KTL-24-WS-C-M-197 Levcon

Sample Received On: 12.06.2024 ULR NO.
: TC1377224000000197F
Heat No.: J-2 T.R. No.: KTL/24/WS/C/M/197
Sample Description: 01 No. Stainless Steel Test Bar (SL. No.-1) Tested On: 12-17.06.2024
Specification: ASTM A 351 CF3 T.R. Date: 17.06.2024
Issued To: M/s. Levcon Valves Private Limited
52/1/A, Natobar Paul Road, Howrah-711 101.
*This is to certify that the above sample(s) has/have been tested within the following results*
CHEMICAL ANALYSIS BY SPECTRO & MECHNICAL TEST

Test Details Obtained Value Specified Value
C% 0.0135 0.03 Max
Mn% 1.0312 1.50 Max
Si% 1.3312 2.00 Max
S% 0.0231 0.040 Max
P% 0.0154 0.040 Max
Cr% 18.1045 17.00-21.00
Ni% 9.1244 8.00-12.00
Mo% 0.2603 0.50 Max
U.T.S. (MPa) 560 485 Min
Y.S. (MPa) 282 205 Min
E% on G.L. 50 mm
41.48 30.00 Min
(Longitudinal Direction)
Statement of Conformity: The above test results obtained conform to the specified value.
Test Method: IS: 9879/1998 & IS: 1608(P-1):2022

Temperature: 24.20C & Humidity: 49%
Decision Rule Employed.
Tested sample Return Page No. 01 of 11
SB
Sample Received On: 12.06.2024 ULR NO.: TC1377224000000197F
Heat No.: J-3 T.R. No.: KTL/24/WS/C/M/197
Sample Description: 01 No. Stainless Steel Test Bar (SL. No.-2) Tested On: 12-17.06.2024
Specification: ASTM A 351 CF3 T.R. Date: 17.06.2024
CHEMICAL ANALYSIS BY SPECTRO & MECHNICAL TEST

C% 0.0126 0.03 Max
Mn% 1.0269 1.50 Max
Si% 1.3288 2.00 Max
S% 0.0224 0.040 Max
P% 0.0147 0.040 Max
Cr% 18.0845 17.00-21.00
Ni% 9.1374 8.00-12.00
Mo% 0.2588 0.50 Max
U.T.S. (MPa) 568 485 Min
Y.S. (MPa) 288 205 Min
E% on G.L. 50 mm
43.16 30.00 Min
(Longitudinal Direction)
Test Method: IS: 9879/1998 & IS: 1608(P-1):2022

SB
Heat No.: xxx T.R. No.: KTL/24/WS/C/M/197
Sample Description: 01 No. Cut Piece from SS Plate (SL. No.-3) Tested On: 12-17.06.2024
Specification: ASTM A 240/2023 Type 304L T.R. Date: 17.06.2024
CHEMICAL ANALYSIS BY SPECTRO & MECHANICAL TEST

C% 0.0198 0.030 Max
Si% 0.6586 0.75 Max
Mn% 1.3142 2.00 Max
P% 0.0214 0.045 Max
S% 0.0168 0.030 Max
Cr% 18.5741 18.00-20.00
Ni% 9.4214 8.00-12.00
U.T.S. (MPa) 540 485 Min
Y.S. (MPa) 224 170 Min
E% on G.L. 50 mm 42.76 40.00 Min
Test Method: IS: 9879:1998 & ASTM A370:2020

SB
Sample Description: 01 No. 28mm dia SS Rod (SL. No.-4) Tested On: 12-17.06.2024
Specification: ASTM A 276-2023, Type-304L [Hot Finished] T.R. Date: 17.06.2024

C% 0.0215 0.030 Max
Si% 0.6412 1.00 Max
Mn% 1.1204 2.00 Max
P% 0.0203 0.045 Max
S% 0.0184 0.030 Max
Cr% 19.4621 18.00-20.00
Ni% 9.5743 8.00-12.00
U.T.S. (MPa) 568 485 Min
Y.S. (MPa) 279 170 Min
E% on G.L. 50 mm 45.16 40.00 Min
RA% 55.36 50.00 Min

SB

C% 0.0184 0.030 Max
Si% 0.5845 1.00 Max
Mn% 1.1149 2.00 Max
P% 0.0189 0.045 Max
S% 0.0144 0.030 Max
Cr% 19.5471 18.00-20.00
Ni% 9.4682 8.00-12.00
U.T.S. (MPa) 554 485 Min
Y.S. (MPa) 270 170 Min
E% on G.L. 50 mm 44.46 40.00 Min
RA% 54.84 50.00 Min

SB

C% 0.0164 0.030 Max
Si% 0.6423 1.00 Max
Mn% 1.2086 2.00 Max
P% 0.0193 0.045 Max
S% 0.0168 0.030 Max
Cr% 19.3841 18.00-20.00
Ni% 9.4534 8.00-12.00
U.T.S. (MPa) 578 485 Min
Y.S. (MPa) 294 170 Min
E% on G.L. 50 mm 45.06 40.00 Min
RA% 54.68 50.00 Min

SB

C% 0.0188 0.030 Max
Si% 0.7480 1.00 Max
Mn% 1.1338 2.00 Max
P% 0.0229 0.045 Max
S% 0.0178 0.030 Max
Cr% 19.2385 18.00-20.00
Ni% 9.5564 8.00-12.00
U.T.S. (MPa) 573 485 Min
Y.S. (MPa) 288 170 Min
E% on G.L. 50 mm 44.94 40.00 Min
RA% 54.32 50.00 Min

SB

C% 0.0202 0.030 Max
Si% 0.7456 1.00 Max
Mn% 1.3748 2.00 Max
P% 0.0205 0.045 Max
S% 0.0184 0.030 Max
Cr% 19.2082 18.00-20.00
Ni% 9.4094 8.00-12.00
U.T.S. (MPa) 586 485 Min
Y.S. (MPa) 276 170 Min
E% on G.L. 50 mm 44.14 40.00 Min
RA% 54.70 50.00 Min

SB
Heat No.: V-1 T.R. No.: KTL/24/WS/C/M/197
Sample Description: 02 Nos. Forged Stainless Steel (SL. No.-9) Tested On: 12-17.06.2024
Specification: ASTM A 182-2021, Type-F304L T.R. Date: 17.06.2024

C% 0.0192 0.030 Max
Si% 0.7512 1.00 Max
Mn% 1.4015 2.00 Max
P% 0.0222 0.045 Max
S% 0.0171 0.030 Max
Cr% 19.3216 18.00-20.00
Ni% 9.5102 8.00-13.00
U.T.S. (MPa) 574 485 Min
Y.S. (MPa) 262 170 Min
E% on G.L. 50 mm 43.22 30.00 Min
RA% 55.08 50.00 Min
Bend Test
Satisfactory Shall Pass the Test
(1800 at 2t)

SB
Heat No.: D-6 T.R. No.: KTL/24/WS/C/M/197
Sample Description: 01 Nos. Cast Iron Test Bar (SL. No.-10) Tested On: 12-17.06.2024
Specification: IS: 210:2009, FG:220 T.R. Date: 17.06.2024
MECHANICAL TEST

U.T.S. (MPa) 264 220 Min
Hardness (Avg.)
210 180 – 220
HBW (10/3000/15sec)
Test Method: IS: 1608(P-1):2022 & IS: 1500(P-1):2019

Tested sample Return
Page No. 10 of 11
SB
Heat No.: C-56 T.R. No.: KTL/24/WS/C/M/197
Sample Description: 01 Nos. Cast Iron Test Bar (SL. No.-11) Tested On: 12-17.06.2024
Specification: IS: 210:2009, FG:200 T.R. Date: 17.06.2024
MECHANICAL TEST

U.T.S. (MPa) 262 200 Min
Hardness (Avg.)
198 160 – 220
HBW (10/3000/15sec)
Test Method: IS: 1608(P-1):2022 & IS: 1500(P-1):2019

Tested sample Return
Page No. 10 of 11
SB
*** End of the Report***

KTL-24-WS-C-M-197 Levcon

Uploaded by

Copyright:

Available Formats

KTL-24-WS-C-M-197 Levcon

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

KTL-24-WS-C-M-197 Levcon

Uploaded by

Copyright:

Available Formats

Sample Received On: 12.06.2024 ULR NO.

CHEMICAL ANALYSIS BY SPECTRO & MECHNICAL TEST

Test Method: IS: 9879/1998 & IS: 1608(P-1):2022

Tested sample Return Page No. 01 of 11

CHEMICAL ANALYSIS BY SPECTRO & MECHNICAL TEST

Test Method: IS: 9879/1998 & IS: 1608(P-1):2022

Tested sample Return Page No. 02 of 11

CHEMICAL ANALYSIS BY SPECTRO & MECHANICAL TEST

Test Method: IS: 9879:1998 & ASTM A370:2020

Tested sample Return Page No. 03 of 11

CHEMICAL ANALYSIS BY SPECTRO & MECHANICAL TEST

Test Details Obtained Value Specified Value

Test Method: IS: 9879:1998 & ASTM A370:2020

Tested sample Return Page No. 04 of 11

CHEMICAL ANALYSIS BY SPECTRO & MECHANICAL TEST

Test Details Obtained Value Specified Value

Test Method: IS: 9879:1998 & ASTM A370:2020

Tested sample Return Page No. 05 of 11

CHEMICAL ANALYSIS BY SPECTRO & MECHANICAL TEST

Test Details Obtained Value Specified Value

Test Method: IS: 9879:1998 & ASTM A370:2020

Tested sample Return Page No. 06 of 11

CHEMICAL ANALYSIS BY SPECTRO & MECHANICAL TEST

Test Details Obtained Value Specified Value

Test Method: IS: 9879:1998 & ASTM A370:2020

Tested sample Return Page No. 07 of 11

CHEMICAL ANALYSIS BY SPECTRO & MECHANICAL TEST

Test Details Obtained Value Specified Value

Test Method: IS: 9879:1998 & ASTM A370:2020

Tested sample Return Page No. 08 of 11

CHEMICAL ANALYSIS BY SPECTRO & MECHANICAL TEST

Test Details Obtained Value Specified Value

Test Method: IS: 9879:1998 & ASTM A370:2020

Tested sample Return Page No. 09 of 11

Test Details Obtained Value Specified Value

Test Method: IS: 1608(P-1):2022 & IS: 1500(P-1):2019

Tested sample Return

Test Details Obtained Value Specified Value

Test Method: IS: 1608(P-1):2022 & IS: 1500(P-1):2019

Tested sample Return