    S235JR is a non-alloy structural steel with a minimum tensile strength of 235 MPa. It has a chemical composition of 0.17% carbon or less, 0.035% phosphorus or less, 0.12% sulfur or less, and other elements. It is available as hot-rolled coils and slit strip in various thicknesses between 1.5-12.7 mm and widths up to 1880 mm. The steel is suitable for cold forming, welding, and applications such as vehicle wheels with close chemical and mechanical property values.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    S235JR Steel

    Uploaded by

    Nguyễn Thanh Cường
    250 views1 page
    S235JR is a non-alloy structural steel with a minimum tensile strength of 235 MPa. It has a chemical composition of 0.17% carbon or less, 0.035% phosphorus or less, 0.12% sulfur or less, and other elements. It is available as hot-rolled coils and slit strip in various thicknesses between 1.5-12.7 mm and widths up to 1880 mm. The steel is suitable for cold forming, welding, and applications such as vehicle wheels with close chemical and mechanical property values.

    Original Description:

    Material

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    S235JR is a non-alloy structural steel with a minimum tensile strength of 235 MPa. It has a chemical composition of 0.17% carbon or less, 0.035% phosphorus or less, 0.12% sulfur or less, and other elements. It is available as hot-rolled coils and slit strip in various thicknesses between 1.5-12.7 mm and widths up to 1880 mm. The steel is suitable for cold forming, welding, and applications such as vehicle wheels with close chemical and mechanical property values.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    250 views1 page

    S235JR Steel

    Uploaded by

    Nguyễn Thanh Cường
    S235JR is a non-alloy structural steel with a minimum tensile strength of 235 MPa. It has a chemical composition of 0.17% carbon or less, 0.035% phosphorus or less, 0.12% sulfur or less, and other elements. It is available as hot-rolled coils and slit strip in various thicknesses between 1.5-12.7 mm and widths up to 1880 mm. The steel is suitable for cold forming, welding, and applications such as vehicle wheels with close chemical and mechanical property values.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    S235JR

    Non-alloy structural steels

    Material no. according to Tensile strength class

    1.0038 DIN EN 10025-2 A

    Mechanical properties 1)
    Nom. thick. e Yield strength R eH 235 MPa 225 MPa

    Available dimensions Hot-rolled coils unpickled, mill edge


    Thickness in mm 1.50 1.79 1.80 1.99 2.00 2.24 2.25 2.49 2.50 2.99 3.00 3.99 4.00 6.00 6.01 12.70 Width in mm 900 1250 900 1390 900 1540 900 1700 900 1880 900 1880 900 1880 900 1880

    16 mm >16 mm

    Usage Suitability for coldforming such as bending, folding, bordering and flanging etc. can be ordered separately. The user of these steel grades must make sure that his calculation, design and processing methods are appropriate for the material. The welding technique used must be suitable for the intended application and comply with the state-of-theart. With distinctly closer chemical composition values and mechanical properties, the steel grades of the S235 S355 series are used as material for wheels of passenger cars, lorries and other vehicles. Chemical composition (in percent by weight)
    min. max. 0.170 % 1.400 % 0.035 % 0.035 % 0.012 % 1) 0.550 % 2) 0.35 %

    Nom. thick. e

    Tensile strength Rm 360 510 MPa 360 510 MPa

    <3 mm 3 mm Nom. thick. e

    Total elong. A 2) (long./trans.) 21/19 % 26/24 %

    <3 mm 3 e 40 mm

    1) The tensile test values given in the table apply to longitudinal samples (l); in case of strip and sheet steel of widths of 600 mm they apply to transverse samples (t). 2) It applies to nominal thickness e: e < 3 mm: A80 e 3 mm: A5

    Hot-rolled slit strip


    Thickness in mm 1.50 1.79 1.80 1.99 2.00 2.24 2.25 7.00 7.01 8.00 Width in mm 100 515 100 635 100 760 100 800 140 800 175 800 233 800

    Min. notch impact energy 1)


    Temperature 20C C Mn P S N Cu CE 3) Min. notch impact energy 27 J

    8.01 9.00 9.01 10.00


    <100 mm on request

    1) Average values of 3 samples; one individual value may fall short of the required minimum value by not more than 30%. The sample width shall equal the product thickness if the latter is between 5 and 10 mm. The tests are performed by using samples similar to Charpy-V samples. The values specified in the table above are to be reduced proportionally to the sample width.

    Welding The steel grades of the JR, JO, J2 and K2 categories are in general suitable for all welding techniques.

    1) The maximum nitrogen content shall not apply if the total aluminium content of the steel is at least 0.020 % or if it contains enough other nitrogenfixing elements. 2) Copper contents higher than 0.400% can cause exfoliation corrosion. 3) Maximum carbon equivalent value CE = C + Mn /6 + (Cr + Mo + V) /5 + (Cu + Ni) /15

    Condition of delivery, scope of testing and certificate The provisions of DIN 10025-2, chapters 6.3 and 8 shall apply for delivery and inspection. Other inspections may be agreed.