    Utp A 3444 - 2

    Uploaded by

    Sun Sun
    Utp A 3444 is a copper aluminium multi-bronze alloy with high nickel and iron additions. It is resistant to seawater and cavitation, making it suitable for applications with simultaneous stress, strain, seawater exposure, cavitation, and erosion. The weld metal has a yield strength of 400 MPa, tensile strength of 700 MPa, and elongation of 15%. Proper welding requires grinding or blasting the seam area to achieve a bright, metallic surface and avoid cracks or pores.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Utp A 3444 - 2

    Uploaded by

    Sun Sun
    159 views1 page
    Utp A 3444 is a copper aluminium multi-bronze alloy with high nickel and iron additions. It is resistant to seawater and cavitation, making it suitable for applications with simultaneous stress, strain, seawater exposure, cavitation, and erosion. The weld metal has a yield strength of 400 MPa, tensile strength of 700 MPa, and elongation of 15%. Proper welding requires grinding or blasting the seam area to achieve a bright, metallic surface and avoid cracks or pores.

    Original Description:

    electrode

    Original Title

    UTP A 3444_2

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Utp A 3444 is a copper aluminium multi-bronze alloy with high nickel and iron additions. It is resistant to seawater and cavitation, making it suitable for applications with simultaneous stress, strain, seawater exposure, cavitation, and erosion. The weld metal has a yield strength of 400 MPa, tensile strength of 700 MPa, and elongation of 15%. Proper welding requires grinding or blasting the seam area to achieve a bright, metallic surface and avoid cracks or pores.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    159 views1 page

    Utp A 3444 - 2

    Uploaded by

    Sun Sun
    Utp A 3444 is a copper aluminium multi-bronze alloy with high nickel and iron additions. It is resistant to seawater and cavitation, making it suitable for applications with simultaneous stress, strain, seawater exposure, cavitation, and erosion. The weld metal has a yield strength of 400 MPa, tensile strength of 700 MPa, and elongation of 15%. Proper welding requires grinding or blasting the seam area to achieve a bright, metallic surface and avoid cracks or pores.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    UTP A 3444

    solid wire

    Classifications
    EN ISO 24373 AWS A5.7 Material-No.
    S Cu 6328 (CuAl9Ni5Fe3Mn2) ER CuNiAl 2.0923
    Characteristics and field of use
    UTP A 3444 is a copper aluminium multi bronzes with a high Ni and Fe addition.
    Weld cladding on cast iron materials and steel. Mixed joints with aluminium bronze steel.
    It is resistant to seawater and cavitation resistant.

    The weld metal of UTP A 3444 is resistant to seawater and cavitation. Good suitability for
    simultaneous stress strain caused by seawater, cavitation and erosion.

    Typical analysis in %
    Mn Ni Cu Al Fe
    1.0 4.5 balance 9.0 3.5
    Mechanical properties of the weld metal
    Yield Tensile El. conduc-
    Elongation A5 Hardness Melting range
    strength RP0.2 strength Rm tivity
    MPa MPa % HB s·m/mm2 °C
    400 700 15 200 4 1015 – 1045
    Welding instruction
    The weld seam area has to be machined to a metallic bright by grinding, sand blasting or pickling in
    order to avoid crack formation or the development of pores.

    Wire diameter [mm] Current type Shielding gas (EN ISO 14175)
    1.0 DC (+) I1
    1.2 DC (+) I1
    1.6 DC (+) I1

    All information provided is based upon careful investigation and intensive research. 03/2014 Rev. 0
    However, we do not assume any liability for correctness and information is subject to change without notice. www.voestalpine.com/welding