine any remaining coarse grained HAZ under the buttered
layer.
The degree of austenite grain growth can be restricted by using a low heat input. However, precautionary measures
may be necessary to avoid the risk of hydrogen-assisted cracking and lack-of-fusion defects. For example, reducing
the heat input will almost certainly require a higher preheat temperature to avoid hydrogen-assisted cracking.
The joint design and welding technique adopted should ensure that the weld is free from localised stress
concentrations which can arise from the presence of notches. Stress concentrations may be produced in the following
situations:
welding with a backing bar

a partial penetration weld leaving a root imperfection
internal weld imperfections such as lack of sidewall fusion
the weld has a poor surface profile, especially sharp weld toes
The weld toes of the capping pass are particularly vulnerable, as the coarse grained HAZ may not have been refined
by subsequent passes. In susceptible steel, the last pass should never be deposited on the parent material, but always
on the weld metal, so that it will refine the HAZ.
Grinding the weld toes with the preheat maintained has been successfully used to reduce the risk of cracking in 0.5Cr
0.5Mo 0.25V steels.
This Job Knowledge article was originally published in Connect, July 2000. It has been updated so the web page no
longer reflects exactly the printed version.

Defects/imperfections in Welds - Reheat Cracking: Identification

Uploaded by

Copyright:

Available Formats

Defects/imperfections in Welds - Reheat Cracking: Identification

Uploaded by

Document Information

Original Description:

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Defects/imperfections in Welds - Reheat Cracking: Identification

Uploaded by

Copyright:

Available Formats

TWI main site Technical Capabilities Industrial Membership Training and Examinations

Accessibility Careers Text Only Site Map Global websites

Defects/imperfections in welds - reheat cracking

The characteristic features and principal causes of reheat

Reheat cracking may occur in low alloy steels containing

Cracking may be in the form of coarse macro-cracks or colonies of micro-cracks.

Fig.1a. Cracking associated with the coarse grained

Best practice in prevention

5 Cr 1Mo lower risk

ΔG1 = 10C + Cr + 3.3Mo + 8.1V - 2

PSR = Cr +Cu + 2Mo + 10V +7Nb + 5Ti - 2

Rs = 0.12Cu +0.19S +0.10As + P +1.18Sn + 1.49Sb

Welding procedure and technique

Producing the maximum refinement of the coarse grain HAZ

Fig.2a. Welding in the flat position - high

welding with a backing bar

You might also like