WPQR No. 2016 02

WELDING PROCEDURE
QUALIFICATION RECORD (WPQR)

WPQR No.: 2016-02 Rev.0 According to: NS-EN ISO 15614-1
Manufacturer: TH RØR-SVEIS AS Place and date of welding: Rygge, 05.07.2016

Project: All Drawing No.:
Requirements beyond standard / Purchasers spec. no.:
Sketch of joint: Material Specification, Delivery Condition:
I: TP316L/ 1.4404/ ASTM A270/ EN 10217-7
Heat no. 0444105, Welded tube, Pickled
II: TP316L/ 1.4404/ ASTM A270/ EN 10217-7
Heat no. 0444105, Welded tube, Pickled
Grade I C, % C eq % Grade II C, % C eq %
TP316L 0,020 NA TP316L 0,020 NA
Diameter and/or thickness, mm: OD 38,0 x WT 1,2
Welding process: 141 – Automatic (Orbital)
Welding position: PK - Rotated
Single-/double sided welding: Single Sided
WELDING CONSUMABLES
Index Consumable(s), trade name and manufacturer Classification
A N/A
WELDING PARAMETERS
Pass Diam. Gas shielding, Gas, Current, Ampere,A Voltage,V Travelspeed Wire feed Heat input
Index
No. mm composition L/min Polarity (Peak/Back) (Peak/Back) mm/min m/min kJ/mm
1 - - 99,998%Ar 14 DC- 35,4 12,7 117 - 0,23
(54,9/15,9) (15,6/9,7)
Program pass No’s. 1: Log no. 25, 27, 31, 33, 35 and 37 ; Pulse freq 3,2/ Pulse width 50
OTHER INFORMATION:
Groove preparation : Machined Weaving, max. : No weaving
Cleaning : Methylated spirits
Gas shielding : Yara Praxair Argon 4.8 (99,998%Ar) Torch angle : 90°
Prepurge 20 sec. and postpurge 20 sec.
Gas backing : Yara Praxair Argon 4.8 (99,998%Ar) Tungsten electrode : WC 20 (grey), Ø 2,4 mm
Pass No. 1: 10-11 L/min Gas cup size : Ø 9 mm
HEAT TREATMENT : Preheat min.: 20°C Interpass max.: N/A PWHT/Ageing: N/A Time, hr(s):
Heating/cooling rate: Others: Digital temp. control
WELDING CARRIED OUT BY: David Axelsson TEST PIECE MARKED: WPQR no. 2016-02, No’s 1-6
VISUAL INSPECTION AND NON-DESTRUCTIVE EXAMINATION:
Visual Inspection: ACCEPTED (IKM) Report No. 120-8919-16-VT-2
Dye Penetrant Inspection: ACCEPTED (IKM) Report No. 120-8919-16-PT-2-REV1
Radiographic Examination: ACCEPTED (IKM) Report No. 120-8919-16-RT-2-REV1
DESTRUCTIVE TESTING AND EXAMINATION: ACCEPTED Test Report No. 024336
TECHNICAL QUERY: N/A
SUPPLEMENTARY INFORMATION: Attachments: Weld Logs, Mat’cert, VT-/PT-/RT-/DT-reports
Welding equipment: Liburdi Dimetrics PTW 160
Certified that test welds prepared, Place and date Oslo, 22.07.2016
welded and tested satisfactorily in
accordance with the requirements of
the code/testing standard indicated
Examiners
above.
name and sign. Jarle Børrud Stamp
Teknologisk Institutt as SK-0746 b
Materials Technology Page 1 of 1
Side 1 av 1
LIBURDI DIMETRICS
CORPORATION
Job Number: Site:
Material: Operator:
Diameter: Wall Thickness:
Electrode Type: Electrode Diameter:
Shielding Gas Type: Shielding Gas Flow:
Backing Gas Type: Backing Gas Flow:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016

HEAD TYPE: 5002V TIME: 11:51:27
LOG NUMBER: 25
WELD NUMBER: 2942
WELD LIMITS
ERROR FAULT VOLTS
PRI AMPS: 160.0 160.0 LOW HIGH
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
SEGMENT SEG SLOPE PULSE PULSE PRI BKG PRI BKG PRI BKG
TIME TIME FREQ WIDTH AMPS AMPS TRAV TRAV VOLTS VOLTS
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 15.9 2,59 2,69 15.5 10.1
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.8 16.0 2,62 2,69 15.1 10.1
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 16.0 2,62 2,67 14.8 10.0
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 16.0 2,62 2,67 14.3 9.9
Liburdi Dimetrics Europe

The Netherlands
LiburdiEurope@liburdi.com www.liburdi.com
file:///F:/TH%20RØR-SVEIS%20AS/ORBITAL%20SVEISEMASKIN/Logg%20Sve... 08.07.2016
Side 1 av 1
LIBURDI DIMETRICS
CORPORATION
Job Number: Site:
Material: Operator:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016

LOG NUMBER: 27
WELD NUMBER: 2944
WELD LIMITS
ERROR FAULT VOLTS
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 16.0 2,59 2,69 15.6 10.2
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.9 16.0 2,59 2,69 15.2 10.1
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 16.0 2,59 2,69 14.8 10.1
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 16.0 2,59 2,69 14.3 10.0

The Netherlands
Side 1 av 1
LIBURDI DIMETRICS
CORPORATION
Job Number: Site:
Material: Operator:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016

LOG NUMBER: 31
WELD NUMBER: 2948
WELD LIMITS
ERROR FAULT VOLTS
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 16.0 2,59 2,69 15.5 10.1
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.9 16.0 2,59 2,69 15.2 10.1
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 16.0 2,59 2,69 14.8 10.0
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 16.0 2,59 2,69 14.3 9.9

The Netherlands
Side 1 av 1
LIBURDI DIMETRICS
CORPORATION
Job Number: Site:
Material: Operator:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016

LOG NUMBER: 33
WELD NUMBER: 2950
WELD LIMITS
ERROR FAULT VOLTS
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 16.0 2,59 2,69 15.4 10.0
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.9 16.0 2,59 2,69 15.1 10.0
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 16.0 2,59 2,69 14.7 9.9
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 16.0 2,62 2,67 14.3 9.9

The Netherlands
Side 1 av 1
LIBURDI DIMETRICS
CORPORATION
Job Number: Site:
Material: Operator:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016

LOG NUMBER: 35
WELD NUMBER: 2952
WELD LIMITS
ERROR FAULT VOLTS
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 15.9 2,59 2,69 15.5 10.0
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.9 15.9 2,59 2,69 15.1 10.0
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.8 15.9 2,59 2,69 14.7 9.8
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 15.9 2,62 2,67 14.2 9.7

The Netherlands
Side 1 av 1
LIBURDI DIMETRICS
CORPORATION
Job Number: Site:
Material: Operator:
QA REPORT
SCHED ID: 3800 DATE: 5/7/2016

LOG NUMBER: 37
WELD NUMBER: 2954
WELD LIMITS
ERROR FAULT VOLTS
BKG AMPS: 160.0 160.0 6.0 50.0
TRAVEL: 25,4 25,4
1 16.7 0.0 3.2 50 54.7 16.4 2,66 2,66
16.7 54.9 15.9 2,59 2,69 15.5 10.0
2 14.3 0.0 3.2 50 52.7 16.4 2,66 2,66
14.3 52.8 15.9 2,59 2,69 15.1 9.9
3 14.3 0.0 3.2 50 50.6 16.4 2,66 2,66
14.3 50.7 15.9 2,59 2,69 14.7 9.9
4 15.9 0.0 3.2 50 48.5 16.4 2,66 2,66
15.9 48.7 15.9 2,59 2,69 14.3 9.8

The Netherlands

VT
CLIENT / KUNDE CLIENT O.NO / KUNDE O.NR DATE OF TESTING / KONTROLLDATO REPORT NO. / RAPPORT NR. PAGE / SIDE
TH Rør-Sveis AS WPQR 12/7-2016 2016-07-12 120-8919-16-VT-2 1 of/av 1
DRAWING NO. / TEGNING NO. PLACE OF WORK / KONTROLLSTED OPERATOR / OPERATØR ATTACHMENT / VEDLEGG
- Larvik Kjartan Sundet 0
OBJECT / KONTROLL AV
WPQRno. 2016-02
PROCEDURE / PROSEDYRE REV EXTENT OF TESTING / KONTROLLOMFANG ACCEPTANCE STANDARD / AKSEPTSTANDARD

BPI-01.01.01 ISO 17637 100% ISO 15614-1
COMMENTS / KOMMENTARER
VT inspection was done on pipe nr: 1-2-3-4-5 and 6.
Accepted according to standard
REPAIRS MARKED ON / REPARASJONER AVMERKET PÅ

OBJECT / OBJEKT SKETCH / SKISSE
N3 NAME CERT. NO. / N3 NAVN SERT. NR. N2 NAME CERT. NO. / N2 NAVN SERT. NR. OPERATOR NAME CERT. NO. / OPERATØR NAVN SERT. NR.
() Kjartan Sundet (8900) Kjartan Sundet (8900)
APPROVED / GODKJENT DATO: APPROVED / GODKJENT DATO:2016-07-12 OPERATOR / OPERATØR DATO:2016-07-12
Approved / Godkjent

PT
TH Rør-Sveis AS WPQR 12/7-2016 2016-07-12 120-8919-16-PT-2-REV1 1 of/av 1
WPQR no. 2016-02

EN ISO 3452-1 100% EN-ISO 15614-1
MATERIAL TYPE / MATERIALTYPE SURFACE / OVERFLATE GROOVE / FUGEGEOMETRI WELDING PROCESS / SVEISEPROSESS
SS Som sveist BW N/A
PENETRANT TYPE / PENETRANTTYPE FLUORRESCENT / FLUORISERENDE APPLICATION METHOD / PÅFØRINGSMETODE
Bycotest YES / JA ✔ NO / NEI Spray
BATCH / PARTI 140405
CLEANER TYPE / FJERNER TYPE
Bycotest WATER / VANN EMULSIFIER / EMULGATOR ✔ SOLVENT / LØSNINGSMIDDEL
DEVELOPER TYPE/ FREMKALLER TYPE
Bycotest D 30 A 1. DRY POWDER / TØRRPULVER 3. SUSPENSION IN WATER / OPPSLEMMET I VANN
BATCH / PARTI 140707 2. SOLUTION IN WATER / OPPLØST I VANN ✔ 4. POWDER IN VOLATILE SOLVENT / PULVER I FLYKTIG VÆSKE (SPRAY)
PENETRATION TIME / PENETRERINGSTID DEVELOPING TEST TIME / FREMKALLINGSTID OBJECT TEMPERATURE /
20 MIN. 20 MIN. OBJEKTTEMPERATUR
20 °C
MATERIAL DIMENSION / MATERIAL DIMENSJON
38X1,2
EQUIPMENT / UTSTYR
BRUSH
TEST RESULTS - REMARKS / RESULTATER - BEMERKNINGER
PT was done on pipe nr 1-2-3-4-5 and 6
no indication was found during the test.

N3 NAME CERT. NO. / N3 NAVN SERT. NR. N2 NAME CERT. NO. / N2 NAVN SERT. NR. OPERATOR NAME CERT. NO. / OPERATØR NAVN SERT. NR.
() Kjartan Sundet (8900) Kjartan Sundet (8900)
Approved / Godkjent

RT
TH Rør-Sveis AS WPQR 12/7-2016 2016-07-12 120-8919-16-RT-2-REV1 1 of/av 1
WPQR no. 2016-02

BPI-01.08.03 RT ISO 17636 100% EN-ISO-15614-1
MATERIAL TYPE / MATERIALTYPE SURFACE / OVERFLATE GROOVE / FUGEGEOMETRI WELDING PROCESS / SVEISEPROSESS
SS Som sveist BW Ingen
EQUIPMENT / UTSTYR EQUIPMENT / UTSTYR
X-RAY TUBE / RØNTGENRØR ISOTOPE / ISOTOP
CP 100 KV Ir 192 Co 60 Se 75 Yt 169 Ingen
FOCAL SPOT SIZE / BRENNFLEKK ACTIVITY / AKTIVITET
3,0x3,0 Gbq,Ci
A B C D I.Q.I SOURCE SIDE/KILDE SIDE RADIATION SOURCE POSITION / KILDEPOSISJON
TECHNIQUE / TEKNIKK
TUBE/RØR VOLT kV SOURCE SIDE/KILDESIDE
1 2 3 4 5 6 7
FILMFOCUS DISTANCE
✔ FILM SIDE /FILMSIDE
EXP. DATA /
FILMFOKUS AVSTAND mm
440
EKS. DATA
EXP.TIME/ TYPE OF I.Q.I. / I.Q.I. TYPE
EKSP. TIME mAmin. Cimin.
3mAmin
W 13 FE
DENSITY / SVERTNING Ug INTENSIFYING SCREENS / FOILER FILM TYPE / FILMTYPE

2,5-3,7 0,2 0,027 D3
WELD NO DATE AND TIME DIA. PIPE FILM LOCATION SENSITIVITY WELDER MATERIAL EVALUATION DEFECT LOCATION REMARKS EXP. TECH.
SVEIS NR DATO KL. DIA RØR FILM PLASSERING FØLSOMHET SVEISER THICKNESS BEDØMMELSE FEILENS PLASSERING BEMERKNINGER DATA TEGN.
% TYKKELSE A-D 1-7
WIRE NR mm
1 12/7-2016 38mm ABC W17 1,2 Accepted A 4

NS-EN ISO 6520-1:2007

Kolonne gir et tresifret referansenummer for hovedgruppen av uregelmessigheten og et firesifret referansenummer for undergrupper. Colum gives a three – figure reference number for the main
group of the imperfection and a four–figure reference number for sub–terms.
Referanse no: - Reference No:
100/1000=Sprekk - Crack 200/2000=Hulrom - Cavity 300/3000=Fast inneslutting - Solid inclusion 400/4000=Bindefeil og manglende gjennomsveising - Lack of fusion and penetration
500/5000=Uregelmessig form - Imperfect shape 600/6000=Andre uregelmessigheter - Miscellaneous imperfection.
COMMENTS / KOMMENTARER
.

N3 NAME CERT. NO. / N3 NAVN SERT. NR. N2 NAME CERT. NO. / N2 NAVN SERT. NR. OPERATOR NAME CERT. NO. / OPERATØR NAVN SERT.
() Kjartan Sundet (8900) NR.
Kjartan Sundet (8900)
Approved /Godkjent
TEST 006
MATERIAL TESTING Report No.: 024336

Page 1 of 3
Client : TH RØR-SVEIS AS Material : I/II: TP316L/ 1.4404/ ASTM A270/ EN

10217-7 - Heat no: 0444105
Augerødveien 15 Other details: Welded tube, Pickled
1591 Sperrebotn
Client Contact : Torgeir Hansen Dimensions : I/II: OD 38,00mm x WT 1,20mm
Order No. : Other Info : WPQR no. 2016-02

Specification : NS-EN ISO 15614-1 141-Automatic (Orbital), Butt weld
Sampling by TI: No
Uncertainty is given upon request Applicable tests: Chemical / Tensile / Charpy Impact / Hardness
(whichever tested)
Accredited test: Vickers hardness test NS-EN ISO 6507-1:2006
Table 1 Tensile test
CROSS-WELD TENSILE TEST acc. to: NS-EN ISO 6892-1:2009 method B

Rate of stressing: 10 MPa/s
Test Dimension So Fmax Rm Remarks
Ident (mm) mm 2 N MPa
1 of 2 Full-size specimen 138.73 76.85 554 Fracture in WM
2 of 2 Full-size specimen 138.73 76.41 551 Fracture in WM
Requirements: At ambient temp. min. NA 490
max. NA 690
LC = 200 mm
Date Test Responsible Authorized Signature
21.07.2016
Petter Dyrnes Department Manager
Copying of this report is only authorised when copied in its complete form. Eventual test results apply only for the tested objects. SK-0750 c
Teknologisk Institutt as
Postadresse: Telefon: 22 86 50 00 Org.nr. 942 340 680 Kongsberg: Pb. 1019, NO-3601 Kongsberg
Pb. 141 Økern Telefaks: 22 72 45 02 Stavanger: Forusbeen 10, NO-4033 Stavanger
0509 Oslo Haugesund: Pb. 93, NO-4299 Avaldsnes
Besøksadresse: E-post: firmapost@ti.no Bergen: Pb. 23, NO-5346 Ågotnes
Kabelgaten 2, 0580 Oslo Web: www.teknologisk.no
21.07.2016

Page 2 of 3
Table 2 Bend test
BEND TEST acc. to: NS-EN ISO 5173:2010

Transverse Bend Test / Testing with a former
Test Dimensions Bending Former Distance Results
Ident. mm Angle Diameter, between Comments
mm Rollers, mm
Face 1 5.0 x 1.20 180 4.8 9.3 Accepted
Face 2 5.0 x 1.20 180 4.8 9.3 Accepted
Root 1 5.0 x 1.20 180 4.8 9.3 Accepted
Root 2 5.0 x 1.20 180 4.8 9.3 Accepted
Table 3 Hardness test
CROSS-SECTION HARDNESS TEST acc. to: NS-EN ISO 9015-1:2011 / NS-EN ISO 6507-1:2006
Test Method: Vickers, HV5
Indentations 6 and 10, close to fusion line
BM HAZ WM HAZ BM
◇◇◇ ◇◇◇ ◇◇◇ ◇◇◇ ◇◇◇
1/2/3 4/5/6 7/8/9 10 / 11 / 12 13 / 14 / 15
RESULTS, HV5:
BM HAZ WM HAZ BM
1 223 4 186 7 170 10 166 13 209
Mid-
2 220 5 178 8 171 11 183 14 212
thickness
3 221 6 156 9 169 12 188 15 210
Requirements: NA
21.07.2016

Page 3 of 3
Table 4 Macro
MACROSTRUCTURE acc. to: NS-EN ISO 17639:2013 / ASTM E3-11/E340-13/NS-EN ISO

5817:2014
One (1) cross-section of the weld metal, heat affected zone and base metal was carried out and
prepared. The macro-section was examined up to 20X magnifications.
Etchant: Kallings
OBSERVATIONS: The macro satisfies the specified requirements.
MACRO 1
1 division = 1 mm

WPQR No. 2016 02

Uploaded by

Copyright:

Available Formats

WPQR No. 2016 02

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

WPQR No. 2016 02

Uploaded by

Copyright:

Available Formats

WELDING PROCEDURE

QUALIFICATION RECORD (WPQR)

Manufacturer: TH RØR-SVEIS AS Place and date of welding: Rygge, 05.07.2016

Diameter: Wall Thickness:

Electrode Type: Electrode Diameter:

Shielding Gas Type: Shielding Gas Flow:

Backing Gas Type: Backing Gas Flow:

SCHED ID: 3800 DATE: 5/7/2016

Liburdi Dimetrics Europe

Diameter: Wall Thickness:

Electrode Type: Electrode Diameter:

Shielding Gas Type: Shielding Gas Flow:

Backing Gas Type: Backing Gas Flow:

SCHED ID: 3800 DATE: 5/7/2016

Liburdi Dimetrics Europe

Diameter: Wall Thickness:

Electrode Type: Electrode Diameter:

Shielding Gas Type: Shielding Gas Flow:

Backing Gas Type: Backing Gas Flow:

SCHED ID: 3800 DATE: 5/7/2016

Liburdi Dimetrics Europe

Diameter: Wall Thickness:

Electrode Type: Electrode Diameter:

Shielding Gas Type: Shielding Gas Flow:

Backing Gas Type: Backing Gas Flow:

SCHED ID: 3800 DATE: 5/7/2016

Liburdi Dimetrics Europe

Diameter: Wall Thickness:

Electrode Type: Electrode Diameter:

Shielding Gas Type: Shielding Gas Flow:

Backing Gas Type: Backing Gas Flow:

SCHED ID: 3800 DATE: 5/7/2016

Liburdi Dimetrics Europe

Diameter: Wall Thickness:

Electrode Type: Electrode Diameter:

Shielding Gas Type: Shielding Gas Flow:

Backing Gas Type: Backing Gas Flow:

SCHED ID: 3800 DATE: 5/7/2016

Liburdi Dimetrics Europe

PROCEDURE / PROSEDYRE REV EXTENT OF TESTING / KONTROLLOMFANG ACCEPTANCE STANDARD / AKSEPTSTANDARD

Accepted according to standard

REPAIRS MARKED ON / REPARASJONER AVMERKET PÅ

PROCEDURE / PROSEDYRE REV EXTENT OF TESTING / KONTROLLOMFANG ACCEPTANCE STANDARD / AKSEPTSTANDARD

no indication was found during the test.

REPAIRS MARKED ON / REPARASJONER AVMERKET PÅ

PROCEDURE / PROSEDYRE REV EXTENT OF TESTING / KONTROLLOMFANG ACCEPTANCE STANDARD / AKSEPTSTANDARD

DENSITY / SVERTNING Ug INTENSIFYING SCREENS / FOILER FILM TYPE / FILMTYPE

1 12/7-2016 38mm ABC W17 1,2 Accepted A 4

NS-EN ISO 6520-1:2007

REPAIRS MARKED ON / REPARASJONER AVMERKET PÅ

MATERIAL TESTING Report No.: 024336

Client : TH RØR-SVEIS AS Material : I/II: TP316L/ 1.4404/ ASTM A270/ EN

Order No. : Other Info : WPQR no. 2016-02

Accredited test: Vickers hardness test NS-EN ISO 6507-1:2006

Table 1 Tensile test

CROSS-WELD TENSILE TEST acc. to: NS-EN ISO 6892-1:2009 method B

Date Test Responsible Authorized Signature

MATERIAL TESTING Report No.: 024336

Table 2 Bend test