CARLSON ALLOY NITRONIC® 60 (UNS S21800) PRODUCT DATA BULLETIN

Galling and wear resistant austenitic stainless steel that provides a signi cantly lower
cost alternative to cobalt-bearing and high nickel alloys. Corrosion resistance superior to
304 in most media. Approximately twice the yield strength of 304 and 316. Possesses
excellent high temperature oxidation resistance and low temperature impact resistance.

GENERAL PROPERTIES AND TYPICAL APPLICATIONS

Nitronic® 60 is an anti-galling and wear resistant austenitic stainless occurs rst followed by dimensional loss due to wear and nally
steel. It provides a signi cantly lower cost alternative to combat corrosion. Although the general corrosion resistance of Nitronic® 60
wear and galling when compared with cobalt-bearing and high is not as good as 316, it does o er better chloride pitting, stress
nickel alloys. The uniform corrosion resistance of Nitronic® 60 is corrosion cracking and crevice corrosion resistance.
superior to 304 in most media. Chloride pitting resistance is superior In high temperature service, Nitronic® 60 exhibits carburization
to 316. Room temperature yield strength is nearly twice that of 304 superior to 316L and 309. It’s oxidation resistance is far superior
and 316. Nitronic® 60 also possesses excellent high temperature to 304 and 316 and comparable to 309.
oxidation resistance and low temperature impact resistance.
APPLICATIONS:
Due to its grain structure, the galling resistance of Nitronic® 60 is
superior to that of any other stainless steel. It resists wear, tearing Infrastructure bridge pin and hanger expansion joints, parking deck
or freeze up of both the primary and contact materials over a wide expansion joint wear plates.
range of service temperatures. The elevated temperature wear Hydroelectric Power – stems, wicket gate wear rings.
resistance of Nitronic® 60 is excellent despite its relatively low Oil and Gas Production – pump wear rings, bushings, valve trim,
hardness when compared with cobalt and nickel-base wear alloys. seals, ttings, logging equipment and screens.
It also performs well in metal-to-metal wear in nominally inert
atmospheres. The cavitation erosion resistance of Nitronic® 60 is Food Processing and Pharmaceuticals – galling resistant
superior to the austenitic stainless steels as well as high strength applications in sanitary equipment where lubricants can not be used.
duplex (ferritic-austenitic) stainless steels. Chemical and Petrochemical – process valve stems, seats and trim,
The general corrosion resistance of Nitronic® 60 falls between 304 pump wear rings.
and 316. However, in a wear system, a galling or seizure failure

CHEMICAL COMPOSITION NOMINAL ANALYSIS, PERCENT

Carbon, max. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .0.10 Phosphorus, max. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .0.060
Manganese . . . . . . . . . . . . . . . . . . . . .8.00 min. – 9.00 max. Chromium . . . . . . . . . . . . . . . . . . . .16.00 min. – 18.00 max.
Silicon . . . . . . . . . . . . . . . . . . . . . . . . .3.50 min. – 4.50 max. Nickel . . . . . . . . . . . . . . . . . . . . . . . . . .8.00 min. – 9.00 max.
Sulfur, max. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .0.030 Nitrogen . . . . . . . . . . . . . . . . . . . . . . .0.08 min. – 0.18 max.
Iron . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . Balance
ALLOY NITRONIC® 60 (UNS S21800) PRODUCT DATA BULLETIN

AVAILABLE PRODUCTS*
Plate 3/16”and thicker. Widths to 126”, lengths to 480” For larger dimensions – inquire.
Plate Products cut bar, plasma cut or machined rings and discs, heads, rolled and tack-welded cylinders, and special cut shapes
* Bar, billet, ingot and master alloy pigs are available from: ELECTRALLOY, a G.O. Carlson Inc. company, 175 Main Street, Oil City, PA 16301 (800) 458-7273

MECHANICAL AND PHYSICAL PROPERTIES

Tensile Strength, ksi, min. 95
Yield Strength (0.2% o set), ksi, min. 50
Elongation in 2 in. (50.8 mm), or 4D, %, min. 35
Hardness, Brinell, max. 241
Rockwell B, max. 100
Density, grams per cu. cm 7.62
Electrical Resistivity, mirohm-cm 98.2
Modulus of Elasticity, tension, psi x 10 6 26.2
Coe cient of Thermal Expansion, in./ in. /˚Fx10-6
75˚ to 200˚F 8.8
75˚ to 400˚F 9.2
75˚ to 600˚F 9.6
75˚ to 800˚F 9.8
75˚ to 1000˚F 10.0
75˚ to 1200˚F 10.3
75˚ to 1400˚F 10.5
75˚ to 1600˚F 10.7
75˚ to 1800˚F 11.0

GALLING RESISTANCE
Unlubricated Galling Resistance of Stainless Steels
Threshold Galling Stress in ksi (MPa) (Stress at which galling began)
Condition
Nominal Hardness Nitronic® Nitronic®
(Brinell) 410 416 430 440C 303 304 316 17-4 32 60
Hardened & Stress
Relieved (352) – 410 3 (21) 4 (28) 3 (21) 3 (21) 4 (28) 2 (14) 2 (14) 3 (21) 46 (317) 50+ (345)
Hardened & Stress
Relieved (342) – 416 4 (28) 13 (90) 3 (21) 21 (145) 9 (62) 24 (165) 42 (290) 2 (14) 45 (310) 50+ (345)
Annealed (159) – 430 3 (21) 3 (21) 2 (14) 2 (14) 2 (14) 2 (14) 2 (14) 3 (21) 8 (56) 36 (248)
Hardened & Stress
Relieved (560) – 440C 3 (21) 21 (145) 2 (14) 11 (76) 5 (34) 3 (21) 37 (255) 3 (21) 50+ (345) 50+ (345)
Annealed (153) – 303 4 (28) 9 (62) 2 (14) 5 (34) 2 (14) 2 (14) 3 (21) 3 (21) 50+ (345) 50+ (345)
Annealed (140) – 304 2 (14) 24 (165) 2 (14) 3 (21) 2 (14) 2 (14) 2 (14) 2 (14) 30 (207) 50+ (345)
Annealed (150) – 316 2 (14) 42 (290) 2 (14) 37 (255) 3 (21) 2 (14) 2 (14) 2 (14) 3 (21) 38 (262)
H 950 (415) – 17-4 PH 3 (21) 2 (14) 3 (21) 3 (21) 2 (14) 2 (14) 2 (14) 2 (14) 50+ (345) 50+ (345)
Annealed (235)
Nitronic® 32 46 (317) 45 (310) 8 (55) 50+ (345) 50 + (345) 30 (207) 3 (21) 50+ (345) 30 (207) 50+ (345)
Annealed (205)
Nitronic® 60 50+ (345) 50+ (345) 36 (248) 50+ (345) 50+ (345) 50+ (345) 38 (262) 50+ (345) 50+ (345) 50+(345)

+ Did Not Gall (Note: Condition and Harness apply to both horizontal and vertical axes.)
ALLOY NITRONIC® 60 (UNS S21800) PRODUCT DATA BULLETIN

WEAR RESISTANCE
Wear Compatibility of Stainless Steel Couples
Weight Loss, mg./1000 cycles

Alloy vs. 304 316 17-4PH Nitronic®32 Nitronic® 50 Nitronic® 60 440C

Hardness
Rockwell B99 B91 C43 B95 B99 B95 C57

304 12.8

316 10.5 12.5

17-4 24.7 18.5 52.8

Nitronic® 32 8.4 9.4 17.2 7.4

Nitronic® 50 9.0 9.5 15.7 8.3 10.0

Nitronic® 60 6.0 4.3 5.4 3.2 3.5 2.8

440C 4.1 3.9 11.7 3.1 4.3 2.4 3.8

CORROSION RESISTANCE
Nitronic® 60 304 316 17-4 PH
Media Annealed Annealed Annealed (H 925)

65% Boiling HNO3 0.060 in./yr. 0.012 in./yr. 0.012 in./yr. 0.132 in./yr.

1% HCI @ 35˚C 0.010 in./yr. 0.053 in./yr. – 0.024 in./yr.

2% H2SO4 @ 80˚C 0.045 in./yr. 0.243 in./yr. 0.011 in./yr. 0.021 in./yr.
5% H2SO4 @ 80˚C 0.521 in./yr. 1.300 in./yr. 0.060 in./yr. –

10% FeCI3 @ room temp 0.004 g./in.2 0.065 g./in.2 0.011 g./in.2 0.154 g./in.2
(pitting test) 50 Hours No Pits Pitted Pitted Pitted

10% FeCI3 @ R T with 0.024 g./in.2 0.278 g./in.2 0.186 g./in.2 –

arti cial crevices 50 Hours Slight Heavy Heavy –

5% Formic Acid @ 80˚C < .001 in./yr. 0.081 in./yr. < .001 in./yr. 0.001 in./yr.

33% Boiling Acetic Acid 0.011 in./yr. 0.151 in./yr. < .001 in./yr. 0.006 in./yr.

70% Hydrazine
168˚F (76˚C), 72 Hours No reaction – Passed

5% Salt Spray @ 95˚F (35˚C) Nitronic® 60 exhibited resistance to general rusting comparable to 304
120 Hours
ALLOY NITRONIC® 60 (UNS S21800) PRODUCT DATA BULLETIN

CARBURIZATION RESISTANCE
UTS 0.2% YS Elongation Reduction Bend
Alloy ksi (MPa) ksi (MPa) % in 4xD of Area % 1.5T

Nitronic® 60 Unexposed 116.0 (800) 49.5 (341) 74.0 66.3 180˚

Exposed 91.5 (630) 58.0 (400) 19.0 21.6 100˚

316L Unexposed 76.0 (524) 30.0 (207) 68.0 74.4 180˚

Exposed 65.0 (448) 36.0 (248) 24.0 21.3 100˚

309 Unexposed 99.0 (683) 41.0 (283) 54.0 64.7 180˚

Exposed 85.5 (589) 45.5 (313) 14.0 11.9 75˚
Conditions: Duplicate tests exposed at 1800ºF (982ºC) for 2 hours in packed 90% graphite + 10% sodium carbonate.

OXIDATION RESISTANCE
Static Oxidation Resistance
Weight Loss, mg./cm2

Test Temperature, F (C) RA 333 310 Nitronic® 60 304

2100 (1149) Before Descaling 3.1 4.6 16.5 1220

After Descaling 12.2 15.7 23.2 1284

2200 (1204) Before Descaling 10.1 10.1 26.1 2260

After Descaling 16.7 20.6 35.4 2265

SPECIFICATIONS
ASME SA240 / ASTM A240
ASTM A276 (Chemistry Only) / ASME SA276 (Chemistry Only)
Information in this product data bulletin is not intended for speci cation purposes. All data should be
considered as typical or average, except when listed as minimum or maximum values.
The applications cited will allow a potential user to consider this Carlson alloy for a particular installation.
But none of the information is to be construed as a warranty of tness for any application.
As with all special-service materials, this alloy must be tested under actual service conditions to determine
its suitability for a speci c project.

Unsurpassed experience with specialty metals

350 Marshallton-Thorndale Road • Downingtown, PA 19335-2063 • Toll Free (800) 338-5622 (All USA & Canada)
Telephone (610) 384-2800 • Fax (610) 383-3429
©2016 G.O. Carlson, Inc. Printed in U.S.A. 04/2016