Steel Type : Quenched and Tempered Steel

Steel Grade: 35CrMo

Property Entry Summary

Steel Grade 35CrMo

Steel Classification Quenched and Tempered Steel

General Steel Grade Comparison, Chemical Composition

Critical temperature, Normalizing,


Heat Treatment Parameter
Quenching ,Tempering

Continuous Cooling Transformation Curve,


Transformation Curve Temperature Time Transformation Curve, Phase
Equilibrium Transformation

General
Steel Grade Comparison

Soviet Union The USA French Japan West Germany

(ΓOCT) (AISI) (NF) (JIS) (DIN)

35XM 4135 35CD4 SCM3 34CrMo4

Chemical Composition (%)

C Si Mn P S Mo Cr Cu

0.32~0.40 0.20~0.40 0.4~0.7 ≤0.04 ≤0.04 0.15~0.25 0.8~1.1 ≤0.30

Reference
[1] Zeng Zhengming.The Handbook of Practical Steel Materials [M]. Electricity Press of
China,2005:232-279,310-453,501-512.
[2] Hu Zhizhong.The Handbook of Steel and Its Heat Treatment Curve.Beijing:
Defence Industry Press,1987.
[3] Lin Huiguo, Lin Gang.The Handbook of Steel Grade [M] .Beijing:Mechanical
Industry Press,1993:9-71,241-262.
Heat Treatment Parameter
Critical Temperature and Heat Treatment Condition
Critical
Temperature Heat Treatment Condition
(oC)
Ac1 Ac3 Ar1 Ar3 Normalizing Quenching Tempering

755 800 695 750 Temperature Temperature Cooling HRC Temperature HRC
o o o
( C) ( C) agents ( C)

830~860 820~850 Water 52~56 520~560 35~30

oil

Reference

[4] Hu Guangli.Heat Treatment of Steels.Beijing :Defence Industry Press,1985.


[5] Bao Xintao.Practical Handbook of Heat Treatment of Steel .Shanghai:Science and

Technology Press of Shanghai,2009.


Transformation Curves
Continuous Cooling Transformation (CCT) Curve

C Si Mn Cr Mo
Element (wt%)
0.38 0.23 0.64 0.99 0.16

Grain size -----

Austenitizing temperature (oC) 860

Reference
[6] Hu Zhizhong.The Handbook of Steel and Its Heat Treatment Curve.Beijing:
Defence Industry Press,1987.
Temperature Time Transformation (TTT) Curve

C Si Mn Cr Mo
Element (wt%)
0.33 0.27 0.53 0.90 0.18

Grain size 9~10

Austenitizing temperature (oC) 843

Reference
[8] H. Yu, S.G. Mhaisalkar. Time–temperature transformation (TTT) cure diagram of a
fast cure non-conductive adhesive, Thin Solid Films 504 (2006) 331 – 335.
[9] Hu Zhizhong.The Handbook of Steel and Its Heat Treatment Curve.Beijing:
Defence Industry Press,1987.
Equilibrium Phase Transformation (EPT) Curve

C Si Mn Cr Mo
Element (wt%)
0.36 0.30 0.55 0.95 0.20

Phases considered Liquid, Fcc, Bcc, M3C2, M7C3,Cementite;

Phases rejected Dia,Graph,Fech_chi,Fe4n_1p1;

Calculation condition P=105Pa, N=1mole

Database TCFE3

Software package Thermo-Calc

Remarks
[10] Sundman B, Jansson B, Andersson J-O. The Thermo-Calc databank system.
Calphad, 1985,9:153-190.