Fosroc Renderoc LA55 constructive solutions

Single component free flowing low alkali micro concrete

Uses Properties

The high fluid nature of Renderoc LA55 obviates the need The following typical results were obtained at a water to
for compaction and vibration and are most suitable for: powder ratio of 0.133 and temperature of 20ºC.
Test method Typical result
 Repair zones with restricted access or congested
Compressive strength : > 25 N/mm2 at 3 days
reinforcement
(BS 1881 Pt.116 )
1
> 45 N/mm2 at 7 days
 Reinstatement of large, strctural sections of concrete > 55 N/mm2 at 28 days

 Repairs to concrete effected by alkali-silica reaction

Note : The low permeability of Renderoc LA55 retards
 Areas where excellent chloride and carbon-di-oxide chemical attack in aggressive environments. The
resistance is required cured micro-concrete is resistant to acid gases,
chloride ions, oxygen and water. For specific data
Advantages regarding chemical resistance, contact the local
Fosroc office.
 Dual expansion system compensates for shrinkage in the
plastic and hardened states.
Design criteria
 Low alkali content minimises risk of alkali-silica reaction
Renderoc LA55 is designed for large volume repairs typically
 Exceptional bond to concrete substrates without inde- in excess of 50mm deep. The product can be applied at
pendent primer sections generally upto 150 mm thick although greater
thicknesses may be achievable dependent on the repair
 Suitable for placement by pumping or pouring techniques
geometry. Attention to the basic design criteria given below
into restricted locations
should ensure that the full benefits of this technology are
 Self-compacting nature eliminates honeycombing and gained in use :
displaces air without vibration
(i) Water addition = 3.33 ltrs / 25kg bag Under no circum-
 High strength and low permeability provide maximum stances should part bags be used or additional water be
protection against carbon-di-oxide and chlorides employed. Either of these two actions will adversely
affect material performance, automatically invalidating
 Pre-bagged to overcome site-batched variations - only
Fosroc’s standard product guarantee.
the site addition of clean water is required

 Contains no chloride admixtures

Description

Renderoc LA55 is supplied as a ready to use blend of dry

powders which requires only the site addition of clean water
to produce a free-flowing, shrinkage compensated mi-
cro-concrete suitable for large volume concrete repairs at
nominal thicknesses in excess of 50mm.

Specification

The fluid repair system (micro-concrete) shall be

Renderoc LA55, a single component, low-alkali ce-
ment-based blend of powders to which only the site-addition
of clean water shall be permitted. The micro-concrete shall
exhibit compressive strength of not less than 45N/mm² at 7
Renderoc LA55

days and not less than 55N/mm² at 28 days.

Fosroc Renderoc LA55

Method Statement Storage

Refer to your local Fosroc office for the method statement Shelf life
specifying surface preparation, priming, mixing, application
Renderoc LA55 has a shelf life of 12 months; if kept in a dry
and cleaning methods.
environment, in its original, unopened packing. If stored in
conditions of high humidity and/or temperature, the shelf life
Estimating
of Renderoc LA55 will be reduced to as little as 4 months.
Supply
Renderoc LA55 : 25kg bags Precautions

Coverage Health and safety

Actual coverage rate is approximate, and will be wholly Renderoc LA55 contains cement powders which, when
dependent upon the general substrate condition. It is mixed with water or upon becoming damp, release alkalis
recommended, therefore, that site trials over a typical area which can be harmful to the skin.
are conducted to determine the likely usage/coverage rates
During use, avoid inhalation of the dust and contact with the
for a particular substrate.
Renderoc LA55 : 12 litres/25kg bag skin or eyes. Wear suitable protective clothing - eye protec-
tion, gloves and respiratory equipment (particularly in
confined spaces).
Limitations
The use of barrier creams to provide additional skin protec-
- Renderoc LA55 should not be used when the ambient
tion is also advised. In case of contact with the skin, rinse
temperature is below 5°C and falling.
with plenty of clean water, then cleanse thoroughly with soap
- Renderoc LA55 should not be part mixed. and water.

- Renderoc LA55 should not be exposed to running water In case of contact with eyes, rinse immediately with plenty of
either during application or prior to final set. clean water and seek medical advice. If swallowed seek
medical attention immediately - do not induce vomiting.
- Water ponding is not recommended for curing.
Fire

Renderoc LA55 is non-flammable and thus presents no fire

hazard.

For further information, please refer to the Product Material

Safety Data Sheets.

* Denotes the trademark of Fosroc International Limited

†
See separate data sheet

Important note
Fosroc products are guaranteed against defective materials and manufacture and are sold subject to its standard Conditions for the Supply of
Goods and Service. All Fosroc datasheets are updated on a regular basis. It is the user’s responsibility to obtain the latest version.

Head Office
telephone: (+9714) 2039699 fax: (+9714) 2859649 email: agf@fosroc.com
Al Gurg Fosroc LLC
Regional offices
Post Box 657, Dubai Abu Dhabi, Al Gurg Fosroc telephone: 673 1779 fax: 673 1449 email: abudhabi@fosroc.com
Bahrain, YBA Kanoo telephone: 17738200 fax: 17732828 email: bahrain@fosroc.com
United Arab Emirates Kuwait, Boodai telephone: 4817618 fax: 4832124 email: kuwait@fosroc.com
Oman, Al Amana telephone: 24815080 fax: 24817554 email: oman@fosroc.com
www.fosroc.com

UAE/0741/12/A