    Quality 11Smn30: Lucefin Group

    Uploaded by

    Paulo Zechin
    The document provides information on the chemical composition, mechanical properties, heat treatment temperatures, and standards for steel grade 11SMn30. Key points include: - The chemical composition limits for carbon, silicon, manganese, phosphorus, sulfur, and lead. - Mechanical properties for various sizes and conditions including hot rolled, cold drawn, and hot rolled peeled reeled. Properties include tensile strength, yield strength, elongation and hardness. - Recommended heat treatment temperatures for processes like hot forming, annealing, carburizing and hardening.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Quality 11Smn30: Lucefin Group

    Uploaded by

    Paulo Zechin
    154 views1 page
    The document provides information on the chemical composition, mechanical properties, heat treatment temperatures, and standards for steel grade 11SMn30. Key points include: - The chemical composition limits for carbon, silicon, manganese, phosphorus, sulfur, and lead. - Mechanical properties for various sizes and conditions including hot rolled, cold drawn, and hot rolled peeled reeled. Properties include tensile strength, yield strength, elongation and hardness. - Recommended heat treatment temperatures for processes like hot forming, annealing, carburizing and hardening.

    Original Description:

    Composição química 11SMn30

    Original Title

    11SMn30

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    The document provides information on the chemical composition, mechanical properties, heat treatment temperatures, and standards for steel grade 11SMn30. Key points include: - The chemical composition limits for carbon, silicon, manganese, phosphorus, sulfur, and lead. - Mechanical properties for various sizes and conditions including hot rolled, cold drawn, and hot rolled peeled reeled. Properties include tensile strength, yield strength, elongation and hardness. - Recommended heat treatment temperatures for processes like hot forming, annealing, carburizing and hardening.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    154 views1 page

    Quality 11Smn30: Lucefin Group

    Uploaded by

    Paulo Zechin
    The document provides information on the chemical composition, mechanical properties, heat treatment temperatures, and standards for steel grade 11SMn30. Key points include: - The chemical composition limits for carbon, silicon, manganese, phosphorus, sulfur, and lead. - Mechanical properties for various sizes and conditions including hot rolled, cold drawn, and hot rolled peeled reeled. Properties include tensile strength, yield strength, elongation and hardness. - Recommended heat treatment temperatures for processes like hot forming, annealing, carburizing and hardening.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    Quality 11SMn30

    According to standards EN 10087: 2000 Lucefin Group


    Number 1.0715
    Chemical composition
    C% Si% Mn% P% S% Pb%
    max max max
    0,14 0,05 0,90-1,30 0,11 0,27-0,33 -- Permissible deviations
    ± 0.02 + 0.01 ± 0.04 + 0.02 ± 0.03 -- on the product
    Temperature °C
    Hot forming Natural forming Soft annealing Carburizing Hardening on Stress relieving
    condition carburized surface
    1250-950 -- 680 (880-950) (770-810) (180-200)
    air
    Preheating Stress relieving
    welding after welding
    Normalizing Core Core Stress not recommended
    hardening hardening relieving
    900 880 890 oil or 150-200 AC1 AC3 MS Mf
    air water polymer furnace cooling -- -- -- --

    Mechanical properties
    Hot-rolled natural forming condition EN 10087: 2000 Hot rolled quenched and tempered
    Testing at room temperature (longitudinal)
    size mm R HB R Rp 0.2 A% HB
    over to N/mm2 for information N/mm2 N/mm2 min min
    5 10 380-570 112-169
    10 16 380-570 112-169 Not suitable for heat treatment
    16 40 380-570 112-169
    40 63 370-570 109-169
    63 100 360-520 107-154
    Cold drawn +C EN 10277-3: 2008 Hot rolled Peeled Reeled +SH
    Values valid also for +C+SL Values valid also for +SH+SL
    size Testing at room temperature (longitudinal) Testing at room temperature (longitudinal)
    mm R a) Rp 0.2 a) A% HB R Rp 0.2 A% HB
    over to N/mm 2 N/mm2 min min for inform. N/mm2 N/mm2 min min
    5 b) 10 510-810 440 6 154-243 -- -- -- --
    10 16 490-760 410 7 149-226 -- -- -- --
    16 40 460-710 375 8 139-218 380-570 -- -- 112-169
    40 63 400-650 305 9 119-200 370-570 -- -- 112-169
    63 100 360-630 245 9 104-192 360-520 -- -- 107-154
    a) for flats and special sections yield point can be – 10% and tensile strenght can be ± 10%
    b) for thickness below 5 mm mechanical properties can be agreed before order placement

    EUROPE EN ITALY UNI CHINA GERMANY DIN FRANCE AFNOR U.K. B.S. RUSSIA USA AISI/SAE
    11SMn30 CF 9SMn28 -- 9SMn28 S250 230M07 -- 1214