Location via proxy:   [ UP ]  
[Report a bug]   [Manage cookies]                
Scribd Logo
Upload

Welcome to Scribd!

  • 91 views

    Bukang Special Industry - Coalloy6, SUS316L, SUS316L BK (20180726)

    Uploaded by

    Việt
    The document provides information on Coalloy 6, a cobalt-based alloy produced by Bukang Special Industries Co., Ltd. Coalloy 6 contains 27-32% chromium, 4-6% tungsten, and 0.9-1.4% carbon. It has a hardness of 36-45HRC or 380-490HV, density of 8.44 g/cm3, and melting range of 2340-2570°F or 1285-1410°C. Coalloy 6 exhibits good wear resistance and retains hardness up to 500°C. It is well-suited for hardfacing and applications like valve seats and pump components. Nominal thermal expansion and mechanical properties are also listed for Coalloy

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Bukang Special Industry - Coalloy6, SUS316L, SUS316L BK (20180726)

    Uploaded by

    Việt
    91 views5 pages
    The document provides information on Coalloy 6, a cobalt-based alloy produced by Bukang Special Industries Co., Ltd. Coalloy 6 contains 27-32% chromium, 4-6% tungsten, and 0.9-1.4% carbon. It has a hardness of 36-45HRC or 380-490HV, density of 8.44 g/cm3, and melting range of 2340-2570°F or 1285-1410°C. Coalloy 6 exhibits good wear resistance and retains hardness up to 500°C. It is well-suited for hardfacing and applications like valve seats and pump components. Nominal thermal expansion and mechanical properties are also listed for Coalloy

    Original Description:

    special 316L

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    The document provides information on Coalloy 6, a cobalt-based alloy produced by Bukang Special Industries Co., Ltd. Coalloy 6 contains 27-32% chromium, 4-6% tungsten, and 0.9-1.4% carbon. It has a hardness of 36-45HRC or 380-490HV, density of 8.44 g/cm3, and melting range of 2340-2570°F or 1285-1410°C. Coalloy 6 exhibits good wear resistance and retains hardness up to 500°C. It is well-suited for hardfacing and applications like valve seats and pump components. Nominal thermal expansion and mechanical properties are also listed for Coalloy

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    91 views5 pages

    Bukang Special Industry - Coalloy6, SUS316L, SUS316L BK (20180726)

    Uploaded by

    Việt
    The document provides information on Coalloy 6, a cobalt-based alloy produced by Bukang Special Industries Co., Ltd. Coalloy 6 contains 27-32% chromium, 4-6% tungsten, and 0.9-1.4% carbon. It has a hardness of 36-45HRC or 380-490HV, density of 8.44 g/cm3, and melting range of 2340-2570°F or 1285-1410°C. Coalloy 6 exhibits good wear resistance and retains hardness up to 500°C. It is well-suited for hardfacing and applications like valve seats and pump components. Nominal thermal expansion and mechanical properties are also listed for Coalloy

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 5

    Bukang special industries Co., Ltd.

    Tel : 82-54-335-9997~9
    Fax : 82-54-335-9996
    E-mail : export@bkcoalloy.co.kr
    Homepage : www.bkcoalloy.co.kr
    Coalloy 6 (Stellite 6 eq)
    Nominal composition(mass%) and Physical
    Properties
    Co Cr W C Others Hardness Density Melting Range

    27 - 0.9 – Ni, Fe, Si 36 - 45HRC 8.44 g/cm3 2340-2570℉


    Base 4-6
    32 1.4 Mn, Mo 380 - 490HV 0.305 lb/in3 1285-1410℃

    Coalloy 6 is the most widely used of the wear resistant cobalt


    based alloys and exhibits good all-round performance.
    It is regarded as the industry standard for general-purpose wear
    resistance applications, has excellent resistance to many forms of
    mechanical and chemical degradation over a wide temperature
    range, and retains a reasonable level of hardness up
    to 500°C (930°F). It also has good resistance to impact and
    cavitation erosion. Coalloy 6 is ideally suited to a variety of
    hardfacing processes and can be turned with carbide tooling.
    Examples include valve seats and gates; pump shafts and
    bearings, erosion shields and rolling couples.
    It is often used self-mated.
    Scanning Electron Micrograph of Cast Coalloy 6 at 1000x magnification .

    BUKANG SPECIAL INDUSTRIES CO., LTD


    Nominal Thermal Expansion Coefficient (from 20°C/68°F to stated
    temperature)
    100℃ 200℃ 300℃ 400℃ 500℃ 600℃ 700℃ 800℃ 900℃ 1000℃
    (212℉) (392℉) (572℉) (752℉) (932℉) (1112℉) (1292℉) (1472℉) (1652℉) (1832℉)

    ㎛/m.k 11.35 12.95 13.6 13.9 14.2 14.5 14.7 15.05 15.5 17.5

    µinch/inch℉
    6.31 7.20 7.56 7.72 7.89 8.06 8.17 8.36 8.61 9.72

    Nominal Tensile Properties at Room Temperature


    Ultimate Tensile Strength Rm Yield Stress Rp(0.2%) Elongation Elastic Modulus

    Ksi MPa Ksi MPa A(%) psi GPa


    Casting 123 850 101.5 700 <1 30.3x106 209

    HS-6 183.5 1265 109 750 3-5 34x106 237

    Nominal Hot Hardness (DPH) as-cast


    20℃ 100℃ 200℃ 300℃ 400℃ 500℃ 600℃ 700℃ 800℃ 900℃
    (68℉) (212℉) (391℉) (572℉) (752℉) (932℉) (1112℉) (1292℉) (1472℉) (1652℉)

    410 390 356 345 334 301 235 155 138 95

    BUKANG SPECIAL INDUSTRIES CO., LTD


    JIS G 4303 SUS 316L & SUS316

    Composition(mass%) and Physical Properties

    % Fe C Si Mn P S Ni Cr Mo

    SUS316L Base ≤0.030 ≤1.00 ≤2.00 ≤0.045 ≤0.030 12~15 16~18 2~3

    0.08 0.045 0.030


    SUS316 Base 1.00 max. 2.00 max. 10~14 16~18 2~3
    max. max. max.

    Yield Strength(N/㎟) Tensile Strength(N/㎟) Elongation(%) Reduction of Area(%)

    175 min 480 min 40 min 50 min

    205 min 520 min 40 min 60 min


    SUS316L BK
    Composition(mass%)
    % Fe C Si Mn P S Ni Cr

    SUS316L BK Base 0.5~0.65 1.75~2.25 0.75~1.5 Max 0.025 Max 0.025 10~14 22~26