Preservation of the High Quality Factor and Accelerating Gradient of Nb3Sn-coated Cavity During Pair Assembly
Authors:
G. Eremeev,
U. Pudasaini,
S. Cheban,
J. Fischer,
D. Forehand,
S. Posen,
A. Reilly,
R. Rimmer,
B. Tennis
Abstract:
Two CEBAF 5-cell accelerator cavities have been coated with Nb3Sn film using the vapor diffusion technique. One cavity was coated in the Jefferson Lab Nb3Sn cavity coating system, and the other in the Fermilab Nb3Sn coating system. Both cavities were measured at 4 K and 2 K in the vertical dewar test in each lab and then assembled into a cavity pair at Jefferson Lab. Previous attempts to assemble…
▽ More
Two CEBAF 5-cell accelerator cavities have been coated with Nb3Sn film using the vapor diffusion technique. One cavity was coated in the Jefferson Lab Nb3Sn cavity coating system, and the other in the Fermilab Nb3Sn coating system. Both cavities were measured at 4 K and 2 K in the vertical dewar test in each lab and then assembled into a cavity pair at Jefferson Lab. Previous attempts to assemble Nb3Sn cavities into a cavity pair degraded the superconducting properties of Nb3Sn-coated cavities. This contribution discusses the efforts to identify and mitigate the pair assembly challenges and will present the results of the vertical tests before and after pair assembly. Notably, one of the cavities reached the highest gradient above 80 mT in the vertical test after the pair assembly.
△ Less
Submitted 17 July, 2023;
originally announced July 2023.
-
First Results from Nb3Sn Coatings of 2.6 GHz Nb SRF Cavities Using DC Cylindrical Magnetron Sputtering System
Authors:
M. S. Shakel,
H. E. Elsayed-Ali,
G. Eremeev,
U. Pudasaini,
A. M. Valente-Feliciano
Abstract:
A DC cylindrical magnetron sputtering system has been commissioned and operated to deposit Nb3Sn onto 2.6 GHz Nb SRF cavities. After optimizing the deposition conditions in a mock-up cavity, Nb-Sn films are deposited first on flat samples by multilayer sequential sputtering of Nb and Sn, and later annealed at 950 °C for 3 hours. X-ray diffraction of the films showed multiple peaks for the Nb3Sn ph…
▽ More
A DC cylindrical magnetron sputtering system has been commissioned and operated to deposit Nb3Sn onto 2.6 GHz Nb SRF cavities. After optimizing the deposition conditions in a mock-up cavity, Nb-Sn films are deposited first on flat samples by multilayer sequential sputtering of Nb and Sn, and later annealed at 950 °C for 3 hours. X-ray diffraction of the films showed multiple peaks for the Nb3Sn phase and Nb (substrate). No peaks from any Nb3Sn compound other than Nb3Sn were detected. Later three 2.6 GHz Nb SRF cavities are coated with ~1 $μ$m thick Nb3Sn. The first Nb3Sn coated cavity reached close to Eacc = 8 MV/m, demonstrating a quality factor Q0 of 3.2 x 108 at Tbath = 4.4 K and Eacc = 5 MV/m, about a factor of three higher than that of Nb at this temperature. Q0 was close to 1.1 x 109, dominated by the residual resistance, at 2 K and Eacc = 5 MV/m. The Nb3Sn coated cavities demonstrated Tc in the range of 17.9 - 18 K. Here we present the commissioning experience, system optimization, and the first results from the Nb3Sn fabrication on flat samples and SRF cavities.
△ Less
Submitted 17 July, 2023;
originally announced July 2023.
-
First Results From Nanoindentation of Vapor Diffused Nb3Sn Films on Nb
Authors:
U. Pudasaini,
G. V. Eremeev,
S. Cheban
Abstract:
The mechanical vulnerability of the Nb3Sn-coated cavities is identified as one of the significant technical hurdles toward deploying them in practical accelerator applications in the not-so-distant future. It is crucial to characterize the material's mechanical properties in ways to address such vulnerability. Nanoindentation is a widely used technique for measuring the mechanical properties of th…
▽ More
The mechanical vulnerability of the Nb3Sn-coated cavities is identified as one of the significant technical hurdles toward deploying them in practical accelerator applications in the not-so-distant future. It is crucial to characterize the material's mechanical properties in ways to address such vulnerability. Nanoindentation is a widely used technique for measuring the mechanical properties of thin films that involves indenting the film with a small diamond tip and measuring the force-displacement response to calculate the film's elastic modulus, hardness, and other mechanical properties. The nanoindentation analysis was performed on multiple vapor-diffused Nb3Sn samples coated at Jefferson Lab and Fermilab coating facilities for the first time. This contribution will discuss the first results obtained from the nanoindentation of Nb3Sn-coated Nb samples prepared via the Sn vapor diffusion technique.
△ Less
Submitted 17 July, 2023;
originally announced July 2023.
-
Development of a prototype superconducting radio-frequency cavity for conduction-cooled accelerators
Authors:
G. Ciovati,
J. Anderson,
S. Balachandran,
G. Cheng,
B. Coriton,
E. Daly,
P. Dhakal,
A. Gurevich,
F. Hannon,
K. Harding,
L. Holland,
F. Marhauser,
K. McLaughlin,
D. Packard,
T. Powers,
U. Pudasaini,
J. Rathke,
R. Rimmer,
T. Schultheiss,
H. Vennekate,
D. Vollmer
Abstract:
The higher efficiency of superconducting radio-frequency (SRF) cavities compared to normal-conducting ones enables the development of high-energy continuous-wave linear accelerators (linacs). Recent progress in the development of high-quality Nb$_3$Sn film coatings along with the availability of cryocoolers with high cooling capacity at 4 K makes it feasible to operate SRF cavities cooled by therm…
▽ More
The higher efficiency of superconducting radio-frequency (SRF) cavities compared to normal-conducting ones enables the development of high-energy continuous-wave linear accelerators (linacs). Recent progress in the development of high-quality Nb$_3$Sn film coatings along with the availability of cryocoolers with high cooling capacity at 4 K makes it feasible to operate SRF cavities cooled by thermal conduction at relevant accelerating gradients for use in accelerators. A possible use of conduction-cooled SRF linacs is for environmental applications, requiring electron beams with energy of $1 - 10$ MeV and 1 MW of power. We have designed a 915 MHz SRF linac for such an application and developed a prototype single-cell cavity to prove the proposed design by operating it with cryocoolers at the accelerating gradient required for 1 MeV energy gain. The cavity has a $\sim 3$ $μ$m thick Nb$_3$Sn film on the inner surface, deposited on a $\sim4$ mm thick bulk Nb substrate and a bulk $\sim7$ mm thick Cu outer shell with three Cu attachment tabs. The cavity was tested up to a peak surface magnetic field of 53 mT in liquid He at 4.3 K. A horizontal test cryostat was designed and built to test the cavity cooled with three Gifford-McMahon cryocoolers. The rf tests of the conduction-cooled cavity, performed at General Atomics, achieved a peak surface magnetic field of 50 mT and stable operation was possible with up to 18.5 W of rf heat load. The peak frequency shift due to microphonics was 23 Hz. These results represent the highest peak surface magnetic field achieved in a conduction-cooled SRF cavity to date and meet the requirements for a 1 MeV energy gain.
△ Less
Submitted 22 March, 2023; v1 submitted 14 February, 2023;
originally announced February 2023.
-
Next-Generation Superconducting RF Technology based on Advanced Thin Film Technologies and Innovative Materials for Accelerator Enhanced Performance and Energy Reach
Authors:
A. - M. Valente-Feliciano,
C. Antoine,
S. Anlage,
G. Ciovati,
J. Delayen,
F. Gerigk,
A. Gurevich,
T. Junginger,
S. Keckert,
G. Keppe,
J. Knobloch,
T. Kubo,
O. Kugeler,
D. Manos,
C. Pira,
T. Proslier,
U. Pudasaini,
C. E. Reece,
R. A. Rimmer,
G. J. Rosaz,
T. Saeki,
R. Vaglio,
R. Valizadeh,
H. Vennekate,
W. Venturini Delsolaro
, et al. (3 additional authors not shown)
Abstract:
Superconducting RF is a key technology for future particle accelerators, now relying on advanced surfaces beyond bulk Nb for a leap in performance and efficiency. The SRF thin film strategy aims at transforming the current SRF technology by using highly functional materials, addressing all the necessary functions. The community is deploying efforts in three research thrusts to develop next-generat…
▽ More
Superconducting RF is a key technology for future particle accelerators, now relying on advanced surfaces beyond bulk Nb for a leap in performance and efficiency. The SRF thin film strategy aims at transforming the current SRF technology by using highly functional materials, addressing all the necessary functions. The community is deploying efforts in three research thrusts to develop next-generation thin-film based cavities. Nb on Cu cavities are developed to perform as good as or better than bulk Nb at reduced cost and with better thermal stability. Recent results showing improved accelerating field and dramatically reduced Q slope show their potential for many applications. The second research thrust is to develop cavities coated with materials that can operate at higher temperatures or sustain higher fields. Proof of principle has been established for the merit of Nb3Sn for SRF application. Research is now needed to further exploit the material and reach its full potential with novel deposition techniques. The third line of research is to push SRF performance beyond the capabilities of the superconductors alone with multilayered coatings. In parallel, developments are needed to provide quality substrates, cooling schemes and cryomodule design tailored to thin film cavities. Recent results in these three research thrusts suggest that SRF thin film technologies are at the eve of a technological revolution. For them to mature, active community support and sustained funding are needed to address fundamental developments supporting material deposition techniques, surface and RF research, technical challenges associated with scaling and industrialization. With dedicated and sustained investment, next-generation thin-film based cavities will become a reality with high performance and efficiency, facilitating energy sustainable science while enabling higher luminosity, and higher energy.
△ Less
Submitted 5 April, 2022;
originally announced April 2022.
-
Key directions for research and development of superconducting radio frequency cavities
Authors:
S. Belomestnykh,
S. Posen,
D. Bafia,
S. Balachandran,
M. Bertucci,
A. Burrill,
A. Cano,
M. Checchin,
G. Ciovati,
L. D. Cooley,
G. Dalla Lana Semione,
J. Delayen,
G. Eremeev,
F. Furuta,
F. Gerigk,
B. Giaccone,
D. Gonnella,
A. Grassellino,
A. Gurevich,
W. Hillert,
M. Iavarone,
J. Knobloch,
T. Kubo,
W. K. Kwok,
R. Laxdal
, et al. (31 additional authors not shown)
Abstract:
Radio frequency superconductivity is a cornerstone technology for many future HEP particle accelerators and experiments from colliders to proton drivers for neutrino facilities to searches for dark matter. While the performance of superconducting RF (SRF) cavities has improved significantly over the last decades, and the SRF technology has enabled new applications, the proposed HEP facilities and…
▽ More
Radio frequency superconductivity is a cornerstone technology for many future HEP particle accelerators and experiments from colliders to proton drivers for neutrino facilities to searches for dark matter. While the performance of superconducting RF (SRF) cavities has improved significantly over the last decades, and the SRF technology has enabled new applications, the proposed HEP facilities and experiments pose new challenges. To address these challenges, the field continues to generate new ideas and there seems to be a vast room for improvements. In this paper we discuss the key research directions that are aligned with and address the future HEP needs.
△ Less
Submitted 21 August, 2022; v1 submitted 3 April, 2022;
originally announced April 2022.
-
Nb3Sn Superconducting Radiofrequency Cavities: a Maturing Technology for Particle Accelerators and Detectors
Authors:
S. Posen,
M. Liepe,
G. Eremeev,
U. Pudasaini,
C. E. Reece
Abstract:
Nb3Sn superconducting radiofrequency (SRF) cavities have substantial potential for enabling new performance capabilities for particle accelerators for high energy physics (HEP), as well as for RF cavity-based detectors for dark matter, gravitational waves, and other quantum sensing applications. Outside of HEP, Nb3Sn SRF cavities can also benefit accelerators for nuclear physics, basic energy scie…
▽ More
Nb3Sn superconducting radiofrequency (SRF) cavities have substantial potential for enabling new performance capabilities for particle accelerators for high energy physics (HEP), as well as for RF cavity-based detectors for dark matter, gravitational waves, and other quantum sensing applications. Outside of HEP, Nb3Sn SRF cavities can also benefit accelerators for nuclear physics, basic energy sciences, and the industry. In this contribution to Snowmass 2021, we overview the potential, status, and outlook of Nb3Sn SRF cavities.
△ Less
Submitted 13 March, 2022;
originally announced March 2022.
-
Effect of substrate temperature on the growth of Nb3Sn film on Nb by multilayer sputtering
Authors:
Md Nizam Sayeed,
Uttar Pudasaini,
Charles E. Reece,
Grigory V. Eremeev,
Hani E. Elsayed-Ali
Abstract:
Nb3Sn films were fabricated by multilayer sequential sputtering on Nb at substrate temperatures ranging from room temperature to 250 °C. The multilayers were then annealed inside a separate vacuum furnace at 950 °C for 3h. The films material properties were characterized by X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy, atomic force microscopy, and transmiss…
▽ More
Nb3Sn films were fabricated by multilayer sequential sputtering on Nb at substrate temperatures ranging from room temperature to 250 °C. The multilayers were then annealed inside a separate vacuum furnace at 950 °C for 3h. The films material properties were characterized by X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy, atomic force microscopy, and transmission electron microscopy. The films superconducting properties were studied by four-point probe resistivity measurements from room temperature to below the superconducting critical temperature Tc. The highest film Tc was 17.76 K, obtained when the multilayers were deposited at room temperature. A superconducting Nb3Sn thin film with a smoother surface morphology but a lower Tc of 17.58 K was obtained on the film deposited at a substrate temperature of 250 °C.
△ Less
Submitted 19 April, 2022; v1 submitted 15 September, 2021;
originally announced September 2021.
-
Properties of Nb3Sn films fabricated by magnetron sputtering from a single target
Authors:
Md. Nizam Sayeed,
Uttar Pudasaini,
Charles E. Reece,
Grigory V. Eremeev,
Hani E. Elsayed-Ali
Abstract:
Superconducting Nb3Sn films were fabricated on sapphire and fine grain Nb substrates by magnetron sputtering from a single stoichiometric Nb3Sn target. The structural, morphological and superconducting properties of the films annealed for 24 h at temperatures of 800-1000 °C were investigated. The effect of the annealing time at 1000 °C was examined for 1, 12, and 24 h. The film properties were cha…
▽ More
Superconducting Nb3Sn films were fabricated on sapphire and fine grain Nb substrates by magnetron sputtering from a single stoichiometric Nb3Sn target. The structural, morphological and superconducting properties of the films annealed for 24 h at temperatures of 800-1000 °C were investigated. The effect of the annealing time at 1000 °C was examined for 1, 12, and 24 h. The film properties were characterized by X-ray diffraction, scanning electron microscopy, atomic force microscopy, energy dispersive X-ray spectroscopy, and Raman spectroscopy. The DC superconducting properties of the films were characterized by a four-point probe measurement down to cryogenic temperatures. The RF surface resistance of films was measured over a temperature range of 6-23 K using a 7.4 GHz sapphire-loaded Nb cavity. As-deposited Nb3Sn films on sapphire had a superconducting critical temperature of 17.21 K, which improved to 17.83 K when the film was annealed at 800 °C for 24 h. For the films annealed at 1000 °C, the surface Sn content was reduced to ~11.3 % for an annealing time of 12 h and to ~4.1 % for an annealing time of 24 h. The Raman spectra of the films confirmed the microstructural evolution after annealing. The RF superconducting critical temperature of the as-deposited Nb3Sn films on Nb was 16.02 K, which increased to 17.44 K when the film was annealed at 800 °C for 24 h.
△ Less
Submitted 14 July, 2020;
originally announced July 2020.
-
Effect of layer thickness on structural, morphological and superconducting properties of Nb$_3$Sn films fabricated by multilayer sequential sputtering
Authors:
Md Nizam Sayeed,
Uttar Pudasaini,
Charles E Reece,
Grigory V Eremeev,
Hani E Elsayed-Ali
Abstract:
Superconducting Nb3Sn films can be synthesized by controlling the atomic concentration of Sn. Multilayer sequential sputtering of Nb and Sn thin films followed by high temperature annealing is considered as a method to fabricate Nb3Sn films, where the Sn composition of the deposited films can be controlled by the thickness of alternating Nb and Sn layers. We report on the structural, morphological…
▽ More
Superconducting Nb3Sn films can be synthesized by controlling the atomic concentration of Sn. Multilayer sequential sputtering of Nb and Sn thin films followed by high temperature annealing is considered as a method to fabricate Nb3Sn films, where the Sn composition of the deposited films can be controlled by the thickness of alternating Nb and Sn layers. We report on the structural, morphological and superconducting properties of Nb3Sn films fabricated by multilayer sequential sputtering of Nb and Sn films on sapphire substrates followed by annealing at 950 °C for 3 h. We have investigated the effect of Nb and Sn layer thickness and Nb:Sn ratio on the properties of the Nb3Sn films. The crystal structure, surface morphology, surface topography, and film composition were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), and energy dispersive X-ray spectroscopy (EDS). The results showed Sn loss from the surface due to evaporation during annealing. Superconducting Nb3Sn films of critical temperature up to 17.93 K were fabricated.
△ Less
Submitted 22 April, 2020;
originally announced April 2020.
-
Multi-metallic conduction cooled superconducting radio-frequency cavity with high thermal stability
Authors:
G. Ciovati,
G. Cheng,
U. Pudasaini,
R. Rimmer
Abstract:
Superconducting radio-frequency cavities are commonly used in modern particle accelerators for applied and fundamental research. Such cavities are typically made of high-purity, bulk Nb and are cooled by a liquid helium bath at a temperature of ~2 K. The size, cost and complexity of operating a particle accelerator with a liquid helium refrigerator makes the current cavity technology not favorable…
▽ More
Superconducting radio-frequency cavities are commonly used in modern particle accelerators for applied and fundamental research. Such cavities are typically made of high-purity, bulk Nb and are cooled by a liquid helium bath at a temperature of ~2 K. The size, cost and complexity of operating a particle accelerator with a liquid helium refrigerator makes the current cavity technology not favorable for use in industrial-type accelerators. We developed a multi-metallic 1.495~GHz elliptical cavity conductively cooled by a cryocooler. The cavity has a ~2 $μ$m thick layer of Nb$_3$Sn on the inner surface, exposed to the rf field, deposited on a ~3 mm thick bulk Nb shell and a bulk Cu shell, of thickness $\geqslant 5$ mm deposited on the outer surface by electroplating. A bolt-on Cu plate 1.27 cm thick was used to thermally connect the cavity equator to the second stage of a Gifford-McMahon cryocooler with a nominal capacity of 2 W at 4.2 K. The cavity was tested initially in liquid helium at 4.3 K and reached a peak surface magnetic field of ~36 mT with a quality factor of $2\times 10^9$. The cavity cooled by the crycooler achieved a peak surface magnetic field of ~29 mT, equivalent to an accelerating gradient of 6.5 MV/m, and it was able to operate in continuous-wave with as high as 5 W dissipation in the cavity for 1 h without any thermal breakdown. This result represents a paradigm shift in the technology of superconducting accelerator cavities.
△ Less
Submitted 31 January, 2020; v1 submitted 29 January, 2020;
originally announced January 2020.
-
Nb3Sn multicell cavity coating system at JLAB
Authors:
G. Eremeev,
W. Clemens,
K. Macha,
C. E. Reece,
A. M. Valente-Feliciano,
S. Williams,
U. Pudasaini,
M. Kelley
Abstract:
SRF niobium cavities are the building blocks of modern accelerators for scientific applications. Lower surface resistance, higher fields, and high operating temperatures advance the reach of the future accelerators for scientific discovery as well as potentially enabling cost-effective industrial solutions. We describe the design and performance of an Nb$_{3}$Sn coating system that converts the in…
▽ More
SRF niobium cavities are the building blocks of modern accelerators for scientific applications. Lower surface resistance, higher fields, and high operating temperatures advance the reach of the future accelerators for scientific discovery as well as potentially enabling cost-effective industrial solutions. We describe the design and performance of an Nb$_{3}$Sn coating system that converts the inner surface of niobium cavities to Nb$_{3}$Sn film. Niobium surface, heated by radiation from the niobium retort, is exposed to Sn and SnCl$_{2}$ vapor during the heat cycle, which results in about 2 $μ$m Nb$_{3}$Sn film on the niobium surface. Film composition and structure as well as RF properties with 1-cell R\&D cavities and 5-cell practical accelerator cavities are presented.
△ Less
Submitted 11 January, 2020;
originally announced January 2020.
-
Analysis of RF losses and material characterization of samples removed from a Nb3Sn-coated superconducting RF cavity
Authors:
Uttar Pudasaini,
Grigory V. Eremeev,
Charles E. Reece,
James Tuggle,
Michael J. Kelley
Abstract:
Nb3Sn (Tc ~ 18 K and Hsh ~ 400 mT) is a prospective material to replace Nb (Tc ~ 9 K and Hsh ~ 200 mT) in SRF accelerator cavities for significant cost reduction and performance enhancement. Because of its material properties, Nb3Sn is best employed as a thin film (coating) inside an already built RF cavity structure. A particular test cavity noted as C3C4 was a 1.5 GHz single-cell Nb cavity, coat…
▽ More
Nb3Sn (Tc ~ 18 K and Hsh ~ 400 mT) is a prospective material to replace Nb (Tc ~ 9 K and Hsh ~ 200 mT) in SRF accelerator cavities for significant cost reduction and performance enhancement. Because of its material properties, Nb3Sn is best employed as a thin film (coating) inside an already built RF cavity structure. A particular test cavity noted as C3C4 was a 1.5 GHz single-cell Nb cavity, coated with Nb3Sn using Sn vapor diffusion process at Jefferson Lab. Cold measurements of the coated cavity indicated the superconducting transition temperature of about 18 K. Subsequent RF measurements indicated field-dependent surface resistance both at 4.3 K and 2.0 K. After initial cold measurements, the cavity RF loss distribution was studied with a thermometry mapping system. Loss regions were identified with thermometry and were cut out for material analysis. The presence of significantly thin patchy regions and other carbon-rich defects is associated with strong local field-dependent surface resistance. This paper summarizes RF and thermometry results correlated with material science findings.
△ Less
Submitted 12 September, 2019;
originally announced September 2019.
-
Initial Growth Of Tin On Niobium For Vapor Diffusion Coating Of Nb3sn
Authors:
Uttar Pudasaini,
Grigory Eremeev,
Charles Reece,
James Tuggle,
Michael J. Kelley
Abstract:
Nb3Sn has the potential to achieve superior performance in terms of quality factor, accelerating gradient and operating temperature (4.2 K vs 2 K) resulting in significant reduction in both capital and operating costs compared to traditional niobium SRF accelerator cavities. Tin vapor diffusion coating of Nb3Sn on niobium appears to be a simple, yet most efficient technique so far to fabricate suc…
▽ More
Nb3Sn has the potential to achieve superior performance in terms of quality factor, accelerating gradient and operating temperature (4.2 K vs 2 K) resulting in significant reduction in both capital and operating costs compared to traditional niobium SRF accelerator cavities. Tin vapor diffusion coating of Nb3Sn on niobium appears to be a simple, yet most efficient technique so far to fabricate such cavities. Here, cavity interior surface coatings are obtained by a two step process: nucleation followed by deposition. The first step is normally accomplished with Sn/SnCl2 at a constant low temperature (500 °C) for several hours. To elucidate the role of this step, we systematically studied the niobium surface nucleated under varying process conditions. The surfaces obtained in typical tin/tin chloride processes were characterized using SEM/EDS, AFM, XPS, SAM and TEM. Examination of the surfaces nucleated under the standard conditions revealed not only tin particles, but also tin film on the surfaces resembling the surface obtained by Stranski-Krastanov growth mode. All the nucleation attempted with SnCl2 yielded better uniformity of Nb3Sn coating compared to coating obtained without nucleation, which often included random patchy regions with irregular grain structure. Even though the variation of nucleation parameters was able to produce different surfaces following nucleation, no evidence was found for any significant impact on the final coating.
△ Less
Submitted 19 June, 2018; v1 submitted 7 June, 2018;
originally announced June 2018.
-
Secondary ion mass spectrometry for SRF cavity materials
Authors:
J. Tuggle,
U. Pudasaini,
A. S. Palczewski,
C. E. Reece,
F. A. Stevie,
M. J. Kelley
Abstract:
Historically, many advances in superconducting radio frequency (SRF) cavities destined for use in advanced particle accelerators have come empirically, through the iterative procedure of modifying processing and then performance testing. However, material structure is directly responsible for performance. Understanding, the link between processing, structure, and performance will streamline and ac…
▽ More
Historically, many advances in superconducting radio frequency (SRF) cavities destined for use in advanced particle accelerators have come empirically, through the iterative procedure of modifying processing and then performance testing. However, material structure is directly responsible for performance. Understanding, the link between processing, structure, and performance will streamline and accelerate the research process. In order to connect processing, structure, and performance, accurate and robust materials characterization methods are needed. Here one such method, SIMS, is discussed with focus on analysis of SRF materials. In addition, several examples are presented, showing how SIMS is being used to further understanding of materials based SRF technologies.
△ Less
Submitted 21 May, 2018; v1 submitted 20 March, 2018;
originally announced March 2018.