42 CR Mo 4
42 CR Mo 4
42CrMo4
According to standards
Number
EN 10083-3: 2006
1.7225
Lucefin Group
Chemical composition
C%
Si%
Mn%
P%
S%
Cr%
max
max
max
0,38-0,45
0,40
0,60-0,90
0,025
0,035
0,90-1,20
0.02
+ 0.03
0.04
+ 0.005
+ 0.005
0.05
42CrMoS4 n 1.7227 S% 0.020-0.040 permissible deviations on the product + 0.005
Calcium (Ca) treatment may be supplied on request. 42CrMo4Pb Lead 0.15 0.35%
Mo%
Permissible deviations
on the product
0,15-0,30
0.03
Temperature C
Hot forming
Normalizing
1100-850
870
air (HB ~ 190)
Soft
Isothermal
annealing
annealing
720 slowly 15 C/h 820 furnace cooling
until 600 after air to 670 after, air
(HB max 241)
(HB 180-240)
Quenching
Quenching
860
850
oil or polymer water
Spheroidizing End quench
hardenability test
730-740
840
furnace cooling water
Tempering
Stress relieving
550-650
air
Preheating
welding
300
AC1
AC3
745
790
362
39
1220
1110
13.5
42
550
336
36
1100
1000
15.8
75
600
294
31
980
870
19.0
114
650
264
27
880
710
21.5
135
700
2 50
100
2 40
2 30
95
90
2 20
2 10
2 00
85
190
180
75
80
70
170
160
65
150
60
140
55
130
50
120
110
45
100
40
90
35
80
30
70
60
25
50
40
20
15
30
10
20
10
0
-80
Temperature c
-6 0
-4 0
-20
20
Cleavagearea%
values
595
57
2200
1520
-24
100
Joule
Table of tempering
HB
HRC
R
N/mm2
Rp 0.2 N/mm2
A
%
Kv
J
Tempering at C
Lucefin Group
HB
max
300
290
285
280
280
HB
min
225
213
178
size mm
HB
A%
min Q
----
Kv +20 C
J min L
30
27
22
Kv +20 C
J min T
16
14
12
Tempering to 620 C
< 200
> 200 < 400
260
250
> 400
230
1.5
11
13
15
20
25
30
35
40
45
50
53
61
53
61
52
61
51
60
49
60
43
59
40
59
37
58
34
56
32
53
31
51
30
48
30
47
29
46
29
45
Temperature
Testing at C
-100
0
20
100
200
300
400
500
600
Density +20 C
Kg/dm3
7.85
EUROPE EN
42CrMo4
Mod. of elasticity
E long.
N/mm2
217000
213000
212000
207000
199000
192000
184000
175000
164000
Thermal
expansion
[(m/mK) 10-6 C-1 ]
10.5
11.4
11.5
12.1
12.7
13.2
13.6
14.0
14.4
Specific heat
capacity
J/(KgK)
423
456
461
479
499
517
536
558
587
Specific electric
resistivity
Ohmmm2/m
--0.231
0.284
0.358
0.448
0.552
0.671
0.806
----
H
normal
Thermal
conductivity
W/(mK)
--45.1
45.1
44.1
41.9
39.4
36.9
34.4
CHINA
ML42CrMo
GERMANY DIN
42CrMo4
FRANCE AFNOR
42CD4
U.K. B.S.
708M40
RUSSIA
38ChM
USA AISI/SAE
4140